CN102504184A - 增强型水性聚氨酯固化剂的制备方法 - Google Patents

增强型水性聚氨酯固化剂的制备方法 Download PDF

Info

Publication number
CN102504184A
CN102504184A CN2011103379711A CN201110337971A CN102504184A CN 102504184 A CN102504184 A CN 102504184A CN 2011103379711 A CN2011103379711 A CN 2011103379711A CN 201110337971 A CN201110337971 A CN 201110337971A CN 102504184 A CN102504184 A CN 102504184A
Authority
CN
China
Prior art keywords
preparation
liquor
reaction
hdi
mdi
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2011103379711A
Other languages
English (en)
Inventor
钱华
张林荣
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
WUJIANG BEISHE SHENGYUAN TEXTILE AUXILIARIES FACTORY
Original Assignee
WUJIANG BEISHE SHENGYUAN TEXTILE AUXILIARIES FACTORY
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by WUJIANG BEISHE SHENGYUAN TEXTILE AUXILIARIES FACTORY filed Critical WUJIANG BEISHE SHENGYUAN TEXTILE AUXILIARIES FACTORY
Priority to CN2011103379711A priority Critical patent/CN102504184A/zh
Publication of CN102504184A publication Critical patent/CN102504184A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种增强型水性聚氨酯固化剂的制备方法，包括以下步骤：a、在干燥清洁的反应釜中加入有机溶剂甲基异丁基酮、MDI、HDI和催化剂量的二月桂酸二丁基锡，加热溶解；b、将计量聚乙二醇PEG-2000、聚丙三醇PPG-800和甲基异丁基酮混溶，得到b液；c、将b液缓慢滴加到a液中，在60~80℃下反应1~5h得到预聚产物；d、在步骤c获得产物中加入1，4-丁二醇和二羟基丙酸，保温反应1~5h，得到封端的聚氨酯乳液；e、向反应液中加入三乙胺水溶液中和剂，调节PH=6~7，降至常温即可。本发明获得的纺织涂层，能提高涂膜的爽滑性和耐水性，具有较强的拉升强度和适中的延展性。

Description

增强型水性聚氨酯固化剂的制备方法
技术领域：
本发明涉及一种增强型水性聚氨酯固化剂，特别涉及增强型水性聚氨酯固化剂的制备方法。
背景技术：
聚氨酯是由多异氰酸酯与多元醇反应生成的以氨基甲酸酯基为重复单元的高分子化合物。聚氨酯树脂具有软硬度可调、耐磨、耐溶剂、耐低温及与大多数材料有较强粘接性等特点，近年来发展迅速。目前聚氨酯已经成功地应用于纺织印染行业，它能赋予织物优良的柔软度、丰满感、耐洗、耐磨、回弹性好、滑爽、手感好、抗静电等，在纺织行业中的研究开发和应用得到了广泛而迅速的发展。常用的多异氰酸酯单体主要有2，4-二甲基二异氰酸酯（TDI）、4,4’-二苯甲烷二异氰酸酯（MDI）、异佛尔酮二异氰酸酯（IPDI）、六亚甲基二异氰酸酯（HDI）等，由于TDI、MDI含有刚性芳环，使得聚氨酯的内聚力比较大，具有较强的拉伸强度，芳环的存在会使胶膜容易发黄。IPDI由于含有脂环也使聚氨酯的强度较大，而HDI不含环状结构，强度较小，但是其结构比较规整，使得聚氨酯胶膜结晶。对于特种高强度，高耐撕裂型纺织材料，作为其固化剂的原料， TDI、MDI不耐黄变， IPDI的强度较大、HDI的胶膜结晶，单独使用都不能取得令人满意的效果。
本实验通过异氰酸酯共混，增加水性聚氨酯结构中硬段与苯环的含量，减少亲水基团的用量，进行部分内交联来提高水性聚氨酯的强度、耐磨性和高耐水性。
发明内容：
发明目的：针对现有技术存在的缺陷，本发明提供了一种增强型水性聚氨酯固化剂的制备方法。
技术方案：为实现上述发明目的，本发明采用以下技术方案：一种增强型水性聚氨酯固化剂的制备方法，包括以下步骤：a、在干燥清洁的反应釜中加入有机溶剂甲基异丁基酮、MDI、HDI和催化剂量的二月桂酸二丁基锡，加热溶解；b、将计量聚乙二醇PEG-2000、聚丙三醇PPG-800和甲基异丁基酮混溶，得到b液；c、将b液缓慢滴加到a液中，在60~80℃下反应1~5h得到预聚产物；d、在步骤c获得产物中加入1，4-丁二醇和二羟基丙酸，保温反应1~5h，得到封端的聚氨酯乳液；e、向反应液中加入三乙胺水溶液中和剂，调节PH=6~7，降至常温即可。
所述MDI与HDI的质量比为1~5：1。
所述PEG-2000与PPG-800的质量比为1~5：1。
有益效果：与现有技术相比，本发明具有以下优点：本发明获得的纺织涂层，能提高涂膜的爽滑性和耐水性，具有较强的拉升强度和适中的延展性。 
具体实施方式：
    下面结合实施例对本发明做进一步地详细说明，但是本发明要求保护的范围并不局限于实施例表示的范围。
实施例1：
在干燥，清洁的反应釜中依次加入有机溶剂甲基异丁基酮（125kg）和4,4’-二苯甲烷二异氰酸酯（320.0kg），六亚甲基二异氰酸酯（100kg）催化剂二月桂酸二丁基锡(1.35kg)，搅拌下加热至40~60℃溶解，待用；称取PEG-2000 (255.0kg)，PPG-800（155.0kg），甲基异丁基酮（150.0kg），混溶，缓慢滴加入上述反应溶液中，控制温度在70~80℃，反应1~5h，反应毕，向反应产物中加入1，4-丁二醇(130.0kg)和二羟基丙酸(12.5kg)，反应1~5h， 降温至80℃，加入中和剂三乙胺水溶液(1905.0kg)， 调节PH=6.7，降温至室温，封装得产品。

Claims (3)

1.一种增强型水性聚氨酯固化剂的制备方法，其特征在于：a、在干燥清洁的反应釜中加入有机溶剂甲基异丁基酮、MDI、HDI和催化剂量的二月桂酸二丁基锡，加热溶解；b、将计量聚乙二醇PEG-2000、聚丙三醇PPG-800和甲基异丁基酮混溶，得到b液；c、将b液缓慢滴加到a液中，在60~80℃下反应1~5h得到预聚产物；d、在步骤c获得产物中加入1，4-丁二醇和二羟基丙酸，保温反应1~5h，得到封端的聚氨酯乳液；e、向反应液中加入三乙胺水溶液中和剂，调节PH=6~7，降至常温即可。
2.根据权利要求1所述增强型水性聚氨酯固化剂的制备方法，其特征在于：所述MDI与HDI的质量比为1~5：1。
3.根据权利要求1所述增强型水性聚氨酯固化剂的制备方法，其特征在于：所述PEG-2000与PPG-800的质量比为1~5：1。
CN2011103379711A 2011-11-01 2011-11-01 增强型水性聚氨酯固化剂的制备方法 Pending CN102504184A (zh)