CN102312260A - 铜铝合金的混合酸硬质阳极氧化交直流叠加法 - Google Patents
铜铝合金的混合酸硬质阳极氧化交直流叠加法 Download PDFInfo
- Publication number
- CN102312260A CN102312260A CN201110240264A CN201110240264A CN102312260A CN 102312260 A CN102312260 A CN 102312260A CN 201110240264 A CN201110240264 A CN 201110240264A CN 201110240264 A CN201110240264 A CN 201110240264A CN 102312260 A CN102312260 A CN 102312260A
- Authority
- CN
- China
- Prior art keywords
- acid
- hard anodizing
- anodic oxidation
- cleaning
- copper
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
铜铝合金的混合酸硬质阳极氧化交直流叠加法，铝制件经化学除油、清洗、中和、清洗、硬质阳极氧化、清洗、封闭后得到膜层，其中硬质阳极氧化步骤的电解液包含以下组分：硫酸5-15g/L、苹果酸 20-40g/L、磺基水杨酸50-100g/L、柠檬酸10-20g/L、枸橼酸1-10g/L；硬质阳极氧化步骤的的工艺参数是：温度15-30℃，阳极电流密度5-10A/dm2 ，时间：30-50min。本发明能在铝材表面形成均匀的蓝黑色膜，厚度为50-60微米，硬度HV>300，适用于含铜5%以下的各种牌号铝合金。
Description
技术领域
本发明涉及一种铜铝合金的混合酸硬质阳极氧化交直流叠加法，属于铝合金的表面处理工艺。
背景技术
铝及其合金经过硬质阳极氧化后，能获得外观呈褐色、深褐色、灰色到黑色的厚膜层，硬度高，耐磨性能好，膜层距哟大量的微小孔隙可吸附各种润滑剂，进而提高减摩能力。而且膜层的抗热、绝缘、耐蚀、结合力均良好。获得硬质阳极氧化膜的溶液，有硫酸、多种有机酸的混合溶液，所用的电源，有直流电、交流电、交直流叠加以及各种脉冲电流。常用的类型是硫酸硬质阳极氧化直流法和混合酸硬质阳极氧化交直流叠加法。
发明内容
本发明所要解决的技术问题是提供一种铜铝合金的混合酸硬质阳极氧化交直流叠加法，获得高硬度的厚膜层。
为解决上述技术问题，本发明是这样实现的
铜铝合金的混合酸硬质阳极氧化交直流叠加法，铝制件经化学除油、清洗、中和、清洗、硬质阳极氧化、清洗、封闭后得到膜层，其中硬质阳极氧化步骤的电解液包含以下组分：硫酸 5-15g/L、苹果酸 20-40g/L、磺基水杨酸50-100g/L、柠檬酸 10-20g/L、枸橼酸 1-10g/L；
硬质阳极氧化步骤的的工艺参数是：温度 15-30℃，阳极电流密度 5-10A/dm2，时间：30-50min。
本发明有以下积极的效果：本发明能在铝材表面形成均匀的蓝黑色、褐色、棕色的膜层，厚度为50-60微米，硬度HV>300，适用于含铜5%以下的各种牌号铝合金。
具体实施方式
下面结合具体实施方式对本发明做进一步的详细说明。
实施例1 采用含铜量为4%的形变铝做试件
铜铝合金的混合酸硬质阳极氧化交直流叠加法，铝制件经化学除油、清洗、中和、清洗、硬质阳极氧化、清洗、封闭后得到膜层，其中硬质阳极氧化步骤的电解液包含以下组分：硫酸 5g/L、苹果酸 20g/L、磺基水杨酸50g/L、柠檬酸 10g/L、枸橼酸 2g/L；
硬质阳极氧化步骤的的工艺参数是：温度 15℃，阳极电流密度 5A/dm2，时间：30min。铝材表面形成均匀的蓝黑色膜，厚度为50微米，硬度HV>350。
实施例2 采用含铜量为1.6%的形变铝做试件
铜铝合金的混合酸硬质阳极氧化交直流叠加法，铝制件经化学除油、清洗、中和、清洗、硬质阳极氧化、清洗、封闭后得到膜层，其中硬质阳极氧化步骤的电解液包含以下组分：硫酸 5g/L、苹果酸 20g/L、磺基水杨酸50g/L、柠檬酸 10g/L、枸橼酸 2g/L；
硬质阳极氧化步骤的的工艺参数是：温度 20℃，阳极电流密度 6A/dm2，时间：40min。铝材表面形成均匀的蓝黑色膜，厚度为40微米，硬度HV>420。
实施例3 采用含铜量为3.2%的铸铝做试件
铜铝合金的混合酸硬质阳极氧化交直流叠加法，铝制件经化学除油、清洗、中和、清洗、硬质阳极氧化、清洗、封闭后得到膜层，其中硬质阳极氧化步骤的电解液包含以下组分：硫酸 5g/L、苹果酸 20g/L、磺基水杨酸50g/L、柠檬酸 10g/L、枸橼酸 2g/L；
硬质阳极氧化步骤的的工艺参数是：温度 30℃，阳极电流密度 10A/dm2，时间：50min。铝材表面形成均匀的蓝黑色膜，厚度为50微米，硬度HV>650。
实施例4 采用含铜量为2.8%的铸铝做试件
铜铝合金的混合酸硬质阳极氧化交直流叠加法，铝制件经化学除油、清洗、中和、清洗、硬质阳极氧化、清洗、封闭后得到膜层，其中硬质阳极氧化步骤的电解液包含以下组分：硫酸 5g/L、苹果酸 20g/L、磺基水杨酸50g/L、柠檬酸 10g/L、枸橼酸 2g/L；
硬质阳极氧化步骤的的工艺参数是：温度 25℃，阳极电流密度 8A/dm2，时间：50min。铝材表面形成均匀的蓝黑色膜，厚度为48微米，硬度HV>680。
上述具体实施方式不以任何形式限制本发明的技术方案，凡是采用等同替换或等效变换的方式所获得的技术方案均落在本发明的保护范围。
Claims (1)
1.铜铝合金的混合酸硬质阳极氧化交直流叠加法，铝制件经化学除油、清洗、中和、清洗、硬质阳极氧化、清洗、封闭后得到膜层，其特征在于硬质阳极氧化步骤的电解液包含以下组分：硫酸 5-15g/L、苹果酸 20-40g/L、磺基水杨酸50-100g/L、柠檬酸 10-20g/L、枸橼酸 1-10g/L；
硬质阳极氧化步骤的的工艺参数是：温度 15-30℃，阳极电流密度 5-10A/dm2，时间：30-50min。