CN102268156A - 一种高密度聚乙烯材料 - Google Patents
一种高密度聚乙烯材料 Download PDFInfo
- Publication number
- CN102268156A CN102268156A CN 201110210741 CN201110210741A CN102268156A CN 102268156 A CN102268156 A CN 102268156A CN 201110210741 CN201110210741 CN 201110210741 CN 201110210741 A CN201110210741 A CN 201110210741A CN 102268156 A CN102268156 A CN 102268156A
- Authority
- CN
- China
- Prior art keywords
- density polyethylene
- hdpe
- eva
- raw material
- polyethylene material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供一种应用于输液针护帽的高密度聚乙烯材料,其特征在于通过简单物理改性得到的,其组成为:高密度聚乙烯:100份,改性剂:EVA5-15份,抗氧剂:1010:0.1-0.3份。此改性HDPE粒料,具有抗环境应力好,韧性好,流动性好。
Description
技术领域
本发明涉及高密度聚乙烯(HDPE)改性领域,具体涉及一种应用于输液针护帽的高密度聚乙烯材料。
背景技术
输液针护帽,一般采用HDPE挤出成型,但是在生产和使用过程中常出出现开裂现象,给生产厂家,医院造成损失的同时也给病人带来一定的医疗隐患。针对此种情况,本发明通过EVA对HDPE改性,使其具备抗应力开裂的性能。
发明内容
为了达到上述目的,本发明使用HDPE通过改性,即通过乙烯-醋酸乙烯酯共聚物(EVA)为改性剂,制备HDPE和EVA共混物,以提高聚乙烯的抗环境应力开裂能力,解决输液针护冒开裂现象。
本发明采取的具体技术方案是:一种高密度聚乙烯材料,该聚乙烯材料按重量份配比计由以下原料制成:聚乙烯100份,改性剂5-15份,抗氧剂1010:0.1-0.3份,前述聚乙烯为5000S的高密度聚乙烯,上述改性剂为EVA,且在EVA中,VA(醋酸乙烯脂)所占的重量百分比为14%。
一种高密度聚乙烯材料的方法,该方法包括由以下步骤组成:
(1)按照上述配方量将各原料加入到高混锅,搅拌30分钟,使各原料充分分散得混合料;
(2)将步骤(1)所得混合料使用平行双螺杆挤出机,水冷抽条切粒,85℃干燥3小时后即得高密度聚乙烯材料。
本发明的有益效果在于:EVA弹性体的加入增强了共混物的韧性,提高了扯断伸长率及共混物熔体的流动性,VA的质量分数为14%较好提高PE的耐开裂性能,但随着EVA用量增大,共混物溶体粘度对剪切速率的敏感性增强,因此按重量份配比计,当聚乙烯用量为100份时,EVA的用量不应超过15份;通过改性,使得普通的HDPE材料的环境应力开裂时间从40小时增加到大于400小时,明显提高了HDPE的耐应力开裂性能,值得推广。
具体实施方式
实施例1
称取5000S的高密度聚乙烯100kg、EVA(VA所占的重量百分比为14%)5kg,抗氧剂1010为0.1kg,将上述称取好的各原料加入到高混锅里,搅拌30分钟,使各原料充分分散得混合料;然后再将混合料使用平行双螺杆挤出机,水冷抽条切粒,85℃干燥3小时后即得高密度聚乙烯材料。
实施例2
称取5000S的高密度聚乙烯100kg、EVA(VA所占的重量百分比为14%)10kg,抗氧剂1010为0.2kg,将上述称取好的各原料加入到高混锅里,搅拌30分钟,使各原料充分分散得混合料;然后再将混合料使用平行双螺杆挤出机,水冷抽条切粒,85℃干燥3小时后即得高密度聚乙烯材料。
实施例3
称取5000S的高密度聚乙烯100kg、EVA(VA所占的重量百分比为14%)15kg,抗氧剂1010为0.3kg,将上述称取好的各成原料加入到高混锅里,搅拌30分钟,使各原料充分分散得混合料;然后再将混合料使用平行双螺杆挤出机,水冷抽条切粒,85℃干燥3小时后即得高密度聚乙烯材料。
将本发明制得的材料与普通HDPE做了相应的试验对比,得出以下数据(见表1)
表1本发明材料性能与HDPE材料性能测试数据对比表
测试项目 | 拉伸强度(Mpa) | 环境应力开裂(小时) | 断裂伸长率 |
普通HDPE | 35 | 40 | 750 |
本发明材料 | 大于25 | 大于400 | 大于600 |
Claims (4)
1.一种高密度聚乙烯材料,其特征在于:该聚乙烯材料按重量份配比计由以下原料制成:
聚乙烯:100份
改性剂:5-15份
抗氧剂1010:0.1-0.3份。
2.根据权利要求1所述的高密度聚乙烯材料,其特征在于所述聚乙烯为5000S的高密度聚乙烯。
3.根据权利要求1所述的高密度聚乙烯材料,其特征在于所述改性剂为EVA,且在EVA中,VA所占的重量百分比为14%。
4.制备如权利要求1所述的高密度聚乙烯材料的方法,其特征在于该方法包括由以下步骤组成:
(1)按照上述配方量将各原料加入到高混锅,搅拌30分钟,使各原料充分分散得混合料;
(2)将步骤(1)所得混合料使用平行双螺杆挤出机,水冷抽条切粒,85℃干燥3小时后即得高密度聚乙烯材料。