CN102153967A - 加强型热缩套管热熔胶粘剂及其制备方法 - Google Patents

加强型热缩套管热熔胶粘剂及其制备方法 Download PDF

Info

Publication number
CN102153967A
CN102153967A CN2011100464515A CN201110046451A CN102153967A CN 102153967 A CN102153967 A CN 102153967A CN 2011100464515 A CN2011100464515 A CN 2011100464515A CN 201110046451 A CN201110046451 A CN 201110046451A CN 102153967 A CN102153967 A CN 102153967A
Authority
CN
China
Prior art keywords
hot melt
melt adhesive
reinforced heat
shrinkable
oxidation inhibitor
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2011100464515A
Other languages
English (en)
Other versions
CN102153967B (zh
Inventor
张玉根
青云凤
彭忠全
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHENGDU DOUBLE-CURRENT SICHUAN DOUBLE PYROCONDENSATION PRODUCT Co Ltd
Original Assignee
CHENGDU DOUBLE-CURRENT SICHUAN DOUBLE PYROCONDENSATION PRODUCT Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHENGDU DOUBLE-CURRENT SICHUAN DOUBLE PYROCONDENSATION PRODUCT Co Ltd filed Critical CHENGDU DOUBLE-CURRENT SICHUAN DOUBLE PYROCONDENSATION PRODUCT Co Ltd
Priority to CN 201110046451 priority Critical patent/CN102153967B/zh
Publication of CN102153967A publication Critical patent/CN102153967A/zh
Application granted granted Critical
Publication of CN102153967B publication Critical patent/CN102153967B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明属于热熔胶技术领域，特别涉及加强型热缩套管热熔胶粘剂及其制备方法。本发明所要解决的第一个技术问题是提供一种加强型热缩套管热熔胶粘剂，该加强型热缩套管热熔胶粘剂密封、防腐效果好。本发明加强型热缩套管热熔胶粘剂是包括下列重量份的组份：萜烯树脂20～50份、EVA 35～75份、抗氧剂0～6份和填料3～20份。本发明加强型热缩套管热熔胶粘剂具有耐高温性能，并且剥离强度较高，PE对PE剥离强度大于182N/cm、PE对环氧底漆剥离强度大于205N/cm，可以满足石油天然气、保温管密封和防腐的要求。

Description

加强型热缩套管热熔胶粘剂及其制备方法
技术领域
本发明属于热熔胶技术领域，特别涉及加强型热缩套管热熔胶粘剂及其制备方法。
背景技术
随着环境要求的提高，管道密封和防腐成为社会日益重视的问题。由于传统用普通型热缩套管穿越有明显缺点，在穿越拖拉工程中容易拉断。而加强型热缩套管采用两边聚乙烯中间纤维网，强度高、柔韧性好，碰撞和变形不会开裂。
聚乙烯是低表面难粘的材料，目前已经有两种穿越方法，这些方法各有缺点。上述连接方法可分为普通型热缩套管和热缩带穿越，在穿越拖拉工程中容易拉断，需要重新再来，那样就给施工带来不必要的麻烦，施工难度增加，相应的成本也增加。因此很需要一种施工方便、性能可靠、成本低的穿越连接方法。
加强型热缩套管内层胶粘剂是由几种材料组成，该胶粘剂粘接强度高，适用于钢管、塑料管的粘接。通常是将石油树脂、EVA、沥青混合成为热熔胶粘剂，但使用时热缩套(带)PE对PE剥离强度70N/cm、PE对FBE剥离强度70N/cm，因此无法满足管道穿越要求的粘接强度。
发明内容
本发明所要解决的第一个技术问题是提供一种加强型热缩套管热熔胶粘剂，该加强型热缩套管热熔胶粘剂密封、防腐效果好。
本发明加强型热缩套管热熔胶粘剂由下列重量份的组份组成：
萜烯树脂20～50份、EVA 35～75份、抗氧剂0～6份和填料3～20份。
优选的，加强型热缩套管热熔胶粘剂由下列重量份的组份组成：
萜烯树脂20～40份、EVA 45～60份、抗氧剂0.1～1份和填料10～20份。
所述萜烯树脂的平均分子量650～1250，软化点≤90～120℃，酸值(mgKOH/g)≤1.0，皂化值(mgKOH/g)≤1.5。
所述EVA为乙烯-醋酸乙烯共聚物，醋酸乙烯含量为5～40％。
优选的EVA由EVA4700和EVA2825组成，用量按重量比计为10～30∶25～45。
所述填料为炭黑、碳酸钙、滑石粉中的至少一种。
为了吸附湿气固化时放出的二氧化碳，可加入适量的炭黑，同时起到颜料、填料的作用；为调节胶粘剂性能，较低成本，还可以加入碳酸钙、滑石粉等填料。
所述抗氧剂可以为单配方抗氧剂，也可以为复配型抗氧剂，单配方抗氧剂优选为1010抗氧剂，复配型抗氧剂优选为B215抗氧剂。
本发明的加强型热缩套管热熔胶粘剂的制备方法：
称取萜烯树脂、EVA、抗氧剂和填料，升温至200～220℃反应1～1.2小时，降温至170～190℃反应20～40min后即得。
本发明加强型热缩套管热熔胶粘剂具有耐高温性能，并且剥离强度较高，PE对PE剥离强度大于182N/cm、PE对环氧底漆剥离强度大于205N/cm。可以满足石油天然气、保温管密封和防腐的要求。
具体实施方式
实施例1
200kg反应罐，装有电动搅拌器、温度调节器、保温装置。加入萜烯树脂60kg、EVA470040kg、EVA2825 70kg、1010抗氧剂0.5kg、碳酸钙29.5kg，将反应罐升温至200℃，搅拌1小时后，降温至190℃，停止搅拌保温半小时，得到的热熔胶粘剂可立即使用。
实施例2
200kg反应罐，装有电动搅拌器，温度调节器，反应保温装置。加入萜烯树脂60kg、EVA470046kg、EVA2825 60kg、抗氧剂(复配型抗氧剂，型号：B215)0.5kg、滑石粉33.5kg，将反应罐升温至200℃，搅拌1-1.5小时后，降温至180℃，保温半小时(停止搅拌)，搅拌好的热熔胶粘剂方可使用。
对比例1
200kg反应罐，装有电动搅拌器、温度调节器、保温装置。加入石油树脂60kg、EVA2825110kg、1010抗氧剂1kg、碳酸钙20kg，将反应罐升温至200℃，搅拌1小时后，降温至190℃，停止搅拌保温半小时，得到热熔胶粘剂。
对比例2
200kg反应罐，装有电动搅拌器、温度调节器、保温装置。加入萜烯树脂30kg、EVA470040kg、EVA2825 70kg、1010抗氧剂0.6kg、碳酸钙28kg，将反应罐升温至200℃，搅拌1小时后，降温至190℃，停止搅拌保温半小时，得到热熔胶粘剂。
试验例
实施例1、2所得热熔胶粘剂为黑色，复合在加强型热缩套管内，套进穿越￠529-500的钢管上，按照SY/T4054-2003标准中进行测试，测试结果见表1：
表1
表1说明本发明的加强型热缩套管热熔胶粘剂超过标准的要求，可以满足石油天然气、保温管密封和防腐的要求。

Claims (9)

1.加强型热缩套管热熔胶粘剂，其特征在于：由下列重量份的组份组成：
萜烯树脂20～50份、EVA 35～75份、抗氧剂0～6份和填料3～20份。
2.根据权利要求1所述的加强型热缩套管热熔胶粘剂，其特征在于：由下列重量份的组份组成：萜烯树脂20～40份、EVA 45～60份、抗氧剂0.1～1份和填料10～20份。
3.根据权利要求1所述的加强型热缩套管热熔胶粘剂，其特征在于：所述EVA为乙烯-醋酸乙烯共聚物，醋酸乙烯含量为5～40％。
4.根据权利要求3所述的加强型热缩套管热熔胶粘剂，其特征在于：EVA由EVA4700和EVA2825组成，用量按重量比计为10～30∶25～45。
5.根据权利要求1～4任一项所述的加强型热缩套管热熔胶粘剂，其特征在于：所述填料为炭黑、碳酸钙、滑石粉中的至少一种。
6.根据权利要求1～4任一项所述的加强型热缩套管热熔胶粘剂，其特征在于：所述抗氧剂为单配方抗氧剂或复配型抗氧剂。
7.根据权利要求6所述的加强型热缩套管热熔胶粘剂，其特征在于：单配方抗氧剂为1010抗氧剂。
8.根据权利要求6所述的加强型热缩套管热熔胶粘剂，其特征在于：复配型抗氧剂为B215抗氧剂。
9.权利要求1～8任一项所述加强型热缩套管热熔胶粘剂的制备方法，其特征在于：称取萜烯树脂、EVA、抗氧剂和填料，升温至200～220℃反应1～1.2小时，降温至170～190℃反应20～40min后即得。
CN 201110046451 2011-02-25 2011-02-25 加强型热缩套管热熔胶粘剂及其制备方法 Active CN102153967B (zh)