CN103641448A - Ceramic heating cup body - Google Patents

Ceramic heating cup body Download PDF

Info

Publication number
CN103641448A
CN103641448A CN201310675366.4A CN201310675366A CN103641448A CN 103641448 A CN103641448 A CN 103641448A CN 201310675366 A CN201310675366 A CN 201310675366A CN 103641448 A CN103641448 A CN 103641448A
Authority
CN
China
Prior art keywords
parts
blank
glaze
ball mill
cup body
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310675366.4A
Other languages
Chinese (zh)
Inventor
吴梓仪
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201310675366.4A priority Critical patent/CN103641448A/en
Publication of CN103641448A publication Critical patent/CN103641448A/en
Pending legal-status Critical Current

Abstract

The invention discloses a ceramic heating cup body which comprises blank and glaze, wherein the blank comprises the following components in parts by weight: 25 parts of purple clay, 16 parts of bauxite clay, 8 parts of kaolin, 8 parts of calcareous clay, 6 parts of kieselguhr and 2 parts of reinforced fiber; and the glaze comprises the following components in parts by weight: 29 parts of blank mud, 13 parts of clinker, 4 parts of frit, 13 parts of loess, 4 parts of iron oxide red and 0.8 part of water glass.

Description

A kind of ceramic heat cup
Technical field
The present invention relates to ceramic heat cup.
Background technology
Boccaro is a kind of containing irony clayey silt rock, by hydromica and kaolin, quartzy, scrap mica, the mineral compositions such as irony form, main chemical has silicon oxide, aluminum oxide, ferric oxide, calcium oxide, magnesium oxide, manganese oxide, potassium oxide, sodium oxide etc., color has the purple mud of multiple main one-tenth, three kinds, green mud and red soil, general term " purple clay ", because of iron content, silicon amount is higher, fire the rear red-purple that is more, therefore claim " boccaro ", it is good that it possesses plasticity-, green strength is high, the processing performances such as dry shrinkage is little, purple clay is through the residual quartz that burnt till shape, mica remains, mullite, red iron-stone, the thing phases such as dual pore, its crystallization phases is many, and glassy phase is few, make red porcelain heating cup there is heat-shock resistance, ventilation property and higher physical strength, because it has been rich in various trace elements, the food that electrothermal dark-red pottery electric soup cooker and inner container of electric cooker stew has nourishing function to human body, and be widely used.The electrothermal dark-red pottery heating cup of prior art easily ftractures.
Summary of the invention
For the shortcoming of prior art, the invention provides a kind of ceramic heat cup.
For solving the problems of the technologies described above, the technical solution used in the present invention is:
A ceramic heat cup, it comprises blank and glaze, by weight percentage, blank comprises following component: 25 parts of Red Stone Wares, 16 parts of bauxite clays, 8 parts of kaolin, 8 parts of calcareous clays, 2 parts of 6 parts, diatomite and fortifying fibres; Glaze comprises following component: 29 parts, this base mud, 13 parts, grog, 4 parts of frits, 13 parts of loess, 4 parts of iron oxide reds, 0.8 part of water glass.
Blank mixing wet ball mill to 100 order; Glaze mixing wet ball mill to 340 order.
Compared with prior art, the invention has the beneficial effects as follows:
The present invention's transportation cost that greatly economizes in raw materials, produce good product quality, cost is low, high efficiency, manufactures out boccaro electric cooker inner bag, the food nutrition that the products such as electric soup cooker inner bag are cooked out, delicious, and the electric cooker of firing, electric soup cooker inner bag, thermostability are strong, and the product that the present invention produces is through 500 ℃ of range temperature thermal cyclings, and indices is all qualified.
Embodiment
Below in conjunction with specific embodiment, the present invention is further illustrated.
A ceramic heat cup, it comprises blank and glaze, by weight percentage, blank comprises following component: 25 parts of Red Stone Wares, 16 parts of bauxite clays, 8 parts of kaolin, 8 parts of calcareous clays, 2 parts of 6 parts, diatomite and fortifying fibres; Glaze comprises following component: 29 parts, this base mud, 13 parts, grog, 4 parts of frits, 13 parts of loess, 4 parts of iron oxide reds, 0.8 part of water glass.
Blank mixing wet ball mill to 100 order; Glaze mixing wet ball mill to 340 order.
In blank of the present invention, glaze raw material, the content of aluminium sesquioxide is 15 parts, and diatomite content is 6 parts.
Production process of the present invention is as follows:
Blank feed proportioning one ball milling one stirs old old mud one moulding of a press filtration one of sieving, glaze is dried in the demoulding one; Glaze is prepared a ball milling one and is sieved;
Dry glaze one glazing one and burn till out product.
Processing requirement: blank prepares former section by ratio requirement and puts into ball mill wet ball mill 12 hours, after 100 mesh sieves, then puts into old about 10 days of the mud cake that feed reservoir press filtration squeezes into water ratio 20% left and right, then enters rear operation moulding.
Glaze is put into ball mill wet ball mill 80 hours after mixing by proportioning raw materials, crosses 340 mesh sieves, wherein tripoly phosphate sodium STPP and other raw material add in the lump, or first add tripoly phosphate sodium STPP, after add other material, and water glass blowing again after ball milling blowing adds ball milling in first about four hours.Water glass Ceramics process water glass, other each processing step is all produced by traditional purple sand ceramics production process process.

Claims (2)

1. a ceramic heat cup, is characterized in that, it comprises blank and glaze, and by weight percentage, blank comprises following component: 25 parts of Red Stone Wares, 16 parts of bauxite clays, 8 parts of kaolin, 8 parts of calcareous clays, 2 parts of 6 parts, diatomite and fortifying fibres; Glaze comprises following component: 29 parts, this base mud, 13 parts, grog, 4 parts of frits, 13 parts of loess, 4 parts of iron oxide reds, 0.8 part of water glass.
2. ceramic heat cup according to claim 1, is characterized in that, blank mixing wet ball mill to 100 order; Glaze mixing wet ball mill to 340 order.
CN201310675366.4A 2013-12-13 2013-12-13 Ceramic heating cup body Pending CN103641448A (en)