CN1316399A - 蓄热砖 - Google Patents

蓄热砖 Download PDF

Info

Publication number
CN1316399A
CN1316399A CN 01114005 CN01114005A CN1316399A CN 1316399 A CN1316399 A CN 1316399A CN 01114005 CN01114005 CN 01114005 CN 01114005 A CN01114005 A CN 01114005A CN 1316399 A CN1316399 A CN 1316399A
Authority
CN
China
Prior art keywords
oxide
proportioning
dioxide
silicon
starting material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 01114005
Other languages
English (en)
Other versions
CN1131184C (zh
Inventor
易继先
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN 01114005 priority Critical patent/CN1131184C/zh
Publication of CN1316399A publication Critical patent/CN1316399A/zh
Application granted granted Critical
Publication of CN1131184C publication Critical patent/CN1131184C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

本发明公开了一种蓄热砖，其是由氧化镁、三氧化二铁、三氧化二铝、二氧化硅、氧化钙材料烧结而成，其配比(重量%)为氧化镁86－90；三氧化二铁7－9；三氧化二铝0.2－1.0；二氧化硅为1－2；氧化钙为1－5。该蓄热砖热传导及蓄热效果好，耐高温可达1600－1700℃。

Description

蓄热砖
本发明涉及一种烧结材料，特别涉及一种蓄热砖。
随着科技的发展及人们生活的提高，各种家用电器在家庭等生活居家内逐渐普及，其中电暖气就是其中一种，目前，世界上有的国家和地区，特别是中国也正在实行分时电价制度，因此，用电量大的电暖气如果能在低谷电价时蓄热，在需要时释放热量，就能使用户节省电费，但是，现在还没有一种蓄热效果特别好的核心材料做为电暖气的蓄热体，因此，开发该种材料就成为当务之急。
本发明的目的是提供一种蓄热及热传导效果好、耐高温的蓄热砖。
为达上述目的，本发明采用以下技术方案：
本发明是由氧化镁、三氧化二铁、三氧化二铝、二氧化硅、氧化钙烧结而成，其配比如下：
原材料名称        配比(重量％)
氧化镁(MgO)          86～90
三氧化二铁(Fe2O3)  7～9
三氧化二铝(Al2O3)  0.2～1.0
二氧化硅(SiO2)      1～2
氧化钙(CaO)          1～5
上述配比烧结而成的蓄热砖，其各种参数为：密度：2.8～2.9Kg/cm3；显气孔率：18-22％；强度大于40MPa；传导系数：600℃时为5.3W/mk,1200℃时为3.1W/mk；耐高温值为1600～1700℃。
本发明的实施例1：
原材料名称        配比(重量％)
氧化镁(MgO)          87
三氧化二铁(Fe2O3)  7.6
三氧化二铝(Al2O3)  0.9
二氧化硅(SiO2)      2
氧化钙(CaO)          2.5
实施例2：
原材料名称    配比(重量％)
氧化镁(MgO)          90
三氧化二铁(Fe2O3)  7
三氧化二铝(Al2O3)  0.5
二氧化硅(SiO2)      1.5
氧化钙(CaO)          1
实施例3：
原材料名称       配比(重量％)
氧化镁(MgO)          86
三氧化二铁(Fe2O3)  9
三氧化二铝(Al2O3)  1.0
二氧化硅(SiO2)      1
氧化钙(CaO)          3
实施例4：
原材料名称       配比(重量％)
氧化镁(MgO)          86
三氧化二铁(Fe2O3)  7.8
三氧化二铝(Al2O3)  0.2
二氧化硅(SiO2)      1
氧化钙(CaO)          5
上述各配比的原材料烧结的蓄热砖，耐高温，而且因为主要成份为金属的氧化物，因此，蓄热效果好，在实际用于电暖气的试验中，所显示的蓄热效果也比较好。

Claims (5)

1、一种蓄热砖，其组份与配比如下：
原材料名称            配比(重量％)
氧化镁(MgO)             86-90
三氧化二铁(Fe2O3)     7-9
三氧化二铝(Al2O3)     0.2-1
二氧化硅(SiO2)         1-2
氧化钙(CaO)             1-5
2、按照权利要求1所述的一种蓄热砖，其组份与配比如下：
原材料名称            配比(重量％)
氧化镁(MgO)             87
三氧化二铁(Fe2O3)     7.6
三氧化二铝(Al2O3)     0.9
二氧化硅(SiO2)         2
氧化钙(CaO)             2.5
3、按照权利要求1所述的一种蓄热砖，其组份与配比如下：
原材料名称            配比(重量％)
氧化镁(MgO)             90
三氧化二铁(Fe2O3)     7
三氧化二铝(Al2O3)     0.5
二氧化硅(SiO2)         1.5
氧化钙(CaO)             1
4、按照权利要求1所述的一种蓄热砖，其组份与配比如下：
原材料名称            配比(重量％)
氧化镁(MgO)             86
三氧化二铁(Fe2O3)     9
三氧化二铝(Al2O3)     1
二氧化硅(SiO2)         1
氧化钙(CaO)             3
5、按照权利要求1所述的一种蓄热砖，其组份与配比如下：
原材料名称            配比(重量％)
氧化镁(MgO)             86
三氧化二铁(Fe2O3)     7.8
三氧化二铝(Al2O3)     0.2
二氧化硅(SiO2)         1
氧化钙(CaO)             5
CN 01114005 2001-05-26 2001-05-26 蓄热砖 Expired - Fee Related CN1131184C (zh)