CN102093710B - 一种抗紫外线抗疲劳耐磨pa66灌装包装设备叉瓶器专用料 - Google Patents
一种抗紫外线抗疲劳耐磨pa66灌装包装设备叉瓶器专用料 Download PDFInfo
- Publication number
- CN102093710B CN102093710B CN2010106069816A CN201010606981A CN102093710B CN 102093710 B CN102093710 B CN 102093710B CN 2010106069816 A CN2010106069816 A CN 2010106069816A CN 201010606981 A CN201010606981 A CN 201010606981A CN 102093710 B CN102093710 B CN 102093710B
- Authority
- CN
- China
- Prior art keywords
- mass parts
- filling
- wear
- resisting
- bottle device
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种抗紫外线抗疲劳耐磨PA66灌装包装设备叉瓶器专用料，其是由以下原料组成：60-80质量份的PA66、10-20质量份的PA6、4-10质量份的增韧剂、3-9质量份的相容剂、3-10质量份的高温润滑剂、2-15质量份的硫酸钙晶须、防老化复配助剂，其中，防老化复配助剂由0.2-1质量份的抗氧剂、0.2-1.5质量份的光稳定剂、0.2-2质量份的硅油组成，所述的高温润滑剂为石墨、二硫化钼、聚四氟乙烯中的至少一种。本发明的紫外线抗疲劳耐磨PA66灌装包装设备叉瓶器专用料的原料做成叉瓶器后，有较好的耐疲劳性能，耐磨性能也很好，同时较耐紫外线作用。
Description
技术领域
本发明涉及一种抗紫外线抗疲劳耐磨PA66灌装包装设备叉瓶器专用料。
背景技术
叉瓶机构在罐装或瓶装包装设备行业中应用广泛，当充填封口机的充填输送带将瓶输送到叉瓶机构处时，叉瓶机构的叉瓶臂合拢，将瓶叉住，然后再由夹瓶机构将瓶子夹住后将瓶输送走。
叉瓶机构在使用过程中，受到紫外线照射而老化，叉瓶臂可能由于频率性地扩张和收缩引起疲劳破坏，叉瓶口也可能因频率性接触造成磨损。目前的叉瓶器用料做成的叉瓶器不耐紫外线、不抗疲劳、不耐磨，使用寿命仅仅在30万次左右。
发明内容
本发明的目的是提供一种抗紫外线抗疲劳耐磨PA66灌装包装设备叉瓶器专用料。
本发明所采取的技术方案是：
一种抗紫外线抗疲劳耐磨PA66灌装包装设备叉瓶器专用料，其是由以下原料组成：防老化复配助剂、60-80质量份的PA66、10-20质量份的PA6、4-10质量份的增韧剂、3-9质量份的相容剂、3-10质量份的高温润滑剂、2-15质量份的硫酸钙晶须，其中，防老化复配助剂由0.2-1质量份的抗氧剂、0.2-1.5质量份的光稳定剂、0.3-2质量份的硅油组成，所述的高温润滑剂为石墨、二硫化钼、聚四氟乙烯中的至少一种。
所述的增韧剂为POE，相容剂为POE-g-MAH，或者增韧剂为EPDM，相容剂为EPDM-g-MAH。
所述的石墨的粒径为1000-5000目。
抗氧剂为1010、168、1076、242、1098中的至少一种。
光稳定剂为770、622、944、327、326中的至少一种。
本发明的有益效果是：本发明的紫外线抗疲劳耐磨PA66灌装包装设备叉瓶器专用料的原料做成叉瓶器后，有较好的耐疲劳性能，耐磨性能也很好，同时较耐紫外线作用。
具体实施方式
将所用组份加工为一种抗紫外线抗疲劳耐磨PA66灌装包装设备叉瓶器专用料的步骤：
1）将各原材料置于混合机中搅拌混合5-10min，获得混合物；
2）将混合物送入长径比为36-42的双螺杆挤出机， 240-280℃下熔融共混、挤出造粒。
下面结合具体的实施例对本发明做进一步的说明：
实施例1：
如表1是抗紫外线抗疲劳耐磨PA66灌装包装设备叉瓶器专用料的原料组成。
表1：紫外线抗疲劳耐磨PA66灌装包装设备叉瓶器专用料的原料组成
| 原料 | 质量份 |
| PA66 | 67 |
| PA6 | 20 |
| POE | 8 |
| POE-g-MAH | 9 |
| 聚四氟乙烯 | 3 |
| 硫酸钙晶须 | 2 |
| 抗氧剂1098 | 0.2 |
| 抗氧剂168 | 0.2 |
| 光稳定剂944 | 0.2 |
| 光稳定剂327 | 0.3 |
| 硅油 | 0.2 |
对原料做成的试件进行力学测试，得到其弯曲强度为60MPa，在1.5kg的负荷下，每分钟100转，摩擦轮转9000转的情况下，磨耗量为0.0078g，由这些原料做成的叉瓶器的可应用次数达82万次，远远超过一般的叉瓶器30万次的使用寿命。
经过氙灯加速老化1000h后，制品的拉伸强度保持率为88.2%。
实施例2：
如表2是抗紫外线抗疲劳耐磨PA66灌装包装设备叉瓶器专用料的原料组成。
表2：紫外线抗疲劳耐磨PA66灌装包装设备叉瓶器专用料的原料组成
| 原料 | 质量份 |
| PA66 | 67 |
| PA6 | 10 |
| EPDM | 6 |
| EPDM-g-MAH | 3 |
| 聚四氟乙烯 | 2 |
| 石墨（5000目） | 1 |
| 硫酸钙晶须 | 8 |
| 抗氧剂1098 | 0.2 |
| 抗氧剂1010 | 0.2 |
| 光稳定剂944 | 0.2 |
| 光稳定剂326 | 0.3 |
| 硅油 | 0.8 |
对原料做成的试件进行力学测试，得到其弯曲强度为66MPa，在1.5kg的负荷下，每分钟100转，摩擦轮转9000转的情况下，磨耗量为0.0018g，由这些原料做成的叉瓶器的可应用次数达105万次，远远超过一般的叉瓶器30万次的使用寿命。
经过氙灯加速老化1000h后，制品的拉伸强度保持率为86.9%。
实施例3：
如表3是抗紫外线抗疲劳耐磨PA66灌装包装设备叉瓶器专用料的原料组成。
表3：紫外线抗疲劳耐磨PA66灌装包装设备叉瓶器专用料的原料组成
| 原料 | 质量份 |
| PA66 | 67 |
| PA6 | 15 |
| EPDM | 4 |
| EPDM-g-MAH | 5 |
| 聚四氟乙烯 | 4 |
| 石墨（3000目） | 2 |
| 硫酸钙晶须 | 15 |
| 抗氧剂1098 | 0.2 |
| 抗氧剂1010 | 0.2 |
| 光稳定剂944 | 0.2 |
| 光稳定剂326 | 0.3 |
| 硅油 | 0.2 |
对原料做成的试件进行力学测试，得到其弯曲强度为86MPa，在1.5kg的负荷下，每分钟100转，摩擦轮转9000转的情况下，磨耗量为0.0045g，由这些原料做成的叉瓶器的可应用次数达89万次，远远超过一般的叉瓶器30万次的使用寿命。
经过氙灯加速老化1000h后，制品的拉伸强度保持率为89.3%。
实施例4：
如表4是抗紫外线抗疲劳耐磨PA66灌装包装设备叉瓶器专用料的原料组成。
表4：紫外线抗疲劳耐磨PA66灌装包装设备叉瓶器专用料的原料组成
| 原料 | 质量份 |
| PA66 | 60 |
| PA6 | 12 |
| EPDM | 10 |
| EPDM-g-MAH | 6 |
| 聚四氟乙烯 | 5 |
| 二硫化钼 | 3 |
| 硫酸钙晶须 | 10 |
| 抗氧剂1098 | 0.1 |
| 抗氧剂1010 | 0.1 |
| 光稳定剂770 | 0.3 |
| 光稳定剂622 | 0.7 |
| 硅油 | 2 |
对原料做成的试件进行力学测试，得到其弯曲强度为89MPa，在1.5kg的负荷下，每分钟100转，摩擦轮转9000转的情况下，磨耗量为0.0078g，由这些原料做成的叉瓶器的可应用次数达92万次，远远超过一般的叉瓶器30万次的使用寿命。
经过氙灯加速老化1000h后，制品的拉伸强度保持率为91.2%。
实施例5：
如表5是抗紫外线抗疲劳耐磨PA66灌装包装设备叉瓶器专用料的原料组成。
表5：紫外线抗疲劳耐磨PA66灌装包装设备叉瓶器专用料的原料组成
| 原料 | 质量份 |
| PA66 | 80 |
| PA6 | 18 |
| EPDM | 7 |
| EPDM-g-MAH | 8 |
| 聚四氟乙烯 | 5 |
| 二硫化钼 | 5 |
| 硫酸钙晶须 | 5 |
| 抗氧剂242 | 0.3 |
| 抗氧剂168 | 0.7 |
| 光稳定剂944 | 0.7 |
| 光稳定剂326 | 0.8 |
| 硅油 | 1.1 |
对原料做成的试件进行力学测试，得到其弯曲强度为75MPa，在1.5kg的负荷下，每分钟100转，摩擦轮转9000转的情况下，磨耗量为0.0045g，由这些原料做成的叉瓶器的可应用次数达96万次，远远超过一般的叉瓶器30万次的使用寿命。
经过氙灯加速老化1000h后，制品的拉伸强度保持率为85.7%。
实施例6：
如表6是抗紫外线抗疲劳耐磨PA66灌装包装设备叉瓶器专用料的原料组成。
表6：紫外线抗疲劳耐磨PA66灌装包装设备叉瓶器专用料的原料组成
| 原料 | 质量份 |
| PA66 | 75 |
| PA6 | 16 |
| POE | 3 |
| POE-g-MAH | 7 |
| 二硫化钼 | 3 |
| 石墨（1000目） | 3 |
| 硫酸钙晶须 | 6 |
| 抗氧剂242 | 0.4 |
| 抗氧剂1098 | 0.3 |
| 光稳定剂944 | 0.1 |
| 光稳定剂326 | 0.1 |
| 硅油 | 1.5 |
对原料做成的试件进行力学测试，得到其弯曲强度为68MPa，在1.5kg的负荷下，每分钟100转，摩擦轮转9000转的情况下，磨耗量为0.0036g，由这些原料做成的叉瓶器的可应用次数达90万次，远远超过一般的叉瓶器30万次的使用寿命。
经过氙灯加速老化1000h后，制品的拉伸强度保持率为91.4%。
从实施例1-6中可以看出，紫外线抗疲劳耐磨PA66灌装包装设备叉瓶器专用料的原料形成试件后，对其进行疲劳测试，其应用次数都可以达到90万次以上，耐疲劳性能较好，满足叉瓶器用料的要求，另外，在进行磨耗测试时，在1.5kg的负荷下，每分钟100转，摩擦轮转9000转的情况下，磨耗量均在0.0045g以下，其耐磨性能较好，另外，由本发明的原料做成的叉瓶器的使用次数均远远大于30万次，使用寿命长。其原料中添加了光稳定剂，因此所制得的产品较耐紫外线作用。
因此，本发明的专用料做成叉瓶器后，具有较好的耐疲劳性能，耐磨性能也很好，同时较耐紫外线作用。
Claims (5)
1.一种抗紫外线抗疲劳耐磨PA66灌装包装设备叉瓶器专用料，其特征在于：其是由以下原料组成：防老化复配助剂、60-80质量份的PA66、10-20质量份的PA6、4-10质量份的增韧剂、3-9质量份的相容剂、3-10质量份的高温润滑剂、2-15质量份的硫酸钙晶须，其中，防老化复配助剂由0.2-1质量份的抗氧剂、0.2-1.5质量份的光稳定剂、0.2-2质量份的硅油组成，所述的高温润滑剂为石墨、二硫化钼、聚四氟乙烯中的至少一种。
2.根据权利要求1所述的一种抗紫外线抗疲劳耐磨PA66灌装包装设备叉瓶器专用料，其特征在于：所述的增韧剂为POE，相容剂为POE-g-MAH，或者增韧剂为EPDM，相容剂为EPDM-g-MAH。
3.根据权利要求1所述的一种抗紫外线抗疲劳耐磨PA66灌装包装设备叉瓶器专用料，其特征在于：所述的石墨的粒径为1000-5000目。
4.根据权利要求1所述的一种抗紫外线抗疲劳耐磨PA66灌装包装设备叉瓶器专用料，其特征在于：抗氧剂为1010、168、1076、242、1098中的至少一种。
5.根据权利要求1所述的一种抗紫外线抗疲劳耐磨PA66灌装包装设备叉瓶器专用料，其特征在于：光稳定剂为770、622、944、327、326中的至少一种。