CN102066120A - 印刷物及印刷物制造方法 - Google Patents
印刷物及印刷物制造方法 Download PDFInfo
- Publication number
- CN102066120A CN102066120A CN200980123233.8A CN200980123233A CN102066120A CN 102066120 A CN102066120 A CN 102066120A CN 200980123233 A CN200980123233 A CN 200980123233A CN 102066120 A CN102066120 A CN 102066120A
- Authority
- CN
- China
- Prior art keywords
- resin
- styrene
- maleic acid
- hyaline layer
- printed article
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明的印刷物具备基材和透明层，所述透明层至少含有树脂乳液和树脂组合物且配置于基材表面，树脂组合物通过如下方式获得：在有机胺化合物及无机碱性化合物中至少一者的存在下，使树脂溶解于由一种以上选自由水、甘油、二醇、二醇衍生物组成的组群中的物质构成的溶剂。
Description
技术领域
本发明涉及印刷物及印刷物制造方法。
背景技术
近年来，伴随着复印机和印刷装置的性能的提高、及电脑、扫描仪等数字处理机技术的提高，DTP技术得以发展，随之而来的是印刷物的模仿·复制变得能简易而精密地进行。于是，一直以来为抑制印刷物的复制，采用了如下技术，即：印刷微缩文字(micro letter)的技术(参考专利文献1)、形成潜像图案及凹凸结构的技术(参考专利文献2)、多色印刷等技术。
现有技术文献
专利文献
专利文献1：特许第3271474号公报
专利文献2：特开2003-281596号公报
发明内容
发明要解决的问题
所述技术被用于抑制对有价证券或各种证明文件等重要文件印刷物的模仿。
另一方面，对于瓦楞纸箱的图案，也希望采用能够抑制商品模仿的印刷技术。但是，在用通常操作步骤印刷瓦楞纸箱的情况下，由于在瓦楞纸板这样没有平滑性的基材上印刷会出现印刷斑点，采用的是再现性低的印刷方法，该印刷方法不能用2-3色色数来印刷微缩文字等细小文字，因此，就不能采用所述技术来抑制对瓦楞纸箱的图案的模仿。
本发明是鉴于所述问题而做出的，目的在于提供一种能够抑制模仿的印刷物及印刷物制造方法。
解决问题的手段
旨在解决所述问题而做出的本发明，其第1个实施方案的印刷物为具备基材和透明层的印刷物，所述透明层至少含有树脂乳液和树脂组合物且配置于所述基材表面，所述树脂组合物通过如下方式获得：在有机胺化合物及无机碱性化合物中至少一者的存在下，使树脂溶解于由一种以上选自由水、甘油、二醇、二醇衍生物组成的组群中的物质构成的溶剂。另外，树脂组合物中的树脂可以是与树脂乳液中含有的树脂相同的树脂，也可以是与其不同的树脂。
在这样构成的印刷物中，对于形成于基材表面的透明层，其图案(沿基板表面的形状，以下也称为抑制模仿图案)不能用复印机或扫描仪等装置读取。因此，通过预先在印刷物上形成由透明层构成的抑制模仿图案，能抑制对抑制模仿图案的模仿。由此，就能够抑制用复印机等制造形成有该抑制模仿图案的印刷物的赝品的现象。
另外，通过包含树脂组合物，能够很好地用有色墨涂布透明层表面。
另外，由于只形成透明层就能达到抑制模仿的效果，因此不需要用于印刷微缩文字或潜像图案等的高品质的印刷装置，由此能以与通常的印刷步骤相同程度的成本来进行制造。
作为确认抑制模仿图案的方法，例如，可以列举，向透明层照射光，从与基材表面的垂线成角度的斜向目视的方法。
另外，所述基材是指能用有色墨涂布表面的基材，例如，可以列举瓦楞纸板。
另外，所述透明层可以是在形成于基材表面的状态下实质上可以看到基材表面的程度的透明。
另外，作为有机胺化合物，例如，可以列举，单乙醇胺、三乙醇胺等。另外，作为无机碱性化合物，可以列举氢氧化钠、氢氧化钾、氢氧化铵等。
本发明的第2个实施方案的印刷物的特征在于，第1个实施方案的印刷物中的所述树脂乳液含有一种以上选自由松香改性马来酸树脂、丙烯酸系树脂、苯乙烯-丙烯酸系树脂、苯乙烯-马来酸系树脂、苯乙烯-丙烯酸系-马来酸系树脂组成的组群中的树脂和由一种以上选自由水、甘油、二醇、二醇衍生物组成的组群中的物质构成的溶剂。
这样构成的印刷物，能很好地实现抑制对抑制模仿图案的模仿。
本发明的第3个实施方案的印刷物的特征在于，第1或2个实施方案的印刷物中的所述树脂组合物中的树脂是一种以上选自由松香改性马来酸树脂、丙烯酸系树脂、苯乙烯-丙烯酸系树脂、苯乙烯-马来酸系树脂、苯乙烯-丙烯酸系-马来酸系树脂组成的组群中的树脂。
这样构成的印刷物，能够在透明层表面很好地涂布有色墨。
本发明的第4个实施方案的印刷物的特征在于，第1至3任一个实施方案的印刷物中的所述透明层含有体质颜料。
这样构成的印刷物，由于透明层的干燥性提高，因此能够减少透明层形成后干燥所需的时间。由此，例如能通过透明层以外的有色墨等用一个步骤容易地进行印刷。另外，能更好地用有色墨进行透明层表面的涂布。
另外，会有有色墨在基材表面形成有色层的情况。例如，在为瓦楞纸板时，可以进行在表面标示出内容物和制造者的印刷。抑制模仿图案能与这样的有色层形成的图案(以下也称为普通图案)组合使用。具体地，可以认为是下文第5、6个实施方案的印刷物的构成。
本发明的第5个实施方案的印刷物的特征在于，第1至4任一个实施方案的印刷物中的所述基材表面及/或所述透明层表面的至少一部分区域上形成有有色层。
这样构成的印刷物，由于能通过有色层构成的普通图案来隐藏透明层或使抑制模仿图案的形状不清楚，因此，能抑制其他人发现和模仿抑制模仿图案。
另外，本发明的第6个实施方案的印刷物的特征在于，第5个实施方案的印刷物中的所述有色层以全部覆盖所述透明层表面的方式形成。
这样构成的印刷物，由于能通过有色层来隐藏基材表面的透明层，因此可以使得发现抑制模仿图案变得更加困难。
本发明的第7个实施方案的印刷物的特征在于，第1至6任一个实施方案的印刷物中的所述透明层含有紫外线吸收剂。
这样构成的印刷物，由于通过照射紫外线使紫外线吸收剂发光而浮现出来，因此能容易地确认透明层的存在。
本发明的第8个实施方案的印刷物的特征在于，第1至7任一个实施方案的印刷物中的所述透明层含有红外线吸收剂。
这样构成的印刷物，由于在照射红外线时，红外线吸收剂吸收红外线，因此通过使用红外线吸收测定装置就能容易地确认透明层的存在。
本发明的第9个实施方案的印刷物制造方法具备透明层形成工序，所述透明层形成工序通过在基材表面涂布含有树脂乳液及树脂组合物的透明层形成材料来形成透明层，所述树脂组合物通过如下方式获得：在有机胺化合物及无机碱性化合物中至少一者的存在下，使树脂溶解于由一种以上选自由水、甘油、二醇、二醇衍生物组成的组群中的物质构成的溶剂。另外，树脂组合物中的树脂可以是与树脂乳液中含有的树脂相同的树脂，也可以是与其不同的树脂。
这样的印刷物制造方法，能制造与本发明的第1个实施方案的印刷物具有同样效果的印刷物。
另外，作为所述涂布的具体方案，可以应用印刷等一般使用的各种各样的方法。
本发明的第10个实施方案的印刷物制造方法的特征在于，本发明的第9个实施方案的印刷物制造方法中的所述树脂乳液含有一种以上选自由松香改性马来酸树脂、丙烯酸系树脂、苯乙烯-丙烯酸系树脂、苯乙烯-马来酸系树脂、苯乙烯-丙烯酸系-马来酸系树脂组成的组群中的树脂和由一种以上选自由水、甘油、二醇、二醇衍生物组成的组群中的物质构成的溶剂。
这样的印刷物制造方法，能制造与本发明的第2个实施方案的印刷物具有同样效果的印刷物。
本发明的第11个实施方案的印刷物的制造方法的特征在于，本发明的第9或10个实施方案的印刷物制造方法中的所述树脂组合物中的树脂是一种以上选自由松香改性马来酸树脂、丙烯酸系树脂、苯乙烯-丙烯酸系树脂、苯乙烯-马来酸系树脂、苯乙烯-丙烯酸系-马来酸系树脂组成的组群中的树脂。
这样的印刷物制造方法，能制造与本发明的第3个实施方案的印刷物具有同样效果的印刷物。
本发明的第12个实施方案的印刷物制造方法的特征在于，本发明的第9至11任一个实施方案的印刷物制造方法中的所述透明层形成材料含有体质颜料。
这样的印刷物制造方法，能制造与本发明的第4个实施方案的印刷物具有同样效果的印刷物。
本发明的第13个实施方案的印刷物制造方法的特征在于在本发明的第9至12任一个实施方案的印刷物制造方法中具有有色层形成工序，所述有色层形成工序在所述基材表面及/或所述透明层表面的至少一部分区域上形成有色层。
这样的印刷物制造方法，能制造与本发明的第5个实施方案的印刷物具有同样效果的印刷物。
本发明的第14个实施方案的印刷物的制造方法的特征在于，本发明的第13实施方案的印刷物制造方法中的所述有色层以全部覆盖所述透明层表面的方式形成。
这样的印刷物制造方法，能制造与本发明的第6个实施方案的印刷物具有同样效果的印刷物。
本发明的第15个实施方案的印刷物制造方法的特征在于，本发明的第9至14任一个实施方案的印刷物制造方法中的所述透明层形成材料含有紫外线吸收剂。
这样的印刷物制造方法，能制造与本发明的第7个实施方案的印刷物具有同样效果的印刷物。
本发明的第16个实施方案的印刷物制造方法的特征在于，本发明的第9至15任一个实施方案的印刷物制造方法中的所述透明层形成材料含有红外线吸收剂。
这样的印刷物制造方法，能制造与本发明的第8个实施方案的印刷物具有同样效果的印刷物。
本发明的第17个实施方案的印刷物制造方法的特征在于，本发明的第9至16任一个实施方案的印刷物制造方法中的所述透明层形成工序通过柔性版印刷术进行。
这样的印刷物制造方法，能通过柔性版印刷术以较低的成本制造印刷物。
附图说明
图1为显示抑制模仿图案的一个实例的图。
图2为显示普通图案在抑制模仿图案上重合的状态的图。
图3为显示普通图案在抑制模仿图案上重合的状态的剖面图。
图4为显示扫描抑制模仿图案的图像的图。
图5为显示用有色墨印刷抑制模仿图案的图像的图。
图6A-6B为显示扫描抑制模仿图案和普通图案的图像的图。
图7A-7C为显示用数码相机拍摄印刷物的图像的图。
附图标记说明
1...瓦楞纸板、2...抑制模仿图案(透明墨构成的透明层)、3...普通图案(有色墨构成的有色层)
具体实施方式
以下，参照附图对本发明的实施方案进行说明。
(实施例)
在本实施例中，使用以下说明的透明墨(本发明的透明层形成材料)制造在瓦楞纸板上印刷有抑制模仿图案的印刷物。
(1)透明墨的构成
本实施例的透明墨由10重量％溶剂、40重量％体质颜料、40重量％水溶性树脂(本发明的树脂组合物)、10重量％树脂乳液构成。以下对各材料进行详细说明。
·溶剂：水
·体质颜料：碳酸钙
·水溶性树脂：25重量％松香改性马来酸树脂、65重量％水(溶剂)和10重量％作为用于使树脂溶解于水的碱性化合物的三乙胺的混合物
·树脂乳液：40重量％松香改性马来酸树脂和60重量％水(溶剂)的混合物
透明墨是由以上材料混合搅拌而制造的。
(2)印刷方法
将由K面纸(liner)和中芯构成的B楞(flute)纸板用于瓦楞原纸。印刷使用瓦楞印刷通常所使用的柔印折叠糊箱机(flexo folder gluer)，准备3个颜色的墨：所述(1)的透明墨+两个颜色的有色墨。有色墨使用DF04红和DF26墨色。
印刷条件表示在下表1中。设定印刷环境为与通常的瓦楞印刷环境同样的环境。
表1
首先，使用透明墨在瓦楞纸板1上印刷抑制模仿图案2。透明墨在印刷后干燥形成由松香改性马来酸树脂共聚物构成的透明薄膜(本发明的透明层)。
在图1中显示了使用透明墨印刷的抑制模仿图案2的一个实例。该抑制模仿图案2使用JURA社的GSア一トスクリ一ン制成。该软件能将任意文字和符号进行随意配置，用其集合体制成图案，能制成更难以模仿的图案。
接着，如图2所示，使用有色墨与抑制模仿图案2重合而印刷普通图案3。将印刷了普通图案3之后的瓦楞纸板剖面的概略图表示在图3中。普通图案3(有色墨)具有印刷于抑制模仿图案2(透明墨)上的区域和直接印刷于瓦楞纸板1的区域。另外，使用该有色墨印刷的普通图案3相当于本发明的有色层。
另外，这些抑制模仿图案2和普通图案3的印刷是通过在所述柔印折叠糊箱机中经过一次而实施的。
这样印刷的抑制模仿图案2，从正面面向瓦楞纸板1观看，肉眼几乎看不到，但将瓦楞纸板对着倾斜的光就能确认其形状。另外，一目了然，普通图案3印刷于抑制模仿图案2的区域和直接印刷于瓦楞纸板1的区域没有差别，在两个区域均可以良好地印刷。
(3)效果确认试验
对于用所述印刷方法印刷的瓦楞纸板的抑制模仿图案，通过以下方法尝试进行模仿。
(3-1)扫描试验
(3-1-1)
使用扫描仪(精工爱普生株式会社制ES-6000HS)，在分辨率9600dpi下，扫描用透明墨印刷了抑制模仿图案的瓦楞纸板。将扫描的用透明墨印刷的抑制模仿图案的图像显示在图4中。
另外，作为参考，图5显示了用有色墨印刷的本试验的抑制模仿图案的图像。
如图4所示，用透明墨印刷的抑制模仿图案完全不能扫描。可以认为，这是由于扫描仪是对媒介照射垂直方向的光而读取反射的数据的机器，只要从垂直方向不能识别图像，就不能读取。
(3-1-2)
用所述扫描仪对在瓦楞纸板上用透明墨印刷了抑制模仿图案、并在其上用有色墨印刷了普通图案的印刷物进行扫描。将扫描的图像显示在图6A中。可知，在图6A中，没有复制出瓦楞纸板上的抑制模仿图案，不能进行扫描。
另外，作为比较例，将透明墨换成一般的清漆形成的印刷物，同样用上述扫描仪进行扫描。将扫描的图像显示在图6B中。可知，在图6B中，在图6A中看不到的抑制模仿图案组成的「NOCOPY」文字的一部分被复印出来，能够扫描(抑制模仿效果弱)。
(3-2)数码相机拍摄实验
使用数码相机从倾斜角度进行拍摄。图7A、7B中显示了拍摄的印刷在不同瓦楞纸板上的抑制模仿图案的图像。另外，作为参考，图7C显示了拍摄的用有色墨印刷的抑制模仿图案的图像。
根据数码相机的角度，可以进行部分图像拍摄，但无法从该图像中提取出用于复制的图像数据。
(4)真伪判定顺序
对于用透明墨制成抑制模仿图案、再用有色墨印刷了普通图案的瓦楞纸板和扫描该瓦楞纸板制成的赝品瓦楞纸板进行真伪判定，只需要以下1-3步就足矣。
1.有无用透明墨印刷的图案
2.用透明墨印刷的图案是否大致吻合
3.有无图案以外的隐藏文字
(5)发明效果
所述印刷物，由于用透明墨印刷的抑制模仿图案不能用扫描仪读取，因此能够抑制对抑制模仿图案的模仿。由此，能够对制造形成有该抑制模仿图案的印刷物的赝品的现象进行抑制。
另外，所述印刷物，由于能通过有色墨构成的普通图案来隐藏透明墨构成的抑制模仿图案或使抑制模仿图案的形状不清楚，因此，能抑制其他人发现和模仿抑制模仿图案。
另外，由于该印刷物的印刷通常能用1台印刷机印刷，因此，能用通常制造瓦楞纸板的成本来制造印刷物；另外，能够使用现有的瓦楞纸板印刷装置而无需改变，因此也能抑制生产性的降低。
(6)变形例
以上对本发明的实施例进行了说明，但毋庸置疑，本发明并不限于所述实施例，只要属于本发明的技术范围，即可采用各种方案。
例如，在所述实施例中，例举了使用水作为形成透明墨、水溶性树脂、树脂乳液的溶剂的组成，但也可以是使用其他溶剂的组成。例如，根据印刷环境，可以选择性地单独或者联合使用水、甘油、二醇、二醇衍生物等。作为所述二醇成分，可以使用乙二醇、丙二醇、丁二醇、二甘醇等二醇化合物，作为其衍生物，可以使用所述二醇的甲基醚、乙基醚、丙基醚、丁基醚、己基醚、辛基醚等烷基醚化合物、乙酸酯、丁酸酯等酯化物及酯醚化合物。
另外，形成所述透明墨、水溶性树脂、树脂乳液的溶剂的含有率可以设定为：至少一种选自由水0-100重量％、甘油0-80重量％、二醇及二醇衍生物组成的组群中的溶剂0-50重量％。
另外，所述实施例中，例举了使用碳酸钙作为体质颜料的构成，但通常可以直接使用柔性凸版印刷油墨所使用的白色体质颜料。具体地，除碳酸钙以外，也可以使用高岭土、粘土、硫酸钡、氢氧化铝、滑石、氧化钛等。另外，体质颜料可以是只使用这些物质中的一种的构成，也可以是使用多种物质的混合物的构成。
另外，在所述实施例中，作为形成水溶性树脂及树脂乳液的树脂，例示了使用松香改性马来酸树脂的构成，但可以使用选自由松香改性马来酸树脂、丙烯酸系树脂、苯乙烯-丙烯酸系树脂、苯乙烯-马来酸系树脂、苯乙烯-丙烯酸系-马来酸系树脂的树脂。另外，构成水溶性树脂及树脂乳液的树脂可以是相同的树脂也可以是不同的树脂。
另外，作为构成水溶性树脂的碱性化合物，例示了使用三乙胺的构成，但也可以使用除此之外的有机胺化合物(单乙醇胺、三乙醇胺等)，还可以使用无机碱性化合物(氢氧化钠、氢氧化钾、氢氧化铵等)。另外，如果将有机胺化合物用作碱性化合物，则如所述实施例那样会生成烷基铵盐。另一方面，如果使用无机碱性化合物，则会生成树脂的皂化物。无论生成哪种物质，都能与所述实施例一样，和包含于树脂乳液中的树脂共聚物共同形成透明层；另外，能很好地在透明层表面印刷有色墨。
另外，水溶性树脂中的树脂、水及碱性化合物的混合比例为树脂15-25重量％、水60-84重量％、碱性化合物1-15重量％的范围比较好。
另外，树脂乳液中树脂和水的混合比例为树脂40-50重量％、水50-60重量％的范围比较好。
另外，透明墨中各构成要素的含有率为溶剂0-30重量％、体质颜料0-50重量％、水溶性树脂20-50重量％、树脂乳液5-20重量％的范围比较好。不是必须一定要含有体质颜料，但通过含有体质颜料，能提高透明墨的干燥性。另外，可以在该透明墨中添加颜料分散剂、蜡、消泡剂、转移性增强剂、均染剂(leveling agent)等各种添加剂。
另外，透明墨中可以含有紫外线吸收剂和红外线吸收剂中的任意一种或者两种。在含有紫外线吸收剂的情况下，由于通过照射紫外线使紫外线吸收剂发光而浮现出来，因此能容易地确认透明层的存在。另外，在含有红外线吸收剂的情况下，由于在照射红外线时，红外线吸收剂吸收红外线，因此通过使用红外线吸收测定装置就能容易地确认透明层的存在。
另外，由于这样就能容易地确认透明层，因此容易进行具有透明层的瓦楞纸板和没有透明层的赝品瓦楞纸板的真伪判定。
另外，作为所述紫外线吸收剂，例如可以使用，二苯甲酮类、苯并三唑类、丙烯酸酯类、水杨酸酯类等紫外线吸收剂。具体地，可以列举2-(2’-羟基-5’-甲基苯基)苯并三唑(Tinuvin P、Ciba Geigy社制)、2-(2’-羟基-3’-叔丁基-5’-甲基苯基)-5-氯代苯并三唑(Tinuvin 326、Ciba Geigy社制)、2-〔2-羟基-3，5-二(α，α-二甲基苄基)〕苯基〕-2H-苯并三唑(Tinuvin 234、Ciba Geigy社制)等。
另外，作为红外线吸收剂，可以使用花青系色素、酞菁系色素、萘醌系色素、蒽醌系色素、二醇系色素、三苯甲烷系色素等红外线吸收剂。具体地，可以列举金属酞菁颜料。
另外，在所述实施例中，例示了在柔印折叠糊箱机处理一次来印刷透明墨和有色墨的构成，但也可以分别印刷。
另外，在所述实施例中，例示了以一部分与抑制模仿图案重合的方式印刷普通图案的构成，但也可以以覆盖抑制模仿图案整体的方式印刷普通图案，也可以以不与抑制模仿图案重合的方式印刷普通图案。另外，也可以是只将抑制模仿图案印刷于瓦楞纸板上的构成。
特别是，通过以覆盖抑制模仿图案整体的方式印刷普通图案，能由普通图案来隐藏瓦楞纸板表面的抑制模仿图案，因此能使发现抑制模仿图案变得更困难。
Claims (17)
1.一种印刷物，具备基材和透明层，所述透明层至少含有树脂乳液和树脂组合物且配置于所述基材表面，其特征在于，
所述树脂组合物通过如下方式获得：在有机胺化合物及无机碱性化合物中至少一者的存在下，使树脂溶解于由一种以上选自由水、甘油、二醇及二醇衍生物组成的组群中的物质构成的溶剂。
2.权利要求1所述的印刷物，其特征在于，所述树脂乳液含有一种以上选自由松香改性马来酸树脂、丙烯酸系树脂、苯乙烯-丙烯酸系树脂、苯乙烯-马来酸系树脂、苯乙烯-丙烯酸系-马来酸系树脂组成的组群中的树脂和由一种以上选自由水、甘油、二醇及二醇衍生物组成的组群中的物质构成的溶剂。
3.权利要求1或2所述的印刷物，其特征在于，所述树脂组合物中的树脂是一种以上选自由松香改性马来酸树脂、丙烯酸系树脂、苯乙烯-丙烯酸系树脂、苯乙烯-马来酸系树脂、苯乙烯-丙烯酸系-马来酸系树脂组成的组群中的树脂。
4.权利要求1至3任一项所述的印刷物，其特征在于，所述透明层含有体质颜料。
5.权利要求1至4任一项所述的印刷物，其特征在于，在所述基材表面及/或所述透明层表面的至少一部分区域上形成有有色层。
6.权利要求5所述的印刷物，其特征在于，所述有色层以全部覆盖所述透明层表面的方式形成。
7.权利要求1至6任一项所述的印刷物，其特征在于，所述透明层含有紫外线吸收剂。
8.权利要求1至7任一项所述的印刷物，其特征在于，所述透明层含有红外线吸收剂。
9.一种印刷物制造方法，具备透明层形成工序，所述透明层形成工序通过在基材表面涂布含有树脂乳液及树脂组合物的透明层形成材料来形成透明层，其特征在于，
所述树脂组合物通过如下方式获得：在有机胺化合物及无机碱性化合物中至少一者的存在下，使树脂溶解于由一种以上选自由水、甘油、二醇及二醇衍生物组成的组群中的物质构成的溶剂。
10.权利要求9所述的印刷物制造方法，其特征在于，所述树脂乳液含有一种以上选自由松香改性马来酸树脂、丙烯酸系树脂、苯乙烯-丙烯酸系树脂、苯乙烯-马来酸系树脂、苯乙烯-丙烯酸系-马来酸系树脂组成的组群中的树脂和由一种以上选自由水、甘油、二醇及二醇衍生物组成的组群中的物质构成的溶剂。
11.权利要求9或10所述的印刷物制造方法，其特征在于，所述树脂组合物中的树脂是一种以上选自由松香改性马来酸树脂、丙烯酸系树脂、苯乙烯-丙烯酸系树脂、苯乙烯-马来酸系树脂、苯乙烯-丙烯酸系-马来酸系树脂组成的组群中的树脂。
12.权利要求9至11任一项所述的印刷物制造方法，其特征在于，所述透明层形成材料含有体质颜料。
13.权利要求9至12任一项所述的印刷物制造方法，其特征在于具有有色层形成工序，所述有色层形成工序在所述基材表面及/或所述透明层表面的至少一部分区域上形成有色层。
14.权利要求13所述的印刷物制造方法，其特征在于，所述有色层以全部覆盖所述透明层表面的方式形成。
15.权利要求9至14任一项所述的印刷物制造方法，其特征在于，所述透明层形成材料含有紫外线吸收剂。
16.权利要求9至15任一项所述的印刷物制造方法，其特征在于，所述透明层形成材料含有红外线吸收剂。
17.权利要求9至16任一项所述的印刷物制造方法，其特征在于，所述透明层形成工序通过柔性版印刷术进行。