CN102381881A - 硅溶胶结合的高铝碳化硅浇注料 - Google Patents

硅溶胶结合的高铝碳化硅浇注料 Download PDF

Info

Publication number
CN102381881A
CN102381881A CN2011102079508A CN201110207950A CN102381881A CN 102381881 A CN102381881 A CN 102381881A CN 2011102079508 A CN2011102079508 A CN 2011102079508A CN 201110207950 A CN201110207950 A CN 201110207950A CN 102381881 A CN102381881 A CN 102381881A
Authority
CN
China
Prior art keywords
granularity
casting material
silicon carbide
parts
silica sol
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2011102079508A
Other languages
English (en)
Inventor
王书明
张松善
钱长见
董寿勇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ZHENGZHOU JINGHUA REFRACTORY INDUSTRIAL Co Ltd
Original Assignee
ZHENGZHOU JINGHUA REFRACTORY INDUSTRIAL Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ZHENGZHOU JINGHUA REFRACTORY INDUSTRIAL Co Ltd filed Critical ZHENGZHOU JINGHUA REFRACTORY INDUSTRIAL Co Ltd
Priority to CN2011102079508A priority Critical patent/CN102381881A/zh
Publication of CN102381881A publication Critical patent/CN102381881A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种硅溶胶结合的高铝碳化硅浇注料，它是由以下重量份数的原料制成：粒度为8-0mm的铝矾土60-80、粒度为180-320目的碳化硅10-15、粒度为0.5μm以下的α-Al2O3微粉2-7、粒度为80-120目的蓝晶石2-5、粒度为160-200目的棕刚玉10-15、三聚磷酸钠2-5、硅溶胶5-10。本发明的有益效果是：硅溶胶化学活性大，容易烧结，中温烧结后，强度不下降，而且在1500℃的条件下，性能有很大提高，热震稳定性好，在1100℃的条件下水冷大于40次。

Description

硅溶胶结合的高铝碳化硅浇注料
技术领域
本发明涉及一种硅溶胶结合的高铝碳化硅浇注料。
背景技术
一般的耐火浇注料所用结合剂都是水泥，虽然常温强度大，施工容易，但是中温烧后强度下降多，而且高温下因为有钙离子的存在，严重影响浇注料的高温性能。
发明内容
本发明要解决的技术问题是耐火浇注料所用结合剂都是水泥，中温烧后强度下降多，提供一种高铝碳化硅浇注料。
本发明的技术方案是：一种硅溶胶结合的高铝碳化硅浇注料，它是由以下重量份数的原料制成：
粒度为8-0 mm的铝矾土               60-80
粒度为180-320目的碳化硅             10-15
粒度为0.5 μm以下的α-Al2O3微粉       2-7
粒度为80-120目的蓝晶石               2-5
粒度为160-200目的棕刚玉              10-15
三聚磷酸钠                            2-5
硅溶胶                                5-10。
所述的硅溶胶结合的高铝碳化硅浇注料，优选由以下重量份数的原料制成：
粒度为8-0 mm的铝矾土               65-70
粒度为180-320目的碳化硅             12-14
粒度为0.5 μm以下的α-Al2O3微粉           3-5
粒度为80-120目的蓝晶石              2-4
粒度为160-200目的棕刚玉             12-14
三聚磷酸钠                           2-4
硅溶胶                               6-9。
所述的硅溶胶结合的高铝碳化硅浇注料，最优由以下重量份数的原料制成：
粒度为8-0 mm的铝矾土               68
粒度为180-320目的碳化硅             13
粒度为0.5 μm以下的α-Al2O3微粉           4
粒度为80-120目的蓝晶石              3
粒度为160-200目的棕刚玉             13
三聚磷酸钠                           3
硅溶胶                               7。
本发明的有益效果是：硅溶胶化学活性大，容易烧结，中温烧结后，强度不下降，而且在1500℃的条件下，性能有很大提高，热震稳定性好，在1100 ℃的条件下水冷大于40次。
具体实施方式
实施例1
一种硅溶胶结合的高铝碳化硅浇注料，它是由以下原料制成：粒度为8-0 mm的铝矾土80 kg、粒度为180目的碳化硅15 kg、粒度为0.5 μm以下的α-Al2O3微粉7 kg、粒度为80目的蓝晶石5 kg、粒度为160目的棕刚玉15 kg、三聚磷酸钠5 kg、硅溶胶10 kg。
实施例2
一种硅溶胶结合的高铝碳化硅浇注料，它是由以下原料制成：粒度为8-0 mm的铝矾土60 kg、粒度为320目的碳化硅10 kg、粒度为0.5 μm以下的α-Al2O3微粉2 kg、粒度为120目的蓝晶石2 kg、粒度为200目的棕刚玉10 kg、三聚磷酸钠2 kg、硅溶胶5 kg。
实施例3
一种硅溶胶结合的高铝碳化硅浇注料，它由以下原料制成：粒度为8-0 mm的铝矾土70 kg、粒度为200目的碳化硅14 kg、粒度为0.5 μm以下的α-Al2O3微粉5 kg、粒度为100目的蓝晶石4 kg、粒度为180目的棕刚玉14 kg、三聚磷酸钠4 kg、硅溶胶9 kg。
实施例4
一种硅溶胶结合的高铝碳化硅浇注料，它由以下原料制成：粒度为8-0 mm的铝矾土65 kg、粒度为240目的碳化硅12 kg、粒度为0.5 μm以下的α-Al2O3微粉3 kg、粒度为120目的蓝晶石2 kg、粒度为200目的棕刚玉12 kg、三聚磷酸钠2 kg、硅溶胶6 kg。
实施例5
一种硅溶胶结合的高铝碳化硅浇注料，它由以下原料制成：粒度为8-0 mm的铝矾土68 kg、粒度为180-320目的碳化硅13 kg、粒度为0.5 μm以下的α-Al2O3微粉4 kg、粒度为80-120目的蓝晶石3 kg、粒度为160-200目的棕刚玉13 kg、三聚磷酸钠3 kg、硅溶胶7 kg。

Claims (3)

1. 一种硅溶胶结合的高铝碳化硅浇注料，其特征在于，它是由以下重量份数的原料制成：
粒度为8-0 mm的铝矾土               60-80
粒度为180-320目的碳化硅             10-15
粒度为0.5 μm以下的α-Al2O3微粉       2-7
粒度为80-120目的蓝晶石               2-5
粒度为160-200目的棕刚玉              10-15
三聚磷酸钠                            2-5
硅溶胶                                5-10。
2. 根据权利要求1所述的硅溶胶结合的高铝碳化硅浇注料，其特征在于，它是由以下重量份数的原料制成：
粒度为8-0 mm的铝矾土               65-70
粒度为180-320目的碳化硅             12-14
粒度为0.5 μm以下的α-Al2O3微粉           3-5
粒度为80-120目的蓝晶石              2-4
粒度为160-200目的棕刚玉             12-14
三聚磷酸钠                           2-4
硅溶胶                               6-9。
3. 根据权利要求2所述的硅溶胶结合的高铝碳化硅浇注料，其特征在于，它是由以下重量份数的原料制成：
粒度为8-0 mm的铝矾土               68
粒度为180-320目的碳化硅             13
粒度为0.5 μm以下的α-Al2O3微粉           4
粒度为80-120目的蓝晶石              3
粒度为160-200目的棕刚玉             13
三聚磷酸钠                           3
硅溶胶                               7。
CN2011102079508A 2011-07-25 2011-07-25 硅溶胶结合的高铝碳化硅浇注料 Pending CN102381881A (zh)