CN102618694A - 一种精炼保温覆盖剂及其制备方法 - Google Patents

一种精炼保温覆盖剂及其制备方法 Download PDF

Info

Publication number
CN102618694A
CN102618694A CN2012100946349A CN201210094634A CN102618694A CN 102618694 A CN102618694 A CN 102618694A CN 2012100946349 A CN2012100946349 A CN 2012100946349A CN 201210094634 A CN201210094634 A CN 201210094634A CN 102618694 A CN102618694 A CN 102618694A
Authority
CN
China
Prior art keywords
parts
covering agent
heat insulation
preparation
agent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2012100946349A
Other languages
English (en)
Other versions
CN102618694B (zh
Inventor
吴大宏
童振兰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
WUHU TIANHAI REFRACTORY FURNACE CHARGE Co Ltd
Original Assignee
WUHU TIANHAI REFRACTORY FURNACE CHARGE Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by WUHU TIANHAI REFRACTORY FURNACE CHARGE Co Ltd filed Critical WUHU TIANHAI REFRACTORY FURNACE CHARGE Co Ltd
Priority to CN201210094634.9A priority Critical patent/CN102618694B/zh
Publication of CN102618694A publication Critical patent/CN102618694A/zh
Application granted granted Critical
Publication of CN102618694B publication Critical patent/CN102618694B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种精炼保温覆盖剂及其制备方法，其主要是将组成原料稻壳灰35-45份、二氧化硅28-32份、氧化镁3-8份、凹凸棒土5-10份、氧化钙4-6份、三氧化二铝13-18份、莹石3-8份、膨胀蛭石8-12份和炭黑5-10份混合搅拌30-40分钟，造球、烘干处理得到成品。本发明的原料配方合理，覆盖剂中有发热剂与供氧剂,有利于自身熔化，减少粘铁与粘包；保温性良好，MgO除调节碱度还有减少保温覆盖剂与包衬的粘结,有利于铁水包清渣操作；保温覆盖剂为颗粒状，大大减轻了粉尘污染。

Description

一种精炼保温覆盖剂及其制备方法
技术领域
本发明涉及一种炼钢技术领域，具体涉及一种精炼保温覆盖剂及其制备方法。
背景技术
    炼钢铁水从铁厂往钢厂运输以及到钢厂后放出的过程中，温度将不断的降低，铁水的温度波动比较大，这样铁水的能量将不断往外流失，同时这样的情况也不利于炼钢工艺，目前，国内采用不同的精炼保温覆盖剂进行保温处理，但是保温的效果一直不理想，浪费了能源但是问题不能得到解决，迫切需求一种新的成本低的高效精炼保温覆盖剂及其制备方法。
发明内容
为了缓解现有技术的不足和缺陷，本发明的目的在于提高一种精炼保温覆盖剂及其制备方法，本发明的原料配方合理，覆盖剂中有发热剂与供氧剂,有利于自身熔化,减少粘铁与粘包；保温性良好，MgO除调节碱度还有减少保温覆盖剂与包衬的粘结,有利于铁水包清渣操作；保温覆盖剂为颗粒状,大大减轻了粉尘污染。
为了实现上述目的本发明采用如下技术方案：
    精炼保温覆盖剂，其特征在于其组成原料的重量份为：稻壳灰35-45份、二氧化硅28-32份、氧化镁3-8份、凹凸棒土5-10份、氧化钙4-6份、三氧化二铝13-18份、莹石3-8份、膨胀蛭石8-12份和炭黑5-10份。
所述的精炼保温覆盖剂，其特征在于其组成原料的重量份为：稻壳灰40份、二氧化硅30份、氧化镁5份、凹凸棒土8份、氧化钙5份、三氧化二铝15份、莹石5份、膨胀蛭石10份和炭黑8份。
所述的精炼保温覆盖剂的制备方法，其特征在于包括以下步骤：
按组成原料的重量份称取各原料，然后混合搅拌30-40分钟，加工业淀粉与水适量造球、烘干处理得到成品。
本发明的有益效果：
本发明的原料配方合理，覆盖剂中有发热剂与供氧剂,有利于自身熔化,减少粘铁与粘包；保温性良好，MgO除调节碱度还有减少保温覆盖剂与包衬的粘结,有利于铁水包清渣操作；保温覆盖剂为颗粒状,大大减轻了粉尘污染。
具体实施方式
    实施例1：精炼保温覆盖剂，其组成原料的重量份为：稻壳灰35份、二氧化硅28份、氧化镁3份、凹凸棒土5份、氧化钙4份、三氧化二铝13份、莹石3份、膨胀蛭石8份和炭黑5份。
精炼保温覆盖剂的制备方法，包括以下步骤：
按组成原料的重量份称取各原料，然后混合搅拌30-40分钟，加工业淀粉与水造球、烘干处理得到成品。
实施例2：精炼保温覆盖剂，其组成原料的重量份为：稻壳灰40份、二氧化硅30份、氧化镁5份、凹凸棒土8份、氧化钙5份、三氧化二铝15份、莹石5份、膨胀蛭石10份和炭黑8份。
精炼保温覆盖剂的制备方法，包括以下步骤：
按组成原料的重量份称取各原料，然后混合搅拌30-40分钟，加工业淀粉与水造球、烘干处理得到成品。
    实施例3：精炼保温覆盖剂，其组成原料的重量份为：稻壳灰45份、二氧化硅32份、氧化镁8份、凹凸棒土10份、氧化钙6份、三氧化二铝18份、莹石8份、膨胀蛭石12份和炭黑10份。
精炼保温覆盖剂的制备方法，包括以下步骤：
按组成原料的重量份称取各原料，然后混合搅拌30-40分钟，造球、烘干处理得到成品。
本发明精炼保温覆盖剂的保温效果数据对比:
项目 加入量Fe/t 平均降温速度（℃/min）
实施例1 3 O.43
实施例2 2.5 0.45
实施例3 2.5 0.46

Claims (3)

1.一种精炼保温覆盖剂，其特征在于其组成原料的重量份为：稻壳灰35-45份、二氧化硅28-32份、氧化镁3-8份、凹凸棒土5-10份、氧化钙4-6份、三氧化二铝13-18份、莹石3-8份、膨胀蛭石8-12份和炭黑5-10份。
2.根据权利要求1所述的精炼保温覆盖剂，其特征在于其组成原料的重量份为：稻壳灰40份、二氧化硅30份、氧化镁5份、凹凸棒土8份、氧化钙5份、三氧化二铝15份、莹石5份、膨胀蛭石10份和炭黑8份。
3.一种如权利要求1所述的精炼保温覆盖剂的制备方法，其特征在于包括以下步骤：
按组成原料的重量份称取各原料，然后混合搅拌30-40分钟，加工业淀粉与水适量造球、烘干处理得到成品。
CN201210094634.9A 2012-03-31 2012-03-31 一种精炼保温覆盖剂及其制备方法 Active CN102618694B (zh)