CN104212024B - A kind of electric fan counterweight chassis adopting reworked material to prepare - Google Patents

A kind of electric fan counterweight chassis adopting reworked material to prepare Download PDF

Info

Publication number
CN104212024B
CN104212024B CN201410405927.3A CN201410405927A CN104212024B CN 104212024 B CN104212024 B CN 104212024B CN 201410405927 A CN201410405927 A CN 201410405927A CN 104212024 B CN104212024 B CN 104212024B
Authority
CN
China
Prior art keywords
parts
ball
powder
straw
properties
Prior art date
Application number
CN201410405927.3A
Other languages
Chinese (zh)
Other versions
CN104212024A (en
Inventor
王志强
Original Assignee
王志强
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 王志强 filed Critical 王志强
Priority to CN201410405927.3A priority Critical patent/CN104212024B/en
Publication of CN104212024A publication Critical patent/CN104212024A/en
Application granted granted Critical
Publication of CN104212024B publication Critical patent/CN104212024B/en

Abstract

A kind of electric fan counterweight chassis adopting reworked material to prepare, relate to electrical accessorie technical field, it is made up of the component of following weight part number: regenerated polythene 25-35 part, regenerating polypropylene 15-25 part, waste cotton fiber 5-15 part, straw 4-6 part, natural rubber 4-6 part, silicone oil 1-3 part, white carbon black 4-6 part, urethane 4-6 part, kaolin 4-6 part, rice bran 4-6 part, linear polyethylene 4-6 part, PVC label paper 4-6 part, fire retardant 1-3 part, talcum powder 4-6 part, epoxy soybean oil 2-4 part, calcium carbonate 1-2 part, oxidation inhibitor 1-2 part, sawdust 1-3 part, properties-correcting agent 1-2 part, the present invention adopts waste as production starting material, and the product of preparation has higher intensity and hardness, acid and alkali-resistance, anticorrosive, be not out of shape, containing formaldehyde, be a kind of new green environment protection material.

Description

A kind of electric fan counterweight chassis adopting reworked material to prepare
Technical field
The present invention relates to electrical accessorie technical field, it is specifically related to a kind of electric fan counterweight chassis adopting reworked material to prepare.
Background technology
The chassis of traditional electrical fan casts by pig iron monoblock, and its weight is big, packaging, transport difficult. In order to alleviate the weight on chassis and have people be cast by iron into below have the chassis of skeleton, except skeleton, other position on chassis is all thinner, so that the lighter overall weight on chassis. But the face, chassis on the skeleton on this kind of chassis and its top is cast by iron and is integrated, and usually ruptures, so that chassis is scrapped in transportation. Along with the development of technology, arise at the historic moment in plastics counterweight chassis. It is low that it has cost, easy-formation, and the advantage such as easy fracture, is not widely used. But existing plastic chassis major part is all adopt virgin material to be prepared from, and does not all improve on formula always.
Summary of the invention
Technical problem to be solved by this invention is to provide a kind of cost low, electric fan counterweight chassis prepared by the employing reworked material that performance is good.
Technical problem to be solved by this invention realizes by the following technical solutions:
Adopt an electric fan counterweight chassis prepared by reworked material, it is made up of the component of following weight part number: regenerated polythene 25-35 part, regenerating polypropylene 15-25 part, waste cotton fiber 5-15 part, straw 4-6 part, natural rubber 4-6 part, silicone oil 1-3 part, white carbon black 4-6 part, urethane 4-6 part, kaolin 4-6 part, rice bran 4-6 part, linear polyethylene 4-6 part, PVC label paper 4-6 part, fire retardant 1-3 part, talcum powder 4-6 part, epoxy soybean oil 2-4 part, calcium carbonate 1-2 part, oxidation inhibitor 1-2 part, sawdust 1-3 part, properties-correcting agent 1-2 part;
Described properties-correcting agent is made up of the component of following weight part number: Graphene 1-2 part, silicon carbide 1-3 part, pitch 2-4 part, modified corn starch 4-6 part, neoprene latex 4-6 part, carbon fiber 4-6 part, boron fibre 1-3 part, tourmalinite 4-6 part, Platinic chloride 1-3 part, aluminum oxide 1-2 part;
The better weight part number of each component is: regenerated polythene 30 parts, regenerating polypropylene 20 parts, waste cotton fiber 10 parts, straw 5 parts, natural rubber 5 parts, silicone oil 2 parts, white carbon black 5 parts, urethane 5 parts, kaolin 5 parts, 5 parts, rice bran, linear polyethylene 5 parts, PVC label paper 5 parts, fire retardant 2 parts, talcum powder 5 parts, epoxy soybean oil 3 parts, 1 part, calcium carbonate, 1 part, oxidation inhibitor, 2 parts, sawdust, properties-correcting agent 2 parts;
Described properties-correcting agent is made up of the component of following weight part number: Graphene 1 part, 2 parts, silicon carbide, pitch 3 parts, modified corn starch 5 parts, neoprene latex 5 parts, 5 parts, carbon fiber, boron fibre 2 parts, 5 parts, tourmalinite, Platinic chloride 2 parts, 1 part, aluminum oxide;
Described waste cotton fiber selects waste and old clothes product.
Its preparation method is as follows:
1) regenerated polythene, regenerating polypropylene, waste cotton fiber cleaned, dry, sterilization, straw is pulverized stand-by;
2) by step 1) in regenerated polythene, regenerating polypropylene, waste cotton fiber take dehydrated alcohol as dispersion medium, wherein the mass ratio of material and ethanol is 1:30, ultrasonic disperse 1 hour on ultrasonic cleaning machine;
3) compound through ultrasonic disperse being put into nylon ball grinder, then add straw, properties-correcting agent, kaolin and rice bran, take agate ball as abrading-ball, ball material mass ratio is 7:1, when rotating speed is 150 revs/min, and continuous ball milling 2 hours;
4) powder complete for ball milling is poured in powder dish together with agate abrading-ball, dry at 80 DEG C, the powder dried is sieved, take out agate abrading-ball, then in compound, add white carbon black, talcum powder, urethane, PVC label paper and sawdust grind, until without, till bigger reunion, so far, the preparation of mixed powder is complete;
5) by step 4) in mixture mix with natural rubber, silicone oil, linear polyethylene, fire retardant, epoxy soybean oil, calcium carbonate and oxidation inhibitor, evenly mixing in kneader, in 18 DEG C process 3 hours, be mixed with sizing material;
6) by step 5) in sizing material hot-press vulcanization 10 minutes under 170 DEG C of conditions, then under 200 DEG C of conditions sulfuration 4 hours in an oven, then send into mould and carry out extrusion moulding.
The invention has the beneficial effects as follows:
1) the present invention adopts waste as production starting material, and the product of preparation has higher intensity and hardness, acid and alkali-resistance, anticorrosive, be not out of shape, containing formaldehyde, be a kind of new green environment protection material;
2) starting material be have employed special treatment process so that the product of preparation has higher stability, resistance to deterioration, the consistence of color and persistence.
Embodiment
In order to the present invention is realized technique means, creation characteristic, reach object and effect is easy to understand, below in conjunction with specific embodiment, set forth the present invention further.
Embodiment 1
Adopt an electric fan counterweight chassis prepared by reworked material, it is made up of the component of following weight part number: regenerated polythene 30 parts, regenerating polypropylene 20 parts, waste and old clothing 10 parts, straw 5 parts, natural rubber 5 parts, silicone oil 2 parts, white carbon black 5 parts, urethane 5 parts, kaolin 5 parts, 5 parts, rice bran, linear polyethylene 5 parts, PVC label paper 5 parts, fire retardant 2 parts, talcum powder 5 parts, epoxy soybean oil 3 parts, 1 part, calcium carbonate, 1 part, oxidation inhibitor, 2 parts, sawdust, properties-correcting agent 2 parts;
Described properties-correcting agent is made up of the component of following weight part number: Graphene 1 part, 2 parts, silicon carbide, pitch 3 parts, modified corn starch 5 parts, neoprene latex 5 parts, 5 parts, carbon fiber, boron fibre 2 parts, 5 parts, tourmalinite, Platinic chloride 2 parts, 1 part, aluminum oxide;
Its preparation method is as follows:
1) regenerated polythene, regenerating polypropylene, waste and old clothing cleaned, dry, sterilization, straw is pulverized stand-by;
2) by step 1) in regenerated polythene, regenerating polypropylene, waste cotton fiber take dehydrated alcohol as dispersion medium, wherein the mass ratio of material and ethanol is 1:30, ultrasonic disperse 1 hour on ultrasonic cleaning machine;
3) compound through ultrasonic disperse being put into nylon ball grinder, then add straw, properties-correcting agent, kaolin and rice bran, take agate ball as abrading-ball, ball material mass ratio is 7:1, when rotating speed is 150 revs/min, and continuous ball milling 2 hours;
4) powder complete for ball milling is poured in powder dish together with agate abrading-ball, dry at 80 DEG C, the powder dried is sieved, take out agate abrading-ball, then in compound, add white carbon black, talcum powder, urethane, PVC label paper and sawdust grind, until without, till bigger reunion, so far, the preparation of mixed powder is complete;
5) by step 4) in mixture mix with natural rubber, silicone oil, linear polyethylene, fire retardant, epoxy soybean oil, calcium carbonate and oxidation inhibitor, evenly mixing in kneader, in 18 DEG C process 3 hours, be mixed with sizing material;
6) by step 5) in sizing material hot-press vulcanization 10 minutes under 170 DEG C of conditions, then under 200 DEG C of conditions sulfuration 4 hours in an oven, then send into mould and carry out extrusion moulding.
Embodiment 2
Adopt an electric fan counterweight chassis prepared by reworked material, it is made up of the component of following weight part number: regenerated polythene 35 parts, regenerating polypropylene 25 parts, waste cotton fiber 15 parts, straw 6 parts, natural rubber 6 parts, silicone oil 3 parts, white carbon black 6 parts, urethane 6 parts, kaolin 6 parts, 6 parts, rice bran, linear polyethylene 6 parts, PVC label paper 6 parts, fire retardant 3 parts, talcum powder 6 parts, epoxy soybean oil 4 parts, 2 parts, calcium carbonate, 2 parts, oxidation inhibitor, 3 parts, sawdust, properties-correcting agent 2 parts;
Properties-correcting agent is made up of the component of following weight part number: Graphene 2 parts, 3 parts, silicon carbide, pitch 4 parts, modified corn starch 6 parts, neoprene latex 6 parts, 6 parts, carbon fiber, boron fibre 3 parts, 6 parts, tourmalinite, Platinic chloride 3 parts, 2 parts, aluminum oxide;
Its preparation method is as follows:
1) regenerated polythene, regenerating polypropylene, waste cotton fiber cleaned, dry, sterilization, straw is pulverized stand-by;
2) by step 1) in regenerated polythene, regenerating polypropylene, waste cotton fiber take dehydrated alcohol as dispersion medium, wherein the mass ratio of material and ethanol is 1:30, ultrasonic disperse 1 hour on ultrasonic cleaning machine;
3) compound through ultrasonic disperse being put into nylon ball grinder, then add straw, properties-correcting agent, kaolin and rice bran, take agate ball as abrading-ball, ball material mass ratio is 7:1, when rotating speed is 150 revs/min, and continuous ball milling 2 hours;
4) powder complete for ball milling is poured in powder dish together with agate abrading-ball, dry at 80 DEG C, the powder dried is sieved, take out agate abrading-ball, then in compound, add white carbon black, talcum powder, urethane, PVC label paper and sawdust grind, until without, till bigger reunion, so far, the preparation of mixed powder is complete;
5) by step 4) in mixture mix with natural rubber, silicone oil, linear polyethylene, fire retardant, epoxy soybean oil, calcium carbonate and oxidation inhibitor, evenly mixing in kneader, in 18 DEG C process 3 hours, be mixed with sizing material;
6) by step 5) in sizing material hot-press vulcanization 10 minutes under 170 DEG C of conditions, then under 200 DEG C of conditions sulfuration 4 hours in an oven, then send into mould and carry out extrusion moulding.
More than show and describe the ultimate principle of the present invention and the advantage of main characteristic sum the present invention. The technician of the industry should understand; the present invention is not restricted to the described embodiments; the principle that the present invention is just described described in above-described embodiment and specification sheets; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements all fall in the claimed scope of the invention.The claimed scope of the present invention is defined by appending claims and equivalent thereof.

Claims (2)

1. one kind adopts electric fan counterweight chassis prepared by reworked material, it is characterized in that, it is made up of the component of following weight part number: regenerated polythene 25-35 part, regenerating polypropylene 15-25 part, waste cotton fiber 5-15 part, straw 4-6 part, natural rubber 4-6 part, silicone oil 1-3 part, white carbon black 4-6 part, urethane 4-6 part, kaolin 4-6 part, rice bran 4-6 part, linear polyethylene 4-6 part, PVC label paper 4-6 part, fire retardant 1-3 part, talcum powder 4-6 part, epoxy soybean oil 2-4 part, calcium carbonate 1-2 part, oxidation inhibitor 1-2 part, sawdust 1-3 part, properties-correcting agent 1-2 part;
Described properties-correcting agent is made up of the component of following weight part number: Graphene 1-2 part, silicon carbide 1-3 part, pitch 2-4 part, modified corn starch 4-6 part, neoprene latex 4-6 part, carbon fiber 4-6 part, boron fibre 1-3 part, tourmalinite 4-6 part, Platinic chloride 1-3 part, aluminum oxide 1-2 part.
2. prepare the method on electric fan counterweight chassis described in claim 1 for one kind, it is characterised in that, method steps is as follows:
1) regenerated polythene, regenerating polypropylene, waste cotton fiber cleaned, dry, sterilization, straw is pulverized stand-by;
2) by step 1) in regenerated polythene, regenerating polypropylene, waste cotton fiber take dehydrated alcohol as dispersion medium, wherein the mass ratio of material and ethanol is 1:30, ultrasonic disperse 1 hour on ultrasonic cleaning machine;
3) compound through ultrasonic disperse being put into nylon ball grinder, then add straw, properties-correcting agent, kaolin and rice bran, take agate ball as abrading-ball, ball material mass ratio is 7:1, when rotating speed is 150 revs/min, and continuous ball milling 2 hours;
4) powder complete for ball milling is poured in powder dish together with agate abrading-ball, dry at 80 DEG C, the powder dried is sieved, take out agate abrading-ball, then in compound, add white carbon black, talcum powder, urethane, PVC label paper and sawdust grind, until without, till bigger reunion, so far, the preparation of mixed powder is complete;
5) by step 4) in mixture mix with natural rubber, silicone oil, linear polyethylene, fire retardant, epoxy soybean oil, calcium carbonate and oxidation inhibitor, evenly mixing in kneader, in 18 DEG C process 3 hours, be mixed with sizing material;
6) by step 5) in sizing material hot-press vulcanization 10 minutes under 170 DEG C of conditions, then under 200 DEG C of conditions sulfuration 4 hours in an oven, then send into mould and carry out extrusion moulding.
CN201410405927.3A 2014-08-18 2014-08-18 A kind of electric fan counterweight chassis adopting reworked material to prepare CN104212024B (en)