CN102241840A - 一种高耐磨矿用橡胶筛网的胶料 - Google Patents
一种高耐磨矿用橡胶筛网的胶料 Download PDFInfo
- Publication number
- CN102241840A CN102241840A CN2010101698775A CN201010169877A CN102241840A CN 102241840 A CN102241840 A CN 102241840A CN 2010101698775 A CN2010101698775 A CN 2010101698775A CN 201010169877 A CN201010169877 A CN 201010169877A CN 102241840 A CN102241840 A CN 102241840A
- Authority
- CN
- China
- Prior art keywords
- rubber
- screen mesh
- mining
- rubber material
- sizing material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了一种高耐磨矿用橡胶筛网的胶料，其原料包括天然橡胶、顺丁橡胶、氧化锌、硬脂酸、防老剂4010NA、防老剂D、炭黑N220、芳烃油、促进剂CZ、硫磺。本发明胶料主要用于矿用橡胶筛网，采用天然橡胶与顺丁橡胶等量并用，使其耐磨性更佳，特别适用于二道矿石或细矿的筛选。
Description
【技术领域】
本发明涉及一种选矿设备，尤其涉及一种高耐磨选矿用的橡胶筛网胶料。
【背景技术】
随着选矿工业的发展和选矿技术的提高，造成高品质的矿产已被大量开采，导致可选矿的品质越来越低。为了提高产量，选矿量必然增加，很多选矿厂选择加大头筛矿石尺寸，甚至不用破碎直接进行筛选的方法来提高产量，这样势必导致对筛网胶料要求越来越高，应更具耐磨性、耐切割性、耐刺轧性、耐老化性，以及能更好地抗崩花掉块，也就是应具有更高的强度和弹性，因天然橡胶的耐穿刺性好，目前筛网的配方，较适用于粗矿的筛选，不太适用于二道矿石或细矿的筛选，这是由于细矿筛选和粗矿筛选对橡胶磨耗的方式有所区别，细矿筛选对橡胶磨耗比较细微。
【发明内容】
本发明要解决的技术问题，在于提供一种高耐磨矿用橡胶筛网的胶料，采用天然橡胶与顺丁橡胶等量并用，使其耐磨性更佳，特别适用于二道矿石或细矿的筛选。
本发明是这样实现的：一种高耐磨矿用橡胶筛网的胶料，其特征在于：所述胶料由下述原料按重量比配制而成：
天然橡胶 50.0；
顺丁橡胶 50.0；
氧化锌 4.0；
硬脂酸 2.0；
防老剂4010NA 1.5；
防老剂D 1.0；
炭黑N220 65.0；
芳烃油 6.0；
促进剂CZ 1.0；
硫磺 1.8。
本发明具有如下优点：采用天然橡胶与顺丁橡胶等量并用，并加入综合性能最好的化工材料中，可明显提高矿用橡胶筛网胶料的耐磨性，特别适用于二道矿石或细矿的筛选。
【具体实施方式】
一、原料准备：将下述原料按重量比称量：
天然橡胶 50.0；
顺丁橡胶 50.0；
氧化锌 4.0；
硬脂酸 2.0；
防老剂4010NA 1.5；
防老剂D 1.0；
炭黑N220 65.0；
芳烃油 6.0；
促进剂CZ 1.0；
硫磺 1.8。
二、将上述称量好的原料采取下述工艺进行混炼：
1、小配合试验胶料
将原料放在XK-160开炼机上进行混炼，加料顺序为：
天然橡胶和顺丁橡胶-氧化锌-硬脂酸-防老剂4010NA和防老剂D-炭黑N220-芳烃油-促进剂CZ-硫磺。
2、生产胶料工艺
将原料放在XN-55捏炼机上进行混炼，并采用二段混炼法，包括一段混炼和二段混炼。
所述一段混炼加料顺序为：
天然橡胶和顺丁橡胶-氧化锌-硬脂酸和三分之二的炭黑N220-芳烃油；
混炼后进行排胶，排胶温度控制在120±10℃，之后再出片，所述一段混炼结束。
所述二段混炼加料顺序为：一段母胶-防老剂4010NA、防老剂D、促进剂CZ、剩余三分之一的炭黑N220；
混炼后进行排胶，排胶温度控制在100±10℃，排胶之后再加硫磺出片，所述二段混炼结束。
三、性能测试数据表
使用本发明配方(针对生产胶料工艺)与普通配方(针对小配合试验胶料)分别制成的胶料的性能测试所得的数据如下表所示：
由上表可见，使用本发明配方制成的胶料比现有技术中普通配方制成的胶料可明显提高耐磨性能。
采用本实施例配方与普通配方分别生产了筛孔8×20的筛网在矿山选矿设备(圆盘振动筛选机)上使用，使用结果对比如下。
| 项目 | 本实施例配方 | 普通配方 |
| 平均选矿量 | 100万吨以上 | 60万吨 |
Claims (1)
1.一种高耐磨矿用橡胶筛网的胶料，其特征在于：所述胶料由下述原料按重量比配制而成：
天然橡胶 50.0；
顺丁橡胶 50.0；
氧化锌 4.0；
硬脂酸 2.0；
防老剂4010NA 1.5；
防老剂D 1.0；
炭黑N220 65.0；
芳烃油 6.0；
促进剂CZ 1.0；
硫磺 1.8。