CN102225780B - 一种高活性氧化钙及其生产方法 - Google Patents

一种高活性氧化钙及其生产方法 Download PDF

Info

Publication number
CN102225780B
CN102225780B CN 201110097391 CN201110097391A CN102225780B CN 102225780 B CN102225780 B CN 102225780B CN 201110097391 CN201110097391 CN 201110097391 CN 201110097391 A CN201110097391 A CN 201110097391A CN 102225780 B CN102225780 B CN 102225780B
Authority
CN
China
Prior art keywords
calcium oxide
carbide slag
production method
weight percent
calcium
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN 201110097391
Other languages
English (en)
Other versions
CN102225780A (zh
Inventor
吴秋华
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SHANGHAI PENGPU METALLURGICAL AUXILIARY MATERIAL CO Ltd
Original Assignee
SHANGHAI PENGPU METALLURGICAL AUXILIARY MATERIAL CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SHANGHAI PENGPU METALLURGICAL AUXILIARY MATERIAL CO Ltd filed Critical SHANGHAI PENGPU METALLURGICAL AUXILIARY MATERIAL CO Ltd
Priority to CN 201110097391 priority Critical patent/CN102225780B/zh
Publication of CN102225780A publication Critical patent/CN102225780A/zh
Application granted granted Critical
Publication of CN102225780B publication Critical patent/CN102225780B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及冶金炼钢领域，主要用于电炉、转炉炼钢及铁水预处理复合脱硫剂和铁水预处理复合脱磷剂的原料生产，具体涉及一种高活性氧化钙及其生产方法，该方法在原料电石渣（氢氧化钙）中加入氯化钠煅烧，所述高活性氧化钙中的各成份所占重量百分比为：CaO占90-96%、SiO2占1-4%、Na2O占0.1-1%、S占<0.05%、P占<0.05%。本发明的优点是，原料电石渣属于电石分解甲烷后的副产品，为资源综合利用产品，通过加入适量的氯化钠，使成品中的氧化钙活性度大幅提高。

Description

一种高活性氧化钙及其生产方法
技术领域
本发明涉及冶金炼钢领域，主要涉及用于电炉、转炉炼钢及铁水预处理复合脱硫剂和铁水预处理复合脱磷剂的原料生产。
背景技术
  氧化钙是电炉、转炉炼钢及铁水预处理复合脱硫剂和铁水复合脱磷剂的主要原料。目前现有技术中的氧化钙是采用碳酸钙煅烧而成，其成份的重量比分别是：CaO占85-95%、SiO2占1-3%， S占0.05%、P占0.05%。氧化钙的活性度一般最多仅在300-380ml。
发明内容
本发明的目的是根据上述现有技术的不足之处，提供一种高活性氧化钙及其生产方法，该方法在原料电石渣（氢氧化钙）中加入氯化钠煅烧，生产的氧化钙活性度与现有技术的氧化钙相比提高30％以上。
本发明目的实现由以下技术方案完成：
一种高活性氧化钙，其特征在于所述高活性氧化钙中的各成份所占重量百分比为：CaO占90-96%、 SiO2 占1-4%、Na2O占0.1-1%、S占<0.05%、P占<0.05%。
所述的CaO所占的重量百分比大于95%，介于95%-96％之间，包括96%。
所述的CaO的活性度不小于400ml。
一种高活性氧化钙的生产方法，其特征在于先将一定量的电石渣中加入适量氯化钠混合均匀，其中氯化钠占电石渣的重量百分比为0.1％-1％，之后压制成球，然后经烘干，使球的含水率在3％以下，再经煅烧后，即得成品。
所述电石渣的组成中的氢氧化钙所占重量百分比不小于97％。
所述电石渣的组成中的二氧化硅所占重量百分比不大于3％。
本发明的优点是，原料电石渣属于电石分解甲烷后的副产品，为资源综合利用产品，通过加入适量的氯化钠，使成品中的氧化钙活性度大幅提高。
具体实施方式
以下通过实施例对本发明特征及其它相关特征作进一步详细说明，以便于同行业技术人员的理解：
本发明涉及的电石渣属于电石分解甲烷后的副产品，其各组成所占的重量百分比是氢氧化钙>97％，二氧化硅<3％，以及其他杂质。
制备方法：
先将电石渣（氢氧化钙）加入重量百分比为0.1-1％的氯化钠混合均匀，压制成40×40×50mm的球，然后经105-160℃烘干，使球水份控制在3％以下，再经700-800℃煅烧3-5小时，即为成品。
实施例1：电石渣含水量20％。
配比：
电石渣120％、氯化钠0.12％混合搅拌均匀，压成40×40×50mm的球，经120℃烘干4小时，水份小于3％，700℃煅烧3小时。
成品检验结果见下表：
CaO SiO2 Na2O S P 活性度
93.60％ 3.90％ 0.06％ 0.043％ 0.036％ 400ml
实施例2：电石渣含水量10％。
配比：
电石渣110％、氯化钠0.4％混合搅拌均匀，压成40×40×50mm的球，经120℃烘干4小时，水份小于3％，800℃煅烧3小时。
成品检验结果见下表：
CaO SiO2 Na2O S P 活性度
94.02％ 3.60％ 0.32％ 0.05％ 0.042％ 420ml
实施例3：电石渣含水量18％。
配比：
电石渣118％、氯化钠1.18％混合搅拌均匀，压成40×40×50mm的球，经120℃烘干4小时，水份小于3％，800℃煅烧3小时。
成品检验结果见下表：
CaO SiO2 Na2O S P 活性度
95.14％ 2.89％ 0.56％ 0.031％ 0.044％ 440ml

Claims (4)

1.一种高活性氧化钙，其特征在于所述高活性氧化钙中各成份所占重量百分比为： CaO所占的重量百分比大于95%，介于95%-96％之间，包括96%、 SiO2 占1-4%、Na2O占0.1-1%、S占<0.05%、P占<0.05%，所述的CaO的活性度不小于400mL。
2.一种如权利要求1所述的高活性氧化钙的生产方法，其特征在于先将一定量的电石渣中加入适量氯化钠混合均匀，其中氯化钠占电石渣的重量百分比为0.1％-1％，之后压制成球，然后经烘干，使球的含水率在3％以下，再经煅烧后，即得成品。
3.根据权利要求2所述的一种高活性氧化钙的生产方法，其特征在于所述电石渣的组成中的氢氧化钙所占重量百分比不小于97％。
4.根据权利要求2所述的一种高活性氧化钙的生产方法，其特征在于所述电石渣的组成中的二氧化硅所占重量百分比不大于3％。
CN 201110097391 2011-04-19 2011-04-19 一种高活性氧化钙及其生产方法 Active CN102225780B (zh)