CN102226056A - 一种快速室温表干的双组份导电涂料 - Google Patents
一种快速室温表干的双组份导电涂料 Download PDFInfo
- Publication number
- CN102226056A CN102226056A CN2011101635253A CN201110163525A CN102226056A CN 102226056 A CN102226056 A CN 102226056A CN 2011101635253 A CN2011101635253 A CN 2011101635253A CN 201110163525 A CN201110163525 A CN 201110163525A CN 102226056 A CN102226056 A CN 102226056A
- Authority
- CN
- China
- Prior art keywords
- component
- surface drying
- electrically conducting
- temperature surface
- room temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开的快速室温表干的双组份导电涂料,由甲、乙两种组份配制而成,两种组份按质量百分数含量的组成分别为,甲组份:热固性树脂25%-54%,导电填料34%-64%,表干助剂3.5%-15%,助剂1%-2%。乙组份:固化剂100%。使用时,将甲、乙两种组份按质量比3~6.5∶1配制混合均匀即可。本发明的室温表干双组份导电涂料不仅有较高的导电性能和耐磨性,而且形成的涂层能于室温6min内表干,使用方便,便于连续生产。且可通过调节涂料组成满足不同场合电性能的要求。
Description
技术领域
本发明涉及一种能快速室温表干的双组份导电涂料,属于化工高分子涂料领域。
背景技术
导电涂层具有传导电流和消除累积静电荷的作用。导电涂料在电磁波屏蔽,油罐内壁除静电,高压电缆外电极,电子元件等领域有着广泛地应用。目前大多数的导电涂料为填充型导电涂料,由成膜剂、导电填料、稀释剂及其它助剂所组成。其中成膜剂又多为热固性树脂与固化剂,通过固化反应成膜。
发明内容
本发明的目的在于提供一种有较长适用期,所制备涂层又能于室温6min内快速表干的双组份导电涂料。
本发明的快速室温表干的双组份导电涂料,由甲、乙两种组份按质量比3~6.5∶1配制而成,甲、乙两种组份按质量百分数含量的组成分别如下:
甲组份:
热固性树脂 25%-54%
导电填料 34%-64%
表干助剂 3.5%-15%
助剂 1%-2%,
乙组份:
固化剂 100%。
本发明中,所说的热固性树脂为环氧树脂。所说的导电填料可以为石墨、炭黑和铜粉中的一种或多种的混合物。
本发明中,所说的表干助剂为一种羧基丁腈橡胶。所说的助剂为γ-氨丙基三乙氧基硅烷。
本发明中,所说的固化剂为胺类固化剂,选自聚酰胺、酚醛改性胺和二乙烯三胺中的一种或几种混合物。
本发明双组份导电涂料中的甲、乙组份的制备方法如下:将环氧树脂和表干助剂溶于适量丙酮中,加入导电填料及助剂,混合均匀,即得甲组份,待用。将固化剂用适量丙酮稀释,即得乙组份,待用。使用时,将甲、乙两种组份按质量比3~6.5∶1配制混合均匀即可。
本发明的室温表干双组份导电涂料不仅有较高的导电性能和耐磨性,而且形成的涂层能于室温6min内表干,使用方便,便于连续生产。且可通过调节涂料组成满足不同场合电性能的要求。
具体实施方式
实施例1:
本实施例中,原料及质量百分数含量为:
甲组份:
环氧树脂E44 32%
石墨 62%
羧基丁腈橡胶 5.5%
γ-氨丙基三乙氧基硅烷 0.5%
乙组份:
聚酰胺 650 65%
二乙烯三胺 35%
快速室温表干双组份导电涂料由甲、乙组份配制而成,甲、乙组份质量比为3.2∶1。
导电涂料制备过程和步骤如下:
(1)将上述原料配方中规定质量的环氧树脂E44、羧基丁腈橡胶溶于适量丙酮稀释剂中。随后加入导电填料石墨和γ-氨丙基三乙氧基硅烷,混合均匀,即得甲组份,待用;
(2)在上述规定质量的乙组分中加入适量丙酮稀释剂,稀释均匀,即得乙组份;
(3)将步骤(1)、(2)所得甲、乙组份按质量比3.2∶1比例混合均匀,得到快速室温表干导电涂料。
性能测试:将制得的导电涂料涂刮在聚氯乙烯板材上,室温固化成膜。用万用表测得表面电阻系数为680Ω。根据GB/T 1720测得涂层与基板附着力为2-3级。根据GB/T 1728测得涂层室温表干时间为4-5 min。
实施例2:
本实施例中,原料及质量百分数含量为:
甲组份:
环氧树脂E44 37%
石墨 42%
炭黑 13%
铜粉 3%
羧基丁腈橡胶 4.5%
γ-氨丙基三乙氧基硅烷 0.5%
乙组份:
酚醛改性胺T31 65%
二乙烯三胺 35%
快速室温表干双组份导电涂料由甲、乙组份配制而成,甲、乙组份质量比为4.3∶1。
导电涂料制备过程和步骤如下:
(1)将上述原料配方中规定质量的环氧树脂E44和羧基丁腈橡胶溶于适量丙酮稀释剂中。随后加入导电填料石墨、炭黑、铜粉和γ-氨丙基三乙氧基硅烷,搅拌均匀,即得导电涂料甲组份,待用;
(2)在上述规定质量的乙组分中加入适量丙酮稀释剂,稀释均匀,即得乙组份;
(3)将步骤(1)、(2)所得甲、乙组份按质量比4.3∶1比例混合均匀,得到快速室温表干导电涂料。
性能测试:将制得的导电涂料涂刮在聚氯乙烯板材上,室温固化成膜。用万用表测得表面电阻系数740Ω。根据GB/T 1720测得涂层与基板附着力为2-3级。根据GB/T 1728测得涂层室温表干时间为4-5 min。
实施例3:
本实施例中,原料及质量百分数含量为:
甲组份:
环氧树脂E51 56%
炭黑 38%
羧基丁腈橡胶 5.5%
γ-氨丙基三乙氧基硅烷 0.5%
乙组份:
酚醛改性胺T31 65%
二乙烯三胺 35%
快速室温表干双组份导电涂料由甲、乙组份配制而成,甲、乙组份质量比为6.4∶1。
导电涂料制备过程和步骤如下:
(1)将上述原料配方中规定质量的环氧树脂E51,羧基丁腈橡胶溶于适量丙酮稀释剂中。随后加入导电填料炭黑和γ-氨丙基三乙氧基硅烷,混合均匀,即得甲组份,待用;
(2)在上述规定质量的乙组分中加入适量丙酮稀释剂,稀释均匀,即得乙组份;
(3)将步骤(1)、(2)所得甲、乙组份按质量比6.4∶1比例混合均匀,得到快速室温表干导电涂料。
性能测试:将制得的导电涂料涂刮在聚氯乙烯板材上,室温固化成膜。用万用表测得表面电阻系数为2000Ω。根据GB/T 1720测得涂层与基板附着力为3级。根据GB/T 1728测得涂层室温表干时间为4-5min。
Claims (6)
1.一种快速室温表干的双组份导电涂料,其特征在于由甲、乙两种组份按质量比3~6.5∶1配制而成,甲、乙两种组份按质量百分数含量的组成分别如下:
甲组份:
热固性树脂 25%-54%
导电填料 34%-64%
表干助剂 3.5%-15%
助剂 1%-2%,
乙组份:
固化剂 100%。
2.根据权利要求1所述的快速室温表干的双组份导电涂料,其特征在于所说的热固性树脂为环氧树脂。
3.根据权利要求1所述的快速室温表干的双组份导电涂料,其特征在于所说的导电填料为石墨、炭黑和铜粉中的一种或多种的混合物。
4.根据权利要求1所述的快速室温表干的双组份导电涂料,其特征在于所说的表干助剂为一种羧基丁腈橡胶。
5.根据权利要求1所述的快速室温表干的双组份导电涂料,其特征在于所说的助剂为γ-氨丙基三乙氧基硅烷。
6.根据权利要求1所述的快速室温表干的双组份导电涂料,其特征在于所说的固化剂为聚酰胺、酚醛改性胺和二乙烯三胺中的一种或几种混合物。