CN102604314A - 一种阻燃abs的配方及其制作方法 - Google Patents
一种阻燃abs的配方及其制作方法 Download PDFInfo
- Publication number
- CN102604314A CN102604314A CN201210049614XA CN201210049614A CN102604314A CN 102604314 A CN102604314 A CN 102604314A CN 201210049614X A CN201210049614X A CN 201210049614XA CN 201210049614 A CN201210049614 A CN 201210049614A CN 102604314 A CN102604314 A CN 102604314A
- Authority
- CN
- China
- Prior art keywords
- flame
- abs
- raw material
- making method
- mbs
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种阻燃ABS的配方,该配方组份为:ABS50-70份、溴代三嗪15-20份、MBS5-10份、三氧化二锑4-6份、抗氧化剂0.2-1份、润滑剂0.5-1份、高胶粉3-8份、其它加工助剂0.5-1份。本发明还公开了一种阻燃ABS的制作方法,选取ABS原料,烘料;将原料搅拌,加入硅油搅拌,再加入抗氧化剂、润滑剂及其它加工助剂搅拌,最后加入溴代三嗪、三氧化二锑、高胶粉、MBS搅拌,得到半成品;将半成品进行挤出,然后进行冷却,最后进行切粒,得到成品。本发明生产出来的阻燃ABS材料不仅外观好、冲击性能好,而且耐寒性好,在加工过程中不会出现变色情况,更符合环保要求。
Description
技术领域
本发明涉及一种阻燃ABS的配方及其制作方法。
背景技术
传统的阻燃剂以固态颗粒形式和ABS结合,微观上分析材料结合性差,目前市场上的ABS阻燃材料大都是用传统阻燃剂生产,产品冲击性低、流动性差、光泽度差、耐寒性能较差,且在注塑过程中容易出现变色的情况。
发明内容
本发明提供了一种新型阻燃ABS配方及其制作方法,这种方法生产出来的阻燃ABS材料不仅外观好、冲击性能好,而且耐寒性好,在加工过程中不会出现变色情况,更符合环保要求。
本发明采用了以下技术方案:一种阻燃ABS的配方,该配方组份为:ABS 50-70份、溴代三嗪 15-20份、MBS 5-10份、三氧化二锑 4-6份、抗氧化剂 0.2-1份、润滑剂 0.5-1份、高胶粉 3-8份、其它加工助剂0.5-1份。
所述抗氧剂为抗氧剂1010和抗氧剂168的组合物,所述润滑剂为EBS,所述其它加工助剂为氧化锌。
一种阻燃ABS的制作方法,它包括以下步骤:步骤一,选取ABS原料,然后烘料;步骤二,将ABS原料搅拌,然后加入硅油搅拌一段时间,再加入抗氧化剂、润滑剂及其它加工助剂搅拌一段时间,最后加入溴代三嗪、三氧化二锑、高胶粉、MBS搅拌一段时间,得到半成品;步骤三,将步骤二中的半成品进行挤出,然后进行冷却,最后进行切粒,得到成品。
所述步骤一中将ABS原料在80-95度下烘1-2小时,所述步骤二中加入硅油搅拌1-2分钟,加入抗氧化剂、润滑剂及其它助剂搅拌1-2分钟,加入溴代三嗪、三氧化二锑、高胶粉、MBS搅拌3-5分钟;所述步骤三中采用同向平行双螺杆将步骤二中的半成品进行挤出,温度设定范围165-220度,主机转速350-600转,螺杆选用高分散性螺杆组合;所述步骤三中采用水冷和风冷方式进行冷却;所述步骤三中采用龙门式切粒机切粒,切得的粒子大小为3*3mm。
本发明具有以下有益效果:本发明制作出的阻燃ABS产品冲击强度高、阻燃性能好、光泽度高、生产成本低,符合环保要求,该阻燃树脂广泛用于空调器、电冰箱、洗衣机、电脑、汽车、电动车、电水壶、电饭煲、电表外壳、燃气表外壳的生产,同时在加工过程中不会出现变色情况,溴代三嗪以液态的形态融入整个配方体系,不会降低材料自身的冲击性能和表面光洁度,而MBS的加入,更好的加强ABS和其它组份的结合力,提高材料的冲击性能和耐寒性。
具体实施方式
本发明提供了一种阻燃ABS的配方,该配方组份为:ABS 50-70份、溴代三嗪 15-20份、MBS 5-10份、三氧化二锑 4-6份、抗氧化剂 0.2-1份、润滑剂 0.5-1份、高胶粉 3-8份、其它加工助剂0.5-1份;所述抗氧剂为抗氧剂1010和抗氧剂168的组合物,所述润滑剂为EBS,所述其它加工助剂为氧化锌。
本发明还提供了一种阻燃ABS的制作方法,它包括以下步骤:步骤一,选取ABS原料,然后烘料,将ABS原料在80-95度下烘1-2小时;步骤二,将ABS原料搅拌,然后加入硅油搅拌1-2分钟,再加入抗氧化剂、润滑剂及其它加工助剂搅拌1-2分钟,最后加入溴代三嗪、三氧化二锑、高胶粉、MBS搅拌3-5分钟,得到半成品;步骤三,采用同向平行双螺杆将步骤二中的半成品进行挤出,温度设定范围165-220度,主机转速350-600转,螺杆选用高分散性螺杆组合,然后采用水冷和风冷方式进行冷却,最后采用龙门式切粒机切粒,得到成品,切得的粒子大小为3*3mm。
Claims (8)
1.一种阻燃ABS的配方,其特征是该配方组份为:ABS 50-70份、溴代三嗪 15-20份、MBS 5-10份、三氧化二锑 4-6份、抗氧化剂 0.2-1份、润滑剂 0.5-1份、高胶粉 3-8份、其它加工助剂0.5-1份。
2.根据权利要求1所述的一种阻燃ABS的配方,其特征是所述抗氧剂为抗氧剂1010和抗氧剂168的复合物,所述润滑剂为EBS,所述其它加工助剂为氧化锌。
3.根据权利要求1所述的一种阻燃ABS的制作方法,其特征是它包括以下步骤:
步骤一,选取ABS原料,然后烘料;
步骤二,将ABS原料搅拌,然后加入硅油搅拌一段时间,再加入抗氧化剂、润滑剂及其它加工助剂搅拌一段时间,最后加入溴代三嗪、三氧化二锑、高胶粉、MBS搅拌一段时间,得到半成品;
步骤三,将步骤二中的半成品进行挤出,然后进行冷却,最后进行切粒,得到成品。
4.根据权利要求3所述的一种阻燃ABS的制作方法,其特征是所述步骤一中将ABS原料在80-95度下烘1-2小时。
5.根据权利要求3所述的一种阻燃ABS的制作方法,其特征是所述步骤二中加入硅油搅拌1-2分钟,加入抗氧化剂、润滑剂及其它助剂搅拌1-2分钟,加入溴代三嗪、三氧化二锑、高胶粉、MBS搅拌3-5分钟。
6.根据权利要求3所述的一种阻燃ABS的制作方法,其特征是所述步骤三中采用同向平行双螺杆将步骤二中的半成品进行挤出,温度设定范围165-220度,主机转速350-600转,螺杆选用高分散性螺杆组合。
7.根据权利要求3所述的一种阻燃ABS的制作方法,其特征是所述步骤三中采用水冷和风冷方式进行冷却。
8.根据权利要求3所述的一种阻燃ABS的制作方法,其特征是所述步骤三中采用龙门式切粒机切粒,切得的粒子大小为3*3mm。