CN102417621A - Wear resistant undersole rubber material for shoes - Google Patents
Wear resistant undersole rubber material for shoes Download PDFInfo
- Publication number
- CN102417621A CN102417621A CN2011103792507A CN201110379250A CN102417621A CN 102417621 A CN102417621 A CN 102417621A CN 2011103792507 A CN2011103792507 A CN 2011103792507A CN 201110379250 A CN201110379250 A CN 201110379250A CN 102417621 A CN102417621 A CN 102417621A
- Authority
- CN
- China
- Prior art keywords
- parts
- wear
- elastomeric material
- big end
- rubber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a wear resistant undersole rubber material for shoes. The rubber material comprises the following components by weight: 60 parts of smoke sheet rubber, 90 parts of cis-butadiene rubber, 3 parts of a vulcanizing agent, 3.3 parts of a promoter, 7.5 parts of zinc carbonate, 3 parts of stearic acid, 3 parts of an antioxidant, 70 parts of white carbon black, 5.6 parts of diethylene glycol, 30 parts of machine oil, 20 parts of potter's clay powder and 7.5 parts of the resin RX-80. The wear resistant undersole rubber material provided in the invention has incomparable super wear resistance compared to common rubber soles and has a plurality of good performance like wet-skid resistance, resistance to impact, etc.
Description
Technical field
The present invention relates to a kind of rubber compounding, particularly a kind of footwear are with elastomeric material of the wear-resisting big end.
Background technology
Prescription and method of manufacture about rubber combination are thousands of, often are furnished with the material different prescription according to different request for utilizations.Common rubber boots quality with the wear resisting property of anti-marquis at present commonly used is lower, not weather-proof, without low with, subduing property of antifatigue, be prone to chap, reliability is good inadequately.
Summary of the invention
In order to overcome above-mentioned defective, the invention provides a kind of elastomeric material that is used for shoemaking with good abrasion resistance.
The present invention for the technical scheme that solves its technical problem and adopt is: a kind of footwear comprise following weight ratio composition: smoke sheet rubber: 60 parts with elastomeric material of the wear-resisting big end; Cis-butadiene cement: 90 parts; Vulcanizing agent: 3 parts; Promotor: 3.3 parts; Zinc carbonate: 7.5 parts; Triple Pressed Stearic Acid: 3 parts; Anti-aging agent: 3 parts; White carbon black: 70 parts; Glycol ether: 5.6 parts; Machine oil: 30 parts; Potter's clay powder: 20 parts; Resin RX-80:7.5 part.
As further improvement of the present invention, said promotor is specially 0.1 part of 1 part of captax, 2 parts of altaxs, 2 0.2 parts of accelerant C and promotor TS.
As further improvement of the present invention, said anti-aging agent is specially 3 parts of antioxidant SP-C.
As further improvement of the present invention, said vulcanizing agent is sulphur S.
As further improvement of the present invention, said Triple Pressed Stearic Acid is a Zinic stearas.
The invention has the beneficial effects as follows: with the shoe rubber sole that this technical scheme is made, have the General Purpose Rubber sole incomparable super wear resisting property, and have good anti-slippery, multiple performance such as shock resistance.
Embodiment
In order to deepen to understanding of the present invention, will combine embodiment that the present invention is made further detailed description below, this embodiment only is used to explain the present invention, does not constitute the qualification to protection domain of the present invention.
Present embodiment shows the embodiment of a kind of footwear with elastomeric material of the wear-resisting big end: comprise following weight ratio composition: smoke sheet rubber: 60 parts; Cis-butadiene cement: 90 parts; Vulcanizing agent: 3 parts; Promotor: 3.3 parts; Zinc carbonate: 7.5 parts; Triple Pressed Stearic Acid: 3 parts; Anti-aging agent: 3 parts; White carbon black: 70 parts; Glycol ether: 5.6 parts; Machine oil: 30 parts; Potter's clay powder: 20 parts; Resin RX-80:7.5 part.Said promotor is specially 0.1 part of 1 part of captax, 2 parts of altaxs, 2 0.2 parts of accelerant C and promotor TS, and said anti-aging agent is specially 3 parts of antioxidant SP-C.Said vulcanizing agent is sulphur S, and said Triple Pressed Stearic Acid is a Zinic stearas, adopt above-mentioned sole with rubber compounding after, can obtain the ideal raw material function combinations, thereby this prescription has the overall performance that improves rubber aniseed itself of good over-all properties.
Claims (5)
1. footwear is characterized in that: comprise following weight ratio composition with elastomeric material of the wear-resisting big end:
Smoke sheet rubber: 60 parts;
Cis-butadiene cement: 90 parts;
Vulcanizing agent: 3 parts;
Promotor: 3.3 parts;
Zinc carbonate: 7.5 parts;
Triple Pressed Stearic Acid: 3 parts;
Anti-aging agent: 3 parts;
White carbon black: 70 parts;
Glycol ether: 5.6 parts;
Machine oil: 30 parts;
Potter's clay powder: 20 parts;
Resin RX-80:7.5 part.
2. footwear according to claim 1 is characterized in that with elastomeric material of the wear-resisting big end: said promotor is specially 0.1 part of 1 part of captax, 2 parts of altaxs, 2 0.2 parts of accelerant C and promotor TS.
3. footwear according to claim 1 is characterized in that with elastomeric material of the wear-resisting big end: said anti-aging agent is specially 3 parts of antioxidant SP-C.
4. footwear according to claim 1 is characterized in that with elastomeric material of the wear-resisting big end: said vulcanizing agent is sulphur S.
5. footwear according to claim 1 is characterized in that with elastomeric material of the wear-resisting big end: said Triple Pressed Stearic Acid is a Zinic stearas.