CN102644144A - Blending shell fabric containing tea fiber and production technology thereof - Google Patents
Blending shell fabric containing tea fiber and production technology thereof Download PDFInfo
- Publication number
- CN102644144A CN102644144A CN2012101485782A CN201210148578A CN102644144A CN 102644144 A CN102644144 A CN 102644144A CN 2012101485782 A CN2012101485782 A CN 2012101485782A CN 201210148578 A CN201210148578 A CN 201210148578A CN 102644144 A CN102644144 A CN 102644144A
- Authority
- CN
- China
- Prior art keywords
- mins
- rev
- speed
- fiber
- tea fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a blending shell fabric containing tea fiber which comprises the following compositions by weight percent: 25-35% of tea fiber, 10-20% of borlar fiber, 25-35% of counterstat and 20-30% of cotton fiber. A production technology of the blending shell fabric containing tea fiber comprises the following steps of: during a blowing process, setting a beater speed of a cotton slitter as 480 revolutions per minute and a beater speed of a single beater scutcher as 950 revolutions per minute; during a cotton carding process, setting a cylinder speed as 330 revolutions per minute, a doffer speed as 18 revolutions per minute and a licker-in speed as 750 revolutions per minute; during a roving process, setting a roving twisting coefficient as 80 and drafting times of a back zone as 1.30; during a spinning process, setting a spinning twisting coefficient as 380 and drafting times of the back zone as 1.25; during a warping process, setting a running speed as 500m/min; and during a weaving process, setting a let-off tension as 370kg. The blending shell fabric containing tea fiber is excellent in visual effect, has a remarkable feature in the aspect of wearing comfort and has environmental friendliness and anti-bacteria mildew-proof function.
Description
Technical field
The present invention relates to a kind of blended yarn woven fabric and production technology thereof, relate in particular to a kind of tea fiber, luxuriant growth Lay suede, Kang Tesi, cotton fiber blended yarn woven fabric and production technology thereof.
Background technology
Ecological environment be 21 century human one of the matter of utmost importance that will face." clothing, food, lodging and transportion--basic necessities of life " as four human big basic factors in living, " clothing " occupies the first place.When referring to ecological environment problem, have to pay close attention to the ecology development of garment material.Now, " environmental protection ", " green pure natural " this idea have become a kind of fashion, not only are popular in the dining table that our cuisines stand in great numbers, also constantly infiltration in the gaudily dressed fashion wardrobe of people gradually.In a word, " fashion " and " environmental protection " has become two important propositions that the textile clothing industry is paid close attention at present.The ecology development of garment material has been the trend of the times of textile clothing industry, and has developed into a kind of fashion, will worldwide fully develop talents.
Traditional chemical & blended fabric is to be difficult to degraded under field conditions (factors), and environment is had potentially contaminated.Run counter to the theory of people's pursuits " ecological clothes ", " environmental protection dress ornament ".The present invention intends and adopts tea fiber, preserves Lay suede, Kang Tesi and cotton fiber to carry out blending, and be woven into fabric in order to adapt to the demand of present people to the environmental protection lining.In the hope of reaching the environmental protection lining of processing a kind of environmentally safe, human body not being had harm.
Tea fiber is the natural antibacterial agent from tealeaves, to extract---natural tea pigment, Tea Polyphenols, a kind of viscose that catechin etc. make with anti-bacterial anti-foul function; Preserving Lay suede is the high hollow core staple fibers of dacron fine-denier of new generation, and feel softens and warms up, heat-insulating property is excellent; The Kang Tesi fiber integrates the good wearability and the antibiotic health-care function of chitin, is a kind of ecological spinning fiber of novel, healthy, fashion.
Summary of the invention
The object of the invention provide a kind ofly have simultaneously that the moisture absorption of wearing is ventilative, skin-friendly, environmental protection and multifrequency natures such as health, antibacterial mildew-resistant, with tea fiber, to preserve tencels such as Lay suede, Kang Tesi, cotton fiber be the lining and the production technology thereof of raw material blending.
For realizing above-mentioned purpose, the technical scheme that the present invention adopts is:
A kind of blended yarn woven fabric that contains tea fiber is characterized in that: lining forms with tea fiber, luxuriant growth Lay suede, Kang Tesi, cotton fiber blending, and the shared percentage by weight of each component is in its lining:
Tea fiber 25～35%;
Preserve Lay suede 10～20%;
Kang Tesi 25～35%;
Cotton fiber 20～30%.
Above-mentioned a kind of blended yarn woven fabric that contains tea fiber is characterized in that: the shared percentage by weight of each component is in the described lining:
Tea fiber 35%;
Preserve Lay suede 20%;
Kang Tesi 25%;
Cotton fiber 20%.
Above-mentioned a kind of blended yarn woven fabric that contains tea fiber is characterized in that: the shared percentage by weight of each component is in the described lining:
Tea fiber 30%;
Preserve Lay suede 15%;
Kang Tesi 35%;
Cotton fiber 20%.
Above-mentioned a kind of blended yarn woven fabric that contains tea fiber is characterized in that: the shared percentage by weight of each component is in the described lining:
Tea fiber 30%;
Preserve Lay suede 10%;
Kang Tesi 30%;
Cotton fiber 30%.
Above-mentioned a kind of production technology that contains the blended yarn woven fabric of tea fiber is characterized in that:
(1) in the cotton cleaning process, 460～500 rev/mins of opener hired roughneck speed, 900～1000 rev/mins of single beater scutcher hired roughneck speed, 10～12 rev/mins of lap roller speed;
(2) in the carding step, 300～350 rev/mins of cylinder speeds, 17～21 rev/mins of doffer speeds, 750～850 rev/mins of licker-in speeds; Cylinder and cover plate spacer 0.30～0.35mm;
(3) in the rove operation, roving twist factor 75～90, back zone drafting multiple 1.2～1.45;
(4) in the spinning process, spun yarn twist factor 370～390,12000～14000 rev/mins of ingot speed, back zone drafting multiple 1.2～1.45;
(5) in the warping process, the speed of a motor vehicle 450～550m/min;
(6) in the weaving process, warp let-off tension force 360～380kg, opening traverse 80～90mm, back rest height 80～100mm, warp stop frame height 20～40 mm, opening time 280～300
o, main jet air pressure 3.0～3.5kg/cm
2, auxilliary jet pressure 3.8～4.4kg/cm
2
Above-mentioned a kind of production technology that contains the blended yarn woven fabric of tea fiber is characterized in that:
(1) in the cotton cleaning process, 480 rev/mins of opener hired roughneck speed, 950 rev/mins of single beater scutcher hired roughneck speed, 12 rev/mins of lap roller speed;
(2) in the carding step, 330 rev/mins of cylinder speeds, 18 rev/mins of doffer speeds, 750 rev/mins of licker-in speeds; 5 0.35mm that space, 0.30mm, 0.30mm, 0.30mm, 0.35mm between cylinder and cover plate;
(3) in the rove operation, roving twist factor 80, back zone drafting multiple 1.30;
(4) in the spinning process, spun yarn twist factor 380,12000 rev/mins of ingot speed, back zone drafting multiple 1.25;
(5) in the warping process, speed of a motor vehicle 500m/min;
(6) in the weaving process, warp let-off tension force 370kg, opening traverse 84mm, back rest height 80mm, warp stop frame height 20 mm, opening time 290
o, main jet air pressure 3.4kg/cm
2, auxilliary jet pressure 4.0kg/cm
2
Above-mentioned a kind of production technology that contains the blended yarn woven fabric of tea fiber is characterized in that:
(1) in the cotton cleaning process, 470 rev/mins of opener hired roughneck speed, 920 rev/mins of single beater scutcher hired roughneck speed, 10 rev/mins of lap roller speed;
(2) in the carding step, 310 rev/mins of cylinder speeds, 17 rev/mins of doffer speeds, 800 rev/mins of licker-in speeds; 5 0.35mm that space, 0.30mm, 0.30mm, 0.30mm, 0.35mm between cylinder and cover plate;
(3) in the rove operation, roving twist factor 85, back zone drafting multiple 1.25;
(4) in the spinning process, spun yarn twist factor 370,12500 rev/mins of ingot speed, back zone drafting multiple 1.20;
(5) in the warping process, speed of a motor vehicle 450m/min;
(6) in the weaving process, warp let-off tension force 365kg, opening traverse 82mm, back rest height 90mm, warp stop frame height 30 mm, opening time 285
o, main jet air pressure 3.2kg/cm
2, auxilliary jet pressure 3.9kg/cm
2
Above-mentioned a kind of production technology that contains the blended yarn woven fabric of tea fiber is characterized in that:
(1) in the cotton cleaning process, 490 rev/mins of opener hired roughneck speed, 980 rev/mins of single beater scutcher hired roughneck speed, 11 rev/mins of lap roller speed;
(2) in the carding step, 340 rev/mins of cylinder speeds, 20 rev/mins of doffer speeds, 850 rev/mins of licker-in speeds; 5 0.35mm that space, 0.30mm, 0.30mm, 0.30mm, 0.35mm between cylinder and cover plate;
(3) in the rove operation, roving twist factor 90, back zone drafting multiple 1.40;
(4) in the spinning process, spun yarn twist factor 390,13500 rev/mins of ingot speed, back zone drafting multiple 1.35;
(5) in the warping process, speed of a motor vehicle 550m/min;
(6) in the weaving process, warp let-off tension force 375kg, opening traverse 88mm, back rest height 95mm, warp stop frame height 35 mm, opening time 295
o, main jet air pressure 3.3kg/cm
2, auxilliary jet pressure 4.2kg/cm
2
A kind of blended yarn woven fabric that contains tea fiber of the present invention combines the good characteristic of tea fiber and other fiber blend, adopts 5/3 satin drill, 5/3 sateen institutional framework, has the following advantages:
1, green environmental protection, tea fiber, luxuriant growth Lay suede, Kang Tesi, cotton fiber blended yarn woven fabric have the natural colour of tea fiber, need not print and dye, and environmentally safe does not have potential hazard to human body, also has the characteristic of natural environmental-protective.
2, antibacterial antimildew function, tea fiber, Kang Tesi and human body skin compatibility are good, and product has functions such as antibacterial deodourizing, skin-protection and health-care, multifrequency natures such as moisture absorption is ventilative, comfortable and easy to wear, antibacterial mildew-resistant.
3, comfortableness is good, and tea fiber, luxuriant growth Lay suede, Kang Tesi, cotton fiber blended yarn woven fabric not only have excellent visual effect, and aspect comfortable and easy to wear, characteristic out of the ordinary are arranged more, have good surface appearance and fine and smooth softness, slide glutinous feel.
The specific embodiment
Below in conjunction with specific embodiment the present invention is described further:
A kind of blended yarn woven fabric that contains tea fiber of the present invention; Be with tea fiber, preserve Lay suede, Kang Tesi, cotton fiber to carry out blowing, comb and parallel cotton fibers prior to spinning, drafting, rove, spun yarn etc. respectively, be spun into the multi-functional environment-protection yarn of four kinds of fiber components at last and be woven into fabric by the operation spinning.It is characterized in that: the shared percentage by weight of each component is in its lining:
Tea fiber 25～35%;
Preserve Lay suede 10～20%;
Kang Tesi 25～35%;
Cotton fiber 20～30%.
Embodiment 1 (most preferred embodiment)
The shared percentage by weight of each component is in a kind of blended yarn woven fabric that contains tea fiber:
Tea fiber 35%;
Preserve Lay suede 20%;
Kang Tesi 25%;
Cotton fiber 20%.
Embodiment 2
The shared percentage by weight of each component is in a kind of blended yarn woven fabric that contains tea fiber:
Tea fiber 30%;
Preserve Lay suede 15%;
Kang Tesi 35%;
Cotton fiber 20%.
Embodiment 3
The shared percentage by weight of each component is in a kind of blended yarn woven fabric that contains tea fiber:
Tea fiber 30%;
Preserve Lay suede 10%;
Kang Tesi 30%;
Cotton fiber 30%.
A kind of production technology that contains the blended yarn woven fabric of tea fiber of the present invention:
(1) in the cotton cleaning process, 460～500 rev/mins of opener hired roughneck speed, 900～1000 rev/mins of single beater scutcher hired roughneck speed, 10～12 rev/mins of lap roller speed;
(2) in the carding step, main technologic parameters: 300～350 rev/mins of cylinder speeds, 17～21 rev/mins of doffer speeds, 750～850 rev/mins of licker-in speeds; Cylinder and cover plate spacer 0.30～0.35mm;
(3) in the rove operation, roving twist factor 75～90; Back zone drafting multiple 1.2～1.45;
(4) in the spinning process, twist factor 370～390 adopts technologies such as moccasin roller, speed of a motor vehicle grasp on the low side, 12000～14000 rev/mins of ingot speed, back zone drafting multiple 1.2～1.45;
(5) in the warping process, the speed of a motor vehicle 450～550m/min;
(6) in the weaving process, warp let-off tension force 360～380kg, opening traverse 80～90mm, back rest height 80～100mm, warp stop frame height 20～40 mm, opening time 280～300
o, main jet air pressure 3.0～3.5kg/cm
2, auxilliary jet pressure 3.8～4.4kg/cm
2
Embodiment 4 (optimised process embodiment)
(1) in the cotton cleaning process, 480 rev/mins of opener hired roughneck speed, 950 rev/mins of single beater scutcher hired roughneck speed, 12 rev/mins of lap roller speed;
(2) in the carding step, 330 rev/mins of cylinder speeds, 18 rev/mins of doffer speeds, 750 rev/mins of licker-in speeds; 5 0.35mm that space, 0.30mm, 0.30mm, 0.30mm, 0.35mm between cylinder and cover plate;
(3) in the rove operation, roving twist factor 80, back zone drafting multiple 1.30;
(4) in the spinning process, spun yarn twist factor 380,12000 rev/mins of ingot speed, back zone drafting multiple 1.25;
(5) in the warping process, speed of a motor vehicle 500m/min;
(6) in the weaving process, warp let-off tension force 370kg, opening traverse 84mm, back rest height 80mm, warp stop frame height 20mm, opening time 290
o, main jet air pressure 3.4kg/cm
2, auxilliary jet pressure 4.0kg/cm
2
Embodiment 5
(1) in the cotton cleaning process, 470 rev/mins of opener hired roughneck speed, 920 rev/mins of single beater scutcher hired roughneck speed, 10 rev/mins of lap roller speed;
(2) in the carding step, 310 rev/mins of cylinder speeds, 17 rev/mins of doffer speeds, 800 rev/mins of licker-in speeds; 5 0.35mm that space, 0.30mm, 0.30mm, 0.30mm, 0.35mm between cylinder and cover plate;
(3) in the rove operation, roving twist factor 85, back zone drafting multiple 1.25;
(4) in the spinning process, spun yarn twist factor 370,12500 rev/mins of ingot speed, back zone drafting multiple 1.20;
(5) in the warping process, speed of a motor vehicle 450m/min;
(6) in the weaving process, warp let-off tension force 365kg, opening traverse 82mm, back rest height 90mm, warp stop frame height 30 mm, opening time 285
o, main jet air pressure 3.2kg/cm
2, auxilliary jet pressure 3.9kg/cm
2
Embodiment 6
(1) in the cotton cleaning process, 490 rev/mins of opener hired roughneck speed, 980 rev/mins of single beater scutcher hired roughneck speed, 11 rev/mins of lap roller speed;
(2) in the carding step, 340 rev/mins of cylinder speeds, 20 rev/mins of doffer speeds, 850 rev/mins of licker-in speeds; 5 0.35mm that space, 0.30mm, 0.30mm, 0.30mm, 0.35mm between cylinder and cover plate;
(3) in the rove operation, roving twist factor 90, back zone drafting multiple 1.40;
(4) in the spinning process, spun yarn twist factor 390,13500 rev/mins of ingot speed, back zone drafting multiple 1.35;
(5) in the warping process, speed of a motor vehicle 550m/min;
(6) in the weaving process, warp let-off tension force 375kg, opening traverse 88mm, back rest height 95mm, warp stop frame height 35 mm, opening time 295
o, main jet air pressure 3.3kg/cm
2, auxilliary jet pressure 4.2kg/cm
2
Embodiment recited above describes preferred implementation of the present invention; Be not that design of the present invention and protection domain are limited; Under the prerequisite that does not break away from design concept of the present invention; Common engineers and technicians make technical scheme of the present invention in this area various modification and improvement all should fall into protection scope of the present invention.
Claims (4)
1. blended yarn woven fabric that contains tea fiber is characterized in that: lining with tea fiber, preserve Lay suede, Kang Tesi, cotton fiber blending to form, the shared percentage by weight of each component is in its lining:
Tea fiber 25～35%;
Preserve Lay suede 10～20%;
Kang Tesi 25～35%;
Cotton fiber 20～30%.
2. a kind of blended yarn woven fabric that contains tea fiber according to claim 1 is characterized in that: the shared percentage by weight of each component is in the lining:
Tea fiber 35%;
Preserve Lay suede 20%;
Kang Tesi 25%;
Cotton fiber 20%.
3. production technology that contains the blended yarn woven fabric of tea fiber is characterized in that:
(1) in the cotton cleaning process, 460～500 rev/mins of opener hired roughneck speed, 900～1000 rev/mins of single beater scutcher hired roughneck speed, 10～12 rev/mins of lap roller speed;
(2) in the carding step, 300～350 rev/mins of cylinder speeds, 17～21 rev/mins of doffer speeds, 750～850 rev/mins of licker-in speeds; Cylinder and cover plate spacer 0.30～0.35mm;
(3) in the rove operation, roving twist factor 75～90, back zone drafting multiple 1.2～1.45;
(4) in the spinning process, spun yarn twist factor 370～390,12000～14000 rev/mins of ingot speed, back zone drafting multiple 1.2～1.45;
(5) in the warping process, the speed of a motor vehicle 450～550m/min;
(6) in the weaving process, warp let-off tension force 360～380kg, opening traverse 80～90mm, back rest height 80～100mm, warp stop frame height 20～40 mm, opening time 280～300
o, main jet air pressure 3.0～3.5kg/cm
2, auxilliary jet pressure 3.8～4.4kg/cm
2
4. a kind of production technology that contains the blended yarn woven fabric of tea fiber according to claim 3 is characterized in that:
(1) in the cotton cleaning process, 480 rev/mins of opener hired roughneck speed, 950 rev/mins of single beater scutcher hired roughneck speed, 12 rev/mins of lap roller speed;
(2) in the carding step, 330 rev/mins of cylinder speeds, 18 rev/mins of doffer speeds, 750 rev/mins of licker-in speeds; 5 0.35mm that space, 0.30mm, 0.30mm, 0.30mm, 0.35mm between cylinder and cover plate;
(3) in the rove operation, roving twist factor 80, back zone drafting multiple 1.30;
(4) in the spinning process, spun yarn twist factor 380,12000 rev/mins of ingot speed, back zone drafting multiple 1.25;
(5) in the warping process, speed of a motor vehicle 500m/min;
(6) in the weaving process, warp let-off tension force 370kg, opening traverse 84mm, back rest height 80mm, warp stop frame height 20 mm, opening time 290
o, main jet air pressure 3.4kg/cm
2, auxilliary jet pressure 4.0kg/cm
2