CN102093710A - 一种抗紫外线抗疲劳耐磨pa66灌装包装设备叉瓶器专用料 - Google Patents
一种抗紫外线抗疲劳耐磨pa66灌装包装设备叉瓶器专用料 Download PDFInfo
- Publication number
- CN102093710A CN102093710A CN 201010606981 CN201010606981A CN102093710A CN 102093710 A CN102093710 A CN 102093710A CN 201010606981 CN201010606981 CN 201010606981 CN 201010606981 A CN201010606981 A CN 201010606981A CN 102093710 A CN102093710 A CN 102093710A
- Authority
- CN
- China
- Prior art keywords
- mass parts
- filling
- wear
- bottle device
- resisting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种抗紫外线抗疲劳耐磨PA66灌装包装设备叉瓶器专用料,其是由以下原料组成:60-80质量份的PA66、10-20质量份的PA6、4-10质量份的增韧剂、3-9质量份的相容剂、3-10质量份的高温润滑剂、2-15质量份的硫酸钙晶须、防老化复配助剂,其中,防老化复配助剂由0.2-1质量份的抗氧剂、0.2-1.5质量份的光稳定剂、0.2-2质量份的硅油组成,所述的高温润滑剂为石墨、二硫化钼、聚四氟乙烯中的至少一种。本发明的紫外线抗疲劳耐磨PA66灌装包装设备叉瓶器专用料的原料做成叉瓶器后,有较好的耐疲劳性能,耐磨性能也很好,同时较耐紫外线作用。
Description
技术领域
本发明涉及一种抗紫外线抗疲劳耐磨PA66灌装包装设备叉瓶器专用料。
背景技术
叉瓶机构在罐装或瓶装包装设备行业中应用广泛,当充填封口机的充填输送带将瓶输送到叉瓶机构处时,叉瓶机构的叉瓶臂合拢,将瓶叉住,然后再由夹瓶机构将瓶子夹住后将瓶输送走。
叉瓶机构在使用过程中,受到紫外线照射而老化,叉瓶臂可能由于频率性地扩张和收缩引起疲劳破坏,叉瓶口也可能因频率性接触造成磨损。目前的叉瓶器用料做成的叉瓶器不耐紫外线、不抗疲劳、不耐磨,使用寿命仅仅在30万次左右。
发明内容
本发明的目的是提供一种抗紫外线抗疲劳耐磨PA66灌装包装设备叉瓶器专用料。
本发明所采取的技术方案是:
一种抗紫外线抗疲劳耐磨PA66灌装包装设备叉瓶器专用料,其是由以下原料组成:防老化复配助剂、60-80质量份的PA66、10-20质量份的PA6、4-10质量份的增韧剂、3-9质量份的相容剂、3-10质量份的高温润滑剂、2-15质量份的硫酸钙晶须,其中,防老化复配助剂由0.2-1质量份的抗氧剂、0.2-1.5质量份的光稳定剂、0.3-2质量份的硅油组成,所述的高温润滑剂为石墨、二硫化钼、聚四氟乙烯中的至少一种。
所述的增韧剂为POE,相容剂为POE-g-MAH,或者增韧剂为EPDM,相容剂为EPDM-g-MAH。
所述的石墨的粒径为1000-5000目。
抗氧剂为1010、168、1076、242、1098中的至少一种。
光稳定剂为770、622、944、327、326中的至少一种。
本发明的有益效果是:本发明的紫外线抗疲劳耐磨PA66灌装包装设备叉瓶器专用料的原料做成叉瓶器后,有较好的耐疲劳性能,耐磨性能也很好,同时较耐紫外线作用。
具体实施方式
将所用组份加工为一种抗紫外线抗疲劳耐磨PA66灌装包装设备叉瓶器专用料的步骤:
1)将各原材料置于混合机中搅拌混合5-10min,获得混合物;
2)将混合物送入长径比为36-42的双螺杆挤出机, 240-280℃下熔融共混、挤出造粒。
下面结合具体的实施例对本发明做进一步的说明:
实施例1:
如表1是抗紫外线抗疲劳耐磨PA66灌装包装设备叉瓶器专用料的原料组成。
表1:紫外线抗疲劳耐磨PA66灌装包装设备叉瓶器专用料的原料组成
原料 | 质量份 |
PA66 | 67 |
PA6 | 20 |
POE | 8 |
POE-g-MAH | 9 |
聚四氟乙烯 | 3 |
硫酸钙晶须 | 2 |
抗氧剂1098 | 0.2 |
抗氧剂168 | 0.2 |
光稳定剂944 | 0.2 |
光稳定剂327 | 0.3 |
硅油 | 0.2 |
对原料做成的试件进行力学测试,得到其弯曲强度为60MPa,在1.5kg的负荷下,每分钟100转,摩擦轮转9000转的情况下,磨耗量为0.0078g,由这些原料做成的叉瓶器的可应用次数达82万次,远远超过一般的叉瓶器30万次的使用寿命。
经过氙灯加速老化1000h后,制品的拉伸强度保持率为88.2%。
实施例2:
如表2是抗紫外线抗疲劳耐磨PA66灌装包装设备叉瓶器专用料的原料组成。
表2:紫外线抗疲劳耐磨PA66灌装包装设备叉瓶器专用料的原料组成
原料 | 质量份 |
PA66 | 67 |
PA6 | 10 |
EPDM | 6 |
EPDM-g-MAH | 3 |
聚四氟乙烯 | 2 |
石墨(5000目) | 1 |
硫酸钙晶须 | 8 |
抗氧剂1098 | 0.2 |
抗氧剂1010 | 0.2 |
光稳定剂944 | 0.2 |
光稳定剂326 | 0.3 |
硅油 | 0.8 |
对原料做成的试件进行力学测试,得到其弯曲强度为66MPa,在1.5kg的负荷下,每分钟100转,摩擦轮转9000转的情况下,磨耗量为0.0018g,由这些原料做成的叉瓶器的可应用次数达105万次,远远超过一般的叉瓶器30万次的使用寿命。
经过氙灯加速老化1000h后,制品的拉伸强度保持率为86.9%。
实施例3:
如表3是抗紫外线抗疲劳耐磨PA66灌装包装设备叉瓶器专用料的原料组成。
表3:紫外线抗疲劳耐磨PA66灌装包装设备叉瓶器专用料的原料组成
原料 | 质量份 |
PA66 | 67 |
PA6 | 15 |
EPDM | 4 |
EPDM-g-MAH | 5 |
聚四氟乙烯 | 4 |
石墨(3000目) | 2 |
硫酸钙晶须 | 15 |
抗氧剂1098 | 0.2 |
抗氧剂1010 | 0.2 |
光稳定剂944 | 0.2 |
光稳定剂326 | 0.3 |
硅油 | 0.2 |
对原料做成的试件进行力学测试,得到其弯曲强度为86MPa,在1.5kg的负荷下,每分钟100转,摩擦轮转9000转的情况下,磨耗量为0.0045g,由这些原料做成的叉瓶器的可应用次数达89万次,远远超过一般的叉瓶器30万次的使用寿命。
经过氙灯加速老化1000h后,制品的拉伸强度保持率为89.3%。
实施例4:
如表4是抗紫外线抗疲劳耐磨PA66灌装包装设备叉瓶器专用料的原料组成。
表4:紫外线抗疲劳耐磨PA66灌装包装设备叉瓶器专用料的原料组成
原料 | 质量份 |
PA66 | 60 |
PA6 | 12 |
EPDM | 10 |
EPDM-g-MAH | 6 |
聚四氟乙烯 | 5 |
二硫化钼 | 3 |
硫酸钙晶须 | 10 |
抗氧剂1098 | 0.1 |
抗氧剂1010 | 0.1 |
光稳定剂770 | 0.3 |
光稳定剂622 | 0.7 |
硅油 | 2 |
对原料做成的试件进行力学测试,得到其弯曲强度为89MPa,在1.5kg的负荷下,每分钟100转,摩擦轮转9000转的情况下,磨耗量为0.0078g,由这些原料做成的叉瓶器的可应用次数达92万次,远远超过一般的叉瓶器30万次的使用寿命。
经过氙灯加速老化1000h后,制品的拉伸强度保持率为91.2%。
实施例5:
如表5是抗紫外线抗疲劳耐磨PA66灌装包装设备叉瓶器专用料的原料组成。
表5:紫外线抗疲劳耐磨PA66灌装包装设备叉瓶器专用料的原料组成
原料 | 质量份 |
PA66 | 80 |
PA6 | 18 |
EPDM | 7 |
EPDM-g-MAH | 8 |
聚四氟乙烯 | 5 |
二硫化钼 | 5 |
硫酸钙晶须 | 5 |
抗氧剂242 | 0.3 |
抗氧剂168 | 0.7 |
光稳定剂944 | 0.7 |
光稳定剂326 | 0.8 |
硅油 | 1.1 |
对原料做成的试件进行力学测试,得到其弯曲强度为75MPa,在1.5kg的负荷下,每分钟100转,摩擦轮转9000转的情况下,磨耗量为0.0045g,由这些原料做成的叉瓶器的可应用次数达96万次,远远超过一般的叉瓶器30万次的使用寿命。
经过氙灯加速老化1000h后,制品的拉伸强度保持率为85.7%。
实施例6:
如表6是抗紫外线抗疲劳耐磨PA66灌装包装设备叉瓶器专用料的原料组成。
表6:紫外线抗疲劳耐磨PA66灌装包装设备叉瓶器专用料的原料组成
原料 | 质量份 |
PA66 | 75 |
PA6 | 16 |
POE | 3 |
POE-g-MAH | 7 |
二硫化钼 | 3 |
石墨(1000目) | 3 |
硫酸钙晶须 | 6 |
抗氧剂242 | 0.4 |
抗氧剂1098 | 0.3 |
光稳定剂944 | 0.1 |
光稳定剂326 | 0.1 |
硅油 | 1.5 |
对原料做成的试件进行力学测试,得到其弯曲强度为68MPa,在1.5kg的负荷下,每分钟100转,摩擦轮转9000转的情况下,磨耗量为0.0036g,由这些原料做成的叉瓶器的可应用次数达90万次,远远超过一般的叉瓶器30万次的使用寿命。
经过氙灯加速老化1000h后,制品的拉伸强度保持率为91.4%。
从实施例1-6中可以看出,紫外线抗疲劳耐磨PA66灌装包装设备叉瓶器专用料的原料形成试件后,对其进行疲劳测试,其应用次数都可以达到90万次以上,耐疲劳性能较好,满足叉瓶器用料的要求,另外,在进行磨耗测试时,在1.5kg的负荷下,每分钟100转,摩擦轮转9000转的情况下,磨耗量均在0.0045g以下,其耐磨性能较好,另外,由本发明的原料做成的叉瓶器的使用次数均远远大于30万次,使用寿命长。其原料中添加了光稳定剂,因此所制得的产品较耐紫外线作用。
因此,本发明的专用料做成叉瓶器后,具有较好的耐疲劳性能,耐磨性能也很好,同时较耐紫外线作用。
Claims (5)
1.一种抗紫外线抗疲劳耐磨PA66灌装包装设备叉瓶器专用料,其特征在于:其是由以下原料组成:防老化复配助剂、60-80质量份的PA66、10-20质量份的PA6、4-10质量份的增韧剂、3-9质量份的相容剂、3-10质量份的高温润滑剂、2-15质量份的硫酸钙晶须,其中,防老化复配助剂由0.2-1质量份的抗氧剂、0.2-1.5质量份的光稳定剂、0.2-2质量份的硅油组成,所述的高温润滑剂为石墨、二硫化钼、聚四氟乙烯中的至少一种。
2.根据权利要求1所述的一种抗紫外线抗疲劳耐磨PA66灌装包装设备叉瓶器专用料,其特征在于:所述的增韧剂为POE,相容剂为POE-g-MAH,或者增韧剂为EPDM,相容剂为EPDM-g-MAH。
3.根据权利要求1所述的一种抗紫外线抗疲劳耐磨PA66灌装包装设备叉瓶器专用料,其特征在于:所述的石墨的粒径为1000-5000目。
4.根据权利要求1所述的一种抗紫外线抗疲劳耐磨PA66灌装包装设备叉瓶器专用料,其特征在于:抗氧剂为1010、168、1076、242、1098中的至少一种。
5.根据权利要求1所述的一种抗紫外线抗疲劳耐磨PA66灌装包装设备叉瓶器专用料,其特征在于:光稳定剂为770、622、944、327、326中的至少一种。