CN102166798B - 脱模剂及其在复合材料模制品生产中的用途 - Google Patents
脱模剂及其在复合材料模制品生产中的用途 Download PDFInfo
- Publication number
- CN102166798B CN102166798B CN201010588517.9A CN201010588517A CN102166798B CN 102166798 B CN102166798 B CN 102166798B CN 201010588517 A CN201010588517 A CN 201010588517A CN 102166798 B CN102166798 B CN 102166798B
- Authority
- CN
- China
- Prior art keywords
- composition
- group
- component
- formula
- alkali metal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明涉及一种脱模剂组合物,其包含以下组分:a)至少一种磷酸盐或磷酸酯,和b)至少一种具有至少两个羟基且分子量小于250g/mol的化合物。基于所述组合物,组分a)的比例为0.1-70重量%,且组分b)的比例为0.5-90重量%。本发明还涉及一种其中使用了该脱模剂组合物生产复合材料模制品的方法,也涉及通过相应方法获得的复合材料模制品及其用途。
Description
技术领域
本发明涉及一种脱模剂及其在复合材料模制品生产中的用途:在开放或封闭的模具中,使任选改性的有机粘结剂与碎片、纤维、垫席或颗粒形态的材料特别是含纤维素的材料(例如,木材、亚麻或稻草)反应,所述脱模剂包含至少一种式I的磷酸盐或磷酸酯和醇。
背景技术
已经有众多专利和文献出版物(WO 98/00464,US 5,008,359,US5,140,086,US 5,204,176,US 3,440,189)公开了在开放或封闭的模具中,任选存在或不存在催化剂、助剂和/或添加剂下,由木材片、纤维或颗粒与异氰酸酯粘结剂生产称为″复合材料″的挤压形状的制品,例如OSB(定向刨花板)、刨花板、纤维板如MDF或HDF板(中密度或高密度纤维板)或胶合板,以及软木板和含有亚麻、稻草的模塑物或其他含纤维素的材料。
在这些方法中,为了确保粘结剂反应以及使材料成型以得到期望的最终形状(例如厚木板或薄板),根据粘结剂的不同,需要20-450℃的温度。在此过程中,压力可达到1-100bar。
基于模制品的总重量,粘结剂的质量比为1-80重量%,优选5-40重量%,特别是小于20重量%,这取决于使用的粘结剂种类和复合材料种类。
使用的粘结剂可以是任意一种多官能化的异氰酸酯,典型地是芳香族聚异氰酸酯。最广泛使用的芳香族聚异氰酸酯是聚合的二苯甲烷二异氰酸酯(PMDI)。除了异氰酸酯之外,各种各样的甲醛树脂也可用作复合材料模制品中的粘结剂。最常用的包括尿素/甲醛、苯酚/甲醛或三聚氰胺/甲醛树脂以及它们的混合物。也可以少量使用含有可再生原料例如丹宁酸、木质素或蛋白质的粘结剂。此外,可以使用铸塑树脂,例如环氧化物、聚酯、聚氨基甲酸酯或聚乳酸树脂。
虽然压缩的纤维素/异氰酸酯模制品的生产具有相当重要的工业价值,但所描述的方法仍有一些技术上的缺陷,例如由于聚氨基甲酸酯与其他材料突出的粘合力。特别不利的是模制品附着于模具上并因此难于从模具上移去,这经常导致破坏模制品,特别是其表面。为了避该缺点,通常使用抛光的、金属模具并使用脱模剂。
这些脱模剂在可固化的纤维素-异氰酸酯的混合物中作为内润滑剂,或者在生产所述模制品之前为内模具表面提供具有外润滑剂的均匀涂层,为了此目的,现有技术中有各种已知的注射法和喷射法以及辊涂法(DE-10 337594)。待模制的颗粒的表面也可以涂有脱模剂。这同样也受喷涂的影响。
传统的内润滑剂或外润滑剂是,例如,脂肪酸及其金属盐(WO-A-03/072324,WO-A-2/36268)、聚合的脂肪酸(EP-A-0 269 869)、羧基官能化的硅氧烷(EP-B-0 129 430)、蜡(EP-B-0 046 014)、特别是酯蜡(EP-B-0057 502)、氧化石蜡(WO-A-00/53381)或聚烯烃蜡(WO-A-98/00464)、聚烯烃蜡与脂肪酸的组合(WO-A-01/58998)或最后地脂肪酸或蜡酸与聚硅氧烷的组合,其用有机键合的活性氢基团改性并且能够与异氰酸酯反应(WO-A-03/008164)。
这些传统的脱模剂具有以下缺点:最终的模制品表面上具有黑斑点,这大大削弱其光学价值。此外,压模经常显示出堆积的黑色残余物。
这些堆积的残余物还可以在所生产的模制品上再累积,用这种方法还会导致其表面结构上有黑斑点和/或凹凸,特别是在含硅树脂的脱模剂的情况下,可以导致相当多的涂布问题。结果导致有时需要进行后处理,例如表面抛光。
DE 19601401公开了在成型的含纤维素-异氰酸酯的制品中,滑石作为热稳定的脱模材料。然而,此无机固体在压缩温度下是固体,并因此同样也会导致压模上相当多的堆积。
EP 1719597描述了利用含有氨丙基的硅氧烷化合物作为脱模剂以避免黑色残余的堆积。
GB 1148016描述了含有游离羟基的有机物质即多元醇例如甘油、乙二醇、聚酯或聚醚作为脱模材料。然而,由于它们的羟基,这些物质会与作为粘结剂的异氰酸酯反应而不能仅作为具有脱模活性的物质。
DE 2932175、US 4257995和DE 3108537描述了含有酸式磷酸酯的脱模剂作为具有脱模活性的物质,特别是内润滑剂,用于生产含(木质)纤维素的产品。
然而,在生产复合材料模制品中提高最优化的过程中,仍然需要提高加工速度并降低加工温度。
发明内容
因此,本发明的目的在于提供一种脱模剂,其可以避免现有技术的脱模剂的一个或多个缺点,而且,其优选可提高加工速度和/或降低加工温度。
令人惊讶地,已经发现本发明的目的可以通过以下方法来达到:往磷酸盐(酯),例如,部分地在DE 2932175、US4257995和DE 3108537中描述的作为具有脱模活性的物质中,添加至少一种具有至少两个羟基且分子量小于250g/mol的化合物,例如乙二醇或甘油。
因此,本发明涉及脱模剂组合物,其在用于生产复合材料模制品的本发明方法中的用途,所述复合材料模制品本身可通过本发明的方法获得,并且其用途如权利要求书中所要求保护的以及本说明所详细描写的。
本发明的脱模剂具有以下优点:通过使用该脱模剂,可以显著地提高加工速度,特别是在连续性生产过程中。
本发明的脱模剂还具有以下优点:使用该脱模剂可以降低加工温度。除了节能之外,这还使得可以以淡色调生产木材(碎片)板,例如在较低温度下生产。
甚至在较高加工温度下,本发明的脱模剂组合物具有以下优点:生产的复合材料模制品表面的斑点和/或黑色着色不存在或者仅以轻微的程度存在。
以下通过举例来描述本发明的脱模剂组合物、其在用于生产复合材料模制品方法中的用途、复合材料模制品本身及其用途,但本发明并不局限于这些示范性的实施方式。以下所述化合物的范围、通式或种类,不仅用来包含明确提及的相应范围或化合物组,而且也包括通过除去个别值(范围)或化合物得到的部分范围或部分化合物组。本发明引用的文件,其全文,特别是涉及到相关的事实,都全部并入到本发明的公开内容中。除非另有说明,以百分比计的数据通常是指质量%。除非另有说明,以下描述的平均值都是指数均平均值。
本发明的脱模剂组合物的特征在于其至少包含以下组分:
a)至少一种通式(Ia)的磷酸酯或磷酸盐
其中
X=R6、H、金属、NRzH4-z +、或式(II)的基团,其中z=0-4,优选2或3,且R=碳原子数为1-10优选1-4的烃基,所述金属优选为碱金属或者碱土金属,所述碱金属优选为Na或K,所述碱土金属例如Mg、Ba、Sr或Ca,优选Ca,
其中
m=0-5,和
R1-R6各自独立地是氢、金属、NRzH4-z +、或者有机基团,其中z和R如上所述,所述金属优选为碱金属或者碱土金属,所述碱金属例如钠或钾,所述碱土金属如Mg、Ba、Sr或Ca,优选Ca,和
b)至少一种具有至少两个羟基且分子量小于250g/mol的化合物,
基于所述组合物,组分a)的比为0.1-70重量%,优选1-20重量%,优选2-10重量%,且组分b)的比为0.5-90重量%。
组分a)与组分b)的质量比为20∶80到80∶20是有利的,优选为40∶60到60∶40,且特别优选约50∶50。
对于组分b),本发明的组合物优选包含一种或多种二醇、三醇和/或多羟基多元醇,优选选自单乙二醇、二乙二醇、三甘醇、四甘醇、丙二醇、丁二醇、甘油、三羟甲基丙烷和季戊四醇中的一种或多种化合物。特别优选地,本发明组合物的组分b)由选自单乙二醇、二乙二醇、三甘醇、四乙二醇、丙二醇、丁二醇、甘油、三羟甲基丙烷和季戊四醇中的一种或多种化合物组成。
如果基团R1-R6是有机基团,其可以相同或不同。有机基团R1-R6优选选自支链的或直链的、无环的或环状的、脂环族或杂环的、脂肪族或芳香族或杂芳族的、取代或未取代的有机基团,优选碳原子数为1-25优选为12-18的直链脂肪族饱和和/或不饱和的基团,或者式(III)的基团
其中
R7=支链的或直链的、无环的或环状的、脂环族或杂环的、脂肪族或芳香族或杂芳族的、取代或未取代的有机基团,优选碳原子数为1-25、优选为12-18的直链脂肪族饱和和/或不饱和的基团。
A或B中一个是氢,且另一个基团是氢或碳原子数为1-10的取代或未取代的、直链或支链的烷基或者芳基,优选苯基基团,优选苯基、乙基或甲基,优选甲基,且n是1-100的数均数值,优选2-10。
如果基团R1-R7中的一个或多个是环状基团,特别是脂肪族烃基,其可以是,例如,环烷基或环烯基。如果基团R1-R7中的一个或多个是杂环基,其优选具有氮、碳和任选的其他杂原子。所述杂环基可以是,例如,可被H、烷基、芳基取代的具有受电子或给电子的取代基的三-、四-、五-、六-或更多-元环,或者是具有受电子或给电子的取代基和/或亲水性或疏水性基团的环系统的一部分。特别优选,所述杂环基是吡咯烷基、吡咯啉基、哌啶基或吗啉基。如果一个或多个的基团R1-R7是芳基,其可以是例如苯基、萘基或蒽基。如果一个或多个的基团R1-R7是杂芳基,其优选是咪唑基、吡唑基、吡啶基、噻吩基、噻唑基、呋喃基或吲哚基。基团R1-R7也可以是一个或多个R1-R7基团彼此连接的那些有机基团。
优选存在至少一种其中R1和R2或者如果合适的话(当X=式(II)的基团)R1-R5不是有机基团的无机磷酸盐作为组分a)。优选的无机磷酸盐是其中X是式(II)的基团且其中m=1-3优选1或2且基团R1-R5可以相同或不同且为H、NH4 +、K或Na优选Na的无机磷酸盐。
进一步优选存在至少一种其中R1和R2中的至少一个,或者如果合适的话(当X=式(II)的基团)R1-R5中的至少一个不是H、金属或NRzH4-z +,其中R和z如上所定义的有机磷酸酯作为组分a)。优选的有机磷酸酯是其中X=H、NH4 +、K或Na优选K,且基团R1或R2中的至少一个或二者(优选仅有一个)是烷基或烯基,优选碳原子数为10-25优选12-18的烷基或烯基,特别优选油基(oleyl)或硬脂酰基,且其他基团任选为H、NH4 +、K或Na,特别是K的式(I)有机磷酸酯。
本发明优选的组合物是包含至少一种其中R1、R2和X或者如果合适的话(当X=式(II)的基团)R1-R5不是有机基团的无机磷酸盐、和至少一种其中R1、R2和X基团中的至少一个或者如果合适的话(当X=式(II)的基团)R1-R5基团中的至少一个不是H、金属或NRzH4-z +有机磷酸酯作为组分a)的组合物,其中R和z如上所定义的。
本发明特别优选的组合物是不包含其中全部的R1、R2和X基团或者如果合适的话(当X=式(II)的基团)全部的R1-R5基团是有机基团的式(I)磷酸酯作为组分a)的组合物。
本发明极特别优选的组合物是那些包含碱金属多磷酸盐例如三聚磷酸钠、和/或单和/或二烷基或烯基磷酸酯的碱金属盐例如单/二-9-十八烯-1-醇磷酸酯的钾盐(potassium mono-/dioleyl phosphate)作为组分a)的组合物。
本发明的组合物优选具有碱金属氢氧化物作为组分C)。优选地,所述组合物包含选自NaOH和KOH的碱金属氢氧化物,优选为水溶液的形式,作为组分c)。
本发明的脱模剂组合物,或者如果所述脱模剂组合物不含水,10重量%的脱模剂组合物在水中的水溶液,优选具有大于或等于7至14、优选7-10且特别优选8-9的pH值,所述pH通过pH试纸检测(对于7.5-9.5范围的pH,其可以通过Marcherey-Nagel作为pH-Fix 7.5-9.5来获得)。本发明组合物的pH值可以通过加入碱金属氢氧化物(溶液)、有机酸例如醋酸、和/或无机酸优选磷酸来调节。
组分a)和b)可以以纯的形式作为脱模剂。然而,由于它们即使在低浓度中也会显示出优异的脱模结果,因而脱模剂组合物也含有溶剂是有利的。因此,本发明的脱模剂组合物具有有机溶剂或无机溶剂优选无机溶剂,优选水作为组分d)。优选的脱模剂组合物具有1-99重量%、优选80-98重量%、特别优选85-97重量%比例的优选为水的溶剂。
有机溶液是不太优选的,因为其具有低燃点,且在使用的温度范围中可能会起火。环状或直链的硅氧烷是更适合的,仅考虑那些燃点高于应用温度的那些硅氧烷。
为了避免过大的运输体积,贮藏和运输不含溶剂或仅含少量溶剂的本发明的脱模剂组合物、并仅在使用前即刻或使用中通过加入溶剂将其稀释至所述的优选的溶剂浓度是有利的。
本发明的组合物可含有其他常用的助剂和添加剂作为组分e)。特别是,以下组分可用在本发明的组合物中作为助剂或添加剂。
A)乳化剂:
阴离子乳化剂,例如烷基醚羧酸酯、烷基硫酸酯、脂肪醇乙氧基化物醚硫酸酯、α-烯基磺酸酯、磷酸烷基酯、烷基聚醚磷酸酯、烷基磺基丁二酸酯;非离子乳化剂,例如脂肪醇、乙氧基化脂肪醇、乙氧基化羰基醇及其他醇醚、脂肪胺例如二甲基烷基胺、脂肪酸烷醇酰胺、脂肪酸的醇酯,包括甘油酯或聚甘油酯或山梨糖醇酯;阳离子乳化剂,例如酸化的烷基二甲基胺、季氮化物;最后,两性离子表面活性剂或所述乳化剂的组合。基于本发明的总组合物,乳化剂的比例优选为0.1-10重量%,优选0.5-6重量%。
B)催化剂:
可使用的催化剂是用于粘合剂反应的典型催化剂。适用于聚氨基甲酸酯反应的催化剂可以是,例如路易斯酸如锡的化合物或路易斯碱如叔胺。就用作粘合剂的甲醛树脂来说,可以使用例如铵盐如硫酸铵或过氧化物作为催化剂。
C)粘度调节剂:
可用于本发明组合物中作为粘度调节剂的是例如典型的增稠剂如被称为卡波姆(carbomer)的聚丙烯酸衍生物,或其他的聚电解质增稠剂如水溶性的纤维素或黄原胶。
D)防腐剂、杀菌剂和/或防霉剂。
E)市场上可买到的抗氧化剂和消泡剂。
F)抗静电剂
市场上可买到的用于影响导电率的添加剂,如抗静电添加剂或增加导电率的添加剂。
本发明的组合物可作为乳剂和/或分散体和/或溶液。
为了制备本发明的组合物,可以使用任何适用于此目的的已知方法。
本发明的脱模剂组合物可用于所有使用脱模剂的方法中。优选地,本发明的脱模剂组合物可用于下述的本发明的方法中。
本发明用于生产复合材料模制品的方法,通过对包含至少一种有机粘结剂和至少一种以碎片、纤维、垫席、粉末或颗粒形式存在的材料的物质进行连续或间歇压缩模塑来进行,其特征在于:所述压缩模塑是在本发明的脱模剂组合物存在的条件下进行的。
取决于压缩模塑过程中的粘结剂,优选通过温度为20-450℃的压模进行本发明的方法。就异氰酸酯/聚异氰酸酯和甲醛树脂而言,使用90-350℃、优选180-275℃的温度,而当使用环氧树脂作为粘合剂时优选使用20-150℃的温度。
本发明的脱模剂组合物可用作内润滑剂(将脱模剂组合物结合到待模制的物质中)或作为外润滑剂(将脱模剂组合物涂敷到待模制的物质上或涂敷到模具上)。优选地,本发明的脱模剂组合物用作外润滑剂。
如果所述脱模剂组合物用作外润滑剂,优选通过通常的涂敷法例如通过喷雾法或辊涂法将其施用到待模制的物质上或压模上或压板上。
如果本发明的方法是连续进行的,则其形状优选受到压板和/或压辊的影响。待模制的物质的移动速度优选为0.5-500m/min,优选10-100m/min且特别优选15-50m/min。
在本发明的方法中,优选使用异氰酸酯、聚异氰酸酯、尿素/甲醛、苯酚/甲醛、三聚氰胺/甲醛、环氧化物(EP)、聚氨基甲酸酯、聚酯和/或聚乳酸树脂(polyactide resin)作为有机粘结剂。特别优选使用聚异氰酸酯特别是二苯甲烷二异氰酸酯(MDI)或聚合的二苯甲烷二异氰酸酯(PMDI)作为粘结剂。
优选使用含纤维素、优选含木质纤维素的材料或者由纤维素优选木质纤维素组成的材料用作生产待模制的物质的材料。
本发明的方法可以通过现有技术中描述的方法进行。一般来说,最初以纤维或颗粒形式引入木质纤维素材料,然后加入粘结剂以生成物质然后用金属模制机或者通过应用减压/真空进行模塑。在压缩模塑工艺之前将所描述的脱模剂喷雾到碎片或所述物质上或者金属板、金属辊或模具上,其可以已经是热的,例如如WO-A-02/36268中所描述的。最后,从赋形模(shape-imparting mould)上除去被模制的材料。
本发明纤维素复合材料模制品可通过本发明的方法得到。其可以具有,例如板状、块状、柱状或者任选模加工的绳状的形状。当然,通过使用相应的模具可以得到各种可能的形状。优选的复合材料模制品可以是例如OSB(定向刨花板)、刨花板、纤维板如MDF和HDF板(分别是中密度和高密度纤维板)和胶合板、以及软木板和包含亚麻、稻草或其他含纤维素材料的模制品。
本发明的复合材料模制品可用于生产家具或家具部件或包装材料或用作房屋建筑和内部装修中的材料。
具体实施方式
下述实施例用来更详细地描述本发明的主题,但本发明并不局限于这些具体的实施例。
实施例:
使用的物质列表:
ILCOPhos 208=单/二-9-十八烯-1-醇磷酸酯(mono-/dioleyl phosphate)
STPP=三聚磷酸钠、制造商Prayon
甘油=超纯的甘油、纯度87%
MDAH=单/二(2-乙基己基)磷酸酯,制造商Clariant
PN Extra=脂肪醇聚乙二醇醚的混合物,制造商Clariant
KPE=含乳化剂的褐煤酯蜡(montan ester wax),制造商Clariant
实施例1:脱模剂乳剂的制备
实施例1a:本发明脱模剂
将12gMDAH与5.4g浓度为50重量%的氢氧化钾水溶液以及32.6g水搅拌以生成分散体。将3g甘油和3g的STPP在44g水中的溶液搅拌加入到该分散体中。
实施例1b:本发明的脱模剂
将10g三聚磷酸钠和10g甘油(纯度87%)溶解在70g水中并搅拌加入到2g 9-十八烯-1-醇磷酸酯、0.9g浓度为50%重量的氢氧化钾水溶液和10g水的分散体中。
对比实施例A:(传统的含石蜡脱模剂)
作为对比脱模剂A,将80gPN Extra与400gKPE在强力搅拌下在升高的温度中与50g水混合,然后用5.47g水稀释以生成最终的乳剂。
对比实施例B
作为对比脱模剂B,将12g Hostaphat MDAH和4.7g浓度为50重量%的氢氧化钾水溶液在强力搅拌下与50g水混合,然后用33.3g水稀释以生成最终的乳剂。
对比实施例C,基于GB 1148016,第3页中第8行:
100%的甘油
实施例2:脱模实验
借助喷嘴将实施例1a和1b以及对比实施例A、B和C的脱模剂以30g/m2的量施加到金属带形式的金属模制机上。使木片与粗制的二苯甲烷二异氰酸酯(MDI)混合并在240℃的温度下模塑。带速为25m/min,片宽为2.5m且木板厚度为11mm。在进一步的实验中(试验2),在相同的木板厚度下在200℃的温度和30m/min的带速下重复实验,以优化制备条件。脱模实验的结果如表1所示。
表1:脱模剂实验的评价
从表1中可以清楚地看出,使用本发明的脱模剂,生产的木板甚至在高带速下也没有黑斑点。
实施例3:实施室脱模实验
在实施室条件下测试下表2所示的脱模剂组合物。为了此目的,将所述脱模剂组合物喷涂到金属测试片(10x15mm)上并将这些金属片用于胶涂有4重量%的PMDI(44V20,Bayer)的碎片的压缩模塑。然后检测从模具中除去得到的模制品所需的力。
借助于弹簧称检测模制品生产中的脱模性质。检测单位为kg。小于0.1kg的力对应于非常好的脱模效果,0.1-0.5kg的力对应于好的脱模效果,以及0.5-1kg的力是令人满意的。评价结果如表2所示。
实验3.1-3.5中使用的醇是甘油。在作为对比实施例的实验3.6中,使用环氧乙烷/环氧丙烷的共聚物作为醇,其是以商标名Polyglycole P41 3000从Clariant购得的。
实施3.1-3.6中使用的聚磷酸盐是三聚磷酸钠。
使用的KOH是浓度为50%重量的氢氧化钾水溶液。
实验3.1-3.2中使用的磷酸酯是Ilcophos 208。实验3.4中使用HostaphatMDAH。实验3.5中,使用Walliphos SPP K,其也含有30%的鲸蜡醇磷酸酯钾,即除了鲸蜡醇磷酸酯钾(potassium monocetyl phosphate)之外还有其他酯。
表2:实验室实验
实施例 | 3.1 | 3.2 | 3.3 | 3.4 | 3.5 | 3.6 |
醇 | 10g | 3g | 10g | 4.8g | 3g | 10g |
聚磷酸盐 | 10g | 3g | 10g | 4.8g | 3g | 5g |
磷酸酯 | 2g | 12g | - | 0.4g | 13.5g | - |
KOH | 0.5g | 5.4g | - | 0.5g | - | - |
水 | 77.5g | 76.6 | 80g | 39.5g | 80.5g | 85g |
脱模性质 | 非常好 | 非常好 | 好 | 满意+ | 非常好 | 满意- |
实施例3.1-3.6显示出使用本发明的脱模剂可以得到良好的结果,并且这些结果优于对比实验的结果。很明显的,具有聚磷酸盐(无机磷酸盐)和磷酸酯(有机磷酸酯)的脱模剂组合物具有特别好的脱模性质。
Claims (16)
1.一种脱模剂组合物,其特征在于:其包含以下组分:
a)至少一种通式(I)的磷酸盐或磷酸酯
其中
X=R6或式(II)的基团,
其中
m=0-5,和
R1-R6各自独立地是氢、碱金属或者碱土金属、NRzH4-z +或者有机基团,其中z=0-4,且R=碳原子数为1-10的烃基,所述有机基团是支链的或直链的、脂肪族饱和的或不饱和的具有1-25个碳原子的基团、或者式(III)的基团
其中
R7=支链的或直链的、脂肪族饱和的或不饱和的具有1-25个碳原子的基团,
A或B中一个是氢,且另一个基团是氢或具有1-10个碳原子的直链或支链的烷基,和
n是1-100的数均数值,
和
b)至少一种具有至少两个羟基且分子量小于250g/mol的化合物,
c)碱金属氢氧化物,
其中至少一种X基团是式(II)且式(II)中m=1-3、且式(I)和(II)中的基团R1-R5为相同或不同的选自H、NH4 +、K或Na的无机磷酸盐、以及至少一种式(I)和(II)中的基团X和R1-R5中的至少一个不是H、金属或NRzH4-z +的有机磷酸酯作为组分a),其中R和z如上所述,
基于所述组合物,组分a)的比例为0.1-70重量%,组分b)的比例为0.5-90重量%。
2.如权利要求1所述的组合物,其中所述碱金属为钠或钾。
3.如权利要求1所述的组合物,其中所述碱金属氢氧化物选自NaOH和KOH。
4.如权利要求1所述的组合物,其特征在于,组分a)与组分b)的质量比为20:80到80:20。
5.如权利要求4所述的组合物,其中,组分a)与组分b)的质量比为40:60到60:40。
6.如权利要求5所述的组合物,其中,组分a)与组分b)的质量比为50:50。
7.如权利要求1所述的组合物,其特征在于,组分b)包含至少一种选自单乙二醇、二乙二醇、三甘醇、四甘醇、丙二醇、丁二醇、甘油、三羟甲基丙烷和季戊四醇中的化合物。
8.如权利要求1所述的组合物,其中,A或B中一个是氢,且另一个基团是氢或碳原子数为1或2的烷基。
9.如权利要求1所述的组合物,其特征在于,存在碱金属多磷酸盐和/或单/二-9-十八烯-1-醇磷酸酯的碱金属盐作为组分a)。
10.一种用于生产复合材料模制品的方法,通过对包含至少一种有机粘结剂和至少一种以碎片、纤维、垫席、粉末或颗粒形式存在的材料的物质进行连续或间歇压缩模塑来进行,其特征在于:所述压缩模塑是在权利要求1-9中任意一项所述的脱模剂组合物存在下进行的。
11.如权利要求10所述的方法,其特征在于,使用异氰酸酯、聚异氰酸酯、尿素/甲醛、苯酚/甲醛、三聚氰胺/甲醛、EP、聚氨基甲酸酯、聚酯和/或聚乳酸树脂作为粘结剂。
12.如权利要求10或11所述的方法,其特征在于,将所述脱模剂组合物涂敷到压模上和/或涂敷到待模制的物质上。
13.一种复合材料模制品,其可通过如权利要求10-12中任意一项所述的方法获得。
14.如权利要求13所述的复合材料模制品,其特征在于,其具有板状、块状、柱状或者任选模加工的绳状的形状。
15.如权利要求13或14所述的复合材料模制品的用途,其用于生产家具或包装材料,或用作房屋建筑和内部装修中的材料。
16.如权利要求15所述的复合材料模制品的用途,其用于生产家具部件。