CN102584133B - 一种乳液型双组分界面剂及其制备方法 - Google Patents
一种乳液型双组分界面剂及其制备方法 Download PDFInfo
- Publication number
- CN102584133B CN102584133B CN201210011156.0A CN201210011156A CN102584133B CN 102584133 B CN102584133 B CN 102584133B CN 201210011156 A CN201210011156 A CN 201210011156A CN 102584133 B CN102584133 B CN 102584133B
- Authority
- CN
- China
- Prior art keywords
- component
- emulsion
- composition
- weight part
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种乳液型双组分界面剂,包括A组分和B组分,A组分包括:硅酸盐水泥、石英砂、可再分散乳胶粉、木质纤维、泛碱抑制剂和玻璃纤维短切丝;B组分包括:丙烯酸乳液、水性消泡剂、分散剂、防腐剂和水。此外,本发明还公开了该乳液型双组分界面剂的制备方法:A组分:将硅酸盐水泥、石英砂、可再分散乳胶粉、木质纤维、泛碱抑制剂和玻璃纤维短切丝加入搅拌机中搅拌制得。B组分:先加水,后将防腐剂加入水中低速搅拌三分钟,依次加入丙烯酸乳液、分散剂、水性消泡剂低速搅拌三十分钟制得。本发明采取了上述方案以后,能够增加瓷砖表面与基面的粗糙程度,提高抹灰砂浆对基层的粘结强度可有效避免抹灰层空鼓,脱落,收缩开裂等问题。
Description
技术领域
本发明涉及一种乳液型双组分界面剂及其制备方法,属于建筑材料技术领域。
背景技术
目前,界面剂在施工领域得到了较为广泛的使用和推广。
七八十年代的建筑外墙装饰材料比较单一,多采用瓷砖、陶瓷锦砖,经过多年的风吹日晒,砖面出现空鼓、开裂、脱落、渗水现象,并且存在脏污、粉化、变色等问题,影响了建筑物的美观及降低了墙体的寿命,基于上述原因,需要对这些建筑物的瓷砖等粘贴技术进行改进,改善人们的居住环境。
发明内容
本发明针对现有技术的缺点,提供了一种双组份界面剂及其制备方法,其主要能够增加瓷砖表面的粗糙程度,提高抹灰砂浆对基层的粘结强度,有效避免抹灰层空鼓、脱落、收缩开裂、吐碱及返黄发白等问题。
本发明解决上述技术问题所采取的技术方案如下:
一种乳液型双组分界面剂,其特征在于,包括A组分和B组分,其中,所述A组分包括:硅酸盐水泥、石英砂、可再分散乳胶粉、木质纤维、泛碱抑制剂和玻璃纤维短切丝;所述B组分包括:丙烯酸乳液、水性消泡剂、分散剂、防腐剂和水。
其中,作为技术方案的细化,所述A组分中的各个成分按照重量份如下:
硅酸盐水泥 32∽35;
石英砂 55∽58;
可再分散乳胶粉 5∽8;
木质纤维 4∽5;
泛碱抑制剂 2∽3;
玻璃纤维短切丝 2∽3;
注:可再分散乳胶粉有助于增加界面剂的粘结力度;木质纤维有助于产品防止涂层开裂;泛碱抑制剂有助于产品防止出现吐碱、返黄发白现象;玻璃纤维短切丝可提高界面剂的抹灰砂浆的韧性,抗冲击和冻融性能。
所述B组分中的各个成分按照重量份如下:
丙烯酸乳液 40∽45;
水性消泡剂 1∽2;
分散剂 1∽2;
防腐剂 2∽3;
水 56∽58。
其中,优选的是,所述硅酸盐水泥的硬度是42.5R,所述石英砂是50-80目的石英砂。
其中,上述的A组分与B组分,重量份可有以下各种优选方案:
方案一、
所述A组分中的各个成分按照重量份如下:
硅酸盐水泥 32;
石英砂 56;
可再分散乳胶粉 6;
木质纤维 5;
泛碱抑制剂 2;
玻璃纤维短切丝 3;
所述B组分中的各个成分按照重量份如下:
丙烯酸乳液 43;
水性消泡剂 2;
分散剂 1;
防腐剂 3;
水 57。
方案二、
所述A组分中的各个成分按照重量份如下:
硅酸盐水泥 33;
石英砂 58;
可再分散乳胶粉 5;
木质纤维 4;
泛碱抑制剂 3;
玻璃纤维短切丝 2;
所述B组分中的各个成分按照重量份如下:
丙烯酸乳液 42;
水性消泡剂 1;
分散剂 2;
防腐剂 2;
水 58。
方案三、
所述A组分中的各个成分按照重量份如下:
硅酸盐水泥 34;
石英砂 57;
可再分散乳胶粉 8;
木质纤维 4;
泛碱抑制剂 2;
玻璃纤维短切丝 2;
所述B组分中的各个成分按照重量份如下:
丙烯酸乳液 45;
水性消泡剂 1;
分散剂 1;
防腐剂 3;
水 56。
方案四、
所述A组分中的各个成分按照重量份如下:
硅酸盐水泥 35;
石英砂 55;
可再分散乳胶粉 7;
木质纤维 5;
泛碱抑制剂 3;
玻璃纤维短切丝 3;
所述B组分中的各个成分按照重量份如下:
丙烯酸乳液 44;
水性消泡剂 2;
分散剂 2;
防腐剂 2;
水 57。
方案五、
所述A组分中的各个成分按照重量份如下:
硅酸盐水泥 33;
石英砂 57;
可再分散乳胶粉 6;
木质纤维 4;
泛碱抑制剂 2;
玻璃纤维短切丝 3;
所述B组分中的各个成分按照重量份如下:
丙烯酸乳液 40;
水性消泡剂 2;
分散剂 2;
防腐剂 3;
水 56。
方案六、
所述A组分中的各个成分按照重量份如下:
硅酸盐水泥 34;
石英砂 56;
可再分散乳胶粉 5;
木质纤维 5;
泛碱抑制剂 3;
玻璃纤维短切丝 2;
所述B组分中的各个成分按照重量份如下:
丙烯酸乳液 41;
水性消泡剂 1;
分散剂 2;
防腐剂 3;
水 58。
此外,本发明还提供了一种乳液型双组分界面剂的制备方法,具体为:A组分:将硅酸盐水泥、石英砂、可再分散乳胶粉、木质纤维、泛碱抑制剂和玻璃纤维短切丝加入搅拌机中搅拌制得。
B组分:先加水,后将防腐剂加入水中低速搅拌三分钟,依次加入丙烯酸乳液、分散剂、水性消泡剂低速搅拌三十分钟制得。
本发明采取了上述技术方案以后,所述乳液型双组分界面剂能够增加瓷砖表面的粗糙程度,提高抹灰砂浆对基层的粘结强度,有效避免抹灰层空鼓、脱落、收缩开裂、吐碱及返黄发白等问题;并且,根据试验证明,本发明具有超强的粘接力,优良的耐水性,耐老化性。可用于处理瓷砖、玻璃马赛克、抛光砖、玻化砖、大理石、混凝土、砂浆等表面,解决由于这些表面吸水性强或光滑引起界面不易粘接,致使抹灰层空鼓、开裂、剥落等。
并且,可以大大增强新旧混凝土之间以及混凝土与抹灰砂浆的粘结力。可以取代传统混凝土表面的凿毛工序,改善加气混凝土表面抹灰工艺,具有很好的技术效果。
具体实施方式
以下结合具体实施例进行详细的描述。
本发明乳液型双组分界面剂,包括A组分和B组分,其中,所述A组分包括:硅酸盐水泥、石英砂、可再分散乳胶粉、木质纤维、泛碱抑制剂和玻璃纤维短切丝;所述B组分包括:丙烯酸乳液、水性消泡剂、分散剂、防腐剂和水。
其中,所述硅酸盐水泥是白色或者灰色的普通硅酸盐水泥,它的硬度是42.5R。
其中,所述石英砂是50-80目的石英砂。
针对以上组分,以下实施例公开了A组分与B组分以不同配比及其制备方法。
实施例1:
A组分中的各个成分按照重量份如下:
硅酸盐水泥 32;
60目的石英砂 56;
可再分散乳胶粉 6;
木质纤维 5;
泛碱抑制剂 2;
玻璃纤维短切丝 3;
所述B组分中的各个成分按照重量份如下:
丙烯酸乳液 43;
水性消泡剂 2;
分散剂 1;
防腐剂 3;
水 57。
实施例2:
A组分中的各个成分按照重量份如下:
硅酸盐水泥 33;
70目的石英砂 58;
可再分散乳胶粉 5;
木质纤维 4;
泛碱抑制剂 3;
玻璃纤维短切丝 2;
B组分中的各个成分按照重量份如下:
丙烯酸乳液 42;
水性消泡剂 1;
分散剂 2;
防腐剂 2;
水 58。
实施例3:
A组分中的各个成分按照重量份如下:
硅酸盐水泥 34;
75目的石英砂 57;
可再分散乳胶粉 8;
木质纤维 4;
泛碱抑制剂 2;
玻璃纤维短切丝 2;
B组分中的各个成分按照重量份如下:
丙烯酸乳液 45;
水性消泡剂 1;
分散剂 1;
防腐剂 3;
水 56。
实施例4:
所述A组分中的各个成分按照重量份如下:
硅酸盐水泥 35;
50目的石英砂 55;
可再分散乳胶粉 7;
木质纤维 5;
泛碱抑制剂 3;
玻璃纤维短切丝 3;
B组分中的各个成分按照重量份如下:
丙烯酸乳液 44;
水性消泡剂 2;
分散剂 2;
防腐剂 2;
水 57。
实施例5:
A组分中的各个成分按照重量份如下:
硅酸盐水泥 33;
80目的石英砂 57;
可再分散乳胶粉 6;
木质纤维 4;
泛碱抑制剂 2;
玻璃纤维短切丝 3;
B组分中的各个成分按照重量份如下:
丙烯酸乳液 40;
水性消泡剂 2;
分散剂 2;
防腐剂 3;
水 56。
实施例6:
A组分中的各个成分按照重量份如下:
硅酸盐水泥 34;
65目的石英砂 56;
可再分散乳胶粉 5;
木质纤维 5;
泛碱抑制剂 3;
玻璃纤维短切丝 2;
B组分中的各个成分按照重量份如下:
丙烯酸乳液 41;
水性消泡剂 1;
分散剂 2;
防腐剂 3;
水 58。
以上6个实施例的制备方法如下:
A组分:将硅酸盐水泥、石英砂、可再分散乳胶粉、木质纤维、泛碱抑制剂和玻璃纤维短切丝加入搅拌机中搅拌制得。
B组分:先加水,后将防腐剂加入水中低速搅拌三分钟,依次加入丙烯酸乳液、分散剂、水性消泡剂低速搅拌三十分钟制得。
以上6个实施例制得的本产品,它的性能检测结果:
本发明所述乳液型双组分界面剂的使用方法如下;
在相对湿度小于70%、通风良好、基面及环境的温度不低于+5℃的环境下进行施工,包括下列步骤:
清洁基面,包括:清除油脂、青苔、地毯胶,并凿出并修补好松动及开裂部位;
搅拌材料,包括:用电动设备将界面剂乳液与粉料搅拌成稀浆状,其比例为4公斤粉料配1升的界面剂乳液;
涂刷与干燥,包括:用滚筒或毛刷把浆料涂刷到基面上,然后让涂面干燥;
养护与成品保护,包括:加强通风,自然养护,待浆料的表面变灰黑色后,封闭基面并进行后续的工序。
其中,工具的清洗:凝固的浆料很难清除。工具用后,应尽快用水清洗干净。
本发明采取了上述技术方案以后,所述乳液型双组分界面剂能够增加瓷砖表面与基面的粗糙程度,提高抹灰砂浆对基层的粘结强度可有效避免抹灰层空鼓,脱落,收缩开裂等问题;并且,根据试验证明,本发明具有超强的粘接力,优良的耐水性,耐老化性。可用于处理瓷砖、玻璃马赛克、抛光砖、玻化砖、大理石、混凝土、砂浆等表面,解决由于这些表面吸水性强或光滑引起界面不易粘接,致使抹灰层空鼓、开裂、剥落等。
并且,可以大大增强新旧混凝土之间以及混凝土与抹灰砂浆的粘结力。可以取代传统混凝土表面的凿毛工序,改善加气混凝土表面抹灰工艺,具有很好的技术效果。
需要注意的是,上述具体实施例仅仅是示例性的,在本发明的上述教导下,本领域技术人员可以在上述实施例的基础上进行各种改进和变形,而这些改进或者变形落在本发明的保护范围内。
本领域技术人员应该明白,上面的具体描述只是为了解释本发明的目的,并非用于限制本发明。本发明的保护范围由权利要求及其等同物限定。
Claims (8)
8.一种如权利要求1所述乳液型双组分界面剂的制备方法,其特征在于,
A组分:将硅酸盐水泥、石英砂、可再分散乳胶粉、木质纤维、泛碱抑制剂和玻璃纤维短切丝加入搅拌机中搅拌制得;
B组分:先加水,后将防腐剂加入水中低速搅拌三分钟,依次加入丙烯酸乳液、分散剂、水性消泡剂低速搅拌三十分钟制得。