CN101429007B - 制作煤矸石烧结砖的方法 - Google Patents
制作煤矸石烧结砖的方法 Download PDFInfo
- Publication number
- CN101429007B CN101429007B CN2008101632037A CN200810163203A CN101429007B CN 101429007 B CN101429007 B CN 101429007B CN 2008101632037 A CN2008101632037 A CN 2008101632037A CN 200810163203 A CN200810163203 A CN 200810163203A CN 101429007 B CN101429007 B CN 101429007B
- Authority
- CN
- China
- Prior art keywords
- coal gangue
- brick
- account
- raw material
- roasting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种制作煤矸石烧结砖的方法，包括以下步骤：a、利用锤式破碎机对煤矸石原料进行破碎，然后用滚筒筛进行颗粒筛分处理，使得到的原料颗粒大小在2mm以下，其中2mm-50μm的占25％，50μm-5μm的占55％，小于5μm的占20％，然后所得原料经搅拌机加水搅拌；b、把搅拌好的原料输入陈化库陈化；c、经陈化完的原料输入真空挤出机挤出成型；d、把成型得到的坯体码放入干燥窑中干燥；e、将干燥好的坯体放入焙烧窑中焙烧。本发明由于采用高细破碎和陈化技术，提高坯料塑性；制坯采用高压真空挤出成型，提高砖坯密实度，优化空心砖的孔型和孔洞排布，进一步提高孔洞率，降低了砖内部传热，提高了砖的保温性能。
Description
技术领域
本发明涉及一种制砖方法，具体说是一种利用废弃煤矸石制作建筑用烧结砖的方法。
背景技术
我国正大力推广墙体材料改革，以煤矸石烧结多孔砖、烧结空心砖、工业废渣砖等新型墙体材料代替粘土实心砖。使用以废弃煤矸石为原料的烧结多孔砖、烧结空心砖可使建筑物自重减轻1/3左右，节省燃料30％～40％，且烧成率高，造价降低20％，施工效率提高40％，并能改善砖的绝热和隔声性能。
目前制作煤矸石烧结砖要经过破碎、搅拌、制坯、焙烧等工序。中国发明专利申请公开说明书CN1311087A公开了一种煤矸石砖的制作方法，采用该方法制成的砖的孔洞率在20％-30％之间，砖的孔洞率低，导致砖内部传热影响了砖的保温性能，同时其表观密度大，抗压强度低，从而影响采用这种砖的建筑墙体的综合性能。
发明内容
本发明所要解决的技术问题是提供一种更有效地优化煤矸石烧结砖性能的制作方法。
为解决上述技术问题，本发明采用如下技术方案：制作煤矸石烧结砖的方法，包括以下步骤：
a、利用锤式破碎机对煤矸石原料进行破碎，然后用滚筒筛进行颗粒筛分处理，使得到的原料颗粒大小在2mm以下，其中2mm-50μm的占25％，50μm-5μm的占55％，小于5μm的占20％，然后所得原料经搅拌机加水搅拌；
b、把搅拌好的原料输入陈化库陈化；
c、经陈化完的原料输入真空挤出机挤出成型；
d、把成型得到的坯体码放入干燥窑中干燥；
e、将干燥好的坯体放入焙烧窑中焙烧。
步骤a中加水搅拌后物料含水率控制在13％-15％之间。
步骤b中陈化时间大于72小时，以提高原料的综合性能。
步骤c中成型含水率控制在15％-17％之间。
步骤d中干燥周期为21.3小时，干燥残余水分小于3％。
步骤e中焙烧温度在960-1050℃之间，烧结后空心砖的抗压强度达到MU5.0以上。
进一步的，对焙烧好的砖孔内塞复合绝热材料，可以进一步提高保温性能，可使采用该产品的砖墙砌体的传热系数小于1.20w/(m2k)，(当量)导热系数达到0.377w/(mk)。
本发明由于采用了上述技术方案，采用高细破碎和陈化技术，提高坯料塑性；制坯采用高压真空挤出成型，提高砖坯密实度，优化空心砖的孔型和孔洞排布，进一步提高孔洞率，降低了砖内部传热，提高了砖的保温性能，使建筑彻体节能指标符合建筑节能要求。
采用该方法制成的煤矸石多孔砖孔率从目前的25％提高到36％，表观密度从1400kg/m3下降到1210kg/m3，抗压强度从10MPa增长到15MPa。煤矸石空心砖孔率从目前的40％提高到50％，表观密度从1100kg/m3下降到900kg/m3，抗压强度从3.5MPa增长到5.0MPa。
具体实施方式
制作煤矸石烧结砖的方法，包括以下步骤：
a、利用锤式破碎机对煤矸石原料进行破碎，然后用滚筒筛进行颗粒筛分处理，使得到的原料颗粒大小在2mm以下，其中2mm-50μm的占25％，50μm-5μm的占55％，小于5μm的占20％，然后经搅拌机加水搅拌，加水搅拌后物料含水率控制在13％-15％之间；
b、把搅拌好的原料输入陈化库陈化，陈化时间大于72小时；
c、经陈化完的原料输入真空挤出机挤出成型，成型含水率控制在15％-17％之间，成型得到的湿坯体抗压强度达到21.7kg/cm2，砖的孔洞率大于40％；
d、把成型得到的坯体码放入干燥窑中干燥，干燥周期为21.3小时，干燥残余水分小于3％；
e、将干燥好的坯体放入焙烧窑中焙烧，焙烧温度在960-1050℃之间，焙烧时间为30～40小时。
焙烧好的砖出窑后，再对砖采取孔内塞复合绝热材料等措施，可以进一步提高保温性能，可使采用该产品的砖墙砌体的传热系数达到1.185w/(m2k)，(当量)导热系数达到0.377w/(mk)。
Claims (9)
1.制作煤矸石烧结砖的方法，包括以下步骤：
a、利用锤式破碎机对煤矸石原料进行破碎，然后用滚筒筛进行颗粒筛分处理，使得到的原料颗粒大小在2mm以下，其中小于等于2mm且大于等于50μm的占25％，小于50μm且大于等于5μm的占55％，小于5μm的占20％，然后经搅拌机加水搅拌；
b、把搅拌好的原料输入陈化库陈化；
c、经陈化完的原料输入真空挤出机挤出成型；
d、把成型得到的坯体码放入干燥窑中干燥；
e、将干燥好的坯体放入焙烧窑中焙烧。
2.制作煤矸石烧结砖的方法，包括以下步骤：
a、利用锤式破碎机对煤矸石原料进行破碎，然后用滚筒筛进行颗粒筛分处理，使得到的原料颗粒大小在2mm以下，其中小于等于2mm且大于50μm的占25％，小于等于50μm且大于等于5μm的占55％，小于5μm的占20％，然后经搅拌机加水搅拌；
b、把搅拌好的原料输入陈化库陈化；
c、经陈化完的原料输入真空挤出机挤出成型；
d、把成型得到的坯体码放入干燥窑中干燥；
e、将干燥好的坯体放入焙烧窑中焙烧。
3.根据权利要求1或2所述制作煤矸石烧结砖的方法，其特征在于：步骤a中加水搅拌后物料含水率控制在13％-15％之间。
4.根据权利要求1或2所述制作煤矸石烧结砖的方法，其特征在于：步骤b中陈化时间大于72小时。
5.根据权利要求1或2所述制作煤矸石烧结砖的方法，其特征在于：步骤c中成型含水率控制在15％-17％之间。
6.根据权利要求1或2所述制作煤矸石烧结砖的方法，其特征在于：步骤d中干燥周期为21.3小时，干燥残余水分小于3％。
7.根据权利要求1或2所述制作煤矸石烧结砖的方法，其特征在于：步骤e中焙烧温度在960-1050℃之间。
8.根据权利要求7所述制作煤矸石烧结砖的方法，其特征在于：所述焙烧时间为30～40小时。
9.根据权利要求1或2所述制作煤矸石烧结砖的方法，其特征在于：对焙烧好的砖孔内塞复合绝热材料。