CN102586938A - 具有保暖功效的复合纤维 - Google Patents
具有保暖功效的复合纤维 Download PDFInfo
- Publication number
- CN102586938A CN102586938A CN2012100509101A CN201210050910A CN102586938A CN 102586938 A CN102586938 A CN 102586938A CN 2012100509101 A CN2012100509101 A CN 2012100509101A CN 201210050910 A CN201210050910 A CN 201210050910A CN 102586938 A CN102586938 A CN 102586938A
- Authority
- CN
- China
- Prior art keywords
- coconut carbon
- composite fibre
- coconut
- carbon micro
- polyester
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开一种具有保暖功效的复合纤维,所述复合纤维通过以下工艺方法获得:将椰子外壳的纤维质加热到一定程度后生成椰子碳微粉;将聚酯切片、硅烷偶联剂、作为表面活性剂的硬脂酸锌和作为分散剂的液腊均匀混合形成熔融状的聚酯物;将椰子碳微粉和熔融状的聚酯物按照1∶3.8~4.2质量比例均匀混合形成混合物;将混合物经造粒机织造形成椰子碳微粉母粒;将椰子碳微粉母粒再与聚酯切按照1∶8.5~9.5质量比例均匀混合后并经熔融纺丝形成椰子碳纤维丝;将椰子碳纤维丝经牵伸形成椰子碳纤维长丝。本发明复合纤维织造形成的面料具有吸附性和大大改善了透气性、升温快且温度高、存储热量能力强、保温时间持久。
Description
技术领域
本发明涉及一种具有保暖功效的复合纤维,属于纺织面料技术领域。
背景技术
目前市场上的保暖纤维,有以天然纤维为原料的,也有以合成纤维为原料的,加工工艺也多种多样,有针刺的,水刺的,热粘合的等等。一方面,这类产品要么太单薄保温性能不好,要么就太厚重了,且节能是我国的一项基本国策,大力推进节能工作,节约资源,实施可持续发展是我国的一项基本举措。另一方面,现有的保暖纤维大大牺牲了其透气性,不利于保暖性能的进一步提升和长时间保暖。
工业的出现,人类对环境的影响越来越大,随着人民生活水平的不断提高,人们已经越来越重视环保与保健,人们迫切需要一种既轻薄又保暖的高性能保暖纤维,因此,如何生产一种既轻薄又保暖的高性能保暖纤维成为本领域普通技术人员努力的方向。
发明内容
本发明目的是提供一种具有保暖功效的复合纤维,此复合纤维织造形成的面料具有吸附性和大大改善了透气性、升温快且温度高、存储热量能力强、保温时间持久。
为达到上述目的,本发明采用的技术方案是:一种具有保暖功效的复合纤维,所述复合纤维通过以下工艺方法获得,此工艺方法包括以下步骤:
步骤一、将椰子外壳的纤维质高温加热获得椰子碳微粉;
步骤二、将聚酯切片、硅烷偶联剂、作为表面活性剂的硬脂酸锌和作为分散剂的液腊按照100∶0.39~0.41∶2.7~2.8∶6.8~7质量比例在高温下均匀混合形成熔融状的聚酯物;
步骤三、将所述椰子碳微粉和熔融状的聚酯物按照1∶3.8~4.2质量比例均匀混合形成混合物;
步骤四、将所述混合物经造粒机织造形成椰子碳微粉母粒;
步骤五、将所述椰子碳微粉母粒再与聚酯切按照1∶8.5~9.5质量比例均匀混合后并经熔融纺丝形成椰子碳纤维丝;
步骤六、将步骤五的椰子碳纤维丝经牵伸形成椰子碳纤维长丝。
作为优选,所述步骤二之前包括:将所述椰子碳微粉放入120℃的烘箱中干燥15min步骤。
作为优选,所述步骤二中混合比例为100∶0.4∶2.75∶6.88。
作为优选,所述步骤三的混合比例为1∶4,所述步骤五的混合比例为1∶9。
作为优选,所述步骤五中熔融纺丝速度为1100~1500m/min。
作为优选,所述步骤六中的牵伸倍数为3.0~3.8倍。
附图说明
附图1为本发明复合纤维与现有技术吸收热量测试比较曲线图;
附图2为本发明复合纤维与现有技术保持温度测试比较曲线图。
由于上述技术方案运用,本发明与现有技术相比具有下列优点和效果:
1、本发明具有保暖功效的复合纤维,由此复合纤维织造形成的面料升温快且温度高,存储热量能力强,保温时间持久;其次,该复合纤维具有除臭除臭、吸附、抗菌、远红外及负离子等功能,并且耐洗涤,永久性保健。存储热量能力强,保温时间持久;其次,该复合纤维具有除臭除臭,吸附,抗菌,远红外及负离子等功能,并且耐洗涤,永久性保健。测试方法:准备两个6L的气袋,充入3L的氨气,分别表示A、B。在B气袋中放入10cm*10cm椰子碳保温棉。2h后测试仍在气袋中的气体浓度风别为PA、PB,从而得到咖啡碳涂层织物的除臭效率。
测试结果:PA=50.0(ppm),PB=25.0(ppm)
除臭效率(%)=((PA-PB)/PA)*100%
=50%
结论:由上述测试得出的数据可以看出椰子碳保温棉具有除臭功效。
2、本发明具有保暖功效的复合纤维由于其含有微孔而积比竹炭的大四倍的椰炭椰子碳比表面积2500m2/g左右,竹炭比表面积700m2/g左右,所以其透气性及吸附性比炭纤维更好;其次,本发明所生产的保温棉具有一定的坚固性,能抵御微生物、真菌、细菌,它无味也不会释放污染物,透气性良好,该保温棉可广泛应用于纺织、建筑、医学等领域,是理想的防寒材料,与人体皮肤直接接触,不会产生任何有害作用,是一种无毒、无害、无污染的新型保温材料。
具体实施方式
下面结合实施例对本发明作进一步描述:
实施例1-3:一种具有保暖功效的复合纤维,所述复合纤维通过以下工艺方法获得,此工艺方法包括以下步骤:
步骤一、将椰子外壳的纤维质高温加热获得椰子碳微粉;
步骤二、将聚酯切片、硅烷偶联剂、作为表面活性剂的硬脂酸锌和作为分散剂的液腊在高温下均匀混合形成熔融状的聚酯物;混合质量比例如表1所示:
表1
聚酯切片 | 硅烷偶联剂 | 硬脂酸锌 | 液腊 | |
实施例1 | 100 | 0.39 | 2.8 | 6.8 |
实施例2 | 100 | 0.41 | 2.75 | 6.9 |
实施例3 | 100 | 0.40 | 2.7 | 7 |
步骤三、将所述椰子碳微粉和熔融状的聚酯物按照1∶3.8~4.2质量比例均匀混合形成混合物;
步骤四、将所述混合物经造粒机织造形成椰子碳微粉母粒;
步骤五、将所述椰子碳微粉母粒再与聚酯切按照1∶8.5~9.5质量比例均匀混合后并经熔融纺丝形成椰子碳纤维丝;
步骤六、将步骤五的椰子碳纤维丝经牵伸形成椰子碳纤维长丝。
上述椰子外壳来源于热带地区重要树种,其果实内果肉被取用后,其外壳被丢弃,影响环境卫生,本发明采用此椰子外壳加热到一定程度后生成活性炭。
上述步骤二之前包括:将所述椰子碳微粉放入120℃的烘箱中干燥15min步骤。
上述步骤二中混合比例为100∶0.4∶2.75∶6.88。
上述步骤三的混合比例为1∶4,所述步骤五的混合比例为1∶9。
上述步骤五中熔融纺丝速度为1100~1500m/min。
上述步骤六中的牵伸倍数为3.0~3.8倍。
保温性测试
(一)相同厚度的椰子碳保温棉与一般涤纶保温棉作对比。
测试方法:用500W的卤素灯分别照射相同克重200g/m2的椰子碳保温棉与一般涤纶保温棉60min后,测试两块面料的温度变化,并记录下数据。
测试结果:由上表及图1可以看出,相同厚度的椰子碳保温棉比一般涤纶保温棉升温快,并且椰子碳纤维织物温度可达到61℃左右,而一般涤纶织物温度只能保持在39℃左右。
结论:由上述测试结果表明椰子碳纤维具有良好的吸收热量的功能。
(二)、不同厚度的椰子碳保温棉与一般涤纶保温棉作对比。
测试方法:用500W的卤素灯分别照射100g/m2的椰子碳保温棉与200g/m2的一般涤纶保温棉60min后,测试两块面料的温度变化,并记录下数据。
测试结果:由上表及图2可以看出,椰子碳保温棉比一般涤纶保温棉升温快,并且椰子碳纤维织物温度可达到54℃左右,而一般涤纶织物温度只能保持在39℃左右。
结论:由上述测试结果表明椰子碳纤维具有良好的吸收热量的功能并且轻薄。
上述实施例只为说明本发明的技术构思及特点,其目的在于让熟悉此项技术的人士能够了解本发明的内容并据以实施,并不能以此限制本发明的保护范围。凡根据本发明精神实质所作的等效变化或修饰,都应涵盖在本发明的保护范围之内。
Claims (6)
1.一种具有保暖功效的复合纤维,其特征在于:所述复合纤维通过以下工艺方法获得,此工艺方法包括以下步骤:
步骤一、将椰子外壳的纤维质高温加热获得椰子碳微粉;
步骤二、将聚酯切片、硅烷偶联剂、作为表面活性剂的硬脂酸锌和作为分散剂的液腊按照100∶0.39~0.41∶2.7~2.8∶6.8~7质量比例在高温下均匀混合形成熔融状的聚酯物;
步骤三、将所述椰子碳微粉和熔融状的聚酯物按照1∶3.8~4.2质量比例均匀混合形成混合物;
步骤四、将所述混合物经造粒机织造形成椰子碳微粉母粒;
步骤五、将所述椰子碳微粉母粒再与聚酯切按照1∶8.5~9.5质量比例均匀混合后并经熔融纺丝形成椰子碳纤维丝;
步骤六、将步骤五的椰子碳纤维丝经牵伸形成椰子碳纤维长丝。
2.根据权利要求1所述的复合纤维,其特征在于:所述步骤二之前包括:将所述椰子碳微粉放入120℃的烘箱中干燥15min步骤。
3.根据权利要求1所述的复合纤维,其特征在于:所述步骤二中混合比例为100∶0.4∶2.75∶6.88。
4.根据权利要求3所述的复合纤维,其特征在于:所述步骤三的混合比例为1∶4,所述步骤五的混合比例为1∶9。
5.根据权利要求1所述的复合纤维,其特征在于:所述步骤五中熔融纺丝速度为1100~1500m/min。
6.根据权利要求1所述的复合纤维,其特征在于:所述步骤六中的牵伸倍数为3.0~3.8倍。