CN102503348B - 一种复合保温板制造方法 - Google Patents

一种复合保温板制造方法 Download PDF

Info

Publication number
CN102503348B
CN102503348B CN2011103547100A CN201110354710A CN102503348B CN 102503348 B CN102503348 B CN 102503348B CN 2011103547100 A CN2011103547100 A CN 2011103547100A CN 201110354710 A CN201110354710 A CN 201110354710A CN 102503348 B CN102503348 B CN 102503348B
Authority
CN
China
Prior art keywords
raw material
heat
preparation
inorganic porous
mixing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN2011103547100A
Other languages
English (en)
Other versions
CN102503348A (zh
Inventor
李春普
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN2011103547100A priority Critical patent/CN102503348B/zh
Publication of CN102503348A publication Critical patent/CN102503348A/zh
Application granted granted Critical
Publication of CN102503348B publication Critical patent/CN102503348B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明提出的是一种复合保温板制造方法，其特征是：经过有机纤维原料制备、无机多孔原料制备、胶结剂制备、辅料制备和添加剂配制制备原料，经原料配合、拌胶、压制过程制成复合保温板。由于本发明复合保温板由有机纤维原料和无机多孔原料及辅料通过无机胶结剂胶合压制制成。所制成的保温板阻燃，容重小、隔热保温性能好、材料来源广泛，价格低，并且利用了废弃物，产生环保的效果。适宜作为建筑墙面保温隔热材料应用。

Description

一种复合保温板制造方法
技术领域
 本发明提出的是建筑材料领域的隔热材料，具体地说是一种复合保温板制造方法。
背景技术
现有用于墙体保温的保温板有聚苯乙烯泡沫板，存在缺点是易燃，容易引起火灾，燃烧时产生有毒气体，危害人身安全。还有珍珠岩保温板，存在缺点是容重大，吸水性强，安装固定困难。也有无机泡沫材料，包括发泡水泥制品、发泡菱镁水泥制品、泡沫玻璃、岩棉板，存在缺点是容重大，保温系数低，隔热性能差。
发明内容
为了克服现有建筑保温板所存在的缺点，本发明提出了一种复合保温板制造方法。该保温板以有机纤维原料和无机多孔原料混合，以掺有拒水剂的水玻璃作为粘结剂，并配合辅料，经常温压合制成，解决保温板隔热、保温和阻燃防火的技术问题。
本发明解决技术问题所采用的方案是：
1、有机纤维原料制备：将植物茎杆切断成为段，经过揉草机揉搓制成纤维束状，与锯末一起作为有机纤维原料。
2、无机多孔原料制备：将珍珠岩或蛭石矿砂经过高温膨化，制成膨胀珍珠岩颗粒或膨胀蛭石，作为无机多孔原料。
3、胶结剂制备：在水玻璃溶液中加入有机硅拒水剂，搅拌均匀，作为胶结剂。
4、辅料制备：选择轻质碳酸钙或生石灰粉作为辅料。
5、添加剂配制：在辅料中加入硫酸钾铝和四硼酸钠的添加剂。
制造过程：
1、原料配合：有机纤维原料与无机多孔原料配合后搅拌均匀，组成混合原料。
2、拌胶：在混合原料中加入胶结剂，搅拌混合均匀，在搅拌混合的同时，加入辅料和添加剂，继续搅拌，直至原料与辅料混合均匀。
3、压制：将混合后的混合料加入到模具中，加压，制成设定厚度板状，干燥后成为成品复合保温板。
积极效果，由于本发明复合保温板由有机纤维原料和无机多孔原料及辅料通过无机胶结剂胶合压制制成。所制成的保温板阻燃，容重小、隔热保温性能好、材料来源广泛，价格低，并且利用了废弃物，产生环保的效果。适宜作为建筑墙面保温隔热材料应用。
具体实施方式
 原料制备：
1、有机纤维原料制备：将植物茎杆切断成为段，段长0.5～2厘米，经过揉草机揉搓制成纤维束状，与锯末一起共同作为有机纤维原料。
2、无机多孔原料制备：将珍珠岩矿砂经过高温膨化，制成粒径在1～5毫米的膨胀珍珠岩颗粒，或粒径1～5毫米膨胀蛭石，作为无机多孔原料。
3、胶结剂制备：在模数为3.0～3.3的水玻璃溶液中加入质量比为6～8%的有机硅拒水剂，搅拌均匀，作为胶结剂。
4、辅料制备：选择粒径在0.15～0.074mm之间的轻质碳酸钙，或粒径在0.1～0.074mm之间的生石灰粉，作为辅料。
5、添加剂配制：在辅料中加入质量比0.5～1%的硫酸钾铝和0.5～1%的四硼酸钠的添加剂。
制造过程：
1、原料配合：有机纤维原料与无机多孔原料配合后搅拌均匀，组成混合原料，配合质量比为有机纤维原料占65～85%，无机多孔原料占35～15%。
2、拌胶：在混合原料中加入质量百分比为30～50%的胶结剂，搅拌混合均匀，在搅拌混合的同时，加入加有硫酸钾铝和四硼酸钠添加剂的轻质碳酸钙或石灰粉辅料，继续搅拌，直至原料与辅料混合均匀。
3、压制：将混合后的混合料加入到模具中，加压，制成设定厚度板状，干燥后成为成品复合保温板。
有机纤维原料用农作物秸秆、蒿草、芦苇、树枝、树叶和锯末。
无机多孔原料用膨胀珍珠岩颗粒或膨胀蛭石颗粒。
用途：
作为墙体外墙保温层，或作为外墙苯板保温板敷设之间的防火隔离板。
优点：
本发明保温板的原材料大部分采用农业废弃物，不但净化了环境，而且变废为宝，增加了农民收入。所制成的复合保温板耐水、容重轻、隔热保温性能好、而且阻燃防腐，制造成本低，节能，减少碳排放，适宜广泛推广应用。

Claims (1)

1.一种复合保温板制造方法，其特征是：
原料制备：
1）、有机纤维原料制备：将植物茎杆切断成为段，段长0.5～2厘米，经过揉草机揉搓制成纤维束状，与锯末一起共同作为有机纤维原料；
2）、无机多孔原料制备：将珍珠岩矿砂经过高温膨化，制成粒径在1～5毫米的膨胀珍珠岩颗粒，或粒径1～5毫米膨胀蛭石，作为无机多孔原料；
3）、胶结剂制备：在模数为3.0～3.3的水玻璃溶液中加入质量比为6～8%的有机硅拒水剂，搅拌均匀，作为胶结剂；
4）、辅料制备：选择粒径在0.15～0.074mm之间的轻质碳酸钙，或粒径在0.1～0.074mm之间的生石灰粉，作为辅料；
5）、添加剂配制：在辅料中加入质量比0.5～1%的硫酸钾铝和0.5～1%的四硼酸钠的添加剂；
制造过程：
1）、原料配合：有机纤维原料与无机多孔原料配合后搅拌均匀，组成混合原料，配合质量比为有机纤维原料占65～85%，无机多孔原料占35～15%；
2）、拌胶：在混合原料中加入质量百分比为30～50%的胶结剂，搅拌混合均匀，在搅拌混合的同时，加入加有硫酸钾铝和四硼酸钠添加剂的轻质碳酸钙或石灰粉辅料，继续搅拌，直至原料与辅料混合均匀；
3）、压制：将混合后的混合料加入到模具中，加压，制成设定厚度板状，干燥后成为成品复合保温板。
CN2011103547100A 2011-11-10 2011-11-10 一种复合保温板制造方法 Expired - Fee Related CN102503348B (zh)