CN102336040A - 双组份双层复合阻尼材料 - Google Patents

双组份双层复合阻尼材料 Download PDF

Info

Publication number
CN102336040A
CN102336040A CN2010102356648A CN201010235664A CN102336040A CN 102336040 A CN102336040 A CN 102336040A CN 2010102356648 A CN2010102356648 A CN 2010102356648A CN 201010235664 A CN201010235664 A CN 201010235664A CN 102336040 A CN102336040 A CN 102336040A
Authority
CN
China
Prior art keywords
double
component
material layer
layer
damping
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2010102356648A
Other languages
English (en)
Other versions
CN102336040B (zh
Inventor
叶海宁
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201010235664.8A priority Critical patent/CN102336040B/zh
Publication of CN102336040A publication Critical patent/CN102336040A/zh
Application granted granted Critical
Publication of CN102336040B publication Critical patent/CN102336040B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明双组份双层复合阻尼材料，第一层材料与第二层材料呈片状叠合，第一层材料原料配比为(按重量比)：溴化丁基橡胶(BIIR)28-32％、碳酸钙(CaCO3)58-62％、促进剂(DM)1％、氧化锌1％、防老剂(D)1％、硬脂酸锌1％、碳黑3％、硫磺3％，第二层材料原料配比为(按重量比)：三元乙丙橡胶(EPDM)28-32％、碳酸钙(CaCO3)58-62％、促进剂(DM)1％，防老剂(D)1％，硬脂酸锌1％，硫磺4％，色粉1％，环烷油2％。本发明主要用于机械设备中的高精密仪器降噪减振、高速铁路高弹性减振垫板、高速机车内降噪减振、舰船多种振源的抑制降噪。对比其它同类型产品，本发明具有中低频降噪性能突出，产品轻质、阻尼温域宽、降噪频段宽、耐老化等特点。

Description

双组份双层复合阻尼材料
技术领域
本发明涉及一种阻尼材料，特别是一种采用高分子材料制造的双组份双层复合阻尼材料。
背景技术
目前，市场上公知的声波阻尼材料都为采用高分子材料制造的单组份单层复合阻尼材料，声波传播只能在同一密度的媒质中产生反射，不能有效错开同一媒质的吻合谷效应，声波能量衰减效果不很理想。
发明内容
本发明的目的是提供一种采用高分子材料制造的双组份双层复合阻尼材料。
本发明解决其技术问题所采用的技术方案是：采用高分子材料(BIIR和EPDM)制造的双组份双层复合阻尼材料构成，第一层材料与第二层材料呈片状叠合，声波传入第一种第一层阻尼材料(BIIR)后，声波的能量由机械振动能转变成为热能而使振动衰减，随即进入第二种第二层阻尼材料(EPDM)，由于声波传播过程中遇到不同密度的材料发生了反射(即减少透射)，机械振动能第二次转变成为热能，因而采用双组份双层复合阻尼材料隔声量会在不同密度的媒质中产生反射，同时能有效错开同一媒质的吻合谷效应，声波能量衰减效果好。
本发明双组份双层复合阻尼材料生产工艺流程为：
1、按原料配方(见表一)分别将第一层材料溴化丁基橡胶(BIIR)及碳酸钙(CaCO3)等辅料、第二层材料三元乙丙橡胶(EPDM)及碳酸钙(CaCO3)等辅料分开称重、混合。丁基橡胶(BIIR)和三元乙丙橡胶(EPDM)为基材，碳酸钙(CaCO3)为填料，促进剂(DM)、氧化锌、硬脂酸锌、环烷油为增速剂，硫磺为硫化剂。
表一原料配方(按重量比)
  第一层材料   配比   第二层材料   配比
  溴化丁基橡胶(BIIR)   28-32   三元乙丙橡胶(EPDM)   28-32
  碳酸钙(CaCO3)   58-62   碳酸钙   58-62
  促进剂(DM)   1   促进剂(DM)   1
  氧化锌   1   防老剂(D)   1
  防老剂(D)   1   硬脂酸锌   1
  硬脂酸锌   1   硫磺   4
  碳黑   3   色粉   1
  硫磺   3   环烷油   2
2、分别将两种配料置入密炼机中在90-110摄氏度下进行密炼。
3、将上述两种密炼后配料在双辊炼胶机上分别混炼出片，混炼温度为100-120摄氏度。
4、将两种配料的片材叠放置入平板硫化机中，进行温度为150-160摄氏度、时间为20分钟硫化，制成各种厚度的双组份双层复合阻尼材料。
本发明主要用于机械设备中的高精密仪器降噪减振、高速铁路高弹性减振垫板、高速机车内降噪减振、舰船多种振源的抑制降噪。对比其它同类型产品，本发明具有中低频降噪性能突出，产品轻质、阻尼温域宽、降噪频段宽、耐老化等特点。
下面结合实施例对本发明进行进一步说明。
具体实施方式
本发明双组份双层复合阻尼材料的一种制造实施例为：
1、按原料配方(见表二)分别将第一层材料溴化丁基橡胶(BIIR)及碳酸钙(CaCO3)等辅料、第二层材料三元乙丙橡胶(EPDM)及碳酸钙(CaCO3)等辅料分开称重、混合。
表二实施例原料配方(按重量比)
  第一层材料   配比   第二层材料   配比
  溴化丁基橡胶(BIIR)   30   三元乙丙橡胶(EPDM)   30
  碳酸钙(CaCO3)   60   碳酸钙   60
  促进剂(DM)   1   促进剂(DM)   1
  氧化锌   1   防老剂(D)   1
  防老剂(D)   1   硬脂酸锌   1
  硬脂酸锌   1   硫磺   4
  碳黑   3   色粉   1
  硫磺   3   环烷油   2
2、分别将两种配料置入密炼机中在100摄氏度下进行密炼。
3、将上述两种密炼后配料在双辊炼胶机上分别混炼出片，混炼温度为120摄氏度。
4、将两种配料的片材叠放置入平板硫化机中，进行温度为150摄氏度、时间为20分钟硫化，既制成各种厚度的双组份双层复合阻尼材料。

Claims (1)

1.一种双组份双层复合阻尼材料，其特征是采用高分子材料(BIIR和EPDM)制造的双组份双层复合阻尼材料构成，第一层材料与第二层材料呈片状叠合，第一层材料原料配比为(按重量比)：溴化丁基橡胶(BIIR)28-32％、碳酸钙(CaCO3)58-62％、促进剂(DM)1％、氧化锌1％、防老剂(D)1％、硬脂酸锌1％、碳黑3％、硫磺3％，第二层材料原料配比为(按重量比)：三元乙丙橡胶(EPDM)28-32％、碳酸钙(CaCO3)58-62％、促进剂(DM)1％，防老剂(D)1％，硬脂酸锌1％，硫磺4％，色粉1％，环烷油2％。
CN201010235664.8A 2010-07-23 2010-07-23 双组份双层复合阻尼材料 Active CN102336040B (zh)