CN102618180A - 夜光型玻璃胶片 - Google Patents

夜光型玻璃胶片 Download PDF

Info

Publication number
CN102618180A
CN102618180A CN2012100804564A CN201210080456A CN102618180A CN 102618180 A CN102618180 A CN 102618180A CN 2012100804564 A CN2012100804564 A CN 2012100804564A CN 201210080456 A CN201210080456 A CN 201210080456A CN 102618180 A CN102618180 A CN 102618180A
Authority
CN
China
Prior art keywords
coupling agent
type glass
layer
luminous type
luminescent layer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2012100804564A
Other languages
English (en)
Inventor
李国勇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
TIANJIN SUNRAY PLASTIC PRODUCT CO Ltd
Original Assignee
TIANJIN SUNRAY PLASTIC PRODUCT CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by TIANJIN SUNRAY PLASTIC PRODUCT CO Ltd filed Critical TIANJIN SUNRAY PLASTIC PRODUCT CO Ltd
Priority to CN2012100804564A priority Critical patent/CN102618180A/zh
Publication of CN102618180A publication Critical patent/CN102618180A/zh
Pending legal-status Critical Current

Abstract

本发明属于夹层玻璃用中间层技术领域，尤其涉及一种夜光型玻璃胶片。其层结构中包括发光层，所述发光层的组成成分包括100重量份的聚合物树脂、5-50重量份的蓄光型长余辉发光颜料、0-10重量份的分散剂和0-5重量份的偶联剂。本发明的玻璃胶片具有良好的夜光性能，由其制作的夹层玻璃可用于装饰、安全指示以及显示功能等，同时兼具现有夹层玻璃的安全性。

Description

夜光型玻璃胶片
技术领域
本发明属于夹层玻璃用中间层技术领域，尤其涉及一种夜光型玻璃胶片。
背景技术
夹层玻璃在现代生活中得到了越来越广泛的应用，其广泛应用于建筑装潢、汽车、工矿、航空航海以及工艺美术等领域。其结构是，在两层玻璃中间夹设有玻璃胶片，玻璃胶片增强了夹层玻璃整体的安全性，在玻璃打碎时玻璃碎屑仍然粘附在玻璃胶片上而不会飞散，确保了人员的安全。在玻璃胶片上着色或者雕刻图案、文字等能增加夹层玻璃的美观效果，并拓展其应用范围，例如用于装饰、安全指示和显示等领域。
现有的玻璃胶片通常只是采用着色的方法，尚未见到蓄光型长余辉发光颜料在玻璃胶片中的应用。
发明内容
本发明为解决公知技术中存在的技术问题而提供一种夜光型玻璃胶片。
本发明为解决公知技术中存在的技术问题所采取的技术方案是：夜光型玻璃胶片的层结构中包括发光层，所述发光层的组成成分包括100重量份的聚合物树脂、5-50重量份的蓄光型长余辉发光颜料、0-10重量份的分散剂和0-5重量份的偶联剂。
本发明还可以采用如下技术方案：
还包括粘结层，其组成成分包括100重量份的聚合物树脂和0-5重量份的偶联剂。
所述的蓄光型长余辉发光颜料选取为多种离子激活的碱土铝酸盐、碱土硅酸盐、碱土硅铝酸盐和锌、钙、钡、锶的硫化物中的一种或多种混合物。
所述的聚合物树脂选取为聚乙烯、聚丙烯、PVC、PS、PET、PVB、EVA、乙烯基弹性体或塑性体、丙烯基弹性体、苯乙烯系弹性体、聚氨酯、离子聚合物和丙烯酸树脂中的一种或多种混合物。
所述的分散剂选取为PE蜡、EVA蜡和PP蜡中的一种或多种混合物。
所述偶联剂选取为硅烷偶联剂、铝酸酯偶联剂、钛酸酯偶联剂和高分子偶联剂中的一种或多种混合物。
所述粘结层为一层，位于所述发光层的一侧。
所述粘结层为两层，位于所述发光层的两侧。
还包括白色反光层，该层紧邻所述发光层。
本发明具有的优点和积极效果是：本发明通过在传统玻璃胶片的组配成分中加入蓄光型长余辉发光颜料，制得作为本发明玻璃胶片其中一层的发光层，具有良好的夜光性能。根据不同需求，可以通过单挤或共挤的加工方式得到只具有发光层的单层玻璃胶片和同时具有发光层和粘结层的复合层玻璃胶片。白色反光层的设计，增强了玻璃胶片的发光亮度。含有本发明玻璃胶片的夹层玻璃可用于装饰、安全指示以及显示功能等，同时兼具现有夹层玻璃的安全性。
具体实施方式
为能进一步了解本发明的发明内容、特点及功效，兹例举以下实施例详细说明如下：
本发明的夜光型玻璃胶片在传统玻璃胶片层结构的基础上增加了发光层，根据不同需求，可以通过单挤或共挤的加工方式得到只具有发光层的单层玻璃胶片和同时具有发光层和粘结层的复合层玻璃胶片。
粘结层的组成成分包括100重量份的聚合物树脂和0-5重量份的偶联剂。
发光层的组成成分包括100重量份的聚合物树脂、5-50重量份的蓄光型长余辉发光颜料、0-10重量份的分散剂和0-5重量份的偶联剂。
其中，聚合物树脂选取为聚乙烯、聚丙烯、PVC、PS、PET、PVB、EVA、乙烯基弹性体或塑性体、丙烯基弹性体、苯乙烯系弹性体、聚氨酯、离子聚合物和丙烯酸树脂中的一种或多种混合物；分散剂选取为PE蜡、EVA蜡和PP蜡中的一种或多种混合物；偶联剂选取为硅烷偶联剂、铝酸酯偶联剂、钛酸酯偶联剂和高分子偶联剂中的一种或多种混合物。
分散剂用于把发光颜料均匀地分散在聚合物树脂中，PE蜡、EVA蜡、PP蜡等均为高分子蜡。某些偶联剂也兼有分散剂的功能，如硅烷偶联剂、铝酸酯偶联剂、钛酸酯偶联剂、高分子偶联剂等。
偶联剂用于增强聚合物树脂对玻璃的粘结能力。有些聚合物树脂对玻璃有比较好的粘结力，如PVB、聚氨酯、离子聚合物、丙烯酸树脂等，此时偶联剂可以选择添加或者不加，视具体生产情况而定。有些聚合物树脂如PE、PP、PVC、PS、PET、EVA、乙烯基弹性体或塑性体、丙烯基弹性体、苯乙烯系弹性体等对玻璃没有粘结力或者粘结力较弱，就需要添加偶联剂以提升聚合物树脂对玻璃的粘结能力。
蓄光型长余辉发光颜料选取为多种离子激活的碱土铝酸盐、碱土硅酸盐、碱土硅铝酸盐和锌、钙、钡、锶的硫化物中的一种或多种混合物。在生产过程中，可以采用先制造高浓度发光颜料母粒，再把母粒按一定比例添加到聚合物树脂中的方法，也可以采用将发光颜料、聚合物树脂、分散剂、偶联剂一次性混合均匀的方式。
在层结构方面，可以根据需要制作成单层结构或复合层结构。当制作成单层时，只有发光层一层；复合层结构可以有多种方式，如①具有一层发光层和一层粘结层，②具有一层发光层两层粘结层，此时粘结层位于发光层的两侧，③其它的组合方式，如多层发光层和多层粘结层的结构等。
为了增强玻璃胶片的发光亮度，可以在上述层结构中设置白色反光层，用于将光亮全部发散至同一侧。此时，该反光层的位置优选为紧邻发光层设置。
该夜光型玻璃胶片可以选用压延、流延或吹膜的方式制造。流延或吹膜的制造也可以选用单挤或共挤的方式成膜，其中单挤是将以上组成在一个挤出机中混合并挤出，共挤则可以选择将发光层和粘结层分开挤出，发光层位于中间，粘结层位于两侧。白色反光层也可以采用共挤的方式作为一层挤出。
实施例1
单层结构，只有一层发光层。
称取100重量份的EVA聚合物树脂、15重量份的碱土铝酸盐型发光颜料、5重量份的EVA蜡作为分散剂、0.5重量份的硅烷偶联剂充分搅拌，用一台挤出机以单挤的方式挤出。
实施例2
双层结构，一层发光层和一层粘结层。
发光层采用100重量份的PE聚合物树脂、20重量份的碱土硅酸盐型发光颜料、5重量份的PE蜡作为分散剂；粘结层采用100重量份的EVA聚合物树脂、3.5重量份的高分子偶联剂；各自进行充分混合，采用共挤的方式挤出。
实施例3
三层结构，一层发光层位于中间、两层粘结层位于两侧。
发光层采用100重量份的PE聚合物树脂、25重量份的碱土铝酸盐型发光颜料、4.5重量份的PE蜡作为分散剂；粘结层采用100重量份的EVA聚合物树脂、0.5重量份的硅烷偶联剂；各自进行充分混合，采用共挤的方式挤出。
实施例4
三层结构，一层发光层位于中间、一层粘结层和一层白色反光层位于两侧。
发光层采用100重量份的聚乙烯树脂和聚丙烯树脂、40重量份的钙的硫化物型发光颜料、5重量份的PP蜡和2.5重量份的钛酸酯偶联剂作为分散剂；粘结层采用100重量份的聚乙烯树脂和聚丙烯树脂、2.5重量份的高分子偶联剂；各自进行充分混合，采用共挤的方式挤出。
实施例5
四层结构，一层发光层和一层白色反光层位于中间、两层粘结层位于两侧。
发光层采用100重量份的PVB聚合物树脂、30重量份的锌的硫化物型发光颜料、7重量份的EVA蜡作为分散剂；粘结层采用100重量份的EVA聚合物树脂、1.0重量份的硅烷偶联剂；各自进行充分混合，采用共挤的方式挤出。
实施例6
五层结构，两层发光层和三层粘结层交替设置。
发光层采用100重量份的聚氨酯树脂、25重量份的锶的硫化物型发光颜料、8重量份的高分子偶联剂作为分散剂；粘结层采用100重量份的的聚氨酯树脂；各自进行充分混合，采用共挤的方式挤出。
实施例7
五层结构，一层白色反光层位于中间、两层发光层位于反光层两侧、两层粘结层位于最外侧。
发光层采用100重量份的EVA聚合物树脂、35重量份的碱土铝酸盐型发光颜料、6.5重量份的EVA蜡作为分散剂；粘结层采用100重量份的EVA聚合物树脂、1.5重量份的硅烷偶联剂；各自进行充分混合，采用共挤的方式挤出。

Claims (10)

1.一种夜光型玻璃胶片，其特征在于：其层结构中包括发光层，所述发光层的组成成分包括100重量份的聚合物树脂、5-50重量份的蓄光型长余辉发光颜料、0-10重量份的分散剂和0-5重量份的偶联剂。
2.按照权利要求1所述的夜光型玻璃胶片，其特征在于：还包括粘结层，其组成成分包括100重量份的聚合物树脂和0-5重量份的偶联剂。
3.按照权利要求1所述的夜光型玻璃胶片，其特征在于：所述的蓄光型长余辉发光颜料选取为多种离子激活的碱土铝酸盐、碱土硅酸盐、碱土硅铝酸盐和锌、钙、钡、锶的硫化物中的一种或多种混合物。
4.按照权利要求1或2所述的夜光型玻璃胶片，其特征在于：所述的聚合物树脂选取为聚乙烯、聚丙烯、PVC、PS、PET、PVB、EVA、乙烯基弹性体或塑性体、丙烯基弹性体、苯乙烯系弹性体、聚氨酯、离子聚合物和丙烯酸树脂中的一种或多种混合物。
5.按照权利要求1或2所述的夜光型玻璃胶片，其特征在于：所述的分散剂选取为PE蜡、EVA蜡和PP蜡中的一种或多种混合物。
6.按照权利要求1或2所述的夜光型玻璃胶片，其特征在于：所述偶联剂选取为硅烷偶联剂、铝酸酯偶联剂、钛酸酯偶联剂和高分子偶联剂中的一种或多种混合物。
7.按照权利要求2所述的夜光型玻璃胶片，其特征在于：所述粘结层为一层，位于所述发光层的一侧。
8.按照权利要求2所述的夜光型玻璃胶片，其特征在于：所述粘结层为两层，位于所述发光层的两侧。
9.按照权利要求7或8所述的夜光型玻璃胶片，其特征在于：还包括白色反光层，该层紧邻所述发光层。
10.含有权利要求1至9任一项所述的夜光型玻璃胶片的夹层玻璃。
CN2012100804564A 2012-03-23 2012-03-23 夜光型玻璃胶片 Pending CN102618180A (zh)