CN103046187A - Multi-material blended yarn and preparation method thereof - Google Patents
Multi-material blended yarn and preparation method thereof Download PDFInfo
- Publication number
- CN103046187A CN103046187A CN2012105418537A CN201210541853A CN103046187A CN 103046187 A CN103046187 A CN 103046187A CN 2012105418537 A CN2012105418537 A CN 2012105418537A CN 201210541853 A CN201210541853 A CN 201210541853A CN 103046187 A CN103046187 A CN 103046187A
- Authority
- CN
- China
- Prior art keywords
- yarn
- cotton
- flax
- preparation
- many materials
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides multi-material blended yarn which is prepared from mixing flax, viscose and cotton in a certain ratio and the mixing ratio of the flax, the viscose and the cotton is 35-55:15-35:10-50. According to mixture of three kinds of materials, the produced yarn has the advantages of being high in strength, good in breathability and tensile performance, superior in extending performance, beautiful and bright in color and not easy to fade.
Description
Technical field
The present invention relates to the cotton spinning industry, relate in particular to a kind of many materials blended yarn and preparation method thereof.
Background technology
Linen fibre is a kind of rare natural fabric, only accounts for 1.5% of natural fabric total amount.Have temperature adjustment, antiallergy, antistatic, antibiotic function, because the good hygroscopicity of flax, can absorb the moisture that is equivalent to 20 times of own wts, so the sodolin feel is dry and comfortable, nowadays, wrinkle resistant, the birth of non-ironing lingerie and the appearance of blending product have further been expanded the market of flax product.
The intensity of cotton fiber is high, good permeability, wrinkle resistance is poor, draftability is also relatively poor, and when making yarn separately, crease-resistant and shortcoming tensile property is highlighted.
Viscose refers to the alpha-cellulose that extracts from the cellulosic materials such as timber and plant straw, or take cotton linter as raw material, through being processed into spinning solution, the artificial fibre of making through wet spinning again.Sticking fine moisture percentage meets the physiological requirement of human body skin most, have smooth nice and cool, ventilative, antistatic, the characteristic such as gorgeous dyes.
At present, when making yarn, normally above any two kinds are mixed, although make moderate progress on the performance, or can't avoid the shortcoming of single material fully.Therefore, solving the bi-material mixed performance still exists the problem of defective just to seem particularly important.
Summary of the invention
The purpose of this invention is to provide a kind of many materials blended yarn and preparation method thereof, solved the problem that still there is defective in the bi-material mixed performance.
In order to address the above problem, the invention provides a kind of many materials blended yarn, this many materials blended yarn is to be mixed according to a certain percentage by flax, viscose glue and cotton, described flax, viscose glue and cotton compound percentages are 35 ~ 55:15 ~ 35:10 ~ 50.
Further improve and be: described flax, viscose glue and cotton compound percentages are 40:20:40.
The present invention also provides a kind of preparation method for the preparation of many materials of power blended yarn, and preparation process is as follows:
(1) shredding: with flax, viscose glue and cotton proportionally being evenly arranged in the buffer bin of griping cotton machine, the handgrip of griping cotton machine laterally grasps material, and material is sent into material sucking port;
(2) combing: material sucking port is sent into the material in the step (1) and is fully mixed combing in the carding machine;
(3) rolling: the material after the combing is sent into rolling in the lapper;
(4) slivering: the material of rolling sent into carry out the combing slivering in the comb and parallel cotton fibers prior to spinning sett frame;
(5) twisting: many composite material rotation windings are become one, make to be parallel to the axial fiber of yarn in the shape of a spiral, thereby produce radial pressure interfibrous vertical linkage is fixed up;
(6) yarn: the composite material that will be strip is put into the yarn machine and is carried out yarn, and further is transported in the fine spining machine and processes, and is wound up at last on the cone, finishes many materials blended yarn finished product.
Further improve and be: step can be wound on the different cylindrical carriers in (6).
Beneficial effect of the present invention: by the mixing of three kinds of materials, so that the yarn strength of making is high, good permeability, pull resistance is good, extension property is superior, and color is beautiful bright-coloured, not fugitive color.
Specific embodiment
In order to deepen the understanding of the present invention, the invention will be further described below in conjunction with embodiment, and this embodiment only is used for explaining the present invention, does not consist of the restriction to protection domain of the present invention.
Embodiment one
Be mixed according to a certain percentage by flax, viscose glue and cotton, described flax, viscose glue and cotton compound percentages are 40:20:40.
Preparation process is as follows:
(1) shredding: with flax, viscose glue and cotton proportionally being evenly arranged in the buffer bin of griping cotton machine, the handgrip of griping cotton machine laterally grasps material, and material is sent into material sucking port;
(2) combing: material sucking port is sent into the material in the step (1) and is fully mixed combing in the carding machine;
(3) rolling: the material after the combing is sent into rolling in the lapper;
(4) slivering: the material of rolling sent into carry out the combing slivering in the comb and parallel cotton fibers prior to spinning sett frame;
(5) twisting: many composite material rotation windings are become one, make to be parallel to the axial fiber of yarn in the shape of a spiral, thereby produce radial pressure interfibrous vertical linkage is fixed up;
(6) yarn: the composite material that will be strip is put into the yarn machine and is carried out yarn, and further is transported in the fine spining machine and processes, and is wound up at last on the cone, finishes many materials blended yarn finished product.
Embodiment two
Be mixed according to a certain percentage by flax, viscose glue and cotton, described flax, viscose glue and cotton compound percentages are 35:15:50.The preparation method is with embodiment one.
Embodiment three
Be mixed according to a certain percentage by flax, viscose glue and cotton, described flax, viscose glue and cotton compound percentages are 55:35:10.The preparation method is with embodiment one.
The yarn strength that result: embodiment one prepares is high, good permeability, pull resistance is good, extension property is superior, and color is beautiful bright-coloured, not fugitive color.
It is slightly not enough on tensile property and extension property that the yarn that embodiment two prepares is compared embodiment one.
Embodiment one compared by the yarn that embodiment three prepares and embodiment two feels are crude a little, and smoothness slightly a little less than.
Claims (4)
1. material blended yarn more than a kind, it is characterized in that: this many materials blended yarn is to be mixed according to a certain percentage by flax, viscose glue and cotton, described flax, viscose glue and cotton compound percentages are 35 ~ 55:15 ~ 35:10 ~ 50.
2. many materials blended yarn as claimed in claim 1 is characterized in that: described flax, viscose glue and cotton compound percentages are 40:20:40.
3. preparation method for the preparation of claim 1 or 2 described many materials blended yarns, preparation process is as follows:
Shredding: with flax, viscose glue and cotton proportionally being evenly arranged in the buffer bin of griping cotton machine, the handgrip of griping cotton machine laterally grasps material, and material is sent into material sucking port;
Combing: material sucking port is sent into the material in the step (1) and is fully mixed combing in the carding machine;
Rolling: the material after the combing is sent into rolling in the lapper;
Slivering: the material of rolling sent into carry out the combing slivering in the comb and parallel cotton fibers prior to spinning sett frame;
Twisting: many composite material rotation windings are become one, make to be parallel to the axial fiber of yarn in the shape of a spiral, thereby produce radial pressure interfibrous vertical linkage is fixed up;
Yarn: the composite material that will be strip is put into the yarn machine and is carried out yarn, and further is transported in the fine spining machine and processes, and is wound up at last on the cone, finishes many materials blended yarn finished product.
4. the preparation method of many materials blended yarn as claimed in claim 3 is characterized in that: step can be wound on the different cylindrical carriers in (6).