CN102108637B - 可溶化止血棉的制作方法 - Google Patents

可溶化止血棉的制作方法 Download PDF

Info

Publication number
CN102108637B
CN102108637B CN2011100221212A CN201110022121A CN102108637B CN 102108637 B CN102108637 B CN 102108637B CN 2011100221212 A CN2011100221212 A CN 2011100221212A CN 201110022121 A CN201110022121 A CN 201110022121A CN 102108637 B CN102108637 B CN 102108637B
Authority
CN
China
Prior art keywords
absorbent cotton
cotton
solution
gained
hemostatic
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN2011100221212A
Other languages
English (en)
Other versions
CN102108637A (zh
Inventor
刘建鸿
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN2011100221212A priority Critical patent/CN102108637B/zh
Publication of CN102108637A publication Critical patent/CN102108637A/zh
Application granted granted Critical
Publication of CN102108637B publication Critical patent/CN102108637B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种可溶化止血棉的制作方法，它包括如下步骤：(1)将脱脂棉放入丙酮和海藻酸钠的混合溶液中，进行改性处理；(2)将步骤(1)所得脱脂棉放入氯乙酸溶液中，进行醚化反应；(3)将步骤(2)所得脱脂棉放入浓度55％的氢氧化钾水溶液中，进行碱化反应；(4)向步骤(3)的溶液中，缓慢分次加入环氧乙烷，充分反应；(5)将浓度80％的乙醇加入步骤(4)所得溶液中均匀搅拌，再加入乙酸进行中和，使PH值调整为6-7；(6)以浓度90％的乙醇洗涤步骤(5)所得脱脂棉，并在70-80℃下进行烘干，即得到可溶化的止血棉。上述制作方法步骤简便，所制作的止血棉遇血液能迅速吸收，膨胀溶解，形成薄膜覆盖于伤口上，不会造成粘连结痂，能起到迅速止血的良好功效。

Description

可溶化止血棉的制作方法
技术领域
本发明涉及医药领域，特别是一种可溶化止血棉的制作方法。
背景技术
目前，人们一般采用医用纱布为伤口包扎止血，而纱布直接与伤口接触后，伤口渗出的体液浸在纱布上凝固后，往往将伤口与纱布粘粘连在一起，形成硬痂，造成纱布难以取下，甚至引起伤口的疼痛或流血。虽然为改变这种状况，人们研究出了一些可溶性止血纱布的制作方法，但往往制作工序比较复杂、产品使用效果也不太理想，有待改进。
发明内容
本发明要解决的技术问题，是提供一种可溶化止血棉的制作方法，制作步骤比较简便、产品使用效果良好。
为解决上述技术问题，本发明的技术方案为：提供一种可溶化止血棉的制作方法，它包括如下步骤：
(1)将脱脂棉放入丙酮和海藻酸钠的混合溶液中，浸泡40-50分钟，进行改性处理；
(2)将步骤(1)所得改性的脱脂棉放入氯乙酸溶液中，在30℃下加热2小时，进行醚化反应；
(3)将步骤(2)所得脱脂棉放入浓度55％的氢氧化钾水溶液中，进行碱化反应；
(4)向步骤(3)经碱化反应后的溶液中，缓慢分次加入环氧乙烷，均匀搅拌7-8小时，使之充分反应；
(5)将浓度80％的乙醇加入步骤(4)所得溶液中，升高温度至50℃，均匀搅拌30-40分钟，再加入乙酸进行中和，使PH值调整为6-7；
(6)以浓度90％的乙醇洗涤步骤(5)所得脱脂棉，使脱脂棉中乙酸钠含量在1.5％以下，再将洗涤后的脱脂棉在70-80℃下进行烘干，即得到可溶化的止血棉。
如上所述的可溶化止血棉的制作方法，所述步骤(1)中丙酮和海藻酸钠所占的百分比分别为65％和35％。
采用上述可溶化止血棉的制作方法，步骤简便，所制作的止血棉遇血液能迅速吸收，膨胀溶解，形成薄膜覆盖于伤口上，不会造成粘连结痂，能起到迅速止血的良好功效。
具体实施方式
提供一种可溶化止血棉的制作方法，它包括如下步骤：
(1)将15公斤脱脂棉放入25升丙酮和海藻酸钠的混合溶液中，浸泡45分钟，进行改性处理；
(2)将步骤(1)所得改性的脱脂棉放入30升氯乙酸溶液中，在30℃下加热2小时，进行醚化反应；
(3)将步骤(2)所得脱脂棉放入20升浓度55％的氢氧化钾水溶液中，进行碱化反应；
(4)向步骤(3)经碱化反应后的溶液中，缓慢分次加入2公斤环氧乙烷，均匀搅拌7小时，使之充分反应；
(5)将12升浓度80％的乙醇加入步骤(4)所得溶液中，升高温度至50℃，均匀搅拌30分钟，再加入10升乙酸进行中和，使PH值调整为6；
(6)以5升浓度90％的乙醇洗涤步骤(5)所得脱脂棉，使脱脂棉中乙酸钠含量在1.5％以下，再将洗涤后的脱脂棉在70℃下进行烘干，即得到可溶化的止血棉，溶化时间可在25秒左右。
所述步骤(1)中丙酮和海藻酸钠所占的百分比分别为65％和35％。
上述实施例为本发明的优选实施例，凡与本发明类似的结构及所作的等效变化，均应属于本发明的保护范畴。

Claims (2)

1.一种可溶化止血棉的制作方法，其特征在于：它包括如下步骤：
(1)将脱脂棉放入丙酮和海藻酸钠的混合溶液中，浸泡40-50分钟，进行改性处理；
(2)将步骤(1)所得改性的脱脂棉放入氯乙酸溶液中，在30℃下加热2小时，进行醚化反应；
(3)将步骤(2)所得脱脂棉放入浓度55％的氢氧化钾水溶液中，进行碱化反应；
(4)向步骤(3)经碱化反应后的溶液中，缓慢分次加入环氧乙烷，均匀搅拌7-8小时，使之充分反应；
(5)将浓度80％的乙醇加入步骤(4)所得溶液中，升高温度至50℃，均匀搅拌30-40分钟，再加入乙酸进行中和，使pH值调整为6-7；
(6)以浓度90％的乙醇洗涤步骤(5)所得脱脂棉，使脱脂棉中乙酸钠含量在1.5％以下，再将洗涤后的脱脂棉在70-80℃下进行烘干，即得到可溶化的止血棉。
2.根据权利要求1所述的可溶化止血棉的制作方法，其特征在于：所述步骤(1)中丙酮和海藻酸钠所占的百分比分别为65％和35％。 
CN2011100221212A 2011-01-19 2011-01-19 可溶化止血棉的制作方法 Expired - Fee Related CN102108637B (zh)