CN102531691A - Matte frit for architectural ceramics and preparation method thereof - Google Patents
Matte frit for architectural ceramics and preparation method thereof Download PDFInfo
- Publication number
- CN102531691A CN102531691A CN2011104160203A CN201110416020A CN102531691A CN 102531691 A CN102531691 A CN 102531691A CN 2011104160203 A CN2011104160203 A CN 2011104160203A CN 201110416020 A CN201110416020 A CN 201110416020A CN 102531691 A CN102531691 A CN 102531691A
- Authority
- CN
- China
- Prior art keywords
- parts
- frit
- zinc oxide
- powder
- calcite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a matte frit for architectural ceramics, belonging to the technical field of ceramic production. The frit comprises the following components in parts by weight: 25-35 parts of quartz, 25-30 parts of calcite, 10-20 parts of potassium feldspar, 5-8 parts of zinc oxide, 3-8 parts of boracic acid, 5-10 parts of zircon powder, 2-5 parts of raw talcum and 1-3 parts of strontium carbonate. A preparation method of the frit comprised the steps of: evenly mixing and stirring the raw materials, melting for 6-8h at a temperature of 1400-1500 DEG C in a frit furnace and subjecting the molten liquid to water quenching by utilizing cold water. The matte frit prepared by adopting the method has the advantages of fine and smooth hand feeling (like a jade), good stability and wider firing range; a ceramic tile made from the frit gives people an elegant feeling and visual enjoyment when being used for decoration; therefore, the value of the ceramic tile is promoted and the additional value is greatly increased.
Description
Technical field
The present invention relates to a kind of preparing ceramic clinker and preparation method thereof, be specifically related to a kind of architectural pottery, belong to the ceramic production technology field with mute light frit and preparation method thereof.
Background technology
Along with the development of society, high-quality pottery becomes the target that current building and ornament materials are pursued, and the many glazes with transparent light of former wall tile for building are main; The decorating interior wall brick surface luster of adopting clear frit to process is beautiful, and the effect of decoration is that light sensation is relatively good, but along with the development of ceramic technology; It is found that unglazed glaze quality is high; Beautiful lubricious sense is arranged, and the effect that decoration comes out is high-grade more, adopts the brick of matting glaze face to decorate; The effect of decorating is given a kind of dignified grand sensation of people; Can be widely used in the decoration of high-grade hotel and villa, so according to the needs in market, researching and developing high-quality architectural pottery becomes an important research tendency with the matting glaze material.
Summary of the invention
The purpose of this invention is to provide a kind of architectural pottery with mute light frit, this frit feel exquisiteness is lubricious, and stability is high, and firing range compares broad.
In order to address the above problem, the technical scheme that the present invention adopted is:
A kind of architectural pottery is with mute light frit, and each ingredients weight parts is:
Quartzy 25 ~ 35 parts, 25 ~ 30 parts in calcite, 10 ~ 20 parts of potassium felspar sands, 5 ~ 8 parts in zinc oxide, 3 ~ 8 parts of boric acid, 5 ~ 10 parts in zirconium English powder, give birth to 2 ~ 5 parts in talcum and 1 ~ 3 part of Strontium carbonate powder.
Another object of the present invention provides the preparation method of a kind of architectural pottery with mute light frit, comprises the steps:
Take by weighing quartzy 25 ~ 35 parts, 25 ~ 30 parts in calcite, 10 ~ 20 parts of potassium felspar sands, 5 ~ 8 parts in zinc oxide, 3 ~ 8 parts of boric acid, 5 ~ 10 parts in zirconium English powder, give birth to 2 ~ 5 parts in talcum and 1 ~ 3 part of Strontium carbonate powder; The above-mentioned powder that takes by weighing is mixed; Place Cinker clew furnace to melt, melt temperature is 1400 ~ 1500 ℃, and the thawing time is 6 ~ 8 hours; Use the cold water shrend with melting good liquid, promptly get the light frit of making mute.
The present invention with respect to the beneficial effect of prior art is:
Adopt the mute light frit feel such as the jade of present method preparation, fine and smooth lubricious, good stability; Firing range is decorated with the ceramic tile that this frit makes than broad, gives the sensation of a kind of elegance of people; Be a kind of enjoyment of vision, the value of ceramic tile gets a promotion, and added value is improved greatly.
Embodiment
Through embodiment the present invention is explained further details below, these embodiment only are used for explaining the present invention, do not limit the scope of the invention.
Embodiment 1
A kind of architectural pottery is with mute light frit, and each ingredients weight parts is:
Quartzy 25 parts, 25 parts in calcite, 10 parts of potassium felspar sands, 5 parts in zinc oxide, 3 parts of boric acid, 5 parts in zirconium English powder, give birth to 1 part of 2 parts in talcum and Strontium carbonate powder.
Its preparation method comprises the steps:
Take by weighing quartzy 25 parts, 25 parts in calcite, 10 parts of potassium felspar sands, 5 parts in zinc oxide, 3 parts of boric acid, 5 parts in zirconium English powder, give birth to 1 part of 2 parts in talcum and Strontium carbonate powder; The above-mentioned powder that takes by weighing is mixed; Place Cinker clew furnace to melt, melt temperature is 1400 ℃, and the thawing time is 6 hours; Use the cold water shrend with melting good liquid, promptly get the light frit of making mute.
Embodiment 2
A kind of architectural pottery is with mute light frit, and each ingredients weight parts is:
Quartzy 35 parts, 30 parts in calcite, 20 parts of potassium felspar sands, 8 parts in zinc oxide, 8 parts of boric acid, 10 parts in zirconium English powder, give birth to 3 parts of 5 parts in talcum and Strontium carbonate powders.
Its preparation method comprises the steps:
Take by weighing quartzy 35 parts, 30 parts in calcite, 20 parts of potassium felspar sands, 8 parts in zinc oxide, 8 parts of boric acid, 10 parts in zirconium English powder, give birth to 3 parts of 5 parts in talcum and Strontium carbonate powders; The above-mentioned powder that takes by weighing is mixed; Place Cinker clew furnace to melt, melt temperature is 1500 ℃, and the thawing time is 8 hours; Use the cold water shrend with melting good liquid, promptly get the light frit of making mute.
Embodiment 3
A kind of architectural pottery is with mute light frit, and each ingredients weight parts is:
Quartzy 30 parts, 27 parts in calcite, 15 parts of potassium felspar sands, 6 parts in zinc oxide, 5 parts of boric acid, 8 parts in zirconium English powder, give birth to 2 parts of 4 parts in talcum and Strontium carbonate powders.
Its preparation method comprises the steps:
Take by weighing quartzy 30 parts, 27 parts in calcite, 15 parts of potassium felspar sands, 6 parts in zinc oxide, 5 parts of boric acid, 8 parts in zirconium English powder, give birth to 2 parts of 4 parts in talcum and Strontium carbonate powders; The above-mentioned powder that takes by weighing is mixed; Place Cinker clew furnace to melt, melt temperature is 1450 ℃, and the thawing time is 7 hours; Use the cold water shrend with melting good liquid, promptly get the light frit of making mute.
Embodiment 4
A kind of architectural pottery is with mute light frit, and each ingredients weight parts is:
Quartzy 25 parts, 25 parts in calcite, 10 parts of potassium felspar sands, 8 parts in zinc oxide, 8 parts of boric acid, 10 parts in zirconium English powder, give birth to 2 parts of 5 parts in talcum and Strontium carbonate powders.
Its preparation method comprises the steps:
Take by weighing quartzy 25 parts, 25 parts in calcite, 10 parts of potassium felspar sands, 8 parts in zinc oxide, 8 parts of boric acid, 10 parts in zirconium English powder, give birth to 2 parts of 5 parts in talcum and Strontium carbonate powders; The above-mentioned powder that takes by weighing is mixed; Place Cinker clew furnace to melt, melt temperature is 1480 ℃, and the thawing time is 6.5 hours; Use the cold water shrend with melting good liquid, promptly get the light frit of making mute.
Embodiment 5
A kind of architectural pottery is with mute light frit, and each ingredients weight parts is:
Quartzy 35 parts, 30 parts in calcite, 20 parts of potassium felspar sands, 5 parts in zinc oxide, 3 parts of boric acid, 5 parts in zirconium English powder, give birth to 1 part of 5 parts in talcum and Strontium carbonate powder.
Another object of the present invention provides the preparation method of a kind of architectural pottery with mute light frit, comprises the steps:
Take by weighing quartzy 35 parts, 30 parts in calcite, 20 parts of potassium felspar sands, 5 parts in zinc oxide, 3 parts of boric acid, 5 parts in zirconium English powder, give birth to 1 part of 5 parts in talcum and Strontium carbonate powder; The above-mentioned powder that takes by weighing is mixed; Place Cinker clew furnace to melt, melt temperature is 1400 ~ 1500 ℃, and the thawing time is 6 ~ 8 hours; Use the cold water shrend with melting good liquid, promptly get the light frit of making mute.
Claims (4)
1. an architectural pottery is characterized in that with mute light frit the weight part of each component is:
Quartzy 25 ~ 35 parts, 25 ~ 30 parts in calcite, 10 ~ 20 parts of potassium felspar sands, 5 ~ 8 parts in zinc oxide, 3 ~ 8 parts of boric acid, 5 ~ 10 parts in zirconium English powder, give birth to 2 ~ 5 parts in talcum and 1 ~ 3 part of Strontium carbonate powder.
2. a kind of architectural pottery according to claim 1 is characterized in that with mute light frit described zinc oxide is that zinc oxide content is 95% zinc oxide.
3. one kind is used to prepare the method for the described architectural pottery of claim 1 with mute light frit, comprises the steps:
Take by weighing quartzy 25 ~ 35 parts, 25 ~ 30 parts in calcite, 10 ~ 20 parts of potassium felspar sands, 5 ~ 8 parts in zinc oxide, 3 ~ 8 parts of boric acid, 5 ~ 10 parts in zirconium English powder, give birth to 2 ~ 5 parts in talcum and 1 ~ 3 part of Strontium carbonate powder; The above-mentioned powder that takes by weighing is mixed; Place Cinker clew furnace to melt, melt temperature is 1400 ~ 1500 ℃, and the thawing time is 6 ~ 8 hours; Use the cold water shrend with melting good liquid, promptly get the light frit of making mute.
4. a kind of architectural pottery according to claim 2 is characterized in that with the preparation method of mute light frit described zinc oxide is that zinc oxide content is 95% zinc oxide.