CN105088777A - Sizing preparation method of super high count ramie fabric - Google Patents
Sizing preparation method of super high count ramie fabric Download PDFInfo
- Publication number
- CN105088777A CN105088777A CN201510542470.5A CN201510542470A CN105088777A CN 105088777 A CN105088777 A CN 105088777A CN 201510542470 A CN201510542470 A CN 201510542470A CN 105088777 A CN105088777 A CN 105088777A
- Authority
- CN
- China
- Prior art keywords
- parts
- superelevation
- props
- ramie fabric
- compound method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A sizing preparation method of a super high count ramie fabric comprises the steps of a, fat emulsification; b, 2-Hydroxy naphthalene preparation; c, blending of PVA and grafted starch; d, blending of auxiliaries. By using the sizing obtained by the method to perform slashing on the super high count ramie fabric, the enhancement rate, the elongation decreasing rate, the hairiness decreasing ratio and abrasion degree growth ratio of the fabric can be improved, the weavability of the fabric is improved, and the breakage of warp yarn can reach the demand of successful weaving.
Description
Technical field
The present invention relates to
a kind of superelevation props up ramie fabric slurry compound method, belong to textile technology field.
Background technology
Conventional ramie garment material has well-pressed, has characteristic and the peculiar health cares such as body bone, smooth, gas permeability is excellent, but in use also there is wrinkle resistance and poor flexibility, and dress has prodding and itching feeling, the part high tightness fabric feel shortcomings such as too plate is hard.For this reason, developed superelevation and propped up ramie fabric, but superelevation props up the fundamental characteristics that ramie fabric still has pure ramie yarn, namely filoplume is many and long, and rigidity is large, and very easily produces electrostatic, cause to weave in process and produce a large amount of broken ends, have a strong impact on quality and the production efficiency of fabric.How to improve its weavability by sizing, the end breakage rate of warp thread is reached and weaves smoothly, most important to raising ramie garment material.And one of key of sizing, be slurry preparation.
Summary of the invention
According to above-mentioned requirements, the invention provides
a kind of superelevation props up ramie fabric slurry compound method, the slip obtained by the method props up ramie fabric to superelevation and carries out sizing, improves its enhancing rate, subtracts the rate of stretching, filoplume reduction rate and increase mill rate, improves its weavability, makes the end breakage rate of warp thread reach smooth woven requirement.
For achieving the above object, the present invention is realized by following technological means:
a kind of superelevation props up ramie fabric slurry compound method, it is characterized in that: comprise the following steps:
A) grease emulsifying: 1 part of grease, 3-5 part caustic soda, 2.2-2.8 part emulsifying agent, 1.1-1.4 part water are put in mixing cirtern, stir emulsification in 1.5-2.5 hour stand-by;
B) 2-how phenol prepare: by 0.22-0.28 part 2-, how phenol, 0.4 part of caustic soda and appropriate cold water lead to vapour hots plate, until 2-how phenol to dissolve cooling stand-by;
C) allotment of PVA, graft starch: the normal-temperature water putting into 0.33 part in mixing cirtern, more slowly add 20-32 part PVA and 39-41 part graft starch, starts about high-speed stirring 13-16min, opens steam and is progressively warming up to and boils, time 25-35min;
D) allotment of auxiliary agent: toward step c) add in the slurry that obtains 20 parts of acid amides slurries, 3 parts of glycerine, 3 parts of antistatic additive and steps a) and step b) slurry that obtains, turn down steam vexed slurry more than 1h.
Further:
Described step c) in PVA be 30 parts.
Described step c) in graft starch be 40 parts.
Described step a) in caustic soda be 4 parts.
Described step a) in emulsifying agent be 2.5 parts.
Described step a) in water be 1.2 parts.
The invention has the beneficial effects as follows: provided by the invention
a kind of superelevation props up ramie fabric slurry compound method, the slip obtained by the method props up ramie fabric to superelevation and carries out sizing, can improve its enhancing rate, subtract the rate of stretching, filoplume reduction rate and increase mill rate, improves its weavability, makes the end breakage rate of warp thread reach smooth woven requirement.
Detailed description of the invention
a kind of superelevation props up ramie fabric slurry compound method, it is characterized in that: comprise the following steps:
A) grease emulsifying: 1 part of grease, 3-5 part caustic soda, 2.2-2.8 part emulsifying agent, 1.1-1.4 part water are put in mixing cirtern, stir emulsification in 1.5-2.5 hour stand-by;
B) 2-how phenol prepare: by 0.22-0.28 part 2-, how phenol, 0.4 part of caustic soda and appropriate cold water lead to vapour hots plate, until 2-how phenol to dissolve cooling stand-by;
C) allotment of PVA, graft starch: the normal-temperature water putting into 0.33 part in mixing cirtern, more slowly add 20-32 part PVA and 39-41 part graft starch, starts about high-speed stirring 13-16min, opens steam and is progressively warming up to and boils, time 25-35min;
D) allotment of auxiliary agent: toward step c) add in the slurry that obtains 20 parts of acid amides slurries, 3 parts of glycerine, 3 parts of antistatic additive and steps a) and step b) slurry that obtains, turn down steam vexed slurry more than 1h.
Further:
Described step c) in PVA be 30 parts.
Described step c) in graft starch be 40 parts.
Described step a) in caustic soda be 4 parts.
Described step a) in emulsifying agent be 2.5 parts.
Described step a) in water be 1.2 parts.
More than show and describe general principle of the present invention, principal character and advantage.The technical staff of the industry should understand; the present invention is not restricted to the described embodiments; what describe in above-described embodiment and description just illustrates principle of the present invention; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements all fall in the claimed scope of the invention.Application claims protection domain is defined by appending claims and equivalent thereof.
Claims (6)
1. superelevation props up a ramie fabric slurry compound method, it is characterized in that: comprise the following steps:
A) grease emulsifying: 1 part of grease, 3-5 part caustic soda, 2.2-2.8 part emulsifying agent, 1.1-1.4 part water are put in mixing cirtern, stir emulsification in 1.5-2.5 hour stand-by;
B) 2-how phenol prepare: by 0.22-0.28 part 2-, how phenol, 0.4 part of caustic soda and appropriate cold water lead to vapour hots plate, until 2-how phenol to dissolve cooling stand-by;
C) allotment of PVA, graft starch: the normal-temperature water putting into 0.33 part in mixing cirtern, more slowly add 20-32 part PVA and 39-41 part graft starch, starts about high-speed stirring 13-16min, opens steam and is progressively warming up to and boils, time 25-35min;
D) allotment of auxiliary agent: toward step c) add in the slurry that obtains 20 parts of acid amides slurries, 3 parts of glycerine, 3 parts of antistatic additive and steps a) and step b) slurry that obtains, turn down steam vexed slurry more than 1h.
2. a kind of superelevation as claimed in claim 1 props up ramie fabric slurry compound method, it is characterized in that: described step c) in PVA be 30 parts.
3. a kind of superelevation as claimed in claim 1 props up ramie fabric slurry compound method, it is characterized in that: described step c) in graft starch be 40 parts.
4. a kind of superelevation as claimed in claim 1 props up ramie fabric slurry compound method, it is characterized in that: described step a) in caustic soda be 4 parts.
5. a kind of superelevation as claimed in claim 1 props up ramie fabric slurry compound method, it is characterized in that: described step a) in emulsifying agent be 2.5 parts.
6. a kind of superelevation as claimed in claim 1 props up ramie fabric slurry compound method, it is characterized in that: described step a) in water be 1.2 parts.