CN103253986A - High-temperature resisting red colored glaze and preparation method thereof - Google Patents
High-temperature resisting red colored glaze and preparation method thereof Download PDFInfo
- Publication number
- CN103253986A CN103253986A CN2013101577736A CN201310157773A CN103253986A CN 103253986 A CN103253986 A CN 103253986A CN 2013101577736 A CN2013101577736 A CN 2013101577736A CN 201310157773 A CN201310157773 A CN 201310157773A CN 103253986 A CN103253986 A CN 103253986A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- zinc oxide
- raw material
- red colored
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the field of inorganic composite materials, and in particular relates to high-temperature resisting red colored glaze and a preparation method thereof. The high-temperature resisting red colored glaze is prepared from quartz powder, feldspar powder, soochow earth, talcum powder, zinc oxide, zircon power, calcium magnesium powder, dolomite and a color former kp-100. The high-temperature resisting red colored glaze is applied to industrial electro ceramics, has the characteristics of uniform color development, high bonding force, good glossiness and the like, and particularly has good thermal stability; and the fire-resistant temperature of the high-temperature resisting red colored glaze is as high as 1,330 DEG C.
Description
Technical field
The present invention relates to the inorganic composite materials field, particularly a kind of high temperature resistant red color glaze and preparation method thereof.
Background technology
Pottery has plurality of advantages such as good slickness, compactness because of its appearance and is widely used in every field.Wherein, electroceramics is the important foundation device of power industry, is to be applied to the main parts that play support and insulating effect, the double container of doing other electric component sometimes in the power system.Therefore, its mechanical property, electric property, environmental resistance (cold and hot, anti-soil is dirty, aging etc.) there is higher requirement.Existing electroceramics color glaze thermostability is not ideal enough.
Summary of the invention
The technical problem to be solved in the present invention is: a kind of high temperature resistant red color glaze and preparation method thereof is provided.
For achieving the above object, the technical solution used in the present invention is: a kind of resistant to elevated temperatures red color glaze, and it is to be made by the raw material of following parts by weight:
Silica powder 20-30 part, Feldspar Powder 20-30 part, Suzhou soil 5-10 part, talcum powder 5-10 part, zinc oxide 2-10 part, zirconium English powder 10-20 part, dry powder 5-15 part, rhombspar 5-15 part, chromogenic reagent kp-1002-10 part.
Preferably, it is to be made by the raw material of following parts by weight:
Silica powder 20-25 part, Feldspar Powder 25-30 part, Suzhou soil 2-8 part, talcum powder 5-10 part, zinc oxide 2-8 part, zirconium English powder 15-20 part, dry powder 5-10 part, rhombspar 5-10 part, chromogenic reagent kp-1003-5 part.
The most best proportioning, it is to be made by the raw material of following parts by weight:
23 parts of silica powders, 28.8 parts of Feldspar Powders, 4.6 parts in Suzhou soil, 7.7 parts of talcum powder, 3.2 parts in zinc oxide, 14.3 parts in zirconium English powder, 7.7 parts of dry powders, 6.8 parts of rhombspars, chromogenic reagent kp-1003.9 part.
High temperature resistant red preparation method of colored glaze of the present invention is as follows: according to the weight percent weighing and burden of raw material, wherein, crude zinc oxide materials is in advance through high temperature sintering; Each material for preparing is put into ball grinding cylinder, add an amount of ballstone and water simultaneously, through behind the continuous approximately 6 hours ball milling, slip is made.This color glaze is applied to industrial electroceramics, and it is even to have a color development, characteristics such as bonding force is strong, glossiness is good.Especially Heat stability is good, refractory temperature is up to 1330 ℃.
Silica powder, Feldspar Powder, Suzhou soil, talcum powder, zirconium English powder, dry powder and rhombspar are powdery, and all about 250 orders, the crude zinc oxide materials powder particle size is about 0.6um to the granularity of raw material, and chromogenic reagent kp-100 is available from the big great enamel frit makeing in Shanghai company.
Embodiment
Embodiment 1
20 parts of silica powders, 25 parts of Feldspar Powders, 2 parts in Suzhou soil, 5 parts of talcum powder, 2 parts in zinc oxide, 15 parts in zirconium English powder, 5 parts of dry powders, 5 parts of rhombspars, chromogenic reagent kp-1003 part.
According to the weight percent weighing and burden of raw material, wherein, crude zinc oxide materials is in advance through 1400 ℃ of high temperature sinterings 1 hour; Each material for preparing is put into ball grinding cylinder, add an amount of ballstone and water simultaneously, through behind the continuous approximately 6 hours ball milling, slip is made.
Processing parameter in the present embodiment in the course of processing and the physicals of color glaze are as follows:
Embodiment 2
25 parts of silica powders, 30 parts of Feldspar Powders, 8 parts in Suzhou soil, 10 parts of talcum powder, 8 parts in zinc oxide, 20 parts in zirconium English powder, 10 parts of dry powders, 10 parts of rhombspars, chromogenic reagent kp-1005 part.
According to the weight percent weighing and burden of raw material, wherein, crude zinc oxide materials is in advance through 1400 ℃ of high temperature sinterings 1 hour; Each material for preparing is put into ball grinding cylinder, add an amount of ballstone and water simultaneously, through behind the continuous approximately 6 hours ball milling, slip is made.
Processing parameter in the present embodiment in the course of processing and the physicals of color glaze are as follows:
Embodiment 3
23 parts of silica powders, 28.8 parts of Feldspar Powders, 4.6 parts in Suzhou soil, 7.7 parts of talcum powder, 3.2 parts in zinc oxide, 14.3 parts in zirconium English powder, 7.7 parts of dry powders, 6.8 parts of rhombspars, chromogenic reagent kp-1003.9 part.
According to the weight percent weighing and burden of raw material, wherein, crude zinc oxide materials is in advance through 1400 ℃ of high temperature sinterings 1 hour; Each material for preparing is put into ball grinding cylinder, add an amount of ballstone and water simultaneously, through behind the continuous approximately 6 hours ball milling, slip is made.
Processing parameter in the present embodiment in the course of processing and the physicals of color glaze are as follows:
Claims (4)
1. a resistant to elevated temperatures red color glaze is characterized in that, it is to be made by the raw material of following parts by weight:
Silica powder 20-30 part, Feldspar Powder 20-30 part, Suzhou soil 5-10 part, talcum powder 5-10 part, zinc oxide 2-10 part, zirconium English powder 10-20 part, dry powder 5-15 part, rhombspar 5-15 part, chromogenic reagent kp-1002-10 part.
2. resistant to elevated temperatures red color glaze as claimed in claim 1 is characterized in that, it is to be made by the raw material of following parts by weight:
Silica powder 20-25 part, Feldspar Powder 25-30 part, Suzhou soil 2-8 part, talcum powder 5-10 part, zinc oxide 2-8 part, zirconium English powder 15-20 part, dry powder 5-10 part, rhombspar 5-10 part, chromogenic reagent kp-1003-5 part.
3. resistant to elevated temperatures red color glaze as claimed in claim 1 is characterized in that, it is to be made by the raw material of following parts by weight:
23 parts of silica powders, 28.8 parts of Feldspar Powders, 4.6 parts in Suzhou soil, 7.7 parts of talcum powder, 3.2 parts in zinc oxide, 14.3 parts in zirconium English powder, 7.7 parts of dry powders, 6.8 parts of rhombspars, chromogenic reagent kp-1003.9 part.
4. one kind as each described high temperature resistant red preparation method of colored glaze of claim 1-3, it is characterized in that comprising following steps:
According to the weight percent weighing and burden of raw material, wherein, crude zinc oxide materials is in advance through high temperature sintering; Each material for preparing is put into ball grinding cylinder, add an amount of ballstone and water simultaneously, through behind the continuous approximately 6 hours ball milling, slip is made.