CN102086126A - 一种不烧镁暖气砖及其生产方法 - Google Patents

一种不烧镁暖气砖及其生产方法 Download PDF

Info

Publication number
CN102086126A
CN102086126A CN 201010562075 CN201010562075A CN102086126A CN 102086126 A CN102086126 A CN 102086126A CN 201010562075 CN201010562075 CN 201010562075 CN 201010562075 A CN201010562075 A CN 201010562075A CN 102086126 A CN102086126 A CN 102086126A
Authority
CN
China
Prior art keywords
heat
hour
brick
magnesia
fragmentation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 201010562075
Other languages
English (en)
Other versions
CN102086126B (zh
Inventor
金昭珍
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI XIAO COUNTY HUALONG REFRACTORY MATERIAL Co Ltd
Original Assignee
ANHUI XIAO COUNTY HUALONG REFRACTORY MATERIAL Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI XIAO COUNTY HUALONG REFRACTORY MATERIAL Co Ltd filed Critical ANHUI XIAO COUNTY HUALONG REFRACTORY MATERIAL Co Ltd
Priority to CN 201010562075 priority Critical patent/CN102086126B/zh
Publication of CN102086126A publication Critical patent/CN102086126A/zh
Application granted granted Critical
Publication of CN102086126B publication Critical patent/CN102086126B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明提供了一种镁暖气砖，其组成原料各组分的重量百分比为：电熔镁砂40-50％、烧结镁砂40-50％、硅微粉2-4％、高龄土4-6％、结合剂1-3％。生产时将块状原材料粉碎过筛后，与粉状材料混合，再加入结合剂混炼后，压力成型，再送入干燥窑干燥，干燥后经磨制、检验合格后，包装、入库即可。本发明材料安装在电暖器设备里能起到吸热快、蓄热时间长、放热慢，从而达到不仅取暖效果好，而且节约能源的效果。

Description

一种不烧镁暖气砖及其生产方法
技术领域
本发明涉及耐火材料的生产加工领域，具体涉及一种不烧镁暖气砖及其生产方法。
背景技术
中国国内冬天大部分地区比较寒冷，供暖大部分使用煤气，供暖时间短而且费用高。现在的暖气设备里通常安装有烧镁砖作为蓄热、放热材料，而烧镁砖的生产周期长，成本高，烧镁砖密度大，重量重，烧制温度高，环境污染严重。
发明内容
本发明提供一种不烧镁暖气砖及其生产方法，电暖器设备里安装有本发明的镁暖气砖，能起到吸热快、蓄热时间长、放热慢，从而达到不仅取暖效果好，而且节约能源的目的。
本发明采用的技术方案如下：
一种镁暖气砖，其特征在于：其组成原料各组分的重量百分比为：
电熔镁砂40-50％
烧结镁砂40-50％
硅微粉  2-4％
高龄土  4-6％
结合剂  1-3％。
所述的镁暖气砖的生产方法，其特征在于：具体包括以下步骤：
(1)将块状的物料破碎；
(2)将破碎后的颗粒过振动筛，要求颗粒粒径小于5mm，大的颗粒返回继续破碎过筛；
(3)将破碎后75-80％的镁砂粉料作为骨料先投入混炼机里，然后将结合剂投入其中预混处理2-4分钟；
(4)将余下的镁砂粉料与硅微粉混合均匀，再将混合料投入步骤(3)的混合料里继续混炼处理30-40分钟；
(4)将步骤(4)混炼后的混合料压力成型，压强为0.2-0.4MP；
(5)将压力成型的镁砖送入干燥窑里，进行分段干燥；
(6)将干燥后的镁砖进行磨制，检验，包装。
所述的镁暖气砖的生产方法，其特征在于：所述的分段干燥具体要求为：
第一段为：常温-80℃，升温速度为15-25℃/小时，当温度升到80℃时，停止升温，保温5-12个小时；
第二段为：80-150℃，升温速度为25-50℃/小时，当温度升到150℃时，停止升温，保温5-12个小时；
第三段为：；150-250℃，度升温速度为25-50℃/小时，当温度升到250℃时，停止升温，保温5-12个小时。
本发明的有益效果：
1、本发明的镁暖气砖含有丰富的氧化镁，在电暖器设备里起到吸热、蓄热、放热的作用。且吸热快、放热时间长，从而达到取暖、保温的效果；
2、本发明的镁暖气砖加工时采用电加热，不需要高温烧制，因此加工费用低，不产生废渣，不污染环境，起到环保、节能的效果；
3、本发明的镁暖气砖使用温度在700℃左右，所以烘烤处理后在250度以下的低温区域使用，物理性能能保持良好的功效，因此镁砖的使用寿命长，节约了社会资源。
附图说明
图1为本发明的镁暖气砖加工时的工艺流程图。
具体实施方式
一种镁暖气砖，其特征在于：其组成原料各组分的重量百分比为：
电熔镁砂40-50％
烧结镁砂40-50％
硅微粉  2-4％
高龄土  4-6％
结合剂  1-3％。
所述的镁暖气砖的生产方法，其特征在于：具体包括以下步骤：
(1)将块状的物料破碎；
(2)将破碎后的颗粒过振动筛，要求颗粒粒径小于5mm，大的颗粒返回继续破碎过筛；
(3)将破碎后75-80％的镁砂粉料作为骨料先投入混炼机里，然后将结合剂投入其中预混处理2-4分钟；
(4)将余下的镁砂粉料与硅微粉混合均匀，再将混合料投入步骤(3)的混合料里继续混炼处理30-40分钟；
(4)将步骤(4)混炼后的混合料压力成型，压强为0.2-0.4MP；
(5)将压力成型的镁砖送入干燥窑里，进行分段干燥；
(6)将干燥后的镁砖进行磨制，检验，包装。
所述的镁暖气砖的生产方法，其特征在于：所述的分段干燥具体要求为：
第一段为：常温-80℃，升温速度为15-25℃/小时，当温度升到80℃时，停止升温，保温5-12个小时；
第二段为：80-150℃，升温速度为25-50℃/小时，当温度升到150℃时，停止升温，保温5-12个小时；
第三段为：；150-250℃，度升温速度为25-50℃/小时，当温度升到250℃时，停止升温，保温5-12个小时。

Claims (3)

1.一种镁暖气砖，其特征在于：其组成原料各组分的重量百分比为：
电熔镁砂  40-50％
烧结镁砂  40-50％
硅微粉    2-4％
高龄土    4-6％
结合剂    1-3％，
所述的结合剂为酚醛树脂。
2.如权利要求1所述的镁暖气砖的生产方法，其特征在于：具体包括以下步骤：
(1)将块状的物料破碎；
(2)将破碎后的颗粒过振动筛，要求颗粒粒径小于5mm，大的颗粒返回继续破碎过筛；
(3)将破碎后75-80％的镁砂粉料作为骨料先投入混炼机里，然后将结合剂投入其中预混处理2-4分钟；
(4)将余下的镁砂粉料与硅微粉混合均匀，再将混合料投入步骤(3)的混合料里继续混炼处理30-40分钟；
(5)将步骤(4)混炼后的混合料压力成型，压强为0.2-0.4MP；
(6)将压力成型的镁砖送入干燥窑里，进行分段干燥；
(7)将干燥后的镁砖进行磨制，检验，包装。
3.根据权利要求2所述的镁暖气砖的生产方法，其特征在于：所述的分段干燥具体要求为：
第一段为：常温-80℃，升温速度为15-25℃/小时，当温度升到80℃时，停止升温，保温5-12个小时；
第二段为：80-150℃，升温速度为25-50℃/小时，当温度升到150℃时，停止升温，保温5-12个小时；
第三段为：；150-250℃，度升温速度为25-50℃/小时，当温度升到250℃时，停止升温，保温5-12个小时。
CN 201010562075 2010-11-26 2010-11-26 一种不烧镁暖气砖及其生产方法 Active CN102086126B (zh)