CN105361599A - Kung Fu tea tray - Google Patents

Kung Fu tea tray Download PDF

Info

Publication number
CN105361599A
CN105361599A CN201410432415.6A CN201410432415A CN105361599A CN 105361599 A CN105361599 A CN 105361599A CN 201410432415 A CN201410432415 A CN 201410432415A CN 105361599 A CN105361599 A CN 105361599A
Authority
CN
China
Prior art keywords
raw material
tea
tea tray
blank
polishing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410432415.6A
Other languages
Chinese (zh)
Inventor
丁小华
丁渊星
戚武强
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Yixing Yuanxing Frp Fan Co Ltd
Original Assignee
Yixing Yuanxing Frp Fan Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Yixing Yuanxing Frp Fan Co Ltd filed Critical Yixing Yuanxing Frp Fan Co Ltd
Priority to CN201410432415.6A priority Critical patent/CN105361599A/en
Publication of CN105361599A publication Critical patent/CN105361599A/en
Pending legal-status Critical Current

Abstract

The invention discloses a Kung Fu tea tray made by: acquisition of materials, mixing, pressing, acquisition of blanks, sizing, cutting, rough polishing, finish polishing, and acquisition of finished products. The materials include: a high-strength reinforcing material 10%-20%, a high-strength binder 30%-40%, a stabilizer 3%-7%, and the balance of a redware material; a forming step includes: loading a mixture above into a mold, performing stamping molding with a stamping molding machine to obtain a tea tray blank, after a suitable time of sizing and qualifying, cutting and styling the tea tray blank with a computer numerical control machining center, polishing the blank in a computer numerical control polishing machine, and performing manual fine grinding and polishing until the outer surface is compact, flat and smooth and edge lines are straightly horizontal and vertical. The finished tea tray never deforms or cracks, has no peculiar odor, good strength and elasticity and never crash beloved tea sets; the produced tea tray has color as changing as that of redware.

Description

A kind of Gung fu tea dish
Technical field
The present invention relates to tea set field, be specifically related to a kind of Gung fu tea dish.
Background technology
Drinking tea is the outstanding traditional culture of a kind of Gung fu tea dish of China, it is not only subject to Western Culture impact, and modern society is superseded, pay attention to gradually people on the contrary deeply being liked in the situation of daily leisure life, although and along with the culture of west fast food and the busy impact of life step, and tea bag, teabag drink appearance, the custom of siping tea of people changes to some extent, but brew the good tea of a kettle and friend share or enjoy voluntarily, remain a quite pleasing pleasure.
But, along with the progress of science and technology and the convenience of siping tea based on making tea are considered, occur that modern technologies are applied in the mode of making tea, such as use electromagnetic oven instead or gas oven boils water, tea tray device drainpipe water conservancy diversion ponding etc., wherein, have many flushings or scald hot kettle body, cup and the what is called unnecessary waste water such as to have urine examined generate during brewing tea, the processing mode of tea tray was after tea tray fills with waste water in the past, the water of tea tray is outwelled by side, then apt to deteriorate smelly the and derivative germ of the ponding in tea tray; Meanwhile, existing tea tray has wooden class, bamboo class, stone class, bakelite class, boccaro class, and wooden class and bamboo class tea tray modification can ftracture, also have paint peculiar smell.Although stone class and boccaro class tea tray can not modification ftracture, bad tea set can be collided in use, and build is heavy.And bakelite class tea tray also can modification, color is single and have peculiar smell.
Summary of the invention
For solving the problems of the technologies described above, we have proposed a kind of Gung fu tea dish, it has never modification cracking, free from extraneous odour, and intensity is good, flexible, and loved tea set of can not damaging; This tea tray color can be equally ever-changing with boccaro simultaneously.
For achieving the above object, technical scheme of the present invention is as follows:
A kind of Gung fu tea dish, adopts following methods to be made: raw material-mixing-compacting-blank-sizing-cutting-corase grind-fine grinding-finished product, wherein:
Raw material, high strength reinforcing material: 10%-20%, high-strength structureal adhesives: 30%-40%, stabilizing agent: 3%-7%, boccaro raw material: surplus;
Shaping, by high strength reinforcing material, high-strength structureal adhesives, stabilizing agent and boccaro raw material according to the above ratio compound load mould, use impact molding machine punch forming, obtain tea tray blank product, through appropriate time sizing and qualitative after, adopt numerical control machining center it is cut and moulding, then enter numerical control sander and polish, finally use artificial manual grinding and buffing meticulously, smooth vertical and horizontal to fine and close, smooth, smooth, each arris fillet of its outer surface.
Preferably, wherein: raw material, the mixed proportion of high strength reinforcing material, high-strength structureal adhesives, boccaro raw material and stabilizing agent is respectively 10%, 35%, 50% and 5%.
Preferably, wherein: in raw material, high strength reinforcing material is high-intensity fiber.
Pass through technique scheme, the present invention is by mixing high strength reinforcing material, high-strength structureal adhesives, boccaro raw material and stabilizing agent according to a certain percentage, then the blank product of tea tray is processed into by HTHP, then by blank product through appropriate time sizing and qualitative after, adopt numerical control machining center to cut and moulding blank product again, and then the product introduction numerical control sander after cutting and moulding is polished; Finally to the artificial manual grinding and buffing meticulously of the product after polishing, tea tray finished product can be obtained.Because high strength reinforcing material has elasticity, add the characteristic of boccaro raw material, make this tea tray have the characteristic of never modification cracking, free from extraneous odour, intensity is good, flexible, and loved tea set of can not damaging when using; The tea tray color simultaneously produced can also be equally ever-changing with boccaro, thus reach modern design, be skillfully constructed, the unique and object that result of use is good of technique.
Detailed description of the invention
Below in conjunction with embodiments of the invention, be clearly and completely described the technical scheme in the embodiment of the present invention, obviously, described embodiment is only the present invention's part embodiment, instead of whole embodiments.Based on the embodiment in the present invention, those of ordinary skill in the art, not making the every other embodiment obtained under creative work prerequisite, belong to the scope of protection of the invention.
The invention provides a kind of Gung fu tea dish, it has never modification cracking, free from extraneous odour, and intensity is good, flexible, and loved tea set of can not damaging; This tea tray color can be equally ever-changing with boccaro simultaneously.
Below in conjunction with embodiment and detailed description of the invention, the present invention is further detailed explanation.
Embodiment.
Gung fu tea dish of the present invention, adopts following methods to be made: raw material-mixing-compacting-blank-sizing-cutting-corase grind-fine grinding-finished product, wherein:
The raw material preparation program of the proportioning of raw material is: the mixed proportion of high-intensity fiber, high-strength structureal adhesives, boccaro raw material and stabilizing agent is respectively 10%, 35%, 50% and 5%, certain pulp furnish also can be the arbitrary collocation in following scope, high-intensity fiber: 10%-20%, high-strength structureal adhesives: 30%-40%, stabilizing agent: 3%-7%, boccaro raw material: surplus.Certainly, at this also not as the restriction to the technical program raw material said ratio, the technical program pulp furnish also can be other ratio collocation, these equally all belong to protection scope of the present invention.
Forming process is as follows: first by high-intensity fiber, high-strength structureal adhesives, stabilizing agent and boccaro raw material are by 10%, 35%, the ratio of 5% and 50% mixes, then compound is loaded mould, with impact molding machine under the condition of HTHP, the blank product of processing punch forming tea tray, through appropriate time sizing and qualitative after, numerical control machining center is adopted to cut and moulding it, the blank of shaping tea tray product, then the blank of numerical control sander to above-mentioned tea tray product is adopted to polish roughly, operating personnel are finally allowed to use artificial manual grinding and buffing meticulously again, outer surface to tea tray is fine and close, smooth, smooth, and each arris fillet is smooth vertical and horizontal, exquisite unique tea tray finished product can be obtained.
In this example, Gung fu tea dish of the present invention is owing to being by high-intensity fiber, high-strength structureal adhesives, boccaro raw material and stabilizing agent being mixed according to a certain percentage, then the blank product of tea tray is processed into by HTHP, then by blank product through appropriate time sizing and qualitative after, adopt numerical control machining center to cut and moulding blank product again, and then the product introduction numerical control sander after cutting and moulding is polished; Finally to the artificial manual grinding and buffing meticulously of the product after polishing, tea tray finished product can be obtained.Because high-intensity fiber has elasticity, add the characteristic of boccaro raw material, make this tea tray have the characteristic of never modification cracking, free from extraneous odour during immersion, in use procedure, intensity is good, flexible, and the tea set that the user that can not damage when using is loved; The tea tray color that above-mentioned tea tray production technology is produced simultaneously can also be equally ever-changing according to boccaro tableware, reach color consistency, itself and tea set is made to arrange in pairs or groups rationally, unified to coordinate, thus reach modern design, be skillfully constructed, the unique and object that the product result of use produced is good of technique.
Above-described is only a kind of Gung fu tea dish preferred embodiment of the present invention; it should be pointed out that for the person of ordinary skill of the art, without departing from the concept of the premise of the invention; can also make some distortion and improvement, these all belong to protection scope of the present invention.

Claims (3)

1. a Gung fu tea dish, is characterized in that, adopts following methods to be made: raw material-mixing-compacting-blank-sizing-cutting-corase grind-fine grinding-finished product, wherein:
Raw material, high strength reinforcing material: 10%-20%, high-strength structureal adhesives: 30%-40%, stabilizing agent: 3%-7%, boccaro raw material: surplus;
Shaping, by high strength reinforcing material, high-strength structureal adhesives, stabilizing agent and boccaro raw material according to the above ratio compound load mould, use impact molding machine punch forming, obtain tea tray blank product, through appropriate time sizing and qualitative after, adopt numerical control machining center it is cut and moulding, then enter numerical control sander and polish, finally use artificial manual grinding and buffing meticulously, smooth vertical and horizontal to fine and close, smooth, smooth, each arris fillet of its outer surface.
2. a kind of Gung fu tea dish according to claim 1, is characterized in that, wherein: raw material, the mixed proportion of high strength reinforcing material, high-strength structureal adhesives, boccaro raw material and stabilizing agent is respectively 10%, 35%, 50% and 5%.
3. a kind of Gung fu tea dish according to claim 1 and 2, is characterized in that, wherein: in raw material, high strength reinforcing material is high-intensity fiber.
CN201410432415.6A 2014-08-28 2014-08-28 Kung Fu tea tray Pending CN105361599A (en)