CN101037844A - Printing paste containing magnetic materials and method of use thereof - Google Patents
Printing paste containing magnetic materials and method of use thereof Download PDFInfo
- Publication number
- CN101037844A CN101037844A CN 200710097417 CN200710097417A CN101037844A CN 101037844 A CN101037844 A CN 101037844A CN 200710097417 CN200710097417 CN 200710097417 CN 200710097417 A CN200710097417 A CN 200710097417A CN 101037844 A CN101037844 A CN 101037844A
- Authority
- CN
- China
- Prior art keywords
- magnetic
- printing paste
- printing
- fabric
- magnetic material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a printing paste containing magnetic materials and its application method. Said magnetic printing paste consists of magnetic powder and promoters, wherein said magnetic powder has an average diameter lower than 10 mu m, and the weight of said magnetic powder is 1-50% of the total weight of the printing paste. Textile printed by said printing paste containing magnetic materials in accordance with the present invention has virtues such as sweat-absorption and gas permeability, wear comfort, soft handle, elegant appearance, low cost, and the like. Especially, printing dress designed according to human body acupuncture points exhibits better curative effects with regard to a variety of diseases.
Description
One, technical field
The present invention relates to a kind of special functional textile material, more particularly relate to a kind of printing paste and application process thereof that contains magnetic material.
Two, background technology
" magnetic therapy " is meant and uses dissimilar and external magnetic field intensity acts on human body affected part or echo area (meridian point), thereby a kind of methods of treatment of treatment disease also comprises for oral administration and the magnetic and medicated methods of treatment of external application.For example magnetic sheet sticks big vertebra, fei shu, Danzhong treatment asthmatic tracheitis; The refreshing threshold of gyromagnet effect has remarkable antidiarrheal curative effect etc.Magnetic therapy has no traumatic pain, safe and reliable characteristics, and magnetic therapy can not cause wound and pain and psychological pressure to the patient.
The earth is the spheroid that a magnetic field surrounds, earth magnetism protection human survival and evolution.Magnetic field acts in people's the body, promotes hemetaboly.Biological little current effect of generation and biological electricity effect under the effect of magnetic field.Human body cell is the miniature body with certain magnetic, and human body has biological magnetic field.Therefore external magnetic field influences the physiological activity of human body, under the effect of magnetic field, produce little current effect and biological electricity effect, by the variation of nerve, humoral system generation electric charge, current potential, biochemistry and physiological function, human body function and raising resistance against diseases to adjust human body have medical care effect.It is introduced that magnetic therapy has certain curative effect to the illness of internal organ, blood vessel, tracheae, for example have analgesic activity, anti-inflammation detumescence, tangible anti-aging effects more rapidly, high blood pressure, rheumatic arthritis, tumour are all had certain therapeutic action.Its reason may be the result that magnetotherapy effect exerts an influence behind channels and collaterals, body fluid, blood etc.
Magnetic fabric and the health-care products thereof sold on market at present have following three kinds:
1, the health-care products of sticking auxilliary magnetic tablet.
CN-96103350.9 discloses a kind of far-infrared magnetic health-care bed clothes, and its method for production is a sticking auxilliary soft magnetic material (soft magnetic stripe) on coated fabric.
CN-200420029418.7 discloses a kind of health care magnetic quilt, is woven with the band tissue of 150-300 hollow on the magnet layer of magnetic quilt, respectively inserts one piece of ndfeb disk in each band tissue.
CN-96122903.9 discloses a kind of Magnetotherapeutic health blanket, and it is made up of rare-earth permanent magnetic film and double-layer fabric knitted fabric etc., and rare-earth permanent magnetic film is fixed in the textiles.
The problem that the said goods exists is that magnetic tablet feel is stiff, airtight, and is not attractive in appearance, can only be used as the local auxiliary material of magnetic health-care garments
2, the magnetic fabric that is woven into by magnetic fibre.
CN-03144195.5 discloses a kind of far-infrared magnetic process for making such fabric, its with magnetic silk and far infrared silk with 1-3: 1 ratio is weaved, and then above-mentioned fabrics is done to bleaching and dyeing and handles and the typing arrangement.
CN-03150401.9 discloses a kind of magnetic antibiotic health care textiles and manufacture method, it adds powders such as hard magnetic material neodymium iron or SmCo in the polyester of molten state, spin long filament or short fiber is reprocessed into textiles, reach fabric and have magnetic characteristic by adding magnetic again.
CN-200410072309.8 discloses a kind of far infrared magnetic fiber and blend kinder fiber blended fabric, and it relates to by far infrared magnetic fiber and bluish dogbane or numb blend fibre blended fabric.
The problem that the said goods exists is magnetic fibre complex manufacturing, cost height.Magnetic fibre is synthetic fiber, absorbing sweat not, and snugness of fit is poor.
3, magnetic film is coated on the magnetic fabric of fabric face.
CN-95110009.2 discloses a kind of cloth with magnetism, and it covers the diaphragm that one deck has magnetic and constitutes by fabric substrate with on fabric substrate.The problem that these products exist is airtight, and dress is felt oppressed, and feel is stiff, can only be used as the local auxiliary material of magnetic health-care garments.
Three, summary of the invention
One of purpose of the present invention provides a kind of printing paste that contains magnetic material.
Two of purpose of the present invention provides a kind of application process that contains the printing paste of magnetic material.
These and other purpose of the present invention will further embody and set forth by following detailed description and explanation.
The printing paste that contains magnetic material of the present invention is made up of magnetic and auxiliary agent, and wherein said magnetic average diameter is less than 10 microns, and magnetic accounts for the 1-50% of magnetic printing paste gross weight, is preferably the 5-15% that magnetic accounts for magnetic printing paste gross weight.
In the printing paste that contains magnetic material of the present invention, described magnetic is selected one or more in the rare earth permanent-magnetic material powders such as ferrite permanent-magnet materials such as strontium ferrite, ferro-aluminum oxysome and barium ferrite, metal permanent-magnet material, NdFeB material for use, and the magnetic average diameter is 50nm-500nm.
In the printing paste that contains magnetic material of the present invention, described solvent is selected one or more in water, polyalcohol, alkylene oxide addition product, acid amides and the polar organic solvent for use.In printing paste, also contain in thickener, adhesive, mill base, surfactant, antisettling agent, softener, antiseptic, far infrared agent, anion agent, mite-proof agent, flavouring agent, vitamin, natural health-care products and the skin conditioner one or more.
The application process that contains the printing paste of magnetic material of the present invention is that to adopt method for printing to be printed on the magnetic printing paste for preparing with chemical fibre, natural fabric be on the one side or tow sides of the fabric of base material or nonwoven fabric.Described printing method is ROTARY SCREAM PRINTING, PLATE SCREAM PRINTING, screen printing, roller printing, transfer printing or ink-jet printed, and fabric behind the stamp or nonwoven fabric are handled through conventional dyeing and printing process such as oven dry, tentering again.At last to the processing of magnetizing of stamp finished product fabric, nonwoven fabric or ready-made clothes, the technology that magnetizes can adopt modes such as electromagnet to magnetize, the magnetic PRINTED FABRIC can reach comparatively ideal effect through magnetizing of very short time, the time of magnetizing is 0.01-30 minute, be preferably 0.1-3 minute, what can select is 0.1-1 minute.Also can after making the health-care clothing of various styles and goods, the magnetic PRINTED FABRIC magnetize.
Magnetic PRINTED FABRIC of the present invention, especially magnetic stamp natural fabric has the following advantages: absorbing sweat is ventilative, and is comfortable and easy to wear, soft, elegant in appearance, with low cost.Dress experimental results show that the magnetic medical health care function clothes that magnetic PRINTED FABRIC of the present invention is made not only have good curative effect, and comfortable and easy to wear.Particularly the print according to the human acupoint design has better therapeutic to numerous disease.Overcome other magnetic health-care garments exist airtight, absorbing sweat not, cost height, problem such as dress is felt oppressed, and feel is stiff.
In the present invention, employed thickener, adhesive, mill base, surfactant, antisettling agent and softener and antiseptic, far infrared agent, anion agent, mite-proof agent, flavouring agent, vitamin, natural health-care products and skin conditioner are conventional use.Those skilled in the art need not spend creative work and promptly know.
Below further specify the present invention by specific embodiment, but embodiment only be used for the explanation, can not limit the scope of the invention.
In the present invention, if not refer in particular to, all parts, amount are the unit of weight based on gross weight, and all raw materials all can be buied from market.
Four, the specific embodiment
Embodiment 1
The magnetic printing paste that is used for fabric magnetic stamp in following ratio preparation
Strontium ferrite magnetic powder (average diameter is 150nm) 30Kg water 70Kg
After stirring, on pure cotton fabric, print the front with the PLATE SCREAM PRINTING mode, screen printing mode back up is used in oven dry more then, and oven dry, tentering adopt the electromagnet mode to magnetize at last again, and the time of magnetizing is 1.5 minutes.
Embodiment 2
The magnetic printing paste that is used for fabric magnetic stamp in following ratio preparation
Ferro-aluminum oxysome magnetic (average diameter is 200nm) 30Kg
Glycerine 68Kg, thickener 2Kg
After stirring, on pure cotton fabric, print the front with the PLATE SCREAM PRINTING mode, screen printing mode back up is used in oven dry more then, and oven dry, tentering adopt the electromagnet mode to magnetize at last again, and the time of magnetizing is 3 minutes.
Embodiment 3
The magnetic printing paste that is used for fabric magnetic stamp in following ratio preparation
Barium ferrite magnetic powder (average diameter is 600nm) 10Kg
Glycerine 6Kg water 52Kg
Thickener 2Kg adhesive 30Kg
After stirring, washing/COTTON FABRIC on (65/35), printing positive and negative with the ROTARY SCREAM PRINTING mode, oven dry then, tentering adopts the electromagnet mode to magnetize at last, and the time of magnetizing is 2 minutes.
Embodiment 4
The magnetic printing paste that is used for fabric magnetic stamp in following ratio preparation
NdFeB magnetic powder (average diameter is 100nm) 10Kg
Water 50Kg dispersant NNO 1Kg
Penetrating agent JFC 1Kg thickener 2Kg
Adhesive 30Kg antisettling agent 1Kg
Dimethyl formamide 5Kg pigment printing paste 5kg
After stirring, washing/COTTON FABRIC on (65/35), printing positive and negative with the ROTARY SCREAM PRINTING mode, oven dry then, tentering adopts the electromagnet mode to magnetize at last, and the time of magnetizing is 2.5 minutes.
Embodiment 5
The magnetic printing paste that is used for fabric magnetic stamp in following ratio preparation
NdFeB magnetic powder (average diameter is 100nm) 10Kg
Glycerine 6Kg water 50Kg
Dispersant NNO 1Kg penetrating agent JFC 1Kg
Thickener JLSUN FAG 2Kg adhesive JLSUN EP 30Kg
After stirring, on pure cotton fabric, print the front with the PLATE SCREAM PRINTING mode, screen printing mode back up is used in oven dry more then, and oven dry, tentering adopt the electromagnet mode to magnetize at last again, and the time of magnetizing is 1 minute.
Embodiment 6
The magnetic printing paste that is used for fabric magnetic stamp in following ratio preparation
NdFeB magnetic powder (average diameter is 100nm) 10Kg
Glycerine 6Kg water 50Kg
Dispersant NNO 1Kg penetrating agent JFC 1Kg
Thickener JLSUN FAG 2Kg adhesive JLSUN EP 30Kg
Antisettling agent 1Kg
After stirring, on pure cotton fabric, print the front with the PLATE SCREAM PRINTING mode, screen printing mode back up is used in oven dry more then, and oven dry, tentering adopt the electromagnet mode to magnetize at last again, and the time of magnetizing is 0.5 minute.
Embodiment 7
The magnetic printing paste that is used for fabric magnetic stamp in following ratio preparation
NdFeB magnetic powder (average diameter is 100nm) 8Kg
Glycerine 2Kg water 50Kg
Dispersant NNO 1Kg penetrating agent JFC 1Kg
Thickener JLSUN FAG 2Kg adhesive JLSUN EP 30Kg
Antisettling agent 1Kg softener 5Kg
After stirring, washing/COTTON FABRIC on (65/35), printing positive and negative with the ROTARY SCREAM PRINTING mode, oven dry then, tentering adopts the electromagnet mode to magnetize at last, and the time of magnetizing is 0.1 minute.
Embodiment 8
The magnetic printing paste that is used for fabric magnetic stamp in following ratio preparation
NdFeB magnetic powder (average diameter is 100nm) 10Kg
Glycerine 6Kg water 50Kg
Dispersant NNO 1Kg penetrating agent JFC 1Kg
Thickener JLSUN FAG 2Kg adhesive JLSUN EP 30Kg
Antisettling agent 1Kg antiseptic JLSUN SCJ-891 1Kg
Far infrared agent JLSUN 777 1Kg flavouring agent 0.01Kg
After stirring, on pure cotton fabric, print the front with the PLATE SCREAM PRINTING mode, screen printing mode back up is used in oven dry more then, and oven dry, tentering adopt the electromagnet mode to magnetize at last again, and the time of magnetizing was 1 second.
Claims (10)
1, a kind of printing paste that contains magnetic material is characterized in that this magnetic printing paste is made up of magnetic and auxiliary agent, and wherein said magnetic average diameter is less than 10 microns, and magnetic accounts for the 1-50% of magnetic printing paste gross weight.
2, the printing paste that contains magnetic material according to claim 1 is characterized in that magnetic accounts for the 5-15% of magnetic printing paste gross weight.
3, the printing paste that contains magnetic material according to claim 1 and 2, it is characterized in that described magnetic selects one or more in the rare earth permanent-magnetic material powders such as ferrite permanent-magnet materials such as strontium ferrite, ferro-aluminum oxysome and barium ferrite, metal permanent-magnet material, NdFeB material for use, the magnetic average diameter is 50nm-500nm.
4, the printing paste that contains magnetic material according to claim 1 and 2 is characterized in that described solvent selects one or more in water, polyalcohol, alkylene oxide addition product, acid amides and the polar organic solvent for use.
5, the printing paste that contains magnetic material according to claim 1 and 2 is characterized in that described printing paste also contains one or more in thickener, adhesive, mill base, surfactant, antisettling agent and the softener.
6, the printing paste that contains magnetic material according to claim 1 and 2 is characterized in that described printing paste also can contain one or more in antiseptic, far infrared agent, anion agent, mite-proof agent, flavouring agent, vitamin, natural health-care products and the skin conditioner.
7, the application process that contains the printing paste of magnetic material according to claim 1 and 2, it is characterized in that adopting method for printing to be printed on the magnetic printing paste for preparing with chemical fibre, natural fabric is on the one side or tow sides of the fabric of base material or nonwoven fabric.
8, the application process that contains the printing paste of magnetic material according to claim 7 is characterized in that described printing method is ROTARY SCREAM PRINTING, PLATE SCREAM PRINTING, screen printing, roller printing, transfer printing or ink-jet printed.
9, the application process that contains the printing paste of magnetic material according to claim 7 is characterized in that fabric or the nonwoven fabric behind the stamp handled through conventional dyeing and printing process such as oven dry, tentering again.
10, the application process that contains the printing paste of magnetic material according to claim 7 is characterized in that the time of magnetizing is 0.01-30 minute, is preferably 0.1-3 minute to the processing of magnetizing of stamp finished product fabric, nonwoven fabric or ready-made clothes.