CN102383318A - 一种珠光纺织物染液 - Google Patents
一种珠光纺织物染液 Download PDFInfo
- Publication number
- CN102383318A CN102383318A CN2011102132798A CN201110213279A CN102383318A CN 102383318 A CN102383318 A CN 102383318A CN 2011102132798 A CN2011102132798 A CN 2011102132798A CN 201110213279 A CN201110213279 A CN 201110213279A CN 102383318 A CN102383318 A CN 102383318A
- Authority
- CN
- China
- Prior art keywords
- pearly
- dye liquor
- coating
- dye solution
- lustre
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种珠光纺织物染液，其特征在于，每升染液所含组分以克计组成为：涂料色浆15～80，脂肪醇聚氧乙烯醚磷酸单酯5～25，山梨醇酐月桂酸酯10～35，聚乙烯醇10～35，硝化纤维素10～20，富马海松酸4～30水30～100。本发明的染液使得涂料有良好的耐摩擦性和耐搓洗牢固性。本发明的染液使得印花具有有良好的耐光、耐气候、耐热性。本发明不含有甲醛、重金属和有机锡等有害物质，环保、健康。
Description
技术领域
本发明属于纺织领域，且特别涉及一种纺织物染液。
背景技术
涂料印花就是用适当的高分子化合物和涂料印到织物上，经过处理，在纤维上形成具有一定弹性、耐磨的透明树脂薄膜，将涂料机械的固着在纤维上的印花方法，这种高分子化合物叫粘合剂。涂料也称颜料是印花色浆中的发色体，主要分为有机颜料和无机颜料两大类，织物的涂料印花主要采用有机颜料，其耐热性能好，适应高温焙烘或汽蒸，色谱也较为齐全。
涂料直接印花在纤维上着色的原理与一般染料不同，它籍粘合剂将不溶性颜料颗粒固着在纺织品上。涂料印花工艺环保，无需水洗，对织物的限制小，工艺简单，拼色方便，色光易于调整和控制，印制的花型轮廓清晰、层次分明、富有立体感。现在还出现一些能够散发类似珍珠闪烁光芒的物质加入到印花色浆中，印制到织物上，经一定温度的烘干后，印花织物在光线的照耀下就可以发出珍珠般的光泽，点缀出光彩夺目的印花图案。但是目前的此类涂料色浆存在的问题主要就是印花后涂料的色牢度和摩擦、皂洗牢度还不够好。
发明内容
本发明为了克服现有的印花涂料耐洗性差的缺陷，本发明提供了一种珠光纺织物染液，耐洗性大大提高。
本发明的技术方案为：一种珠光纺织物染液，每升染液所含组分以克计组成为：
珠光涂料色浆 15～80，
脂肪醇聚氧乙烯醚磷酸单酯 5～25，
山梨醇酐月桂酸酯 10～35，
聚乙烯醇 10～35
硝化纤维素 10～20，
富马海松酸 4～30
水 30～100。
所述的珠光涂料色浆中含有珠光颜料，所述的珠光颜料为涂敷有金属、金属氧化物或其混合物涂层的天然云母片。
所述的天然云母片的厚度≤50ｎｍ，直径为0.25～0.5微米涂层的厚度为20～200ｎｍ。
所述的金属为金、铜、铝、铬、钛、钨中的任一。
所述的金属氧化物为三氧化二铝、氧化钛、三氧化二铁、氧化铁、三氧化二铬、氧化锌、氧化锗、氧化锆中的任意一种。
有益效果
1. 本发明的染液使得涂料有良好的耐摩擦性和耐搓洗牢固性。
2. 本发明的染液使得印花具有有良好的耐光、耐气候、耐热性。
3. 本发明不含有甲醛、重金属和有机锡等有害物质，环保、健康。
具体实施方式
下面对本发明进行进一步的说明。
一种珠光纺织物染液，每升染液所含组分以克计组成为：
珠光涂料色浆 15～80，
脂肪醇聚氧乙烯醚磷酸单酯 5～25，
山梨醇酐月桂酸酯 10～35，
聚乙烯醇 10～35
硝化纤维素 10～20，
富马海松酸 4～30
水 30～100。
所述的珠光涂料色浆中含有珠光颜料，所述的珠光颜料为涂敷有金属、金属氧化物或其混合物涂层的天然云母片，购自巴斯夫德国公司。
所述的天然云母片的厚度≤50ｎｍ，直径为0.25～0.5微米涂层的厚度为20～200ｎｍ。
所述的金属为金、铜、铝、铬、钛、钨中的任一。
所述的金属氧化物为三氧化二铝、氧化钛、三氧化二铁、氧化铁、三氧化二铬、氧化锌、氧化锗、氧化锆中的任意一种。
实施例1
一种珠光纺织物染液，每升染液所含组分以克计组成为：
珠光涂料色浆 80，
脂肪醇聚氧乙烯醚磷酸单酯 25，
山梨醇酐月桂酸酯 35，
聚乙烯醇 35
硝化纤维素 20，
富马海松酸 30
水 80。
所述的珠光涂料色浆中含有珠光颜料，所述的珠光颜料为涂敷有金属铬涂层的天然云母片。所述的天然云母片的厚度40ｎｍ，直径为0.25微米涂层的厚度为100ｎｍ。
实施例2
一种珠光纺织物染液，每升染液所含组分以克计组成为：
珠光涂料色浆 30，
脂肪醇聚氧乙烯醚磷酸单酯 15，
山梨醇酐月桂酸酯 15，
聚乙烯醇 15
硝化纤维素 12，
富马海松酸 10
水 50。
所述的珠光涂料色浆中含有珠光颜料，所述的珠光颜料为涂敷有氧化锆涂层的天然云母片。所述的天然云母片的厚度50ｎｍ，直径为0.5微米，涂层的厚度为20ｎｍ。
实施例3
一种珠光纺织物染液，每升染液所含组分以克计组成为：
珠光涂料色浆 15，
脂肪醇聚氧乙烯醚磷酸单酯 5，
山梨醇酐月桂酸酯 10，
聚乙烯醇 10
硝化纤维素 10，
富马海松酸 4
水 40。
所述的珠光涂料色浆中含有珠光颜料，所述的珠光颜料为涂敷有铬、氧化钛混合物涂层的天然云母片。
所述的天然云母片的厚度≤50ｎｍ，直径为0.25～0.5微米涂层的厚度为20～200ｎｍ。
实施例4
对实施例1~3的染液效果进行测试，采用浸轧染液，一浸一轧，轧余率60%，80℃烘干2min，110℃气蒸10min。
1. 耐光试验：热处理后用碳弧灯照20h，其中耐光度级别为0-8；
2. 耐热试验：180℃热风烘干30s，耐热级别为0-5；
3. 耐溶剂试验：热处理后加四氯乙烯，用40℃温水浸泡30min，耐溶剂级别为0-5，
4. 耐皂洗试验：热处理后加入碱粉，在70℃温水中水洗45min，耐皂洗级别为0-5；
表1性能测试结果
| 耐光试验 | 耐热试验 | 耐溶剂试验 | 耐皂洗试验 | |
| 实施例1 | 8 | 5 | 5 | 5 |
| 实施例2 | 7 | 4 | 4 | 4 |
| 实施例3 | 6 | 3 | 3 | 3 |
Claims (5)
1.一种珠光纺织物染液，其特征在于，每升染液所含组分以克计组成为：
珠光涂料色浆 15～80，
脂肪醇聚氧乙烯醚磷酸单酯 5～25，
山梨醇酐月桂酸酯 10～35，
聚乙烯醇 10～35
硝化纤维素 10～20，
富马海松酸 4～30
水 30～100。
2.如权利要求1所述的珠光纺织物染液，其特征在于，所述的珠光涂料色浆中含有珠光颜料，所述的珠光颜料为涂敷有金属、金属氧化物或其混合物涂层的天然云母片。
3.如权利要求2所述的珠光纺织物染液，其特征在于，所述的天然云母片的厚度≤50ｎｍ，直径为0.25～0.5微米涂层的厚度为20～200ｎｍ。
4.如权利要求2所述的珠光纺织物染液，其特征在于，所述的金属为金、铜、铝、铬、钛、钨中的任一。
5.如权利要求2所述的珠光纺织物染液，其特征在于，所述的金属氧化物为三氧化二铝、氧化钛、三氧化二铁、氧化铁、三氧化二铬、氧化锌、氧化锗、氧化锆中的任意一种。