CN102329541A - 导电涂料 - Google Patents
导电涂料 Download PDFInfo
- Publication number
- CN102329541A CN102329541A CN201110211455A CN201110211455A CN102329541A CN 102329541 A CN102329541 A CN 102329541A CN 201110211455 A CN201110211455 A CN 201110211455A CN 201110211455 A CN201110211455 A CN 201110211455A CN 102329541 A CN102329541 A CN 102329541A
- Authority
- CN
- China
- Prior art keywords
- parts
- ethanol
- copper powder
- conductive coating
- electrically conducting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种导电涂料,包括以质量份计的以下组分:聚丙烯酸树脂溶液10-30份、铜粉 20-30、镍粉10-15、纳米级高岭土1-5、二氧化硅1-5、三聚磷酸钠1-5、乙醇50-70。将聚丙烯酸树脂基料和乙醇加入反应器中混合均匀,加入铜粉、镍粉、高岭土、二氧化硅混合均匀后,加入三聚磷酸钠,球磨机中研磨两次,即可。本发明获得的导电涂料对织物具有良好的附着力,且具有良好的电磁屏蔽率。
Description
技术领域
本发明涉及导电涂料,属于纺织化学领域。
背景技术
在电子等技术领域,要求织物具有一定的导电性,以避免静电的危害,一般是采用在织物表层涂覆导电涂料,使之具有一定的传导电流和消散静电荷能力的功能性涂料,从而达到防静电和屏蔽电磁波的目的。
发明内容
本发明所要解决的技术问题是提供一种织物用导电涂料。
为解决上述技术问题,本发明是这样实现的
导电涂料,包括以质量份计的以下组分:
聚丙烯酸树脂溶液 10-30份
铜粉 20-30
镍粉 10-15
纳米级高岭土 1-5
二氧化硅 1-5
三聚磷酸钠 1-5
乙醇 50-70
制备方法如下:
将聚丙烯酸树脂基料和乙醇加入反应器中混合均匀,加入铜粉、镍粉、高岭土、二氧化硅 混合均匀后,加入三聚磷酸钠,球磨机中研磨两次,即可。
本发明的导电涂料中各组分的作用如下:
聚丙烯酸树脂溶液在导电涂料中起骨架作用,使制备的导电涂料具有成膜性、附着性和耐久性,且对导电填料具有亲和性和润湿性。
铜粉和镍粉是金属系填料,镍粉性能稳定,价格适中,铜粉具有良好的导电性,但抗氧化性较差,为了防止铜粉的氧化以及保持稳定的导电性能,采用抗氧化剂对铜粉进行表面处理,二氧化硅是抗氧化剂。 高岭土主要成分是氧化铝,属于金属氧化物填料,为纳米级的颗粒,提高了涂料的导电性,导电填料的用量对导电性有很大影响,太少,则涂料无法形成连续的网络,影响导电性,太多会使涂料的强度降低。三聚磷酸钠能够保证涂料与天然纤维类织物具有良好的附和性。
制备过程中,研磨的次数对导电性能有影响,时间过程,涂料胶凝。
本发明获得的导电涂料对织物具有良好的附着力,且具有良好的电磁屏蔽率。
具体实施方式
下面结合具体实施方式对本发明做进一步的详细说明。
实施例1-4导电涂料所采用的组分如表1所示(单位kg)
表1
实施例1 | 实施例2 | 实施例3 | 实施例4 | |
聚丙烯酸树脂 | 10.2 | 15.2 | 19.5 | 29.8 |
铜粉 | 20.5 | 26.7 | 29.8 | 21.6 |
镍粉 | 10.3 | 14.9 | 12.5 | 11.9 |
高岭土 | 1.2(200nm) | 3.5(500nm) | 4.9(400nm) | 2.7(700nm) |
二氧化硅 | 1.3 | 2.6 | 4.8 | 3.6 |
三聚磷酸钠 | 1.4 | 3.6 | 4.5 | 2.9 |
乙醇 | 50.3 | 69.8 | 61.7 | 55.8 |
制备方法如下:
将聚丙烯酸树脂基料和乙醇加入反应器中混合均匀,加入铜粉、镍粉、高岭土、二氧化硅 混合均匀后,加入三聚磷酸钠,球磨机中研磨两次,即可。
实施例1制备的导电涂料,附着力(0级)100/100,表干时间(50-55℃)10min,体积电阻率 3×10-3Ω·cm,表面电阻率0.1Ω/cm2。
上述具体实施方式不以任何形式限制本发明的技术方案,凡是采用等同替换或等效变换的方式所获得的技术方案均落在本发明的保护范围。
Claims (2)
1.导电涂料,其特征在于包括以质量份计的以下组分:
聚丙烯酸树脂溶液 10-30份
铜粉 20-30
镍粉 10-15
纳米级高岭土 1-5
二氧化硅 1-5
三聚磷酸钠 1-5
乙醇 50-70。
2.基于权利要求1所述的导电涂料的制备方法,其特征在于包括如下的步骤:将聚丙烯酸树脂基料和乙醇加入反应器中混合均匀,加入铜粉、镍粉、高岭土、二氧化硅 混合均匀后,加入三聚磷酸钠,球磨机中研磨两次,即可。