CN102493059A - Blended yarn of jute fiber, cotton fiber and viscose fiber and application of blended yarn - Google Patents
Blended yarn of jute fiber, cotton fiber and viscose fiber and application of blended yarn Download PDFInfo
- Publication number
- CN102493059A CN102493059A CN2011103999108A CN201110399910A CN102493059A CN 102493059 A CN102493059 A CN 102493059A CN 2011103999108 A CN2011103999108 A CN 2011103999108A CN 201110399910 A CN201110399910 A CN 201110399910A CN 102493059 A CN102493059 A CN 102493059A
- Authority
- CN
- China
- Prior art keywords
- jute
- cotton
- fabric
- viscose
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a blended yarn of a jute fiber, a cotton fiber and a viscose fiber. The blended yarn is made by blending the following raw materials in percentage by weight: 30 to 50 percent of jute fiber, 22 to 30 percent of cotton fiber and 20 to 48 percent of viscose fiber. By blending the jute fiber, the cotton fiber and the viscose fiber in a reasonable proportion, the blended yarn overcomes the defects that the jute fabric is rough and hard and easy to drape, and has the characteristics of moisture absorption, air permeability and antibacterium and the like of the jute fiber; besides, the blended yarn has the advantages of softness, smoothness, breathability, antistatic performance, and the like, and rich color can be obtained by dyeing. Blended fabric made of the yarn is applied to undershirts, sportswear, coats and the like.
Description
Technical field
The invention belongs to field of textiles, relate in particular to the blended yarn and the application thereof of a kind of jute and cotton and viscose.
Background technology
Along with constantly riseing of the prices of raw and semifnished materials such as viscose, chemical fiber; Begin to demand other fibers of alternative chemical fibre, viscose glue of people; Flax fibre tossa particularly wherein, it is cheap, and China has abundant jute resource; Be third place in the world big jute plantation state, the exploitation of tossa more and more receives people's attention with application.The plantation of tossa does not take the good farmland; Need not apply a large amount of chemical fertilizer; Also need not too many labor management, and jute has more humidity absorption and release performance than ramie and flax, its antimildew and antibacterial ability also is stronger in bast-fibre; If can tossa be widely used in the garment material field, then protection, sustainable development and the solution of environment national " rural economy, rural development and rural demography " be had major and immediate significance.But, restricting application and the development of tossa in the garment material field because there are shortcomings such as fiber is thick, length is short, rigidity is big, prodding and itching feeling is serious in tossa always.
Summary of the invention
Technical problem to be solved by this invention provides a kind of shortcoming that overcomes above-mentioned flax fibre, and integrates jute and the blended yarn of cotton and viscose of the advantage of jute, cotton, viscose.
The technical problem that the present invention also will solve provides fabric and the production method thereof that adopts above-mentioned yarn production.
For solving the problems of the technologies described above, the technical scheme that the present invention adopted is following:
The blended yarn of a kind of jute and cotton and viscose, it is to be that raw material makes through blending with jute, cotton, three kinds of fibers of viscose glue; In raw material weight percentage, jute accounts for the 30-50% of whole weight ratio; Cotton accounts for the 22-30% of whole weight ratio; Viscose glue accounts for the 20-48% of whole weight ratio.
Wherein, in above-mentioned jute and cotton and the viscose fiber blended yarn, said jute preferably accounts for 40.6% of whole weight ratio; Cotton 26.4% of the whole weight ratio that preferably accounts for; Viscose glue preferably accounts for 33% of whole weight ratio.
Yarn of the present invention can spin the yarn that props up for 15-40 English for fineness, also can be spun into the yarn of other standard according to demand.It can produce various fabrics such as fabrics such as plain weave, twill according to the production technology of existing organic fabric as raw material, and it is applicable to underwear, overcoat clothes or the like, to satisfy the demand in market.
Further, the invention provides the BLENDED FABRIC of a kind of jute and cotton and viscose, its raw material is above-mentioned blended yarn.The production technology of this BLENDED FABRIC can adopt technology well known to those skilled in the art, and preferred following technology comprises the steps:
1, draws materials: select above-mentioned yarn as raw material.
2, starching: adopt sizing liquor that the raw material of choosing in the step 1 is carried out starching.
3, weave:, be made into fabric loom on the raw material after the starching in the step 2.
4, fabric desizing: adopt the amylase liquid destarch, destarch concentration is 0.2-2g/L, and the time is more than 30 minutes;
5, kiering bleaching: adopt the fabric after single bath process is handled destarch, concrete steps are following: with bath raio 1: 15-25 preparation treatment fluid, the concentration of scouring agent TA-110 is 2-8ml/L in this treatment fluid, and the concentration of hydrogen peroxide solution is 3-11ml/L, and treatment temperature is 45-85 ℃; Handle after 10-40 minute, the hydrogen peroxide solution promoting agent TA-116 by every liter of treatment fluid adding 1-7ml handled 20-50 minute.
6, dyeing: adopt the normal dyeing method of cellulose fibre to dye.
7, soft finish: the fabric after will dyeing earlier carries out biology enzyme to be handled, and carries out soft finish then; Wherein in the biology enzyme processing procedure: bath raio is 1: 10-30, cellulase consumption are the 0.5-4% of fabric weight, and the penetrating agent JFC consumption is the 0.02-0.2% of fabric weight, and the pH value is 3.5-6, and treatment temperature is 40-60 ℃, and the processing time is 30-120 minute; The soft finish method: it be 5-30g/L amino-silicone oil softening agent 8040 with concentration is two to soak two and roll in the mixed solution of 0.5-4g/L JFC that the fabric after biology enzyme is handled is containing earlier concentration; Wherein pick-up is 60-100%, under 130-180 ℃ temperature, bakes 0.5-4.5 minute then.
8, post processing: the fabric after the soft finish is carried out the routine washing, and oven dry promptly gets the BLENDED FABRIC of described jute and cotton and viscose.
Sizing liquor described in the above-mentioned steps 2 is the mixed liquor of PVA slurries, graft starch and polyacrylamide slurry, and wherein, the part by weight of PVA slurries and graft starch is 1: 1-4; The weight ratio of the mixture of PVA slurries and graft starch and polyacrylamide slurry is 3-15: 1.
Beneficial effect: though tossa has the advantage of moisture absorption, ventilative, antibiotic, anti-mite, the tossa feel is coarse, and the lining of processing has been prone to fold; The advantage of cotton fiber is that softness and spinning property are good; Viscose has smooth nice and cool, ventilative, anlistatig characteristic, and it is individual particularly also to have the gorgeous characteristics of dyeing.The present invention carries out blending with jute and cotton and viscose glue according to reasonable proportioning; Can improve the shortcoming that the jute lining is thick and stiff, be prone to fold; Keep its moisture absorption, characteristics such as ventilative, antibiotic simultaneously; Also have advantages such as gentle right, smooth, ventilative, antistatic in addition, and can obtain abundant colors through dyeing.The blended yarn woven fabric that adopts this yarn to make adapts to and is used for underskirt, sportswear, overcoat clothes etc.
The specific embodiment
Embodiment 1
The blended yarn of a kind of jute and cotton and viscose, it is to be that raw material makes through blending with jute, cotton, three kinds of fibers of viscose glue; In raw material weight percentage, jute accounts for 40.6% of whole weight ratio; Cotton accounts for 26.4% of whole weight ratio; Viscose glue accounts for 33% of whole weight ratio.
Utilize above-mentioned blended yarn to produce the BLENDED FABRIC of jute and cotton and viscose, its process for making comprises the steps:
1, draw materials: the yarn of selecting to be propped up for 15-40 English by the viscose blended fineness that forms of 40.6% jute, 26.4% cotton and 33% is as raw material.
2, starching: adopt sizing liquor that the raw material of choosing in the step 1 is carried out starching, this sizing liquor is the mixed liquor of PVA slurries, graft starch and polyacrylamide slurry, and wherein, the part by weight of PVA slurries and graft starch is 1: 1; The weight ratio of the mixture of PVA slurries and graft starch and polyacrylamide slurry is 5: 1.
3, weave:, be made into fabric loom on the raw material after the starching in the step 2;
4, fabric desizing: adopt the amylase liquid destarch, destarch concentration is 0.2g/L, and the time is more than 30 minutes;
5, kiering bleaching: adopt the fabric after single bath process is handled destarch, concrete steps are following: with bath raio preparation in 1: 15 treatment fluid, the concentration of scouring agent TA-110 is 2ml/L in this treatment fluid, and the concentration of hydrogen peroxide solution is 11ml/L, and treatment temperature is 45-85 ℃; Handle after 10 minutes, the hydrogen peroxide solution promoting agent TA-116 by every liter of treatment fluid adding 1ml handled 20 minutes.
6, dyeing: adopt the normal dyeing method of cellulose fibre to dye.
7, soft finish: the fabric after will dyeing earlier carries out biology enzyme to be handled, and carries out soft finish then; Wherein in the biology enzyme processing procedure: bath raio is 1: 10, and the cellulase consumption is 0.5% of a fabric weight, and the penetrating agent JFC consumption is 0.02% of a fabric weight, and the pH value is 3.5-6, and treatment temperature is 40-60 ℃, and the processing time is 30-120 minute; The soft finish method: it be 5g/L amino-silicone oil softening agent 8040 with concentration is two to soak two and roll in the mixed solution of 4g/L JFC that the fabric after biology enzyme is handled is containing earlier concentration; Wherein pick-up is 60%, under 130-180 ℃ temperature, bakes 0.5 minute then.
8, post processing: the fabric after the soft finish is carried out the routine washing, and oven dry promptly gets the BLENDED FABRIC of described jute and cotton and viscose.
Embodiment 2
The blended yarn of a kind of jute and cotton and viscose, it is to be that raw material makes through blending with jute, cotton, three kinds of fibers of viscose glue; In raw material weight percentage, jute accounts for 30% of whole weight ratio; Cotton accounts for 22% of whole weight ratio; Viscose glue accounts for 48% of whole weight ratio.
Utilize above-mentioned blended yarn to produce the BLENDED FABRIC of jute and cotton and viscose, its process for making comprises the steps:
1, draw materials: the yarn of selecting to be propped up for 15-40 English by the viscose blended fineness that forms of 30% jute, 22% cotton and 48% is as raw material.
2, starching: adopt sizing liquor that the raw material of choosing in the step 1 is carried out starching, this sizing liquor is the mixed liquor of PVA slurries, graft starch and polyacrylamide slurry, and wherein, the part by weight of PVA slurries and graft starch is 1: 2; The weight ratio of the mixture of PVA slurries and graft starch and polyacrylamide slurry is 15: 1.
3, weave:, be made into fabric loom on the raw material after the starching in the step 2;
4, fabric desizing: adopt the amylase liquid destarch, destarch concentration is 1.0g/L, and the time is more than 30 minutes;
5, kiering bleaching: adopt the fabric after single bath process is handled destarch, concrete steps are following: with bath raio preparation in 1: 20 treatment fluid, the concentration of scouring agent TA-110 is 4ml/L in this treatment fluid, and the concentration of hydrogen peroxide solution is 7ml/L, and treatment temperature is 45-85 ℃; Handle after 20 minutes, the hydrogen peroxide solution promoting agent TA-116 by every liter of treatment fluid adding 4ml handled 40 minutes.
6, dyeing: adopt the normal dyeing method of cellulose fibre to dye.
7, soft finish: the fabric after will dyeing earlier carries out biology enzyme to be handled, and carries out soft finish then; Wherein in the biology enzyme processing procedure: bath raio is 1: 20, and the cellulase consumption is 1.5% of a fabric weight, and the penetrating agent JFC consumption is 0.1% of a fabric weight, and the pH value is 3.5-6, and treatment temperature is 40-60 ℃, and the processing time is 30-120 minute; The soft finish method: it be 20g/L amino-silicone oil softening agent 8040 with concentration is two to soak two and roll in the mixed solution of 2g/L JFC that the fabric after biology enzyme is handled is containing earlier concentration; Wherein pick-up is 100%, under 130-180 ℃ temperature, bakes 2 minutes then.
8, post processing: the fabric after the soft finish is carried out the routine washing, and oven dry promptly gets the BLENDED FABRIC of described jute and cotton and viscose.
Embodiment 3
The blended yarn of a kind of jute and cotton and viscose, it is to be that raw material makes through blending with jute, cotton, three kinds of fibers of viscose glue; In raw material weight percentage, jute accounts for 45% of whole weight ratio; Cotton accounts for 25% of whole weight ratio; Viscose glue accounts for 30% of whole weight ratio.
Utilize above-mentioned blended yarn to produce the BLENDED FABRIC of jute and cotton and viscose, its process for making comprises the steps:
1, draw materials: the yarn of selecting to be propped up for 15-40 English by the viscose blended fineness that forms of 45% jute, 25% cotton and 30% is as raw material.
2, starching: adopt sizing liquor that the raw material of choosing in the step 1 is carried out starching, this sizing liquor is the mixed liquor of PVA slurries, graft starch and polyacrylamide slurry, and wherein, the part by weight of PVA slurries and graft starch is 1: 4; The weight ratio of the mixture of PVA slurries and graft starch and polyacrylamide slurry is 3: 1.
3, weave:, be made into fabric loom on the raw material after the starching in the step 2;
4, fabric desizing: adopt the amylase liquid destarch, destarch concentration is 2g/L, and the time is more than 30 minutes;
5, kiering bleaching: adopt the fabric after single bath process is handled destarch, concrete steps are following: with bath raio preparation in 1: 20 treatment fluid, the concentration of scouring agent TA-110 is 6ml/L in this treatment fluid, and the concentration of hydrogen peroxide solution is 3ml/L, and treatment temperature is 45-85 ℃; Handle after 20 minutes, the hydrogen peroxide solution promoting agent TA-116 by every liter of treatment fluid adding 4ml handled 30 minutes.
6, dyeing: adopt the normal dyeing method of cellulose fibre to dye.
7, soft finish: the fabric after will dyeing earlier carries out biology enzyme to be handled, and carries out soft finish then; Wherein in the biology enzyme processing procedure: bath raio is 1: 20, and the cellulase consumption is 2.5% of a fabric weight, and the penetrating agent JFC consumption is 0.2% of a fabric weight, and the pH value is 3.5-6, and treatment temperature is 40-60 ℃, and the processing time is 30-120 minute; The soft finish method: it be 20g/L amino-silicone oil softening agent 8040 with concentration is two to soak two and roll in the mixed solution of 0.5g/L JFC that the fabric after biology enzyme is handled is containing earlier concentration; Wherein pick-up is 85%, under 130-180 ℃ temperature, bakes 4.5 minutes then.
8, post processing: the fabric after the soft finish is carried out the routine washing, and oven dry promptly gets the BLENDED FABRIC of described jute and cotton and viscose.
Embodiment 4
The blended yarn of a kind of jute and cotton and viscose, it is to be that raw material makes through blending with jute, cotton, three kinds of fibers of viscose glue; In raw material weight percentage, jute accounts for 48% of whole weight ratio; Cotton accounts for 30% of whole weight ratio; Viscose glue accounts for 20% of whole weight ratio.
Utilize above-mentioned blended yarn to produce the BLENDED FABRIC of jute and cotton and viscose, its process for making comprises the steps:
1, draw materials: the yarn of selecting to be propped up for 15-40 English by the viscose blended fineness that forms of 48% jute, 30% cotton and 20% is as raw material.
2, starching: adopt sizing liquor that the raw material of choosing in the step 1 is carried out starching, this sizing liquor is the mixed liquor of PVA slurries, graft starch and polyacrylamide slurry, and wherein, the part by weight of PVA slurries and graft starch is 1: 2; The weight ratio of the mixture of PVA slurries and graft starch and polyacrylamide slurry is 10: 1.
3, weave:, be made into fabric loom on the raw material after the starching in the step 2;
4, fabric desizing: adopt the amylase liquid destarch, destarch concentration is 1g/L, and the time is more than 30 minutes;
5, kiering bleaching: adopt the fabric after single bath process is handled destarch, concrete steps are following: with bath raio preparation in 1: 25 treatment fluid, the concentration of scouring agent TA-110 is 8ml/L in this treatment fluid, and the concentration of hydrogen peroxide solution is 7ml/L, and treatment temperature is 45-85 ℃; Handle after 40 minutes, the hydrogen peroxide solution promoting agent TA-116 by every liter of treatment fluid adding 3ml handled 50 minutes.
6, dyeing: adopt the normal dyeing method of cellulose fibre to dye.
7, soft finish: the fabric after will dyeing earlier carries out biology enzyme to be handled, and carries out soft finish then; Wherein in the biology enzyme processing procedure: bath raio is 1: 30, and the cellulase consumption is 4% of a fabric weight, and the penetrating agent JFC consumption is 0.15% of a fabric weight, and the pH value is 3.5-6, and treatment temperature is 40-60 ℃, and the processing time is 30-120 minute; The soft finish method: it be 30g/L amino-silicone oil softening agent 8040 with concentration is two to soak two and roll in the mixed solution of 2g/L JFC that the fabric after biology enzyme is handled is containing earlier concentration; Wherein pick-up is 75%, under 130-180 ℃ temperature, bakes 2 minutes then.
8, post processing: the fabric after the soft finish is carried out the routine washing, and oven dry promptly gets the BLENDED FABRIC of described jute and cotton and viscose.
The foregoing description does not limit the present invention in any way, and every employing is equal to the technical scheme that replacement or the mode of equivalent transformation obtain and all drops in protection scope of the present invention.
Claims (7)
1. the blended yarn of a jute and cotton and viscose is characterized in that: it is to be that raw material makes through blending with jute, cotton, three kinds of fibers of viscose glue; In raw material weight percentage, jute accounts for the 30-50% of whole weight ratio; Cotton accounts for the 22-30% of whole weight ratio; Viscose glue accounts for the 20-48% of whole weight ratio.
2. the blended yarn of jute according to claim 1 and cotton and viscose, it is characterized in that: in raw material weight percentage, jute accounts for 40.6% of whole weight ratio; Cotton accounts for 26.4% of whole weight ratio; Viscose glue accounts for 33% of whole weight ratio.
3. the blended yarn of jute according to claim 1 and 2 and cotton and viscose, it is characterized in that: described fineness of yarn props up for 15-40 English.
4. the blended yarn of each described jute of claim 1-3 and cotton and viscose is as the application of raw material in underskirt.
5. jute and BLENDED FABRIC cotton and viscose is characterized in that: its textile is each described jute of claim 1-3 and the blended yarn of cotton and viscose.
6. the production method of the BLENDED FABRIC of the described jute of claim 5 and cotton and viscose comprises the steps:
(1) draws materials: select each described yarn of claim 1-3 as raw material;
(2) starching: adopt sizing liquor that the raw material of choosing in the step (1) is carried out starching;
(3) weave:, be made into fabric loom on the raw material after the starching in the step (2);
(4) fabric desizing: adopt the amylase liquid destarch, destarch concentration is 0.2-2g/L, and the time is more than 30 minutes;
(5) kiering bleaching: adopt the fabric after single bath process is handled destarch, concrete steps are following: with bath raio 1: 15-25 preparation treatment fluid, the concentration of scouring agent TA-110 is 2-8ml/L in this treatment fluid, and the concentration of hydrogen peroxide solution is 3-11ml/L, and treatment temperature is 45-85 ℃; Handle after 10-40 minute, the hydrogen peroxide solution promoting agent TA-116 by every liter of treatment fluid adding 1-7ml handled 20-50 minute;
(6) dyeing: adopt the normal dyeing method of cellulose fibre to dye;
(7) soft finish: the fabric after will dyeing earlier carries out biology enzyme to be handled, and carries out soft finish then; Wherein in the biology enzyme processing procedure: bath raio is 1: 10-30, cellulase consumption are the 0.5-4% of fabric weight, and the penetrating agent JFC consumption is the 0.02-0.2% of fabric weight, and the pH value is 3.5-6, and treatment temperature is 40-60 ℃, and the processing time is 30-120 minute; The soft finish method: it be 5-30g/L amino-silicone oil softening agent 8040 with concentration is two to soak two and roll in the mixed solution of 0.5-4g/L JFC that the fabric after biology enzyme is handled is containing earlier concentration; Wherein pick-up is 60-100%, under 130-180 ℃ temperature, bakes 0.5-4.5 minute then;
(8) post processing: the fabric after the soft finish is carried out the routine washing, and oven dry promptly gets the BLENDED FABRIC of described jute and cotton and viscose.
7. the production method of the BLENDED FABRIC of jute according to claim 6 and cotton and viscose; It is characterized in that: the sizing liquor described in the step (2) is the mixed liquor of PVA slurries, graft starch and polyacrylamide slurry; Wherein, the part by weight of PVA slurries and graft starch is 1: 1-4; The weight ratio of the mixture of PVA slurries and graft starch and polyacrylamide slurry is 3-15: 1.