CN103194074A - Cork wood swim ring and production method thereof - Google Patents
Cork wood swim ring and production method thereof Download PDFInfo
- Publication number
- CN103194074A CN103194074A CN2012102789959A CN201210278995A CN103194074A CN 103194074 A CN103194074 A CN 103194074A CN 2012102789959 A CN2012102789959 A CN 2012102789959A CN 201210278995 A CN201210278995 A CN 201210278995A CN 103194074 A CN103194074 A CN 103194074A
- Authority
- CN
- China
- Prior art keywords
- cork
- water wing
- granulated
- production method
- make
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a cork wood swim ring and a production method thereof, and belongs to the technical field of cork wood product production. The existing swim ring products in China comprise a plastic inflatable swim ring and a rubber inflatable swim ring. The preparation method comprises that cork wood particles are bound by a binder gasoline solution; and the bound cork wood particles are vulcanized into the cork wood swim ring.
Description
(1) technical field
The present invention discloses a kind of cork water wing and production method thereof, belongs to the cork article production technical field.
(2) background technology
Now internal travel swimming life-buoy product principal mode kind has 2 kinds of plastic inflatable water wing and inflated rubber water wings, and in the cork article production technical field, the used glue of bonding granulated cork is generally Polyurethane glue at home.
(3) summary of the invention
A kind of cork water wing and production method thereof involved in the present invention, the cork of cork water wing partly are to be constructed by the industrial chemicals gummed of granulated cork and a kind of adhesive formulation to form.This gluing gasoline solution, can be fine with the granulated cork glue bond, after treating the industrial naptha volatilization, the irony die box of can the granulated cork that viscose glue is good putting into the cork water wing, after compacting sealing under the pressure condition of 10MPa, put into baker again and vulcanize in the temperature of 110~130 degree Celsius, make the cork case material of cork water wing, wrap the plastic cement foreskin, the cork water wing.
The production method of a kind of cork water wing involved in the present invention is finished by following steps:
A. the diameter of selecting particle for use is that 0.5~5.00mm, unit weight are that the granulated cork of 50~65g/L is major ingredient;
B. with prescription (weight part)
The industrial chemicals of (1)~(11) with the mixing one-tenth film of opening rubber mixing machine, is put into the gasoline stirrer and added the solvent gas and oil and stir after shredding with scissors, dissolve fully up to oddments, make tackiness agent gasoline solution;
C. the granulated cork of selecting for use is put into the cork stirrer with the tackiness agent gasoline solution of making and stir 10min; Make granulated cork and tackiness agent gasoline solution evenly and fully contact and covering;
D. start vacuum fan, extract and be transported to the industrial naptha gas of volatilization in stirrer out the baker burning.
E. the drying that measures the granulated cork that is covered with industrial chemicals put in the iron die box of cork water wing and putting into the baker internal heating after the compacting sealing under the pressure condition of 10MPa, make the temperature of iron die box in the environment of 110~130 degree Celsius, vulcanize 2h, the airing 24h that comes out of the stove then, breakdown iron die box namely gets the case material of cork water wing.
F. plastic cement foreskin on the case material package of cork water wing, the commodity cork buoy.
(4) description of drawings
Accompanying drawing is the local structure synoptic diagram of cork water wing.
Wherein the label among the figure 1 is granulated cork.
Label 2 among the figure is the industrial chemicals of adhesive formulation.
(5) embodiment
Son is described further the technical scheme of a kind of cork water wing of the present invention and production method thereof by the following examples.
A kind of cork water wing and production method thereof, finished by following steps:
A. the diameter of selecting particle for use is that 0.5~5.00mm, unit weight are that the granulated cork 15kg of 50~65g/L is major ingredient;
B. with prescription:
The industrial chemicals of (1)~(11) with the mixing one-tenth film of opening rubber mixing machine, is put into the gasoline stirrer and added the solvent gas and oil and stir after shredding with scissors, dissolve fully up to oddments, make tackiness agent gasoline solution;
C. the granulated cork of selecting for use is put into the cork stirrer with the tackiness agent gasoline solution of making and stir 10min; Make granulated cork and tackiness agent gasoline solution evenly and fully contact and covering;
D. start vacuum fan, extract and be transported to the industrial naptha gas that volatilizees in stirrer out the baker burning, taken away up to feeling that by range estimation and hand sth. made by twisting the gas of industrial naptha has volatilized;
E is the dry granulated cork that is covered with industrial chemicals, after putting into the pressure condition compacting sealing of the inherent 10MPa of iron die box of a plurality of cork water wings, put into the baker internal heating again, the temperature of iron die box is vulcanized 2h in the environment of 110~130 degree Celsius, treating to come out of the stove after the vulcanization of rubber cools 24h, opens the case material that the iron die box namely gets the cork water wing.
F. plastic cement foreskin on the case material package of cork water wing commodity cork water wing.
Claims (4)
1. a cork water wing and production method thereof is characterized in that the cork water wing is by the chemical materials structure of granulated cork and adhesive formulation and make.
2. a kind of cork water wing according to claim 1 and production method thereof is characterized in that used granulated cork is that diameter 0.5~5mm, unit weight are the granulated cork of 50~65g/L.
4. according to claim 1,2,3 described a kind of cork water wing and production methods thereof, it is characterized in that the technology of making of cork water wing is finished by following steps:
A. the diameter of selecting particle for use is that 0.5~5.00mm, unit weight are that the granulated cork of 50~65g/L is major ingredient;
B. with industrial chemicals with opening rubber mixing machine mixing one-tenth film, put into the gasoline stirrer after shredding with scissors, and add the solvent gas and oil and stir, dissolve fully up to oddments, make tackiness agent gasoline solution;
C.. the granulated cork of selecting for use is put into the cork stirrer with the tackiness agent gasoline solution of making and stir 10min; Make granulated cork and tackiness agent gasoline solution evenly and fully contact and covering;
D. start vacuum fan, extract and be transported to the industrial naptha gas of volatilization in stirrer out the baker burning.
E. drying the granulated cork that the is covered with industrial chemicals iron die box intrinsic pressure of putting the cork water wing into be to put into the baker internal heating after the compacting sealing under the condition of 10MPa, make the temperature of iron die box in the environment of 110~130 degree Celsius, vulcanize 2h, the airing 24h that comes out of the stove then, breakdown iron die box namely gets the case material of cork water wing.
F. plastic cement foreskin on the case material package of cork water wing commodity cork water wing.