CN102115527A - 一种新戊二醇树脂 - Google Patents
一种新戊二醇树脂 Download PDFInfo
- Publication number
- CN102115527A CN102115527A CN 201010582940 CN201010582940A CN102115527A CN 102115527 A CN102115527 A CN 102115527A CN 201010582940 CN201010582940 CN 201010582940 CN 201010582940 A CN201010582940 A CN 201010582940A CN 102115527 A CN102115527 A CN 102115527A
- Authority
- CN
- China
- Prior art keywords
- neopentyl glycol
- percent
- acid
- glycol resin
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种新戊二醇树脂,主要由:新戊二醇30%,己二酸6-8%,间苯二甲酸20-25%,偏笨三酸酐6-8%,对苯二甲酸2-4%,催化剂0.1%,S-150 15-20%,DBE 10-15%,二甲苯3-5%,经物理搅拌混合而制成。该树脂是一种复合环保要求的涂料,防腐、防锈效果好,耐介质好,有利于环境保护。
Description
所属技术领域
本发明涉及一种材料树脂,特别是一种新戊二醇树脂,适合于各种卷材钢板。
背景技术
目前,预涂卷材钢板用涂料主要防锈的原料是铬酸锶、铬酸锌,它的的防锈能力强,水溶性好,耐高温烘烤,但毒性较强,对人伤害较大,不利于环保。
发明内容
本发明所要解决的问题在于,克服现有技术的缺点,提供了一种新戊二醇树脂。该树脂不仅配方新颖,操作简单,使用安全无毒,不含有对人体有害的重金属原料,而且涂膜更环保,防腐防锈能力强,满足彩钢板各项物理性能,符合对环境保护的要求。
本发明采用的配方为:
原材料 百分比
新戊二醇 30
己二酸 6--8
间苯二甲酸 20--25
偏笨三酸酐 6--8
对苯二甲酸 2--4
催化剂 0.1
S-150 15--20
DBE 10--15
二甲苯 3--5
为了进一步提高产品的特性及要求,其最佳配方为:
原材料 百分比
新戊二醇 30
己二酸 7
间苯二甲酸 22.5
偏笨三酸酐 7
对苯二甲酸 3
催化剂 0.1
S-150 17.5
DBE 12.5
二甲苯 4
通过实施本发明,可以见到以下显著效果:
复合无机原料的性能特点:耐高温、耐气候、耐酸碱、易分散、环保无毒,它是高惰性的化学复合物,稳定性好,防止或减缓金属底材锈蚀,属于无毒颜料,完全适用于要求对人体无毒害的安全体系。从长远观点来看,含有对人体有害的传统的铬酸盐颜料,最终将被淘汰,。新戊二醇树脂其涂膜具有较好的耐热性、耐溶剂性、耐化学品性。
本发明的有益效果是,该树脂不仅配方新颖,操作简单,使用安全无毒,不含有对人体有害的重金属原料,而且新戊二醇树脂生产出来的涂料、硬度较高、涂膜光亮、耐候性好、耐老化性能优异,符合对环境保护的要求。
具体实施方式
选用新戊二醇树脂配方各种原料用量如下:
原材料 百分比
新戊二醇 30
己二酸 6--8
间苯二甲酸 20--25
偏笨三酸酐 6--8
对苯二甲酸 2--4
催化剂 0.1
S-150 15--20
DBE 10--15
二甲苯 3--5
为了进一步提高产品的特性及要求,其最佳新戊二醇树脂配方为:
原材料 百分比
新戊二醇 30
己二酸 7
间苯二甲酸 22.5
偏笨三酸酐 7
对苯二甲酸 3
催化剂 0.1
S-150 17.5
DBE 12.5
二甲苯 4
经搅拌物理合成,即可使用。
该新戊二醇树脂是一种复合环保要求的涂料,防腐、防锈效果好,耐介质好,有利于环境保护。
Claims (2)
1.一种新戊二醇树脂,其特征在于:采用的配方为:
原材料 百分比
新戊二醇 30
己二酸 6--8
间苯二甲酸 20--25
偏笨三酸酐 6--8
对苯二甲酸 2--4
催化剂 0.1
S-150 15--20
DBE 10--15
二甲苯 3--5。
2.根据权利要求1所述的一种新戊二醇树脂,其特征在于:最佳配方为:
原材料 百分比
新戊二醇 30
己二酸 7
间苯二甲酸 22.5
偏笨三酸酐 7
对苯二甲酸 3
催化剂 0.1
S-150 17.5
DBE 12.5
二甲苯 4。