CN102503240B - 软陶泥及其制作方法 - Google Patents
软陶泥及其制作方法 Download PDFInfo
- Publication number
- CN102503240B CN102503240B CN 201110342177 CN201110342177A CN102503240B CN 102503240 B CN102503240 B CN 102503240B CN 201110342177 CN201110342177 CN 201110342177 CN 201110342177 A CN201110342177 A CN 201110342177A CN 102503240 B CN102503240 B CN 102503240B
- Authority
- CN
- China
- Prior art keywords
- cooling
- mix
- pottery clay
- calcium stearate
- soft pottery
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明涉及一种软陶泥及其制作方法，所述软陶泥，包括混合搅拌在一起的以下成分：聚氯乙烯糊树脂、双硬脂酸铝、硬脂酸锌、硬脂酸钙、邻苯二甲酸二辛酯、钛白粉、搀混树脂、二氧化硅。所述软陶泥的制作方法，其包括以下步骤：1)提供聚氯乙烯糊树脂、双硬脂酸铝、硬脂酸锌、硬脂酸钙、邻苯二甲酸二辛酯、钛白粉、搀混树脂、二氧化硅，混合搅拌后放置冷却；2)冷却后放入搅拌机搅拌，之后取出等待它冷却；3)冷却后再放入搅拌机搅拌，之后取出等待它冷却；4)冷却后混入色粉并搅拌均匀，然后等它冷却后即为成品。本发明经手工艺可做出各种花形，花形附与物体表面及内部，如不经过高温此软陶泥可以反复使用，有很强的可塑性，粘性高。
Description
技术领域
本发明涉及软陶领域，尤其涉及一种软陶泥及其制作方法。
背景技术
现有技术中的软陶泥可塑性和粘性均不强，而且做出的产品花形也仅限于在表层体现，产品内部并无该花形体现，趣味性和艺术鉴赏性差。
发明内容
有鉴于此，本发明所要解决的技术问题是：提供一种可塑性和粘性更高的软陶泥及其制作方法。
为了达到上述目的，本发明采用如下技术方案来实现的：
一种软陶泥，其中，包括混合搅拌在一起的以下成分：聚氯乙烯糊树脂、双硬脂酸铝、硬脂酸锌、硬脂酸钙、邻苯二甲酸二辛酯、钛白粉、搀混树脂、二氧化硅。
作为优选，各所述成分的重量份分别为：聚氯乙烯糊树脂20、双硬脂酸铝1.1、硬脂酸锌1.1、硬脂酸钙1.1、邻苯二甲酸二辛酯10、钛白粉1、搀混树脂2、二氧化硅1.5。
所述软陶泥的制作方法，其包括以下步骤：
1)提供以下成分：聚氯乙烯糊树脂、双硬脂酸铝、硬脂酸锌、硬脂酸钙、邻苯二甲酸二辛酯、钛白粉、搀混树脂、二氧化硅，混合搅拌后放置冷却；
2)冷却后放入搅拌机搅拌，之后取出等待它冷却；
3)冷却后再放入搅拌机搅拌，之后取出等待它冷却；
4)冷却后混入色粉并搅拌均匀，然后等它冷却后即为成品。
作为优选，所述步骤1中混合搅拌40分钟，步骤2中搅拌40分钟，步骤3中搅拌30分钟。
作为优选，各所述成分的重量份分别为：聚氯乙烯糊树脂20、双硬脂酸铝1.1、硬脂酸锌1.1、硬脂酸钙1.1、邻苯二甲酸二辛酯10、钛白粉1、搀混树脂2、二氧化硅1.5。
由上述技术方案可知，本发明的有益效果是：
相比现有技术，本发明通过采用上述成分制成的软陶泥，经过手工艺可以做出各种漂亮的花形，做出的花形不仅附与物体的表面，拿刀切下去后会发现里面也是这样的一种花形，是任何一种产品无法代替与达到的。而且如不经过高温此软陶泥可以反复使用，有很强的可塑性，粘性高，例如：橡皮泥与此软陶泥无法相比。此产品做出各种成品后颜色非常漂亮，可以做各种各样的小商品或商品配件，无任何条件限制。同时，产品经过高温后可以达到长期放置的效果，不因时间，水，火而变型。
具体实施方式
为了使本领域技术人员能更进一步了解本发明的特征及技术内容，请参阅以下有关本发明的详细说明。
本发明提供了一种软陶泥，其中，包括混合搅拌在一起的以下成分：聚氯乙烯糊树脂、双硬脂酸铝、硬脂酸锌、硬脂酸钙、邻苯二甲酸二辛酯、钛白粉、搀混树脂、二氧化硅。
在本实施例中，各所述成分的重量份分别为：聚氯乙烯糊树脂20、双硬脂酸铝1.1、硬脂酸锌1.1、硬脂酸钙1.1、邻苯二甲酸二辛酯10、钛白粉1、搀混树脂2、二氧化硅1.5。
所述软陶泥的制作方法，其包括以下步骤：
1)提供以下成分：聚氯乙烯糊树脂、双硬脂酸铝、硬脂酸锌、硬脂酸钙、邻苯二甲酸二辛酯、钛白粉、搀混树脂、二氧化硅，混合搅拌后放置冷却；
2)冷却后放入搅拌机搅拌，之后取出等待它冷却；
3)冷却后再放入搅拌机搅拌，之后取出等待它冷却；
4)冷却后混入色粉并搅拌均匀，然后等它冷却后即为成品。
在本实施例中，所述步骤1中混合搅拌40分钟，步骤2中搅拌40分钟，步骤3中搅拌30分钟。各所述成分的重量份分别为：聚氯乙烯糊树脂20、双硬脂酸铝1.1、硬脂酸锌1.1、硬脂酸钙1.1、邻苯二甲酸二辛酯10、钛白粉1、搀混树脂2、二氧化硅1.5。
其中，所述聚氯乙烯糊树脂优选采用聚氯乙烯糊树脂P-440GP620，所述钛白粉优选采用钛白粉A100，所述搀混树脂优选采用搀混树脂SB-100，所述邻苯二甲酸二辛酯也可以用柠檬酸替代。步骤1中的混合搅拌时间通常按产品需要决定时间，时间长就变得软，短则硬些，一般为40分钟左右即可。步骤2和步骤3中的搅拌步骤是必须的，否则无法达到本发明预定效果，本发明制作方法做出的成品就可以给工人操作使用了，根据客户各种需求来样订做。各种形态的样子做好后，将其放入烤箱中烘烤30分钟左右(因产品的不同烘靠的时间也有所变化)，烤的过程中注意温度，温度一般是130度，(因产品厚度不一样有所变化，温度过高或过久会有一些变黑)。
经过实验数据论证得出，本发明中软陶泥的可塑性是普通橡皮泥产品的1.5倍，粘性是普通橡皮泥产品的1.2倍，而且本发明成本更低，趣味性和艺术鉴赏性更强
但以上所述仅为本发明的较佳可行实施例，并非用以局限本发明的专利范围，故凡运用本发明说明书内容所作的等效结构变化，均同理包含在本发明的范围内。
Claims (3)
1.一种软陶泥，其特征在于，其包括混合搅拌在一起的以下成分：聚氯乙烯糊树脂、双硬脂酸铝、硬脂酸锌、硬脂酸钙、邻苯二甲酸二辛酯、钛白粉、搀混树脂、二氧化硅，各所述成分的重量份分别为：聚氯乙烯糊树脂20、双硬脂酸铝1.1、硬脂酸锌1.1、硬脂酸钙1.1、邻苯二甲酸二辛酯10、钛白粉1、搀混树脂2、二氧化硅1.5。
2.一种软陶泥的制作方法，其特征在于，包括以下步骤：
1)提供以下成分：聚氯乙烯糊树脂、双硬脂酸铝、硬脂酸锌、硬脂酸钙、邻苯二甲酸二辛酯、钛白粉、搀混树脂、二氧化硅，混合搅拌后放置冷却；
2)冷却后放入搅拌机搅拌，之后取出等待它冷却；
3)冷却后再放入搅拌机搅拌，之后取出等待它冷却；
4)冷却后混入色粉并搅拌均匀，然后等它冷却后即为成品；
各所述成分的重量份分别为：聚氯乙烯糊树脂20、双硬脂酸铝1.1、硬脂酸锌1.1、硬脂酸钙1.1、邻苯二甲酸二辛酯10、钛白粉1、搀混树脂2、二氧化硅1.5。
3.如权利要求2所述的软陶泥的制作方法，其特征在于，所述步骤1中混合搅拌40分钟，步骤2中搅拌40分钟，步骤3中搅拌30分钟。