CN102605522A - Wet-permeating, warm-keeping and magnetic healthcare functional fabric and manufacturing method thereof - Google Patents
Wet-permeating, warm-keeping and magnetic healthcare functional fabric and manufacturing method thereof Download PDFInfo
- Publication number
- CN102605522A CN102605522A CN2012100696517A CN201210069651A CN102605522A CN 102605522 A CN102605522 A CN 102605522A CN 2012100696517 A CN2012100696517 A CN 2012100696517A CN 201210069651 A CN201210069651 A CN 201210069651A CN 102605522 A CN102605522 A CN 102605522A
- Authority
- CN
- China
- Prior art keywords
- fabric
- magnetic
- blended yarn
- wet
- yarn
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a wet-permeating, warm-keeping and magnetic healthcare functional fabric, which consists of a blended yarn fabric outer layer and a polyester yarn fabric inner layer. The blended yarn fabric outer layer includes from 40 to 50% of viscose, from 47 to 53% of hollow terylene and from 6 to 12% of water soluble vinylon, the blended yarn fabric outer layer and the polyester yarn fabric inner layer are interwoven, and circular dot-shaped magnetic printing patterns are arranged on the surface of the fabric inner layer. The manufacturing method of the wet-permeating, warm-keeping and magnetic healthcare functional fabric includes fabric weaving; fabric cleaning; fabric hydrophilic treatment; magnetic layer printing; fabric drying; and fabric shaping. The fabric interwoven by the fabric inner layer woven by polyester yarns and the fabric outer layer woven by blended yarns has wet-permeating and warm-keeping effects, and the circular dot-shaped magnetic printing patterns are printed on the surface of the fabric inner layer, so that the fabric has a magnetic healthcare effect. Besides, cleanout fluid, hydrophilic finishing agent and magnetic printing pulp which are prepared specially are adopted in a fabric manufacturing process, and accordingly the wet-permeating, warm-keeping and magnetic healthcare effects of the fabric are guaranteed.
Description
Technical field
The present invention relates to a kind of function fabric and manufacturing approach thereof, relate to a kind of fabric and manufacturing approach thereof of leading functions such as wet warming magnetic health care that have specifically.
Background technology
The Along with people's quality of life improve constantly the fast development with amusement and recreation, sports, tourist industry, People more and more requires to take textiles and has multinomial comfortable function, has health care but also require to take textiles, for example leads wet, warming fabric and has the wet comfortable function of heat; It is dry and comfortable, warm, comfortable that the people is worn, and magnetic health care fabric has the health care that biological effect of magnetic field produces, as promoting cellular metabolism, activating cell; The balance endocrinopathy stimulates circulation, the microcirculation improvement state; Promote that inflammation disappears, eliminate swelling and pain, the adjustment blood pressure; The effect that particularly brings high blood pressure down, allaying tiredness promotes antisecosis etc.Lead wet, heat-preserving function fabric and magnetic health care fabric and have demand and development prospect widely in amusement and recreation, sports, travel clothing field.But; The great majority of existing market circulation are taken textiles and are only had individual event comfortable function or health care; For example or warming, otherwise lead wet, or magnetic health care etc.; Utilize innovative principle, creatively wet leading, warming, magnetic health care is incorporated into one exploitation clothes with textiles also beyond example.Simultaneously, also there is not a kind of manufacturing approach that has the fabric of leading wet, warming and magnetic health care simultaneously now.
Summary of the invention
For overcoming above-mentioned defective, the present invention aims to provide a kind of fabric and manufacturing approach thereof of leading wet, warming and magnetic health care that have simultaneously.
For achieving the above object; The technical scheme that the present invention adopts is: a kind of warming magnetic health care fabric that wets of leading; Comprise the fabric nexine and the fabric outer that are interwoven, said fabric nexine is formed by the terylene yarn weaving, and said fabric outer is formed by the blended yarn braiding; The surface of said fabric nexine has magnetosphere, the constituting of said blended yarn: the formation mass percent of viscose glue, hollow polyester, water soluble vinylon is 40-50%, 47-53%, 6-12%.
The line density of said blended yarn is that 28-32 props up, and the thread density of said terylene yarn is 120-150D.
Said magnetosphere is the decalcomania that circular point-like magnetic constitutes, and the diameter of said magnetic decalcomania is the 1-3 millimeter, and the distribution density of said magnetic decalcomania is 80-100/square metre.
The warming magnetic health care fabric that wets of leading of the present invention, its manufacturing approach is divided into following steps:
Steps A: weaving textile, terylene yarn and blended yarn are passed through two-faced machine, adopt compound cotton wool structure, be made into fabric with fabric nexine and fabric outer;
Step B: fabric cleans, and the good fabric that will interweave is put into common rope impregnating mangle and cleaned, and in impregnating mangle, needs to inject in advance cleaning fluid, and cleaning fluid adds cleaning agent by clear water and processes, and cleaning temperature is 60-80 ℃, scavenging period 30-40 minute;
Step C: fabric hydrophilic is handled, and carries out the hydrophilic treated dipping putting into common rope impregnating mangle through clear fabric successively, and dipping temperature 60-80 ℃, time 20-30 minute, dipping finished fabric was dewatered 3-5 minute, again 100-105 ℃ of oven dry 3-5 minute;
Step D: print magnetosphere, print magnetosphere with flat screen printing machine on the surface of fabric nexine;
Step e:, drying printed magnetospheric fabric 3-5 minute under 60-80 ℃ temperature with rotary screen drier fabric drying;
Step F: the fabric typing, under 170-180 ℃ temperature, finalize the design the fabric after the oven dry 3-5 second with the hot blast framing shaping machine.
Its innovative point mainly is in steps A: before the weaving textile, needing earlier to make blended yarn, is mass percent that the ratio of 40-50%, 45-50%, 5-10% is processed blended yarn in the blending machine; In braiding machine, be woven into fabric to blended yarn and terylene yarn then, the fabric nexine of said fabric adopts the terylene yarn weaving to form, and fabric outer adopts the blended yarn braiding to form;
At step B: in the fabric cleaning process, the mass percent of fabric and cleaning fluid is: fabric, cleaning fluid: 95-97%, 3-5%; The cleaning fluid that is adopted is pressed: emulsifying agent LF100, sheet alkali PJ, water be with 15-19%, 5-8%, and the mass percent of 70-80% stirs and processes;
At step C: in the fabric hydrophilic processing procedure, the mass percent of fabric and hydrophilic processing liquid is: fabric, hydrophilic processing liquid: 90-95%, 5-10%; The hydrophilic processing liquid that is adopted is pressed: hydrophilic finishing agent, water are with 0.5-1%, and the mass percent of 99-99.5% is processed through stirring;
At step D: print in the magnetosphere, said magnetosphere is the decalcomania 3 that circular point-like magnetic constitutes, and the material that is adopted is the magnetic printing paste; Said magnetic printing paste is pressed: by volume percentage is: the magnetic slurry of 10-15%; The titanate coupling agent TMC-981 of 3-5%, the water-borne acrylic resin of 46-60%, the A group slurry of 15-25%; The water-based efficient thickeners DT-208 of 2-5%, the advection agent SE2200 of 5-10% stirred through 30-40 minute in container and process.
Adopted wet warming magnetic health care fabric and the manufacturing approach thereof led of the present invention; The fabric that is interwoven of the fabric outer that fabric nexine that forms through the terylene yarn weaving and blended yarn braiding form has leads wet warming effect; And pass through to print the decalcomania that circular point-like magnetic constitutes on the surface of inner textile layer, make fabric have the effect of magnetic health care; Simultaneously; In the manufacture process of fabric; Adopted that the cleaning fluid of special modulation carries out that fabric cleans, the hydrophilic processing liquid of special modulation carries out that fabric hydrophilic is handled, the magnetic printing paste of special modulation carries out magnetosphere and prints, the fabric after having guaranteed to process lead wet warming magnetic health-care efficacy.
Description of drawings
Fig. 1 is a structural representation of the present invention.
Among the figure: 1-fabric nexine, 2-fabric outer, 3-decalcomania.
The specific embodiment
As shown in Figure 1; The invention discloses a kind of wet warming magnetic health care fabric of leading; Comprise the fabric nexine 1 and fabric outer 2 that are interwoven, said fabric nexine 1 is formed by the terylene yarn weaving, and said fabric outer 2 is formed by the blended yarn braiding; The surface of said fabric nexine 1 has magnetosphere, and innovative point of the present invention mainly is constituting of said blended yarn: the formation mass percent of viscose glue, hollow polyester, water soluble vinylon is 40-50%, 47-53%, 6-12%.
In practical application, the line density of said blended yarn can be made as 28-32 usually and prop up, and the thread density of said terylene yarn is 120-150D.
In practical application, said magnetosphere is specially the decalcomania 3 that circular point-like magnetic constitutes, and the diameter of said magnetic decalcomania 3 is the 1-3 millimeter, and the distribution density of said magnetic decalcomania 3 is 80-100/square metre.
The basic principle of leading wet warming magnetic health care fabric of the present invention is: after human body is perspired, form the fabric nexine by the terylene yarn weaving and can fast sweat be transmitted to fabric outer, the fabric nexine is kept dry; Realize high wet guiding function, simultaneously, in the fabric outer that forms by blended yarn braiding after the contained viscose moisture absorption; Emit heat, and the blended yarn of fabric outer is owing to be made up of viscose glue, hollow polyester, water soluble vinylon, and water soluble vinylon can dissolve in cleaning process; Make to have in the blended yarn and have a large amount of holes; Can hold than juicy, simultaneously, blended yarn comprises more still air; Play the heat-insulation warm keeping effect, thereby realize perspiring-leading wet-moisture absorption-heating-heat-preserving function.Owing to have decalcomania 3 one side that circular point-like magnetic constitutes on the surface of fabric nexine 1; Has the magnetic healthy functions; On the other hand, the decalcomania 3 that point-like magnetic constitutes exceeds fabric nexine 1 plane, has reduced the contact area of human body and fabric; When having reduced human body and having perspired fabric and human body paste effect, further improved the dry and comfortable comfortableness of fabric.
The manufacturing approach of leading wet warming magnetic health care fabric of the present invention is divided into following steps:
Steps A: weaving textile, design textile structure braided fabric is realized that the best is warming and is led wet effect, and terylene yarn and blended yarn are passed through two-faced machine, adopts compound cotton wool structure, is made into the fabric with fabric nexine and fabric outer;
Step B: fabric cleans; With the finish and the spot of removing fiber surface, dissolve water soluble vinylon fully simultaneously, the good fabric that will interweave is put into common rope impregnating mangle and is cleaned; In impregnating mangle, need to inject in advance cleaning fluid; Cleaning fluid adds cleaning agent by clear water and processes, and cleaning temperature is 60-80 ℃, scavenging period 30-40 minute;
Step C: fabric hydrophilic is handled, and to reduce liquid/material contact angle, leading of raising fabric is moist; Hydrophilic finiss adopts dipping hydrophilic finiss technology; Carry out hydrophilic treated dipping, dipping temperature 60-80 ℃, time 20-30 minute putting into common rope impregnating mangle through clear fabric successively; Dipping finishes fabric was dewatered 3-5 minute, again 100-105 ℃ of oven dry 3-5 minute;
Step D: print magnetosphere, print magnetosphere with flat screen printing machine on the surface of fabric nexine 1;
Step e:, drying printed magnetospheric fabric 3-5 minute under 60-80 ℃ temperature with rotary screen drier fabric drying;
Step F: the fabric typing, under 170-180 ℃ temperature, finalize the design the fabric after the oven dry 3-5 second with the hot blast framing shaping machine.
Innovative point in the manufacturing approach of leading wet warming magnetic health care fabric of the present invention mainly is in steps A: before the weaving textile; Need to make blended yarn earlier; At first need confirm the best blending ratio and the yarn parameter of viscose glue, hollow polyester, water soluble vinylon, realize maximum yarn porosity and stable water storage, accumulation of heat effect.In practical application, be the mass percent of viscose glue, hollow polyester, water soluble vinylon that the ratio of 40-50%, 47-53%, 6-12% is processed blended yarn in the blending machine usually; In braiding machine, be woven into fabric to blended yarn and terylene yarn then, the fabric nexine 1 of said fabric adopts the terylene yarn weaving to form, and fabric outer 2 adopts the blended yarn braiding to form;
At step B: in the fabric cleaning process, the mass percent of fabric and cleaning fluid is: fabric, cleaning fluid: 95-97%, 3-5%; The cleaning fluid that is adopted is pressed: emulsifying agent LF100, sheet alkali PJ, water be with 15-19%, 5-8%, and the mass percent of 70-80% stirs and processes; Wherein said emulsifying agent LF100 can be buied by Taiwan hundred grand International Trading Company Ltd, and sheet alkali PJ can be buied by the big negotiation trade of Wuxi City Co., Ltd;
At step C: in the fabric hydrophilic processing procedure, the mass percent of fabric and hydrophilic processing liquid is: fabric, hydrophilic processing liquid: 90-95%, 5-10%; The hydrophilic processing liquid that is adopted is pressed: hydrophilic finishing agent, water are with 0.5-1%, and the mass percent of 99-99.5% is processed through stirring; Wherein said hydrophilic finishing agent can be buied by Shenzhen Tianding Fine Chemical Engineering Manufacturing Co., Ltd; Because fabric has carried out hydrophilic finiss, reduce liquid/material contact angle, improve the wet guiding function of inner textile layer,
At step D: print in the magnetosphere, said magnetosphere is the decalcomania 3 that circular point-like magnetic constitutes, and the material that is adopted is the magnetic printing paste; Said magnetic printing paste is pressed: by volume percentage is: the magnetic slurry of 10-15%; The titanate coupling agent TMC-981 of 3-5%, the water-borne acrylic resin of 46-60%, the A group slurry of 15-25%; The water-based efficient thickeners DT-208 of 2-5%, the advection agent SE2200 of 5-10% stirred through 30-40 minute in container and process.Wherein said magnetic slurry can be buied by the refreshing High Seience Technology Co., Ltd. of the clean that in Beijing, and titanate coupling agent TMC-981 can be buied by Tianzhang City's green chemical industry auxiliary reagent factory; Water-borne acrylic resin can be contained chemical industry Co., Ltd by the Dongying armour and buy; A group slurry can be buied by Liaoning Province Xiliu Chemical Co Ltd, Haicheng City; Water-based efficient thickeners DT-208 can be buied by Guangzhou Di Te Chemical Industry Science Co., Ltd, and advection agent SE2200 can buy from organosilicon international trade Shanghai Co., Ltd of SHIN-ETSU HANTOTAI;
Specific embodiment given below can further specify the manufacturing approach of leading wet warming magnetic health care fabric of the present invention, but they are not to qualification of the present invention.
Embodiment 1:Carry out as follows:
1, designing the ratio of viscose glue, hollow polyester, water soluble vinylon in the blended yarn, is the mass percent of viscose glue, hollow polyester, water soluble vinylon that 40%, 50%, 10% ratio is processed blended yarn in the blending machine, and the line density of blended yarn is 28.
2, the line density of confirming the terylene yarn is 120D, and the filament line density is 1.0d, through two-faced machine, adopts compound cotton wool structure to blended yarn and Polyester Yarns, is made into the blended yarn to be the fabric outer of material and to be the fabric nexine of material with the Polyester Yarns.
3, fabric is put into impregnating mangle and clean, 60 ℃ of cleaning temperatures, scavenging period 30 minutes; The cleaning fluid that in fabric cleans, adopts and the mass percent of fabric are confirmed as 5%:95%; The cleaning fluid that is adopted is pressed: emulsifying agent LF100, and sheet alkali PJ, water is with 15%; 8%, 77% mass percent stirs and processes.
4, fabric is carried out hydrophilic finiss; Putting into common rope impregnating mangle through the fabric that cleans, the mass percent of fabric and hydrophilic processing liquid is a fabric, hydrophilic processing liquid: 90%; 10%; The hydrophilic processing liquid that is adopted is pressed: hydrophilic finishing agent, water is processed through stirring with 0.5%, 99.5% mass percent.60 ℃ of dipping temperatures, 20 minutes time, dipping finishes fabric dehydration 3 minutes, again 100 ℃ of oven dry 3 minutes.
5, composite magnetic printing paste; Guarantee the flexibility after magnetic functional effect, washing fastness and the printing paste film forming, said magnetic printing paste is pressed: by volume percentage is: 10% magnetic slurry, 3% titanate coupling agent TMC-981; 60% water-borne acrylic resin; 15% A group slurry, 2% water-based efficient thickeners DT-208,10% advection agent SE2200 stirred through 30 minutes in container and process.
6, the design decalcomania is circular on plain net, and diameter of a circle is 1 millimeter, and 80/square metre of the distribution densities of circle are imprinted on the magnetic printing paste on the fabric nexine surface with flat screen printing machine.
7, under the temperature of 60 ℃ of oven dry, drying by the fire the fabric of printed magnetic decalcomania 3 minutes on the rotary screen drier.
8, the fabric after oven dry under 170 ℃ the temperature on the hot blast framing shaping machine 3 seconds of typing, make fabric smooth, magnetic printing paste wash resistant fastness further improves, and leads wet warming magnetic health care fabric thereby make.
Embodiment 2:Carry out as follows:
1, designing the ratio of viscose glue, hollow polyester, water soluble vinylon in the blended yarn, is the mass percent of viscose glue, hollow polyester, water soluble vinylon that 45%, 47%, 8% ratio is processed blended yarn in the blending machine, and the line density of blended yarn is 30.
2, the line density of confirming the terylene yarn is 140D, and the filament line density is 0.9d, through two-faced machine, adopts compound cotton wool structure to blended yarn and Polyester Yarns, is made into the blended yarn to be the fabric outer of material and to be the fabric nexine of material with the Polyester Yarns.
3, fabric is put into impregnating mangle and clean, 70 ℃ of cleaning temperatures, scavenging period 35 minutes; The cleaning fluid that in fabric cleans, adopts and the mass percent of fabric are confirmed as 4%:96%; The cleaning fluid that is adopted is pressed: emulsifying agent LF100, and sheet alkali PJ, water is with 17%; 7%, 76% mass percent stirs and processes.
4, fabric is carried out hydrophilic finiss; Putting into common rope impregnating mangle through the fabric that cleans, the mass percent of fabric and hydrophilic processing liquid is a fabric, hydrophilic processing liquid: 93%; 7%; The hydrophilic processing liquid that is adopted is pressed: hydrophilic finishing agent, water is processed through stirring with 0.7%, 99.3% mass percent.70 ℃ of dipping temperatures, 25 minutes time, dipping finishes fabric dehydration 4 minutes, again 103 ℃ of oven dry 4 minutes.
5, composite magnetic printing paste; Guarantee the flexibility after magnetic functional effect, washing fastness and the printing paste film forming, said magnetic printing paste is pressed: by volume percentage is: 13% magnetic slurry, 4% titanate coupling agent TMC-981; 46% water-borne acrylic resin; 24% A group slurry, 4% water-based efficient thickeners DT-208,9% advection agent SE2200 stirred through 35 minutes in container and process.
6, the design decalcomania is circular on plain net, and diameter of a circle is 2 millimeters, and 90/square metre of the distribution densities of circle are imprinted on the magnetic printing paste on the fabric nexine surface with flat screen printing machine.
7, under the temperature of 70 ℃ of oven dry, drying by the fire the fabric of printed magnetic decalcomania 4 minutes on the rotary screen drier.
8, the fabric after oven dry under 180 ℃ the temperature on the hot blast framing shaping machine 5 seconds of typing, make fabric smooth, magnetic printing paste wash resistant fastness further improves, and leads wet warming magnetic health care fabric thereby make.
Embodiment 3:Carry out as follows:
1, designing the ratio of viscose glue, hollow polyester, water soluble vinylon in the blended yarn, is the mass percent of viscose glue, hollow polyester, water soluble vinylon that 50%, 45%, 5% ratio is processed blended yarn in the blending machine, and the line density of blended yarn is 32.
2, the line density of confirming the terylene yarn is 150D, and the filament line density is 0.8d, through two-faced machine, adopts compound cotton wool structure to blended yarn and Polyester Yarns, is made into the blended yarn to be the fabric outer of material and to be the fabric nexine of material with the Polyester Yarns.
3, fabric is put into impregnating mangle and clean, 80 ℃ of cleaning temperatures, scavenging period 40 minutes; The cleaning fluid that in fabric cleans, adopts and the mass percent of fabric are confirmed as 3%:97%; The cleaning fluid that is adopted is pressed: emulsifying agent LF100, and sheet alkali PJ, water is with 19%; 6%, 75% mass percent stirs and processes.
4, fabric is carried out hydrophilic finiss, putting into common rope impregnating mangle through the fabric that cleans, the mass percent of fabric and hydrophilic processing liquid is a fabric; Hydrophilic processing liquid: 95%, 5%, the hydrophilic processing liquid that is adopted is pressed: hydrophilic finishing agent; Water is processed through stirring with 1%, 99 mass percent.80 ℃ of dipping temperatures, 30 minutes time, dipping finishes fabric dehydration 5 minutes, again 105 ℃ of oven dry 5 minutes.
5, composite magnetic printing paste; Guarantee the flexibility after magnetic functional effect, washing fastness and the printing paste film forming, said magnetic printing paste is pressed: by volume percentage is: 15% magnetic slurry, 5% titanate coupling agent TMC-981; 48% water-borne acrylic resin; 22% A group slurry, 5% water-based efficient thickeners DT-208,5% advection agent SE2200 stirred through 35 minutes in container and process.
6, the design decalcomania is circular on plain net, and diameter of a circle is 3 millimeters, and 100/square metre of the distribution densities of circle are imprinted on the magnetic printing paste on the fabric nexine surface with flat screen printing machine.
7, under the temperature of 80 ℃ of oven dry, drying by the fire the fabric of printed magnetic decalcomania 5 minutes on the rotary screen drier.
8, the fabric after oven dry under 180 ℃ the temperature on the hot blast framing shaping machine 5 seconds of typing, make fabric smooth, magnetic printing paste wash resistant fastness further improves, and leads wet warming magnetic health care fabric thereby make.
Wet warming magnetic health care fabric property such as the table 1 of leading of the present invention:
Table 1
Claims (4)
1. lead wet warming magnetic health care fabric for one kind; Comprise the fabric nexine (1) and the fabric outer (2) that are interwoven; Said fabric nexine (1) is formed by the terylene yarn weaving; Said fabric outer (2) is formed by the blended yarn braiding, and the surface of said fabric nexine (1) has magnetosphere, it is characterized in that constituting of said blended yarn: the formation mass percent of viscose glue, hollow polyester, water soluble vinylon is 40-50%, 47-53%, 6-12%.
2. the warming magnetic health care fabric that wets of leading according to claim 1, the line density that it is characterized in that said blended yarn is that 28-32 props up, the thread density of said terylene yarn is 120-150D.
3. the warming magnetic health care fabric that wets of leading according to claim 1; It is characterized in that said magnetosphere is the decalcomania (3) that circular point-like magnetic constitutes; The diameter of said magnetic decalcomania (3) is the 1-3 millimeter, and the distribution density of said magnetic decalcomania (3) is 80-100/square metre.
4. according to claim 1 or the 2 or 3 described warming magnetic health care fabrics that wet of leading, its manufacturing approach is divided into following steps:
Steps A: weaving textile, terylene yarn and blended yarn are passed through two-faced machine, adopt compound cotton wool structure, be made into fabric with fabric nexine and fabric outer;
Step B: fabric cleans, and the good fabric that will interweave is put into common rope impregnating mangle and cleaned, and in impregnating mangle, needs to inject in advance cleaning fluid, and cleaning fluid adds cleaning agent by clear water and processes, and cleaning temperature is 60-80 ℃, scavenging period 30-40 minute;
Step C: fabric hydrophilic is handled, and carries out the hydrophilic treated dipping putting into common rope impregnating mangle through clear fabric successively, and dipping temperature 60-80 ℃, time 20-30 minute, dipping finished fabric was dewatered 3-5 minute, again 100-105 ℃ of oven dry 3-5 minute;
Step D: print magnetosphere, print with flat screen printing machine on the surface of fabric nexine (1) and go up magnetosphere;
Step e:, drying printed magnetospheric fabric 3-5 minute under 60-80 ℃ temperature with rotary screen drier fabric drying;
Step F: the fabric typing, under 170-180 ℃ temperature, finalize the design the fabric after the oven dry 3-5 second with the hot blast framing shaping machine;
It is characterized in that in steps A: before the weaving textile, needing earlier to make blended yarn, is mass percent that the ratio of 40-50%, 45-50%, 5-10% is processed blended yarn in the blending machine; In braiding machine, be woven into fabric to blended yarn and terylene yarn then, the fabric nexine (1) of said fabric adopts the terylene yarn weaving to form, and fabric outer (2) adopts the blended yarn braiding to form;
At step B: in the fabric cleaning process, the mass percent of fabric and cleaning fluid is: fabric, cleaning fluid: 95-97%, 3-5%; The cleaning fluid that is adopted is pressed: emulsifying agent LF100, sheet alkali PJ, water be with 15-19%, 5-8%, and the mass percent of 70-80% stirs and processes;
At step C: in the fabric hydrophilic processing procedure, the mass percent of fabric and hydrophilic processing liquid is: fabric, hydrophilic processing liquid: 90-95%, 5-10%; The hydrophilic processing liquid that is adopted is pressed: hydrophilic finishing agent, water are with 0.5-1%, and the mass percent of 99-99.5% is processed through stirring;
At step D: print in the magnetosphere, said magnetosphere is the decalcomania (3) that circular point-like magnetic constitutes, and the material that is adopted is the magnetic printing paste; Said magnetic printing paste is pressed: by volume percentage is: the magnetic slurry of 10-15%; The titanate coupling agent TMC-981 of 3-5%, the water-borne acrylic resin of 46-60%, the A group slurry of 15-25%; The water-based efficient thickeners DT-208 of 2-5%, the advection agent SE2200 of 5-10% stirred through 30-40 minute in container and process.