CN105455574A - Production technology for art tea tray - Google Patents
Production technology for art tea tray Download PDFInfo
- Publication number
- CN105455574A CN105455574A CN201410432433.4A CN201410432433A CN105455574A CN 105455574 A CN105455574 A CN 105455574A CN 201410432433 A CN201410432433 A CN 201410432433A CN 105455574 A CN105455574 A CN 105455574A
- Authority
- CN
- China
- Prior art keywords
- product
- tea tray
- tea
- production technology
- strength
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a production technology for an art tea tray. The production technology comprises the following steps that a high-strength reinforcing material, a high-strength adhesive, a purple sand raw material and a stabilizer are mixed uniformly according to the proportion; the high-strength reinforcing material, the high-strength adhesive, the purple sand raw material and the stabilizer mixed uniformly are processed into a blank product of the tea tray through high temperature and high pressure; the blank product is subjected to setting and nature determining for a proper period of time; a CNC machining center is adopted for cutting and shaping the blank product which is subjected to setting and nature determining; the product which is cut and shaped enters a numerical control sander to be polished; finally, the polished product is polished and burnished manually and elaborately to obtain the finished tea tray product. The tea tray produced through the technology never deforms or cracks, and is free of extraneous odor, high in strength and elastic, and damage to teaware is avoided; meanwhile, the color of the produced tea tray can change like purple sand, and the purposes of novel design, ingenious conception, unique process and good use effects are achieved.
Description
Technical field
The present invention relates to tea set field, be specifically related to a kind of production technology of Gung fu tea dish.
Background technology
As everyone knows, drinking tea is Chinese a kind of outstanding traditional culture, it is not only subject to eliminating of the modern society of Western Culture impact, pay attention to gradually people on the contrary deeply being liked in the situation of daily leisure life, although and along with the culture of west fast food and the busy impact of life step, and tea bag, teabag drink appearance, the custom of siping tea of people changes to some extent, but brew the good tea of a kettle and friend share or enjoy voluntarily, remain a quite pleasing pleasure.But, along with the progress of science and technology and the convenience of siping tea based on making tea are considered, occur that modern technologies are applied in the mode of making tea, such as use electromagnetic oven instead or gas oven boils water, tea tray device drainpipe water conservancy diversion ponding etc., wherein, have many flushings or scald hot kettle body, cup and the what is called unnecessary waste water such as to have urine examined generate during brewing tea, the processing mode of tea tray was after tea tray fills with waste water in the past, the water of tea tray is outwelled by side, then apt to deteriorate smelly the and derivative germ of the ponding in tea tray; Meanwhile, existing tea tray has wooden class, bamboo class, stone class, bakelite class, boccaro class, and wooden class and bamboo class tea tray there will be modification cracking after long-term use, also have paint peculiar smell.Although stone class and boccaro class tea tray can not modification ftracture, bad tea set can be collided in use, and build is heavy.And bakelite class tea tray also can modification, color is single and have peculiar smell.
Summary of the invention
For solving the problems of the technologies described above, we have proposed a kind of production technology of Gung fu tea dish, its tea tray produced is modification cracking never, free from extraneous odour, and intensity is good, flexible, and loved tea set of can not damaging; The tea tray color simultaneously produced can be equally ever-changing with boccaro.
For achieving the above object, technical scheme of the present invention is as follows:
A production technology for Gung fu tea dish, comprises the following steps:
The first step, high strength reinforcing material, high-strength structureal adhesives, boccaro raw material and stabilizing agent mix in proportion;
Second step, by HTHP, the blank product of tea tray is processed into above-mentioned high strength reinforcing material, high-strength structureal adhesives, boccaro raw material and the stabilizing agent mixed;
3rd step, by blank product through the sizing of appropriate time and qualitative;
4th step, to sizing and qualitative after blank product adopt numerical control machining center it is cut and moulding;
5th step, again by cutting and moulding after product introduction numerical control sander polish;
6th step, finally to the artificial manual grinding and buffing meticulously of the product after polishing.
Preferably, high strength reinforcing material, high-strength structureal adhesives, boccaro raw material and stabilizing agent mixed proportion is in a first step 10:35:50:5.
Preferably, high strength reinforcing material is in a first step high-intensity fiber.
Pass through technique scheme, the present invention is by mixing high strength reinforcing material, high-strength structureal adhesives, boccaro raw material according to a certain percentage with stabilizing agent, then the blank product of tea tray is processed into by HTHP, then by blank product through appropriate time sizing and qualitative after, adopt numerical control machining center to cut and moulding blank product again, and then the product introduction numerical control sander after cutting and moulding is polished; Finally to the artificial manual grinding and buffing meticulously of the product after polishing, tea tray finished product can be obtained.The tea tray finished product gone out by above-mentioned explained hereafter is modification cracking never, free from extraneous odour, and intensity is good, flexible, and loved tea set of can not damaging; The tea tray color simultaneously produced can also be equally ever-changing with boccaro, thus reach modern design, be skillfully constructed, the unique and object that the product result of use produced is good of technique.
Accompanying drawing explanation
In order to be illustrated more clearly in the embodiment of the present invention or technical scheme of the prior art, be briefly described to the accompanying drawing used required in embodiment or description of the prior art below, apparently, accompanying drawing in the following describes is only some embodiments of the present invention, for those of ordinary skill in the art, under the prerequisite not paying creative work, other accompanying drawing can also be obtained according to these accompanying drawings.
Fig. 1 is the flow chart of the production technology of a kind of Gung fu tea dish disclosed in the embodiment of the present invention.
Detailed description of the invention
Below in conjunction with the accompanying drawing in the embodiment of the present invention, be clearly and completely described the technical scheme in the embodiment of the present invention, obviously, described embodiment is only the present invention's part embodiment, instead of whole embodiments.Based on the embodiment in the present invention, those of ordinary skill in the art, not making the every other embodiment obtained under creative work prerequisite, belong to the scope of protection of the invention.
The invention provides a kind of production technology of Gung fu tea dish, its tea tray produced is modification cracking never, free from extraneous odour, and intensity is good, flexible, and loved tea set of can not damaging; The tea tray color simultaneously produced can be equally ever-changing with boccaro.
Below in conjunction with embodiment and detailed description of the invention, the present invention is further detailed explanation.
Embodiment.
As shown in Figure 1, a kind of production technology of Gung fu tea dish, comprises the following steps:
A1, high-intensity fiber, high-strength structureal adhesives and boccaro raw material, stabilizing agent to be mixed in proportion;
A2, the high-intensity fiber, high-strength structureal adhesives and the boccaro raw material that mix above-mentioned, stabilizing agent are processed into the blank product of tea tray by HTHP;
A3, by blank product through the sizing of appropriate time and qualitative;
A4, to sizing and qualitative after blank product adopt numerical control machining center it is cut and moulding;
A5, again by cutting and moulding after product introduction numerical control sander polish;
A6, finally to the artificial manual grinding and buffing meticulously of the product after polishing.
Wherein, in A1 step, the ratio that described high-intensity fiber mixes with high-strength structureal adhesives, boccaro raw material, stabilizing agent is 10:35:50:5.
In this example, the machining process that the present invention produces Gung fu tea dish is as follows: first by high-intensity fiber, high-strength structureal adhesives and boccaro raw material, stabilizing agent mixes in the ratio of 10:35:50:5 weight ratio, then above-mentioned mixed raw material is pressed the specification of tea tray, through the blank product of HTHP machine-shaping tea tray, then by blank product through the sizing of certain hour and qualitative, after making it reach the performance of next step procedure calls, adopt numerical control machining center to sizing and qualitative after blank product cut and moulding, with the tea tray product making it reach requirement moulding, and then the tea tray product that molded surface of being polished roughly by tea tray product introduction numerical control sander is comparatively smooth, finally, manually again craft grinding and buffing is meticulously carried out to the tea tray product after sander polishing, reject flaw, exquisite firm tea tray finished product can be obtained.Certainly, above-mentioned high-intensity fiber, high-strength structureal adhesives and boccaro raw material, stabilizing agent also can in the ratio mixed preparing of the weight ratio of other component, and at this, will not do special restriction, these equally all belong to protection scope of the present invention.
The tea tray finished product produced by above-mentioned Gung fu tea dish production technology, have the performance of never modification cracking, free from extraneous odour during immersion, in use procedure, intensity is good, has elasticity, and the tea set that the user that can not damage is loved; The tea tray color that above-mentioned tea tray production technology is produced simultaneously can also be equally ever-changing according to boccaro tableware, reach color consistency, itself and tea set is made to arrange in pairs or groups rationally, unified to coordinate, thus reach modern design, be skillfully constructed, the unique and object that the product result of use produced is good of technique.
Above-described is only the production technology preferred embodiment of a kind of Gung fu tea dish of the present invention; it should be pointed out that for the person of ordinary skill of the art, without departing from the concept of the premise of the invention; can also make some distortion and improvement, these all belong to protection scope of the present invention.
Claims (3)
1. a production technology for Gung fu tea dish, is characterized in that, comprises the following steps:
The first step, high strength reinforcing material, high-strength structureal adhesives, boccaro raw material and stabilizing agent to be mixed in proportion;
Second step, by HTHP, the blank product of tea tray is processed into above-mentioned high strength reinforcing material, high-strength structureal adhesives, boccaro raw material and the stabilizing agent mixed;
3rd step, by blank product through the sizing of appropriate time and qualitative;
4th step, to sizing and qualitative after blank product adopt numerical control machining center it is cut and moulding;
5th step, again by cutting and moulding after product introduction numerical control sander polish;
6th step, finally to the artificial manual grinding and buffing meticulously of the product after polishing.
2. the production technology of a kind of Gung fu tea dish according to claim 1, is characterized in that, high strength reinforcing material in a first step, high-strength structureal adhesives, boccaro raw material and stabilizing agent mixed proportion are 10:35:50:5.
3. the production technology of a kind of Gung fu tea dish according to claim 1 and 2, is characterized in that, high strength reinforcing material is in a first step high-intensity fiber.