CN102493060A - Blended yarn of jute fiber, hemp fiber and silk fiber and application of blended yarn - Google Patents
Blended yarn of jute fiber, hemp fiber and silk fiber and application of blended yarn Download PDFInfo
- Publication number
- CN102493060A CN102493060A CN2011103999112A CN201110399911A CN102493060A CN 102493060 A CN102493060 A CN 102493060A CN 2011103999112 A CN2011103999112 A CN 2011103999112A CN 201110399911 A CN201110399911 A CN 201110399911A CN 102493060 A CN102493060 A CN 102493060A
- Authority
- CN
- China
- Prior art keywords
- jute
- hemp
- fabric
- fiber
- silk
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a blended yarn of a jute fiber, a hemp fiber and a silk fiber. The blended yarn is made by blending the following raw materials in percentage by weight: 30 to 55 percent of jute fiber, 20 to 30 percent of hemp fiber and 25 to 40 percent of silk fiber. By blending the jute yarn, the jute fiber, the hemp fiber and the silk fiber in a reasonable proportion, the blended yarn overcomes the defects that the jute fabric is rough and hard and easy to drape, and has the advantages of moisture absorption, air permeability, antibacterium and the like of the jute fabric. Blended fabric made of the blended yarn is elegant, bright and exquisite in dyeing effect, is smooth and warm, has soft handfeel, and has the functions of dispersing sound wave, broadcast, ultraviolet and the like. Besides, the blended yarn is suitable for making warm clothes, ultraviolet radiation prevention clothes and the like.
Description
Technical field
The invention belongs to field of textiles, relate in particular to the blended yarn and the application thereof of a kind of jute and hemp and silk fiber.
Background technology
Along with constantly riseing of the prices of raw and semifnished materials such as silk fiber, chemical fiber; People begin to demand alternative chemical fibre, the silk other fibers; Flax fibre tossa particularly wherein, it is cheap, and China has abundant jute resource; Be third place in the world big jute plantation state, the exploitation of tossa more and more receives people's attention with application.The plantation of tossa does not take the good farmland; Need not apply a large amount of chemical fertilizer; Also need not too many labor management, and jute has more humidity absorption and release performance than ramie and flax, its antimildew and antibacterial ability also is stronger in bast-fibre; If can tossa be widely used in the garment material field, then protection, sustainable development and the solution of environment national " rural economy, rural development and rural demography " be had major and immediate significance.But, restricting application and the development of tossa in the garment material field because there are shortcomings such as fiber is thick, length is short, rigidity is big, prodding and itching feeling is serious in tossa always.
Summary of the invention
Technical problem to be solved by this invention provides a kind of shortcoming that overcomes above-mentioned flax fibre, and integrates jute and the blended yarn of hemp and silk fiber of the advantage of jute, hemp, silk fiber.
The technical problem that the present invention also will solve provides fabric and the production method thereof that adopts above-mentioned yarn production.
For solving the problems of the technologies described above, the technical scheme that the present invention adopted is following:
The blended yarn of a kind of jute and hemp and silk fiber, it is to be that raw material makes through blending with jute, hemp, three kinds of fibers of silk; In raw material weight percentage, jute accounts for the 30-55% of whole weight ratio; Hemp accounts for the 20-30% of whole weight ratio; Silk accounts for the 25-40% of whole weight ratio.
Wherein, in above-mentioned jute and hemp and the silk fiber blended yarn, said jute preferably accounts for 42.2% of whole weight ratio; Hemp preferably accounts for 27% of whole weight ratio; Silk preferably accounts for 30.8% of whole weight ratio.
Yarn of the present invention can spin the yarn that props up for 15-40 English for fineness, also can be spun into the yarn of other standard according to demand.It can be according to the various fabrics of existing production of woven fabrics explained hereafter such as plain weave, twill, satin weave etc. as raw material, and it also can be applicable to insulation garment, ultraviolet radiation preventing clothes etc. except that being used for business suit, to satisfy the demand in market.
Further, the invention provides the BLENDED FABRIC of a kind of jute and hemp and silk fiber, its raw material is above-mentioned blended yarn.The production technology of this BLENDED FABRIC can adopt technology well known to those skilled in the art, and preferred following technology comprises the steps:
1, draws materials: select above-mentioned yarn as raw material.
2, starching: adopt sizing liquor that the raw material of choosing in the step 1 is carried out starching.
3, weave:, be made into fabric loom on the raw material after the starching in the step 2.
4, fabric desizing: adopt the amylase liquid destarch, destarch concentration is 0.2-2g/L, and the time is more than 30 minutes;
5, kiering bleaching: adopt the fabric after single bath process is handled destarch, concrete steps are following: with bath raio 1: 15-25 preparation treatment fluid, the concentration of scouring agent TA-110 is 2-8ml/L in this treatment fluid, and the concentration of hydrogen peroxide solution is 3-11ml/L, and treatment temperature is 45-85 ℃; Handle after 10-40 minute, the hydrogen peroxide solution promoting agent TA-116 by every liter of treatment fluid adding 1-7ml handled 20-50 minute.
6, dyeing: adopt direct dyes or REACTIVE DYES to dye.
7, soft finish: the fabric after will dyeing earlier carries out biology enzyme to be handled, and carries out soft finish then; Wherein in the biology enzyme processing procedure: bath raio is 1: 10-30, cellulase consumption are the 0.5-4% of fabric weight, and the penetrating agent JFC consumption is the 0.02-0.2% of fabric weight, and the pH value is 3.5-6, and treatment temperature is 40-60 ℃, and the processing time is 30-120 minute; The soft finish method: it be 5-30g/L amino-silicone oil softening agent 8040 with concentration is two to soak two and roll in the mixed solution of 0.5-4g/L JFC that the fabric after biology enzyme is handled is containing earlier concentration; Wherein pick-up is 60-100%, under 130-180 ℃ temperature, bakes 0.5-4.5 minute then.
8, post processing: the fabric after the soft finish is carried out the routine washing, and oven dry promptly gets the BLENDED FABRIC of described jute and hemp and silk fiber.
Sizing liquor described in the above-mentioned steps 2 is the mixed liquor of PVA slurries, graft starch and polyacrylamide slurry, and wherein, the part by weight of PVA slurries and graft starch is 1: 1-4; The weight ratio of the mixture of PVA slurries and graft starch and polyacrylamide slurry is 3-15: 1.
Beneficial effect: though tossa has the advantage of moisture absorption, ventilative, antibiotic, anti-mite, the tossa feel is coarse, and the lining of processing has been prone to fold; Hemp contains the hemp aldehydes matter, therefore have the excellent antibiotic bacteriostasis, and the cross section of hemp shows as irregular triangle, polygon etc.; Many ribs of its molecule result shape; Looser, the spiral strain line is arranged, so it has good dissipation role to sound wave, broadcasting; In addition, hemp also has good anti-ultraviolet function; Silk fiber has soft and high resilience, and smooth surface is even, and warmth retention property is good, and Color is attractive in appearance, distinct, fine and smooth.The present invention carries out blending with jute and hemp and silk according to reasonable proportioning, can improve the shortcoming that the jute lining is thick and stiff, be prone to fold, keeps its moisture absorption, advantage such as ventilative, antibiotic simultaneously.The blended yarn woven fabric that adopts this yarn to make has soft, smooth, warming; Color is attractive in appearance, distinct, fine and smooth; Functions such as dissipation sound wave, broadcasting and antiultraviolet are applicable to and make insulation garment, anti-ultraviolet radiation clothes etc.
The specific embodiment
Embodiment 1
The blended yarn of a kind of jute and hemp and silk fiber, it is to be that raw material makes through blending with jute, hemp, three kinds of fibers of silk; In raw material weight percentage, jute accounts for 42.2% of whole weight ratio; Hemp accounts for 27% of whole weight ratio; Silk accounts for 30.8% of whole weight ratio.
Utilize above-mentioned blended yarn to produce the BLENDED FABRIC of jute and hemp and silk fiber, its process for making comprises the steps:
1, draws materials: select yarn that fineness that the silk blend by 42.2% jute, 27% hemp and 30.8% forms props up for 15-40 English as raw material.
2, starching: adopt sizing liquor that the raw material of choosing in the step 1 is carried out starching, this sizing liquor is the mixed liquor of PVA slurries, graft starch and polyacrylamide slurry, and wherein, the part by weight of PVA slurries and graft starch is 1: 1; The weight ratio of the mixture of PVA slurries and graft starch and polyacrylamide slurry is 5: 1.
3, weave:, be made into fabric loom on the raw material after the starching in the step 2;
4, fabric desizing: adopt the amylase liquid destarch, destarch concentration is 0.2g/L, and the time is more than 30 minutes;
5, kiering bleaching: adopt the fabric after single bath process is handled destarch, concrete steps are following: with bath raio preparation in 1: 15 treatment fluid, the concentration of scouring agent TA-110 is 2ml/L in this treatment fluid, and the concentration of hydrogen peroxide solution is 11ml/L, and treatment temperature is 45-85 ℃; Handle after 10 minutes, the hydrogen peroxide solution promoting agent TA-116 by every liter of treatment fluid adding 1ml handled 20 minutes.
6, dyeing: adopt direct dyes to dye.
7, soft finish: the fabric after will dyeing earlier carries out biology enzyme to be handled, and carries out soft finish then; Wherein in the biology enzyme processing procedure: bath raio is 1: 10, and the cellulase consumption is 0.5% of a fabric weight, and the penetrating agent JFC consumption is 0.02% of a fabric weight, and the pH value is 3.5-6, and treatment temperature is 40-60 ℃, and the processing time is 30-120 minute; The soft finish method: it be 5g/L amino-silicone oil softening agent 8040 with concentration is two to soak two and roll in the mixed solution of 4g/L JFC that the fabric after biology enzyme is handled is containing earlier concentration; Wherein pick-up is 60%, under 130-180 ℃ temperature, bakes 0.5 minute then.
8, post processing: the fabric after the soft finish is carried out the routine washing, and oven dry promptly gets the BLENDED FABRIC of described jute and hemp and silk fiber.
Embodiment 2
The blended yarn of a kind of jute and hemp and silk fiber, it is to be that raw material makes through blending with jute, hemp, three kinds of fibers of silk; In raw material weight percentage, jute accounts for 45% of whole weight ratio; Hemp accounts for 30% of whole weight ratio; Silk accounts for 25% of whole weight ratio.
Utilize above-mentioned blended yarn to produce the BLENDED FABRIC of jute and hemp and silk fiber, its process for making comprises the steps:
1, draws materials: select yarn that fineness that the silk blend by 45% jute, 30% hemp and 25% forms props up for 15-40 English as raw material.
2, starching: adopt sizing liquor that the raw material of choosing in the step 1 is carried out starching, this sizing liquor is the mixed liquor of PVA slurries, graft starch and polyacrylamide slurry, and wherein, the part by weight of PVA slurries and graft starch is 1: 4; The weight ratio of the mixture of PVA slurries and graft starch and polyacrylamide slurry is 3: 1.
3, weave:, be made into fabric loom on the raw material after the starching in the step 2;
4, fabric desizing: adopt the amylase liquid destarch, destarch concentration is 2g/L, and the time is more than 30 minutes;
5, kiering bleaching: adopt the fabric after single bath process is handled destarch, concrete steps are following: with bath raio preparation in 1: 20 treatment fluid, the concentration of scouring agent TA-110 is 6ml/L in this treatment fluid, and the concentration of hydrogen peroxide solution is 3ml/L, and treatment temperature is 45-85 ℃; Handle after 20 minutes, the hydrogen peroxide solution promoting agent TA-116 by every liter of treatment fluid adding 4ml handled 30 minutes.
6, dyeing: adopt REACTIVE DYES to dye.
7, soft finish: the fabric after will dyeing earlier carries out biology enzyme to be handled, and carries out soft finish then; Wherein in the biology enzyme processing procedure: bath raio is 1: 20, and the cellulase consumption is 2.5% of a fabric weight, and the penetrating agent JFC consumption is 0.2% of a fabric weight, and the pH value is 3.5-6, and treatment temperature is 40-60 ℃, and the processing time is 30-120 minute; The soft finish method: it be 20g/L amino-silicone oil softening agent 8040 with concentration is two to soak two and roll in the mixed solution of 0.5g/L JFC that the fabric after biology enzyme is handled is containing earlier concentration; Wherein pick-up is 80%, under 130-180 ℃ temperature, bakes 4.5 minutes then.
8, post processing: the fabric after the soft finish is carried out the routine washing, and oven dry promptly gets the BLENDED FABRIC of described jute and hemp and silk fiber.
Embodiment 3
The blended yarn of a kind of jute and hemp and silk fiber, it is to be that raw material makes through blending with jute, hemp, three kinds of fibers of silk; In raw material weight percentage, jute accounts for 55% of whole weight ratio; Hemp accounts for 25% of whole weight ratio; Silk accounts for 20% of whole weight ratio.
Utilize above-mentioned blended yarn to produce the BLENDED FABRIC of jute and hemp and silk fiber, its process for making comprises the steps:
1, draws materials: select yarn that fineness that the silk blend by 55% jute, 25% hemp and 20% forms props up for 15-40 English as raw material.
2, starching: adopt sizing liquor that the raw material of choosing in the step 1 is carried out starching, this sizing liquor is the mixed liquor of PVA slurries, graft starch and polyacrylamide slurry, and wherein, the part by weight of PVA slurries and graft starch is 1: 2; The weight ratio of the mixture of PVA slurries and graft starch and polyacrylamide slurry is 15: 1.
3, weave:, be made into fabric loom on the raw material after the starching in the step 2;
4, fabric desizing: adopt the amylase liquid destarch, destarch concentration is 1.0g/L, and the time is more than 30 minutes;
5, kiering bleaching: adopt the fabric after single bath process is handled destarch, concrete steps are following: with bath raio preparation in 1: 20 treatment fluid, the concentration of scouring agent TA-110 is 4ml/L in this treatment fluid, and the concentration of hydrogen peroxide solution is 7ml/L, and treatment temperature is 45-85 ℃; Handle after 20 minutes, the hydrogen peroxide solution promoting agent TA-116 by every liter of treatment fluid adding 4ml handled 40 minutes.
6, dyeing: adopt direct dyes to dye.
7, soft finish: the fabric after will dyeing earlier carries out biology enzyme to be handled, and carries out soft finish then; Wherein in the biology enzyme processing procedure: bath raio is 1: 20, and the cellulase consumption is 1.5% of a fabric weight, and the penetrating agent JFC consumption is 0.1% of a fabric weight, and the pH value is 3.5-6, and treatment temperature is 40-60 ℃, and the processing time is 30-120 minute; The soft finish method: it be 20g/L amino-silicone oil softening agent 8040 with concentration is two to soak two and roll in the mixed solution of 2g/L JFC that the fabric after biology enzyme is handled is containing earlier concentration; Wherein pick-up is 100%, under 130-180 ℃ temperature, bakes 2 minutes then.
8, post processing: the fabric after the soft finish is carried out the routine washing, and oven dry promptly gets the BLENDED FABRIC of described jute and hemp and silk fiber.
Embodiment 4
The blended yarn of a kind of jute and hemp and silk fiber, it is to be that raw material makes through blending with jute, hemp, three kinds of fibers of silk; In raw material weight percentage, jute accounts for 30% of whole weight ratio; Hemp accounts for 40% of whole weight ratio; Silk accounts for 30% of whole weight ratio.
Utilize above-mentioned blended yarn to produce the BLENDED FABRIC of jute and hemp and silk fiber, its process for making comprises the steps:
1, draws materials: select yarn that fineness that the silk blend by 30% jute, 40% hemp and 30% forms props up for 15-40 English as raw material.
2, starching: adopt sizing liquor that the raw material of choosing in the step 1 is carried out starching, this sizing liquor is the mixed liquor of PVA slurries, graft starch and polyacrylamide slurry, and wherein, the part by weight of PVA slurries and graft starch is 1: 2; The weight ratio of the mixture of PVA slurries and graft starch and polyacrylamide slurry is 10: 1.
3, weave:, be made into fabric loom on the raw material after the starching in the step 2;
4, fabric desizing: adopt the amylase liquid destarch, destarch concentration is 1g/L, and the time is more than 30 minutes;
5, kiering bleaching: adopt the fabric after single bath process is handled destarch, concrete steps are following: with bath raio preparation in 1: 25 treatment fluid, the concentration of scouring agent TA-110 is 8ml/L in this treatment fluid, and the concentration of hydrogen peroxide solution is 7ml/L, and treatment temperature is 45-85 ℃; Handle after 40 minutes, the hydrogen peroxide solution promoting agent TA-116 by every liter of treatment fluid adding 3ml handled 50 minutes.
6, dyeing: adopt REACTIVE DYES to dye.
7, soft finish: the fabric after will dyeing earlier carries out biology enzyme to be handled, and carries out soft finish then; Wherein in the biology enzyme processing procedure: bath raio is 1: 30, and the cellulase consumption is 4% of a fabric weight, and the penetrating agent JFC consumption is 0.15% of a fabric weight, and the pH value is 3.5-6, and treatment temperature is 40-60 ℃, and the processing time is 30-120 minute; The soft finish method: it be 30g/L amino-silicone oil softening agent 8040 with concentration is two to soak two and roll in the mixed solution of 2g/L JFC that the fabric after biology enzyme is handled is containing earlier concentration; Wherein pick-up is 90%, under 130-180 ℃ temperature, bakes 2 minutes then.
8, post processing: the fabric after the soft finish is carried out the routine washing, and oven dry promptly gets the BLENDED FABRIC of described jute and hemp and silk fiber.
The foregoing description does not limit the present invention in any way, and every employing is equal to the technical scheme that replacement or the mode of equivalent transformation obtain and all drops in protection scope of the present invention.
Claims (7)
1. the blended yarn of a jute and hemp and silk fiber is characterized in that: it is to be that raw material makes through blending with jute, hemp, three kinds of fibers of silk; In raw material weight percentage, jute accounts for the 30-55% of whole weight ratio; Hemp accounts for the 20-30% of whole weight ratio; Silk accounts for the 25-40% of whole weight ratio.
2. the blended yarn of jute according to claim 1 and hemp and silk fiber is characterized in that: in raw material weight percentage, jute accounts for 42.2% of whole weight ratio; Hemp accounts for 27% of whole weight ratio; Silk accounts for 30.8% of whole weight ratio.
3. the blended yarn of jute according to claim 1 and 2 and hemp and silk fiber is characterized in that: described fineness of yarn props up for 15-40 English.
4. the blended yarn of each described jute of claim 1-3 and hemp and silk fiber is as the application of raw material in the ultraviolet radiation preventing clothes.
5. the BLENDED FABRIC of a jute and hemp and silk fiber, it is characterized in that: its textile is the blended yarn of each described jute of claim 1-3 and hemp and silk fiber.
6. the production method of the BLENDED FABRIC of the described jute of claim 5 and hemp and silk fiber comprises the steps:
(1) draws materials: select each described yarn of claim 1-3 as raw material;
(2) starching: adopt sizing liquor that the raw material of choosing in the step (1) is carried out starching;
(3) weave:, be made into fabric loom on the raw material after the starching in the step (2);
(4) fabric desizing: adopt the amylase liquid destarch, destarch concentration is 0.2-2g/L, and the time is more than 30 minutes;
(5) kiering bleaching: adopt the fabric after single bath process is handled destarch, concrete steps are following: with bath raio 1: 15-25 preparation treatment fluid, the concentration of scouring agent TA-110 is 2-8ml/L in this treatment fluid, and the concentration of hydrogen peroxide solution is 3-11ml/L, and treatment temperature is 45-85 ℃; Handle after 10-40 minute, the hydrogen peroxide solution promoting agent TA-116 by every liter of treatment fluid adding 1-7ml handled 20-50 minute;
(6) dyeing: adopt direct dyes or REACTIVE DYES to dye;
(7) soft finish: the fabric after will dyeing earlier carries out biology enzyme to be handled, and carries out soft finish then; Wherein in the biology enzyme processing procedure: bath raio is 1: 10-30, cellulase consumption are the 0.5-4% of fabric weight, and the penetrating agent JFC consumption is the 0.02-0.2% of fabric weight, and the pH value is 3.5-6, and treatment temperature is 40-60 ℃, and the processing time is 30-120 minute; The soft finish method: it be 5-30g/L amino-silicone oil softening agent 8040 with concentration is two to soak two and roll in the mixed solution of 0.5-4g/L JFC that the fabric after biology enzyme is handled is containing earlier concentration; Wherein pick-up is 60-100%, under 130-180 ℃ temperature, bakes 0.5-4.5 minute then;
(8) post processing: the fabric after the soft finish is carried out the routine washing, and oven dry promptly gets the BLENDED FABRIC of described jute and hemp and silk fiber.
7. the production method of the BLENDED FABRIC of jute according to claim 6 and hemp and silk fiber; It is characterized in that: the sizing liquor described in the step (2) is the mixed liquor of PVA slurries, graft starch and polyacrylamide slurry; Wherein, the part by weight of PVA slurries and graft starch is 1: 1-4; The weight ratio of the mixture of PVA slurries and graft starch and polyacrylamide slurry is 3-15: 1.