CN102115625A - 一种led灯具用高反射率的漫反射涂料及其制备方法 - Google Patents

一种led灯具用高反射率的漫反射涂料及其制备方法 Download PDF

Info

Publication number
CN102115625A
CN102115625A CN2009102477796A CN200910247779A CN102115625A CN 102115625 A CN102115625 A CN 102115625A CN 2009102477796 A CN2009102477796 A CN 2009102477796A CN 200910247779 A CN200910247779 A CN 200910247779A CN 102115625 A CN102115625 A CN 102115625A
Authority
CN
China
Prior art keywords
pva
reflectivity
diffuse reflection
reflection coating
polyvinyl alcohol
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2009102477796A
Other languages
English (en)
Other versions
CN102115625B (zh
Inventor
陈必寿
程广斌
陈惜峰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanghai Sansi Technology Co Ltd
Shanghai Sansi Electronic Engineering Co Ltd
Jiashan Sansi Photoelectric Technology Co Ltd
Pujiang Sansi Optoelectronics Technology Co Ltd
Original Assignee
Jiashan Jinghui Optoelectronics Technology Co Ltd
Shanghai Sansi Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiashan Jinghui Optoelectronics Technology Co Ltd, Shanghai Sansi Technology Co Ltd filed Critical Jiashan Jinghui Optoelectronics Technology Co Ltd
Priority to CN 200910247779 priority Critical patent/CN102115625B/zh
Publication of CN102115625A publication Critical patent/CN102115625A/zh
Application granted granted Critical
Publication of CN102115625B publication Critical patent/CN102115625B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种LED灯具用高反射率的漫反射涂料及其制备方法，漫反射涂料主要成分包括高分子树脂和硫酸钡，所述高分子树脂是以水作为溶剂、质量分数为0.3～15％的聚乙烯醇(PVA)溶液，所述硫酸钡的粒径范围是700～8000目，所述涂料还包括消泡剂和流平剂。LED灯具反射腔采用该涂料时，能够有效提高光线的反射率。当聚乙烯醇(PVA)溶液的质量浓度控制在0.5％，醇解度88，聚合度1700，可以更好的溶于水，且具有更强的粘接性和较佳的表面状态。还有，本涂料采用水作为溶剂，而且聚乙烯醇(PVA)亦环境友好，完全满足室内环保的要求。

Description

一种LED灯具用高反射率的漫反射涂料及其制备方法
技术领域
本发明涉及一种光学涂料，更进一步的，涉及一种能提高LED照明灯腔反射率的漫反射涂料及其制备方法。
背景技术
LED照明行业正以其节能、环保等优势获得空前的发展。LED照明灯具一般均采用大功率的LED芯片，这种大功率LED芯片由于其体积小，亮度高，应用在灯具上特别是室内照明上容易产生眩光，解决眩光问题关键在于灯具中反射腔体的选材。
LED室内照明灯具的腔体一般采用漫反射材料，高反射率的高分子复合材料如PET、PPO等虽然反射率满足要求，但由于其存在玻璃化温度、熔点较高，很难加工等问题，因此一般转而采用漫反射涂料。一般的漫反射涂料以丙烯酸树脂为基材，其又分为水溶性和油溶性，由于室内灯具的环保性要求可选用水性丙烯酸树脂涂料，其中添加硫酸钡、氧化钛、氧化镁等，各种填料的比例、粒径均对最后的反射率产生影响。
发明内容
本发明为解决上述技术问题，提供一种LED灯具用高反射率的漫反射涂料，采用该漫反射涂料的LED照明灯具的反射腔体具有较好的反射率，能解决一般涂料反射率不高的问题。同时本发明还提供了一种制备该高反射率的漫反射涂料的方法。
为达到上述目的，本发明采用的技术方案如下：
一种LED灯具用高反射率的漫反射涂料，主要成分包括高分子树脂和硫酸钡，所述高分子树脂是以水作为溶剂、质量分数为0.3～15％的聚乙烯醇(PVA)溶液，所述硫酸钡的粒径范围是700～8000目，其质量是水溶剂的0.4～1.2倍，所述涂料还包括消泡剂和流平剂。
所述聚乙烯醇(PVA)溶液的质量分数是0.5％。
上述聚乙烯醇(PVA)溶液的醇解度是78～98，聚合度是1500～1800。优选方案是醇解度88，聚合度1700。
所述硫酸钡是一种粒径，其粒径范围是4000～6000目，或者是两种粗细搭配，其粒径分别是1000目和5000目。
作为LED灯具用，优选方案是该漫反射涂料中还添加有防霉剂。
一种LED灯具，具有反射腔体，所述反射腔体上涂覆有上述高反射率的漫反射涂料。
上述LED灯具用高反射率的漫反射涂料的制备方法，其步骤是：将聚乙烯醇(PVA)倒入温度为10～20℃的水中，保持水浴恒温，充分搅拌，使聚乙烯醇(PVA)分散均匀，充分溶胀；逐渐升温并保持搅拌，待温度升高至90-100℃，保持此温度到聚乙烯醇(PVA)完全溶解，然后再冷却至室温，过滤，形成质量分数为0.3-15％的聚乙烯醇(PVA)溶液；以上搅拌过程中，同时向聚乙烯醇(PVA)溶液中加入消泡剂和流平剂；最后再加入硫酸钡，搅拌混合均匀而成该高反射率的漫反射涂料。
本发明所公开的涂料以质量分数为0.3～15％的聚乙烯醇(PVA)溶液作为粘接基材，用水作为溶剂，选择硫酸钡的粒径范围为700～8000目，其质量是水溶剂的0.4～1.2倍，再加入消泡剂、流平剂。LED灯具的反射腔体采用该涂料时，能够有效提高光线的反射率。当聚乙烯醇(PVA)溶液的质量分数控制在0.5％，醇解度88，聚合度1700，可以较好的溶于水，且具有较强的粘接性和较佳的表面状态。还有，本涂料采用水作为溶剂，而且聚乙烯醇(PVA)亦环境友好，完全满足室内环保的要求。
具体实施方式
实施例一
称量500g水，可以是去离子水、蒸馏水、纯净水或自来水，本实施例采用自来水。2.5g聚乙烯醇(PVA)，其醇解度范围是78～98、聚合度范围是1500～1800，本实施例选用醇解度是88，聚合度是1700。将聚乙烯醇(PVA)倒入10～20℃水中，水浴恒温保持30分钟，进行充分搅拌，使聚乙烯醇(PVA)分散均匀，充分溶胀。然后逐渐升温并保持持续搅拌，待温度升高至90～100℃时，开始保温2小时。在上述搅拌过程中，同时加入消泡剂和流平剂，并注意在此过程由于水分蒸发造成流失，所以需补加水以满足对该溶液浓度的要求。待聚乙烯醇(PVA)完全溶解后冷却至室温，进行过滤，滤液待用。在该滤液中再加入500g硫酸钡，该硫酸钡的粗细在700～8000目范围内，可采用一种硫酸钡或者两种不同粗细的硫酸钡搭配。本实施例选用1000目和5000目两种硫酸钡搭配，与上述聚乙烯醇(PVA)滤液搅拌混合均匀，即可制成本发明的高反射率涂料。
实验证明，采用本实施例涂料的LED灯具反射腔，反射率可达96％，并有很好的粘接性，与采用普通涂料，比如以碳酸钙为填料的涂料相比较，反射率可以提高约1倍，粘接度可以提高0.5倍。
实施例二
称量500g自来水，50g聚乙烯醇(PVA)，其醇解度是88，聚合度是1500。将聚乙烯醇(PVA)倒入10～20℃水中，水浴恒温保持30分钟，进行充分搅拌，使聚乙烯醇(PVA)分散均匀，充分溶胀。然后逐渐升温并保持持续搅拌，待温度升高至90～100℃时，开始保温2小时。在上述搅拌过程中，同时加入消泡剂和流平剂，并注意在此过程由于水分蒸发造成流失，所以需补加水以满足对该溶液浓度的要求。待聚乙烯醇(PVA)完全溶解后冷却至室温，进行过滤，滤液待用。在该滤液中再加入300g硫酸钡，该硫酸钡选用一种粗细为6000目的硫酸钡，与上述聚乙烯醇(PVA)滤液搅拌混合均匀，制成本发明的高反射率涂料。
实验证明，采用本实施例涂料的LED灯具反射腔，反射率可达94％，并有很好的粘接性。

Claims (10)

1.一种LED灯具用高反射率的漫反射涂料，主要成分包括高分子树脂和硫酸钡，其特征在于：所述高分子树脂是以水作为溶剂、质量分数为0.3～15％的聚乙烯醇(PVA)溶液，所述硫酸钡的粒径范围是700～8000目，其质量是溶剂的0.4～1.2倍，所述涂料还包括消泡剂和流平剂。
2.根据权利要求1所述的LED灯具用高反射率的漫反射涂料，其特征在于：所述聚乙烯醇(PVA)溶液的质量分数是0.5％。
3.根据权利要求2所述的LED灯具用高反射率的漫反射涂料，其特征在于：所述聚乙烯醇(PVA)溶液的醇解度是78～98，聚合度是1500～1800。
4.根据权利要求3所述的LED灯具用高反射率的漫反射涂料，其特征在于：所述聚乙烯醇(PVA)溶液的醇解度是88，聚合度是1700。
5.根据权利要求1所述的LED灯具用高反射率的漫反射涂料，其特征在于：所述硫酸钡是两种粗细搭配，其粒径分别是700目和5000目。
6.根据权利要求1所述的LED灯具用高反射率的漫反射涂料，其特征在于：所述水包括去离子水、蒸馏水或自来水。
7.根据权利要求1所述的LED灯具用高反射率的漫反射涂料，其特征在于：还添加有防霉剂。
8.根据权利要求1所述的LED灯具用高反射率的漫反射涂料，其特征在于：所述硫酸钡与水溶剂的质量比例为1∶1。
9.如权利要求1所述的LED灯具用高反射率的漫反射涂料的制备方法，其步骤是：将聚乙烯醇(PVA)倒入温度为10～20℃的水中，保持水浴恒温，充分搅拌，使聚乙烯醇(PVA)分散均匀，充分溶胀；逐渐升温并保持搅拌，待温度升高至90-100℃，保持此温度到聚乙烯醇(PVA)完全溶解，然后再冷却至室温，过滤，形成质量分数为0.3-15％的聚乙烯醇(PVA)溶液；以上搅拌过程中，同时向聚乙烯醇(PVA)溶液中加入消泡剂和流平剂；最后再加入硫酸钡，搅拌混合均匀而成该漫反射涂料。
10.根据权利要求9所述的LED灯具用高反射率的漫反射涂料的制备方法，其特征在于：所述过滤后的聚乙烯醇(PVA)溶液的质量分数是0.5％，醇解度是88，聚合度是1700。
CN 200910247779 2009-12-31 2009-12-31 一种led灯具用高反射率的漫反射涂料及其制备方法 Active CN102115625B (zh)