CN102190500A - Golden sculpture method for wine bottle - Google Patents
Golden sculpture method for wine bottle Download PDFInfo
- Publication number
- CN102190500A CN102190500A CN2011100297372A CN201110029737A CN102190500A CN 102190500 A CN102190500 A CN 102190500A CN 2011100297372 A CN2011100297372 A CN 2011100297372A CN 201110029737 A CN201110029737 A CN 201110029737A CN 102190500 A CN102190500 A CN 102190500A
- Authority
- CN
- China
- Prior art keywords
- ceramic body
- glaze
- carcass
- golden
- gold
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a golden sculpture method for a wine bottle. The method successively comprises the following steps: providing an original sculpture pattern, making a production mould with gypsum, and grouting so as to form a ceramic body; washing the surface of the ceramic body with a soft brush; sintering the ceramic body at the temperature of 700-1000 DEG C for the first time for removing water steam and organic impurities out of the ceramic body so as to increase the surface strength of the ceramic body; coating glaze on partial patterns on the surface of the ceramic body, and then sintering the ceramic body at the temperature of 1250-1350 DEG C for the second time; and after brushing gold on the surface of the ceramic body, sintering the ceramic body at the temperature of 700-820 DEG C for the third time to complete the manufacturing of the golden sculpture pattern. In the golden sculpture method for the wine bottle, glaze coating is used for replacing traditional glaze spraying, gold coating is used for replacing traditional gold spraying, and finally the golden sculpture pattern with diverse color levels, and no defects of foaming, decoloring and crazing can be obtained by carrying multiple sintering processes and controlling sintering temperature.
Description
Technical field
The present invention relates to a kind of faience manufacture method, relate in particular to a kind of true golden eagle molding process that is used for bottle.
Background technology
Pottery is according to dissimilar, different performance requirement, and the different shapes of product, size and thickness etc., and manufacture method is also different, but passes through following technological process substantially:
1. idiosome pre-burning; 2, transfer the colouring of colored glaze or transparent; 3, idiosome surface finish; 4, step such as sinter molding, seeing also application number is 201010280934.7, denomination of invention is the patent documentation of " method of making cloisonne patterns on ceramic matrix ".
The pottery that aforesaid method is made is white basically, in order to form color on pottery, can add ceramic toner in pug, execute transparent glaze firing again after the biscuiting, make the multicolored entire body porcelain, the toner amount that this method is used is big, cost significantly improves, and can only realize monochrome decoration.
In order to form polychrome colored glaze pattern, two kinds of methods are arranged generally now: a kind of in porcelainization but also do not add coloured silk on the idiosome of glazing, this method is simple to operate, but because product moulding, pattern comes off easily, and the pattern level of decorating out in addition is abundant inadequately, and stereoscopic sensation is poor; Another kind method is directly to add coloured silk on idiosome, and this method is difficult to be grasped, and will carry out high temperature behind the coloured silk and burns till owing to add, and easily bubbles, decolours, ftractures after the burning of colored glaze district.
Further form the metal carving pattern on pottery, degree-of-difficulty factor is bigger.Because the differences in materials, particularly coefficient of expansion difference in metal pattern area and colored glaze district.If burn till excessively, easily bubble, decolour, ftracture after the burning of colored glaze district; If burn till deficiency, then the metal pattern hill height is not enough, and stereoscopic sensation is poor, metal pattern low in glossiness, metal pattern burnt hair.In addition,, then can absorb metallic pigment, not only influence glossiness, and waste raw material, increase cost if the ceramic surface slickness is not enough.Therefore must improve above-mentioned technology and just may on ceramic matrix, make true golden eagle and mould pattern.
Summary of the invention
Technical problem to be solved by this invention provides a kind of true golden eagle molding process that is used for bottle, and the formation gradation enriches true golden eagle and moulds pattern, and can not bubble, decolour, ftracture.
The present invention solves the problems of the technologies described above the technical scheme that adopts to provide a kind of true golden eagle molding process that is used for bottle, in turn includes the following steps: the original shape depiction is provided, makes production mould with gypsum, grouting forms ceramic matrix; Clean the carcass surface with banister bruss; Above-mentioned carcass is carried out burning till the first time under 700～1000 ℃, remove aqueous vapor and organic impurities in the carcass, increase the carcass surface strength; After the part pattern on above-mentioned carcass surface retouched glaze, under 1250～1350 ℃, carry out burning till the second time; Behind the brush gold to above-mentioned carcass surface, under 700～820 ℃, burn till for the third time, finish true golden eagle and mould design producing.
The above-mentioned true golden eagle molding process that is used for bottle, wherein, when the carcass picture on surface was retouched glaze, the interpolation weight percent was 20%～50% glycerine in glaze.
The above-mentioned true golden eagle molding process that is used for bottle wherein, adopts very gold of 18K or 24K during to carcass surface brush gold.
The present invention contrasts prior art following beneficial effect: the true golden eagle molding process that is used for bottle provided by the invention, replace existing glaze spraying by retouching glaze, replace existing metal spraying by painting in gold, by repeatedly burning till and control firing temperature, the formation gradation enriches true golden eagle and moulds pattern, and can not bubble, decolour, ftracture.
Description of drawings
Fig. 1 is used for the true golden eagle molding process process flow sheet of bottle for the present invention.
Embodiment
The invention will be further described below in conjunction with drawings and Examples.
Fig. 1 is used for the true golden eagle molding process process flow sheet of bottle for the present invention.
See also Fig. 1, the true golden eagle molding process that is used for bottle provided by the invention in turn includes the following steps:
Step S1: the original shape depiction is provided, makes production mould with gypsum, grouting forms ceramic matrix, enters step S2;
Step S2: clean the carcass surface with banister bruss, as the banister bruss of selecting the T5 model for use enters step S3 to avoid destroying the lines on the idiosome;
Step S3: above-mentioned carcass is carried out burning till the first time under 700～1000 ℃, remove aqueous vapor and organic impurities in the carcass, increase the carcass surface strength, enter step S4;
Step S4: the part pattern to above-mentioned carcass surface is retouched glaze, adds weight percent and is 20%～50% glycerine lubricate in glaze and be convenient to glazing, carries out burning till the second time under 1250～1350 ℃, enters step S5;
Step S5: behind the brush gold to above-mentioned carcass surface, adopt very gold of 18K or 24K, under 700～820 ℃, burn till for the third time, finish true golden eagle and mould design producing.
Though the present invention discloses as above with preferred embodiment; right its is not in order to qualification the present invention, any those skilled in the art, without departing from the spirit and scope of the present invention; when can doing a little modification and perfect, so protection scope of the present invention is when with being as the criterion that claims were defined.
Claims (3)
1. true golden eagle molding process that is used for bottle is characterized in that described method in turn includes the following steps:
The original shape depiction is provided, makes production mould with gypsum, grouting forms ceramic matrix;
Clean the carcass surface with banister bruss;
Above-mentioned carcass is carried out burning till the first time under 700～1000 ℃, remove aqueous vapor and organic impurities in the carcass, increase the carcass surface strength;
After the part pattern on above-mentioned carcass surface retouched glaze, under 1250～1350 ℃, carry out burning till the second time;
Behind the brush gold to above-mentioned carcass surface, under 700～820 ℃, burn till for the third time, finish true golden eagle and mould design producing.
2. the true golden eagle molding process that is used for bottle as claimed in claim 1 is characterized in that, when the carcass picture on surface was retouched glaze, the interpolation weight percent was 20%～50% glycerine in glaze.
3. the true golden eagle molding process that is used for bottle as claimed in claim 1 is characterized in that, adopts very gold of 18K or 24K during to carcass surface brush gold.