CN102329573B - 一种不干胶生产配方及其制备方法 - Google Patents
一种不干胶生产配方及其制备方法 Download PDFInfo
- Publication number
- CN102329573B CN102329573B CN 201110140565 CN201110140565A CN102329573B CN 102329573 B CN102329573 B CN 102329573B CN 201110140565 CN201110140565 CN 201110140565 CN 201110140565 A CN201110140565 A CN 201110140565A CN 102329573 B CN102329573 B CN 102329573B
- Authority
- CN
- China
- Prior art keywords
- setting adhesive
- reactor
- resin
- acetic monomer
- vinyl acetic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种不干胶生产配方及其制备方法，该不干胶是由甲基丙烯酸乙酯、丙烯酸丁酯、丙烯酸羟丙酯、丙烯酸羟乙酯、醋酸乙烯酯、SBS树脂、溴化聚苯乙烯树脂、过氧化苯甲酰、醋酸乙酯所组成。不干胶生产时，控制反应釜搅拌浆的搅拌速度为80γ/min，升温速率为2℃/min，当反应釜釜温达到90℃时，将溶解有SBS树脂的醋酸乙酯溶液和溶解有溴化聚苯乙烯树脂的醋酸乙酯溶液加入反应釜中，继续恒温反应30～50Min后即制得成品。该方法生产的不干胶具有耐水好、持粘性能好、不易变色、残留气味小、耐老化以及阻燃和生产成本低的特点。
Description
技术领域
本发明属化工技术领域，涉及一种不干胶生产配方及其制备方法。
背景技术
目前，市场上的不干胶存在着持粘性差、易变色发黄、产品中残留气味较大和产品不阻燃以及产品生产成本高等缺陷。
发明内容
本发明的目的是提供一种生产制造成本低、持粘性能好、不易变色、阻燃性能好、残留气味小的不干胶的生产配方及其制备方法。
为了达到上述目的，本发明的一种不干胶生产配方是由甲基丙烯酸乙酯、丙烯酸丁酯、丙烯酸羟丙酯、丙烯酸羟乙酯、醋酸乙烯酯、SBS树脂、溴化聚苯乙烯树脂、过氧化苯甲酰、醋酸乙酯所组成，其配方组成的重量百分比为：甲基丙烯酸乙酯1%～3%、丙烯酸丁酯5%～10% 、丙烯酸羟丙酯 1%～3% 、丙烯酸羟乙酯 1%～3%、醋酸乙烯酯 2%～5%、SBS树脂 2%～6％，溴化聚苯乙烯树脂2%～10%、过氧化苯甲酰0.01～0.02%、醋酸乙酯70%～85%，配方中各组成含量之和为100%。
本发明的具体实施方式是：
用占总量五分之一的醋酸乙酯溶解过氧化苯甲酰，将其配制成溶解有过氧化苯甲酰的醋酸乙酯溶液，用占总量五分之一的醋酸乙酯溶解SBS树脂将其配制成溶解有SBS树脂的醋酸乙酯溶液，用占总量五分之一的醋酸乙酯溶解溴化聚苯乙烯树脂，将其配制成溶解有溴化聚苯乙烯树脂的醋酸乙酯溶液，将余下的醋酸乙酯全部加入反应釜中，将甲基丙烯酸乙酯、醋酸乙烯酯、丙烯酸羟丙酯、丙烯酸羟乙酯全部加入反应釜中，将占总量五分之一的丙烯酸丁酯加入反应釜中，将占总量十分之一的溶有过氧化苯甲酰的醋酸乙酯溶液加入反应釜中，开启反应釜的搅拌浆，控制搅拌速度为80γ/min，开启反应釜的电加热开关，缓慢将反应釜的温度升至85℃，控制升温速率为2℃/min，恒温反应30～50min后将占总量十分之九的溶有过氧化苯甲酰的醋酸乙酯溶液和剩余下来的丙烯酸丁酯溶液同时缓慢向反应釜中滴加,控制丙烯酸丁酯的滴加量与反应釜液体的回流量相近，滴加结束后，继续恒温搅拌30Min,然后将温度缓慢升至90℃，控制升温速率为0.2℃/min，当反应釜釜温达到90℃时，将溶解有SBS树脂的醋酸乙酯溶液和溶解有溴化聚苯乙烯树脂的醋酸乙酯溶液加入反应釜中，继续恒温反应30～50Min，然后将反应釜的温度降至室温时出料。
本发明的有益效果是，该方法生产的不干胶具有耐水、持粘性能好、不易变色、残留气味小、耐老化以及阻燃和生产成本低的特点。
实施例1
不干胶生产配方的重量百分比组成为：甲基丙烯酸乙酯2%、丙烯酸丁酯10% 、丙烯酸羟丙酯 2% 、丙烯酸羟乙酯 2%、醋酸乙烯酯 3.99%、SBS树脂 3％，溴化聚苯乙烯树脂3%、过氧化苯甲酰0.01%、醋酸乙酯75%。
用占总量五分之一的醋酸乙酯溶解过氧化苯甲酰，将其配制成溶解有过氧化苯甲酰的醋酸乙酯溶液，用占总量五分之一的醋酸乙酯溶解SBS树脂将其配制成溶解有SBS树脂的醋酸乙酯溶液，用占总量五分之一的醋酸乙酯溶解溴化聚苯乙烯树脂，将其配制成溶解有溴化聚苯乙烯树脂的醋酸乙酯溶液，将余下的醋酸乙酯全部加入反应釜中，将甲基丙烯酸乙酯、醋酸乙烯酯、丙烯酸羟丙酯、丙烯酸羟乙酯全部加入反应釜中，将五分之一的丙烯酸丁酯加入反应釜中，将占总量十分之一的溶有过氧化苯甲酰的醋酸乙酯溶液加入反应釜中，开启反应釜的搅拌浆，控制搅拌速度为80γ/min，开启反应釜的电加热开关，缓慢将反应釜的温度升至85℃，控制升温速率为2℃/min，恒温反应30min后将占总量十分之九的溶有过氧化苯甲酰的醋酸乙酯溶液和剩余下来的丙烯酸丁酯溶液同时缓慢向反应釜中滴加,控制丙烯酸丁酯的滴加量与反应釜液体的回流量相近，滴加结束后，继续恒温搅拌30Min,然后将温度缓慢升至90℃，控制升温速率为0.2℃/min，当反应釜釜温达到90℃时，将溶解有SBS树脂的醋酸乙酯溶液和溶解有溴化聚苯乙烯树脂的醋酸乙酯溶液加入反应釜中，继续恒温反应30Min，然后将反应釜的温度降至室温出料。
Claims (3)
1.一种不干胶，其特征在于它是由甲基丙烯酸乙酯、丙烯酸丁酯、丙烯酸羟丙酯、丙烯酸羟乙酯、醋酸乙烯酯、SBS树脂、溴化聚苯乙烯树脂、过氧化苯甲酰、醋酸乙酯所组成，其配方组成的重量百分比为：甲基丙烯酸乙酯1%～3%、丙烯酸丁酯5%～10% 、丙烯酸羟丙酯 1%～3% 、丙烯酸羟乙酯 1%～3%、醋酸乙烯酯 2%～5%、SBS树脂 2%～6％，溴化聚苯乙烯树脂2%～10%、过氧化苯甲酰0.01～0.02%、醋酸乙酯70%～85%，配方中各组分含量之和为100%。
2.根据权利要求1所述的一种不干胶，其特征是，不干胶合成反应过程中反应釜搅拌浆的搅拌速度为80r/min，反应釜的升温速率为2℃/min。
3.根据权利要求1所述的一种不干胶，其特征是，不干胶合成反应过程中，当反应釜釜温达到90℃时，将溶解有SBS树脂的醋酸乙酯溶液和溶解有溴化聚苯乙烯树脂的醋酸乙酯溶液加入反应釜中。