CN102091658A - 一种防粉尘粘附的包裹脱硝催化球及其制备方法 - Google Patents
一种防粉尘粘附的包裹脱硝催化球及其制备方法 Download PDFInfo
- Publication number
- CN102091658A CN102091658A CN 201010606666 CN201010606666A CN102091658A CN 102091658 A CN102091658 A CN 102091658A CN 201010606666 CN201010606666 CN 201010606666 CN 201010606666 A CN201010606666 A CN 201010606666A CN 102091658 A CN102091658 A CN 102091658A
- Authority
- CN
- China
- Prior art keywords
- catalyst
- ball
- shell
- denitration
- parcel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种防粉尘粘附的包裹脱硝催化球及其制备方法,属于脱销催化技术领域。所述催化球为核-壳结构,外壳为聚四氟乙烯,外壳上设有均匀的贯通孔,用活性炭为载体的MnO2-X-CeO2基脱销催化剂为填充物。制备方法是先制备聚四氟乙烯外壳半球,在半球上打孔,将用活性炭为载体的MnO2-X-CeO2基脱销催化剂装入半球并热压焊接法形成一个整体圆球,从而制成包裹脱硝催化球。本发明防止了粉尘对催化剂的粘附,使催化剂更大程度、更长时间的发挥着效用。
Description
技术领域
本发明涉及一种防粉尘粘附的包裹脱硝催化球及其制备方法,属于脱销催化技术领域。
背景技术
氮氧化物(NOx)是主要的大气污染物,主要包括NO、NO2、N2O等,可以引起酸雨、光化学烟雾、温室效应及臭氧层的破坏。减少NOx排放有燃烧过程控制和燃烧后烟气脱硝2条途径。在现有烟气脱硝工艺中,选择性催化还原(SCR,Selective Catalytic Reduction)脱硝又是其主流工艺。催化剂在该工艺中起着决定性作用,是SCR技术的关键,其活性对脱硝装置的正常运行至关重要。同时,SCR装置的运行成本在很大程度上也取决于催化剂的寿命。催化剂的利用有不同结构形式,蜂窝状结构就是用得很普遍的一种。虽然它有着比表面积高的优点,但它在用于水泥厂等飞灰较大的环境下,由于SCR反应器布置在除尘器之前,大量飞灰的存在不仅容易堵塞催化剂引起催化剂物理活性破坏,而且也能使催化剂化学性中毒。从而给催化剂的应用增加了难度。
发明内容
本发明的目的是克服现有SCR工艺中催化剂易被飞灰堵塞及引起中毒的缺点,提供一种使催化剂不粘附或极少粘附飞灰的催化球及其制备方法。
本发明制备的防粉尘粘附的包裹脱硝催化球,其特征在于,总体结构是核-壳结构,以聚四氟乙烯为外壳,外壳上设有均匀的贯通孔,以用活性炭为载体的MnO2-X-CeO2(X=0~0.5)基脱销催化剂为填充物。
上述圆球外壳内径为8-10mm,壳壁厚度为1-1.5mm;贯通孔孔径尺寸为0.3-0.5mm;载有催化剂的填充物颗粒度为1-3mm,重量为0.1-0.2克。
本发明催化球的制备方法如包括以下步骤:用分散状聚四氟乙烯模压成半圆球壳坯体,再在350℃下烧结成型,之后用打孔机在球壳上打出均匀的贯通孔。然后在一半球内装入载有催化剂的颗粒活性炭填充物,最后将二个半球通过热压焊接法形成一个整体圆球,从而制成包裹脱硝催化球。
本发明的优点:
本发明制备的防粉尘粘附的包裹脱硝催化球,其优点在于,用包裹式的方式来利用催化剂。这防止了粉尘对催化剂的粘附,使催化剂更大程度、更长时间的发挥着效用。这不仅降低了SCR工艺的成本,还更加有效的达到了脱硝的目的。
附图说明
图1本发明制备的防粉尘粘附的包裹脱硝催化球的结构示意图1为带孔的聚四氟乙烯外壳,2为贯通孔,3为载有催化剂的活性炭颗粒填充物
具体实施方式
实例1
以带孔的聚四氟乙烯为外壳,以用活性炭为载体的MnO2-CeO2基脱销催化剂为填充物。用分散状聚四氟乙烯模压成内径为8mm、壳壁厚度为1mm的半圆球壳坯体,再在350℃下烧结成半圆球外壳,之后用打孔机在其上打出均匀的孔径为0.3mm的贯通孔。然后在一半球内装入载有催化剂的颗粒度为1mm的颗粒活性炭0.1克,最后将二个半球通过热压焊接法形成一个整体圆球,从而制成包裹脱硝催化剂。
实例2
以带孔的聚四氟乙烯为外壳,以用活性炭为载体的MnO1.7-CeO2基脱销催化剂为填充物。用分散状聚四氟乙烯模压成内径为10mm、壳壁厚度为1.5mm的半圆球壳坯体,再在350℃下烧结成半圆球外壳,之后用打孔机在其上打出均匀的孔径为0.5mm的贯通孔。然后在一半球内装入载有催化剂的颗粒度为3mm的颗粒活性炭0.2克,最后将二个半球通过热压焊接法形成一个整体圆球,从而制成包裹脱硝催化剂。
实例3
以带孔的聚四氟乙烯为外壳,以用活性炭为载体的MnO1.5-CeO2基脱销催化剂为填充物。用分散状聚四氟乙烯模压成内径为10mm、壳壁厚度为1.3mm的半圆球壳坯体,再在350℃下烧结成半圆球外壳,之后用打孔机在其上打出均匀的孔径为0.4mm的贯通孔。然后在一半球内装入载有催化剂的颗粒度为2mm的颗粒活性炭0.15克,最后将二个半球通过热压焊接法形成一个整体圆球,从而制成包裹脱硝催化剂。
Claims (3)
1.一种防粉尘粘附的包裹脱硝催化球,其特征在于,总体结构是核-壳结构,以聚四氟乙烯为外壳,外壳上设有均匀的贯通孔,以用活性炭为载体的MnO2-X-CeO2基脱销催化剂为填充物,其中X=0~0.5。
2.按照权利要求1的防粉尘粘附的包裹脱硝催化球,其特征在于,圆球外壳内径为8-10mm,壳壁厚度为1-1.5mm,贯通孔孔径尺寸为0.3-0.5mm;载有催化剂的填充物颗粒度为1-3mm,重量为0.1-0.2克。
3.按照权利要求1的防粉尘粘附的包裹脱硝催化球的制备方法,其特征在于,包括以下步骤:用分散状聚四氟乙烯模压成半圆球壳坯体,再在350℃下烧结成型,之后用打孔机在球壳上打出均匀的贯通孔,然后在一半球内装入载有催化剂的颗粒活性炭填充物,最后将二个半球通过热压焊接法形成一个整体圆球,从而制成包裹脱硝催化球。