CN102070790A - 一种硅烷交联聚乙烯绝缘自然交联的方法 - Google Patents
一种硅烷交联聚乙烯绝缘自然交联的方法 Download PDFInfo
- Publication number
- CN102070790A CN102070790A CN 201010615392 CN201010615392A CN102070790A CN 102070790 A CN102070790 A CN 102070790A CN 201010615392 CN201010615392 CN 201010615392 CN 201010615392 A CN201010615392 A CN 201010615392A CN 102070790 A CN102070790 A CN 102070790A
- Authority
- CN
- China
- Prior art keywords
- crosslinked polyethylene
- crosslinking
- organosilane crosslinked
- days
- polyethylene insulation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明提供一种硅烷交联聚乙烯绝缘自然交联的方法，其特征在于将挤包硅烷交联聚乙烯绝缘的绝缘线芯放入透明密闭空间内，该透明、密闭空间内含有适量的水，并且白天用太阳光照射使得绝缘线芯处于大量水蒸汽之中，经过10~90天的该处理，从而实现硅烷交联聚乙烯绝缘的自然交联。通过该自然交联的方法，能够实现60%左右的交联，投资量较小，成本低，能够节约大量成本并能保证产品的性能，具有较好的经济效益。
Description
技术领域
本发明属于电线电缆行业制造加工领域，具体涉及一种硅烷交联聚乙烯绝缘自然交联的方法。
背景技术
聚乙烯制造电线电缆绝缘料的主要缺点是耐温性能差、易燃烧、抗老化性能不是很好，为了提高绝缘材料的综合性能，提高绝缘材料的使用寿命，通过交联的方式使聚烯烃绝缘发生交联，以获得更好的性能。目前聚乙烯交联的方法主要有化学交联法、辐照交联法和硅烷交联法。化学交联法是以有机过氧化物作为交联剂，由于交联过程中所需的温度、压力控制较为苛刻，且对设备要求较高，带来了工艺上的困难；辐照交联是高能辐射方式进行交联，其缺点是设备造价高、安全防护问题复杂，且对材料性能损失大；硅烷交联是集投资少、适应性强和工艺简单于一体的重要交联方法，被广泛使用。
硅烷交联是在导体挤包绝缘线芯的过程中，导体挤包绝缘后经过水槽，水槽带加热装置，水温一般保持在80~90℃，且水槽要保证足够的长度，以保证满足交联度的要求；或者单独采用一个容器，里面装有足够量的水，并带有加热装置，水温保持在80~90℃，且需要一定的时间，以满足交联度的要求；或在采用蒸汽方式进行交联，但交联所需的时间较长。通过以上方式交联投资大，成本较高。
发明内容
本发明提供一种能大量节约资本的方式且能实现交联的方式的硅烷交联聚乙烯绝缘自然交联的方法。
该发明是通过以下技术方案实现的：
一种硅烷交联聚乙烯绝缘自然交联的方法，其特征在于将挤包硅烷交联聚乙烯绝缘的绝缘线芯放入透明、密闭空间内，该透明、密闭空间内含有适量的水，并且白天用太阳光照射使得绝缘线芯处于大量水蒸汽之中，经过10~90天的该处理，从而实现硅烷交联聚乙烯绝缘的自然交联。
上述技术方案中，所述绝缘线芯放在所述密闭透明含水空间中的时间为：夏天经过10~30天、冬天经过30~90天。硅烷交联聚乙烯绝缘用其它硅烷交联聚烯烃绝缘料所替代。
本发明中，将挤包硅烷交联聚乙烯绝缘的绝缘线芯成圈或装盘后，放入密封的装置、容器、房间或空间里，该密封空间材料由白色透明的无机玻璃、有机玻璃或薄膜组成，必须保证具有较好的透光性，密封空间能提供适量的水，在强烈的阳光照射下能形成大量的水蒸气，夏天经过10~30天、冬天经过30~90天就能达到很好的交联效果，经过力学性能检测，交联度能达到60%。
该密封空间所用的密封由白色透明的无机玻璃、有机玻璃或薄膜组成，必须保证具有较好的透光性，以保证密封空间内达到较高的温度，为交联提供必要的能量。
该方法更适宜于夏天，由于夏天的温度较高，且日照时间长，硅烷交联聚乙烯绝缘能在很快的时间完成预期的交联度，而冬天由于日照温度相对较低，且日照时间段，因而需要更长的时间才能达到预期的交联度。
采用该自然交联方法投资少，交联效果较好，对于交货期较长的特别适用。
具体实施方式
实施例1
一种硅烷交联聚乙烯绝缘自然交联的方法，将挤包硅烷交联聚乙烯绝缘的绝缘线芯放入透明、密闭空间内，该透明、密闭空间内含有适量的水，并且白天用太阳光照射使得绝缘线芯处于大量水蒸汽之中，经过10~90天的该处理，从而实现硅烷交联聚乙烯绝缘的自然交联。本实施例中，处理时间可以为15天，30天，50天，70天，85天，本实施例中，密闭空间中的适量水是指，在所处理的时间内，在白天强烈太阳光照射下，在透明、密闭空间内能够形成大量水蒸汽和水的共存体系，
上述技术方案中，所述绝缘线芯放在所述密闭透明含水空间中的时间为：夏天经过10~30天，例如12天，20天，25天，或冬天经过30~90天，例如35天，50天，55天，80天。硅烷交联聚乙烯绝缘用其它硅烷交联聚烯烃绝缘料所替代。
实施例2
一种硅烷交联聚乙烯绝缘自然交联的方法，将绝缘线芯规格为50mm2长度为1km的硅烷交联聚乙烯绝缘线芯成盘后，放入一个密封的装置里，该密封空间材料由白色透明的无机玻璃组成，该玻璃具有较好的透光性，密封空间能提供适量的水，在强烈的阳光照射下能形成大量的水蒸气，夏天经过15天后，通过热延伸测试其交联度。
热延伸试验条件：
烘箱温度：200±3℃；负荷时间：15min；机械应力：20N/cm2。
评价标准：
载荷下最大伸长率：17%；冷却后最大永久伸长率：15%。
经试验检测，载荷下最大伸长率8%，冷却后最大永久伸长率5%。。交联度符合标准要求。
实施例3
一种硅烷交联聚乙烯绝缘自然交联的方法，将绝缘线芯规格为240mm2长度为1km的硅烷交联聚乙烯绝缘线芯成盘后，放入一个密封的装置里，该密封空间材料由白色透明的有机玻璃组成，该玻璃具有较好的透光性，密封空间能提供适量的水，在强烈的阳光照射下能形成大量的水蒸气，夏天经过25天后，通过热延伸测试其交联度。
热延伸试验条件：烘箱温度：200±3℃；负荷时间：15min；机械应力：20N/cm2。
评价标准：载荷下最大伸长率：17%；冷却后最大永久伸长率：15%。
经试验检测，载荷下最大伸长率5%，冷却后最大永久伸长率2%。。交联度符合标准要求。
实施例4
一种硅烷交联聚乙烯绝缘自然交联的方法，将绝缘线芯规格为95mm2长度为1km的硅烷交联聚乙烯绝缘线芯成盘后，放入一个密封的装置里，该密封空间材料由白色透明的无机玻璃组成，该玻璃具有较好的透光性，密封空间能提供适量的水，在强烈的阳光照射下能形成大量的水蒸气，冬天经过45天后，通过热延伸判断其交联度。
热延伸试验条件：
烘箱温度：200±3℃；负荷时间：15min；机械应力：20N/cm2。
评价标准：
载荷下最大伸长率：17%；冷却后最大永久伸长率：15%。
经试验检测，载荷下最大伸长率13%，冷却后最大永久伸长率10%。交联度符合标准要求。
Claims (3)
1.一种硅烷交联聚乙烯绝缘自然交联的方法，其特征在于将挤包硅烷交联聚乙烯绝缘的绝缘线芯放入透明密闭空间内，该透明、密闭空间内含有适量的水，并且白天用太阳光照射使得绝缘线芯处于大量水蒸汽之中，经过10~90天的该处理，从而实现硅烷交联聚乙烯绝缘的自然交联。
2.根据权利要求1所述的一种硅烷交联聚乙烯绝缘自然交联的方法，其特征在于所述绝缘线芯放在所述密闭透明含水空间中的时间为：夏天经过10~30天、冬天经过30~90天。
3.根据权利要求1所述的一种硅烷交联聚乙烯绝缘自然交联的方法，其特征在于：硅烷交联聚乙烯绝缘用其它硅烷交联聚烯烃绝缘料所替代。