CN102516756A - 一种透明尼龙的制备方法 - Google Patents
一种透明尼龙的制备方法 Download PDFInfo
- Publication number
- CN102516756A CN102516756A CN2011104192986A CN201110419298A CN102516756A CN 102516756 A CN102516756 A CN 102516756A CN 2011104192986 A CN2011104192986 A CN 2011104192986A CN 201110419298 A CN201110419298 A CN 201110419298A CN 102516756 A CN102516756 A CN 102516756A
- Authority
- CN
- China
- Prior art keywords
- mass parts
- nylon
- preparation
- transparent nylon
- transparent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种透明尼龙的制备方法，该方法包括如下步骤：将170-175质量份尼龙6、130-135质量份尼龙66、30-45质量份POE、10-15质量份硬脂酸钙、50-60质量份聚燃烃弹性体、19质量份抗氧剂1010、20质量份双马来酰亚胺和15质量份己二酸搅拌混合，将混合均匀的物料加入挤出机，经挤出造粒并干燥，即得。本发明方法工艺简单，便于大规模生产，且该方法生产出的产品具有良好的拉伸强度、耐冲击强度、刚性、耐磨性、耐化学性、表面硬度等性能，透光率高，与光学玻璃相近。
Description
技术领域
本发明属于高分子材料领域，具体涉及一种透明尼龙的制备方法。
技术背景
聚酰胺纤维俗称尼龙（Nylon），英文名称Polyamide（简称PA），是分子主链上含有重复酰胺基团—[NHCO]—的热塑性树脂总称。尼龙作为工程塑料中最大最重要的品种，具有很强的生命力，主要在于它改性后实现高性能化，其次是汽车、电器、通讯、电子、机械等产业自身对产品高性能的要求越来越强烈，相关产业的飞速发展，促进了工程塑料高性能化的进程，未来发展趋势是各种各样的改性尼龙。透明尼龙由于高透光率和高耐冲击强度、刚性渐渐替换玻璃，但是在成型加工时，熔体温度难以控制，太高会因降解而导致制品变色，温度太低会因塑化不良而影响制品的透明度。
发明内容
本发明目的是提供一种透明尼龙的制备方法。
本发明的目的是通过以下技术方案实现的：一种透明尼龙的制备方法，该方法包括如下步骤：将170-175质量份尼龙6、130-135质量份尼龙66、30-45质量份POE、10-15质量份硬脂酸钙、50-60质量份聚燃烃弹性体、19质量份抗氧剂1010、20质量份双马来酰亚胺和15质量份己二酸搅拌混合，将混合均匀的物料加入挤出机，经挤出造粒并干燥，即得。 尼龙6：相对粘度2.5-3.0，岳阳石油化工总厂化纤厂；尼龙66：相对粘度2.8-3.0，上海塑料十八厂；抗氧剂1010：瑞士汽巴公司。
有益效果：本发明方法工艺简单，便于大规模生产，且该方法生产出的产品具有良好的拉伸强度、耐冲击强度、刚性、耐磨性、耐化学性、表面硬度等性能，透光率高，与光学玻璃相近。
具体实施方式
实施例1
一种透明尼龙的制备方法，该方法包括如下步骤：将170-175质量份尼龙6、130-135质量份尼龙66、30-45质量份POE、10-15质量份硬脂酸钙、50-60质量份聚燃烃弹性体、19质量份抗氧剂1010、20质量份双马来酰亚胺和15质量份己二酸搅拌混合，将混合均匀的物料加入挤出机，经挤出造粒并干燥，即得。 尼龙6：相对粘度2.5-3.0，岳阳石油化工总厂化纤厂；尼龙66：相对粘度2.8-3.0，上海塑料十八厂；抗氧剂1010：瑞士汽巴公司。
Claims (1)
1.一种透明尼龙的制备方法，其特征在于该方法包括如下步骤：将170-175质量份尼龙6、130-135质量份尼龙66、30-45质量份POE、10-15质量份硬脂酸钙、50-60质量份聚燃烃弹性体、19质量份抗氧剂1010、20质量份双马来酰亚胺和15质量份己二酸搅拌混合，将混合均匀的物料加入挤出机，经挤出造粒并干燥，即得。