CN102205681A - 防风透湿保暖复合衬布及其生产方法 - Google Patents
防风透湿保暖复合衬布及其生产方法 Download PDFInfo
- Publication number
- CN102205681A CN102205681A CN2011100670616A CN201110067061A CN102205681A CN 102205681 A CN102205681 A CN 102205681A CN 2011100670616 A CN2011100670616 A CN 2011100670616A CN 201110067061 A CN201110067061 A CN 201110067061A CN 102205681 A CN102205681 A CN 102205681A
- Authority
- CN
- China
- Prior art keywords
- rete
- lining fabric
- lining cloth
- composite lining
- polyurethane
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种防风透湿保暖复合衬布及其生产方法,产品包括衬布本体,衬布本体通过胶层与聚氨酯膜层或聚四氟乙烯膜层或热塑性聚氨酯弹性体膜层复合。本发明产品结构合理,具有优良的防风保暖透湿性,同时保留了原有衬布“轻、薄、软、挺、弹”性能,延伸和拓宽衬布的应用范围,提高了服装的服用性能和档次。主要作为服装加强和防风保暖,通过粘合也能做成复合面料,广泛应用于服装行业中集美观防风透湿保暖于一体。
Description
技术领域
本发明涉及一种复合衬布及其生产方法。
背景技术
随着人们生活水平的提高,人们对服装的美观、防风、保暖性和透湿性的多重要求日益增强。目前的衬布仅起到承托面料,改善服装面料的性能,赋予服装“轻、薄、软、挺、弹”的性能。休闲,运动,户外活动已成为当今最时尚的话题,为了展现个性特征和健康的需求,休闲装,运动装,户外服,越来越受到人们的亲睐。
为了迎合当今的服装市场的需求,发明出一种防风透湿保暖复合衬布尤为重要。
发明内容
本发明的目的在于提供一种结构合理,透湿、保暖的防风透湿保暖复合衬布及其生产方法。
本发明的技术解决方案是:
一种防风透湿保暖复合衬布,其特征是:包括衬布本体,衬布本体通过胶层与聚氨酯膜层或聚四氟乙烯膜层或热塑性聚氨酯弹性体膜层复合;所述胶层是点涂层;所述胶是醇溶性聚氨酯粘合剂,胶的制备方法为:将5份端异氰酸酯基聚氨酯树脂、1份改性环氧树脂、搅拌均匀后加入催化剂2,4,6,—三(二甲氨基甲基)苯酚,在70~100℃下固化,再向聚氨酯粘合剂中加入5~10份的乙醇溶液(质量浓度30%~95%)。
聚氨酯膜层或聚四氟乙烯膜层或热塑性聚氨酯弹性体膜层的厚度为10~25μm。
一种防风透湿保暖复合衬布的生产方法,其特征是:包括下列步骤:
将5份端异氰酸酯基聚氨酯树脂、1份改性环氧树脂、搅拌均匀后加入催化剂2,4,6,—三(二甲氨基甲基)苯酚,在70~100℃下固化,再向聚氨酯粘合剂中加入5~10份的乙醇溶液,得到醇溶性聚氨酯粘合剂,存放于密闭容器中待用;控制粘合温度在50℃~90℃,将粘合剂通过雕刻辊以点状转移至聚氨酯膜层或聚四氟乙烯膜层或热塑性聚氨酯弹性体膜层上,再将衬布复合在粘合剂上。
本发明产品结构合理,具有优良的防风保暖透湿性,同时保留了原有衬布“轻、薄、软、挺、弹”性能,延伸和拓宽衬布的应用范围,提高了服装的服用性能和档次。主要作为服装加强和防风保暖,通过粘合也能做成复合面料,广泛应用于服装行业中集美观防风透湿保暖于一体。
使用的聚四氟乙烯膜 (英文名称Poly tetra fluoro ethylene,简称PTFE)属于合成膜中具有选择性透过的渗透膜。PTFE膜由高结晶的大分子组成,它以PTFE树脂为原料,通过延伸、热处理立体络合成具有无数微细孔隙的膜。孔隙率高达80%以上,孔径连接呈蜘蛛网状,最大孔径为0.5μm(一般在0.2μm到0.5μm之间),水滴的大小(水滴的直径在20μm~1000μm之间)是该孔径的5000~20000倍,而水蒸气分子(水蒸气分子直径为0.0004μm)只是其孔径的1/700。PTFE具有良好的防风、透气及透湿性功能外,又具有极好的双向弹性、弹性恢复性、防污性和耐水洗性等。
使用的PU,TPU膜TPU是热塑型聚氨酯薄膜的简称,我们选择有孔和无孔亲水性薄膜。由于薄膜本身没有孔隙,防水效果自然很好,同时也还使面料防风保暖。透湿主要通过其的亲水特性来实现,依靠衣服内外蒸汽压的差异,将蒸汽从压力高的地方转移到低的地方,从而实现了透湿的功能。有孔的PU膜能达到可呼吸性能,透气性比较好。
使用的粘合剂为醇溶性聚氨酯粘合剂,该粘合剂属于双组份溶剂型粘合剂。使用时按一定比例配制,搅拌均匀后,两组分混合后发生交联反应而固化。为了调整聚氨酯粘合剂的粘度便于操作,通过乙醇和水进行稀释,粘合剂通过雕刻辊顺利转移至薄膜上且具有饱满的点状。使用合成法生产的乙醇作为稀释剂可以优化工作环境;降低操作人员的被害程度;减少溶剂残留;常温熟化,省去熟化室的土建和加热能源费用;溶剂成本费用较使用醋酸乙酯具有更强的价格优势。
通过衬布与功能性PU.TPU.PTFE膜的复合能够满足人们对服装美观、防风、保暖和透湿的多重要求,提高服装的服用性能和服装的质量档次。
经ASTM E 96-2005试验方法检测,产品透湿性为4.58-9.28g/m2·24h。
下面结合附图和实施例对本发明作进一步说明。
图1是本发明产品的结构示意图。
具体实施方式
将5重量份端异氰酸酯基聚氨酯树脂、1重量份改性环氧树脂、搅拌均匀后加入催化剂2,4,6,—三(二甲氨基甲基)苯酚,在70~100℃下固化,再向聚氨酯粘合剂中加入5~10重量份(例5、8、10份)质量浓度30%~95%(例30%、60%、95%)的乙醇溶液,得到醇溶性聚氨酯粘合剂,存放于密闭容器中待用;控制粘合温度在50℃~90℃,将粘合剂2通过雕刻辊以点状转移至聚氨酯膜层或聚四氟乙烯膜层或热塑性聚氨酯弹性体膜层1上,再将衬布3复合在粘合剂2上,得产品。聚氨酯膜层或聚四氟乙烯膜层或热塑性聚氨酯弹性体膜层的厚度为10~25μm。
Claims (3)
1.一种防风透湿保暖复合衬布,其特征是:包括衬布本体,衬布本体通过胶层与聚氨酯膜层或聚四氟乙烯膜层或热塑性聚氨酯弹性体膜层复合;所述胶层是点涂层;所述胶是醇溶性聚氨酯粘合剂,胶的制备方法为:将5份端异氰酸酯基聚氨酯树脂、1份改性环氧树脂、搅拌均匀后加入催化剂2,4,6,—三(二甲氨基甲基)苯酚,在70~100℃下固化,再向聚氨酯粘合剂中加入5~10份的乙醇溶液。
2.根据权利要求1或2所述的防风透湿复合衬布,其特征是:聚氨酯膜层或聚四氟乙烯膜层或热塑性聚氨酯弹性体膜层的厚度为10~25μm。
3.一种权利要求1所述的防风透湿保暖复合衬布的生产方法,其特征是:包括下列步骤:
将5份端异氰酸酯基聚氨酯树脂、1份改性环氧树脂、搅拌均匀后加入催化剂2,4,6,—三(二甲氨基甲基)苯酚,在70~100℃下固化,再向聚氨酯粘合剂中加入5~10份的乙醇溶液,得到醇溶性聚氨酯粘合剂,存放于密闭容器中待用;控制粘合温度在50℃~90℃,将粘合剂通过雕刻辊以点状转移至聚氨酯膜层或聚四氟乙烯膜层或热塑性聚氨酯弹性体膜层上,再将衬布复合在粘合剂上。