CN104446353B - High-temperature-resistant ceramic material for manufacturing pot body - Google Patents

High-temperature-resistant ceramic material for manufacturing pot body Download PDF

Info

Publication number
CN104446353B
CN104446353B CN201410742185.3A CN201410742185A CN104446353B CN 104446353 B CN104446353 B CN 104446353B CN 201410742185 A CN201410742185 A CN 201410742185A CN 104446353 B CN104446353 B CN 104446353B
Authority
CN
China
Prior art keywords
parts
temperature
pot
resistant ceramic
raw
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201410742185.3A
Other languages
Chinese (zh)
Other versions
CN104446353A (en
Inventor
成延栓
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nantong Henglong rack Co. Ltd.
Original Assignee
Nantong Henglong Rack Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nantong Henglong Rack Co Ltd filed Critical Nantong Henglong Rack Co Ltd
Priority to CN201410742185.3A priority Critical patent/CN104446353B/en
Publication of CN104446353A publication Critical patent/CN104446353A/en
Application granted granted Critical
Publication of CN104446353B publication Critical patent/CN104446353B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention relates to a high-temperature-resistant ceramic material for manufacturing a pot body. A manufacturing method of the high-temperature-resistant ceramic material comprises the following steps: S1, weighing raw materials in parts by mass: 11-18 parts of purple clay, 5-9 parts of black soil, 15-17 parts of sericite, 4-7 parts of hornblendes, 3-9 parts of vermiculite, 2-4 parts of pyroxene, 8-11 parts of granite, 5-10 parts of calcined talcum and 4-7 parts of quartz, mixing the raw materials, introducing the raw materials to a ball mill for grinding, and sieving with a 250-mesh sieve for later use; S2, dehydrating products obtained in the step S1; S3, drying, preserving the heat for 30 minutes and calcining the products dehydrated in the step S2 at the sintering temperature of 1320-1380 DEG C, thereby obtaining the high-temperature-resistant ceramic material for manufacturing the pot body. A special raw material formula is adopted, so that the high-temperature-resistant ceramic material for manufacturing the pot body has the properties, such as high strength, wear resistance and high temperature resistance, and is suitable for manufacturing various pot bodies.

Description

The high temperature ceramic material manufacturing for pot
Technical field
The present invention relates to pot material field, more particularly, to a kind of high temperature ceramic material for pot manufacture.
Background technology
Ceramic pan is safe and sanitary, and be suitable for boiling health cooking, and robust pot face is nontoxic, non-sticky spot and will not produce chemical action with food, heat conduction rapid with uniformly, that is, save trouble and fuel-efficient, have numerous benefits compared with iron pan or stainless-steel pan.But ceramic pan heat resistance on the market is general at present.
Content of the invention
It is an object of the invention to provide a kind of high temperature ceramic material for pot manufacture.
The object of the invention is achieved by the following technical programs:
There is provided a kind of high temperature ceramic material for pot manufacture, manufacture method comprises the following steps:
S1 weighs raw material: 11~18 parts of Red Stone Ware by following mass fraction, 5~9 parts of black earth, 15~17 parts of sericite, 4~7 parts of hornblend, 3~9 parts of Vermiculitum, 2~4 parts of pyroxene, 8~11 parts of granite, 5~10 parts of calcination of talc, 4~7 parts of quartz, raw material is mixed, honed 250 mesh sieves of goal barreling, standby;
S2 is by step s1 products therefrom processed;
Step s2 is dried and soak calcining by s3 through the product of processed.
Preferably, the raw material in step s1 is grouped into by each group of following weight fraction: 13 parts of Red Stone Ware, 7 parts of black earth, 16 parts of sericite, 6 parts of hornblend, 7 parts of Vermiculitum, 3 parts of pyroxene, 9 parts of granite, 8 parts of calcination of talc, 6 parts of quartz.
Preferably, in step s3, sintering temperature is 1320~1380 DEG C, temperature retention time 30min.
Compared with prior art, the method have the advantages that
The invention provides a kind of high temperature ceramic material for pot manufacture, using special composition of raw materials, thus there is high intensity, the performance such as wear-resisting, high temperature resistant it is adaptable to various pot manufacture.
Specific embodiment
With reference to specific embodiment, the present invention is further illustrated.
Embodiment 1
Present embodiment discloses a kind of high temperature ceramic material for pot manufacture, manufacture method comprises the following steps:
S1 weighs raw material: 13 parts of Red Stone Ware, 7 parts of black earth, 16 parts of sericite, 6 parts of hornblend, 7 parts of Vermiculitum, 3 parts of pyroxene, 9 parts of granite, 8 parts of calcination of talc, 6 parts of quartz by following mass fraction, raw material is mixed, honed 250 mesh sieves of goal barreling, standby;
S2 is by step s1 products therefrom processed;
Step s2 is dried by s3 through the product of processed, and soak is calcined, and sintering temperature is 1320 DEG C, temperature retention time 30min.
Embodiment 2
Present embodiment discloses a kind of high temperature ceramic material for pot manufacture, manufacture method comprises the following steps:
S1 weighs raw material: 11 parts of Red Stone Ware, 9 parts of black earth, 15 parts of sericite, 4 parts of hornblend, 9 parts of Vermiculitum, 2 parts of pyroxene, 11 parts of granite, 10 parts of calcination of talc, 4 parts of quartz by following mass fraction, raw material is mixed, honed 250 mesh sieves of goal barreling, standby;
S2 is by step s1 products therefrom processed;
Step s2 is dried by s3 through the product of processed, and soak is calcined, and sintering temperature is 1380 DEG C, temperature retention time 30min.
Embodiment 3
Present embodiment discloses a kind of high temperature ceramic material for pot manufacture, manufacture method comprises the following steps:
S1 weighs raw material: 18 parts of Red Stone Ware, 5 parts of black earth, 17 parts of sericite, 7 parts of hornblend, 3 parts of Vermiculitum, 4 parts of pyroxene, 8 parts of granite, 5 parts of calcination of talc, 7 parts of quartz by following mass fraction, raw material is mixed, honed 250 mesh sieves of goal barreling, standby;
S2 is by step s1 products therefrom processed;
Step s2 is dried by s3 through the product of processed, and soak is calcined, and sintering temperature is 1350 DEG C, temperature retention time 30min.
Embodiment 4
Present embodiment discloses a kind of high temperature ceramic material for pot manufacture, manufacture method comprises the following steps:
S1 weighs raw material: 12 parts of Red Stone Ware, 6 parts of black earth, 16 parts of sericite, 6 parts of hornblend, 5 parts of Vermiculitum, 3 parts of pyroxene, 10 parts of granite, 9 parts of calcination of talc, 5 parts of quartz by following mass fraction, raw material is mixed, honed 250 mesh sieves of goal barreling, standby;
S2 is by step s1 products therefrom processed;
Step s2 is dried by s3 through the product of processed, and soak is calcined, and sintering temperature is 1360 DEG C, temperature retention time 30min.

Claims (2)

1. a kind of high temperature ceramic material for pot manufacture is it is characterised in that the manufacture method of the described high temperature ceramic material for pot manufacture comprises the following steps:
S1 weighs raw material: 11~18 parts of Red Stone Ware by following mass fraction, 5~9 parts of black earth, 15~17 parts of sericite, 4~7 parts of hornblend, 3~9 parts of Vermiculitum, 2~4 parts of pyroxene, 8~11 parts of granite, 5~10 parts of calcination of talc, 4~7 parts of quartz, raw material is mixed, honed 250 mesh sieves of goal barreling, standby;
S2 is by step s1 products therefrom processed;
Step s2 is dried and soak calcining by s3 through the product of processed, and sintering temperature is 1320~1380 DEG C, temperature retention time 30min.
2. the high temperature ceramic material for pot manufacture according to claim 1, it is characterized in that, raw material in step s1 is grouped into by each group of following weight fraction: 13 parts of Red Stone Ware, 7 parts of black earth, 16 parts of sericite, 6 parts of hornblend, 7 parts of Vermiculitum, 3 parts of pyroxene, 9 parts of granite, 8 parts of calcination of talc, 6 parts of quartz.
CN201410742185.3A 2014-12-09 2014-12-09 High-temperature-resistant ceramic material for manufacturing pot body Active CN104446353B (en)